CN108104421A - A kind of hot spring bathing insulation ceramic tile and preparation method thereof - Google Patents
A kind of hot spring bathing insulation ceramic tile and preparation method thereof Download PDFInfo
- Publication number
- CN108104421A CN108104421A CN201711437840.4A CN201711437840A CN108104421A CN 108104421 A CN108104421 A CN 108104421A CN 201711437840 A CN201711437840 A CN 201711437840A CN 108104421 A CN108104421 A CN 108104421A
- Authority
- CN
- China
- Prior art keywords
- brick body
- cavity
- sub
- female
- ceramic tile
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a kind of hot spring bathing insulation ceramic tile and preparation method thereof, and hot spring bathing insulation ceramic tile includes sub- brick body, female brick body, pebble layer；Cementation is passed on left with female brick body to determine, card convex there are three settings on the left of sub- brick body, gap is provided among card convex on the right side of the sub- brick body；The card slot with the cooperation of sub- brick body left surface is provided on the right side of female brick body, gap is provided among card slot, female brick body is internally provided with parallel to bottom surface, and cavity arranged in arrays, cavity is divided into the first cavity, the second cavity, the 3rd cavity, the 4th cavity, the 5th cavity, filled phenolic foam in wherein the second cavity, the interior filling glue powder polyphenyl particle of the 4th cavity；The sub- brick body and female brick body upper surface are covered with pebble layer.The present invention has good heat-insulation effect, makes the characteristics of simple, of low cost.
Description
Technical field
The present invention relates to building construction applications, and in particular to a kind of good heat-insulation effect makes simple, low-cost hot spring
Bathing insulation ceramic tile and preparation method thereof.
Background technology
The health-care effect of hot spring bathing is expansion blood vessel, and active passages through which vital energy circulates accelerates blood circulation, boosts metabolism, from
And reach and set up, body-building, the purpose prevented and cured diseases.Natural hot spring generally all contains one in addition to water temperature is higher
A little chemical compositions are such as：Sodium ion, potassium ion, calcium ion, chlorion, sulfate ion, carbanion etc..In natural hot spring because
Containing there are many chemical element and beneficial gas such as carbon dioxide etc., therefore to many diseases, for example, skin disease, rheumatalgia,
Arthritis, neurogenic disease, gynaecology and angiocardiopathy etc. have preferable auxiliary curative effect, to the Healthy People of no disease, often
It baths in hot spring, also there is relaxing tendons and activating collaterals, relieving fatigue and certain health-care effect.
The construction in the hot spring bathing pond in hot spring bathing place needs the ceramic tile that heat insulation effect protrudes, while needs to have certain
Health-care effect.Traditional ceramic tile is clay and cement, yellow sand mixed sintering is into monolithic thin layer brick body, without heat-insulated well
Heat insulation effect causes hot spring temperature leak very fast, it is necessary to frequently heat hot spring water.
The content of the invention
In view of the deficiencies of the prior art, the present invention provides a kind of hot spring bathing insulation ceramic tiles and its making side
Method has good heat-insulation effect, makes the characteristics of simple, of low cost.
A kind of hot spring bathing insulation ceramic tile, including sub- brick body, female brick body, pebble layer；
Cementation is passed on left on the right side of the sub- brick body with female brick body to determine, there are three card convex, card convexs for setting on the left of sub- brick body
Centre is provided with gap；The card slot with the cooperation of sub- brick body left surface is provided on the right side of female brick body, gap is provided among card slot, it is female
Brick body is internally provided with parallel to bottom surface, and cavity arranged in arrays, and cavity is divided into the first cavity, the second cavity, the 3rd sky
Chamber, the 4th cavity, the 5th cavity, wherein filled phenolic foam in the second cavity, the interior filling glue powder polyphenyl particle of the 4th cavity；Institute
Sub- brick body and female brick body upper surface are stated covered with pebble layer；
The sub- brick body is identical with female brick body thickness；
First cavity, second cavity, the 3rd cavity, the 4th cavity and the 5th cavity are big
Small, shape is identical with spacing；
The height of first cavity is the 1/10~3/20 of female brick body thickness；
The thickness of the pebble layer is the 1/10~1/5 of female brick body thickness；
The sub- brick body and female brick body are determined by acrylic acid adhesive cementation.
A kind of hot spring bathing production method of insulation ceramic tile, comprises the following steps：
Step 1: shaping：By the mixing of clay mud and quartz sand, sub- brick body mold and female brick body mold are respectively put into
In, compression moulding obtains clay mud layer embryo material；
Step 2: high-temperature firing：Above-mentioned clay mud layer embryo material is put into high temperature furnace, 1 is fired in 900~1000 DEG C of high temperature
~4 it is small when, sub- brick body and female brick body are obtained after taking-up；
Step 3: filling：Phenol formaldehyde foam and glue powder polyphenyl particle are filled respectively to the second cavity, the 4th cavity, and
Compacting；
Step 4: close brick：By acrylic acid adhesive even application in the right flank of sub- brick body and the left surface of female brick body, and
By sub- brick body right flank and female brick body left surface contact and be compacted to fix 24 it is small when, sub- brick body and mother's brick body cementation are determined, and obtain
Insulation ceramic tile brick body；
Step 5: make pebble layer：By cement, yellow sand and water in mass ratio 1:0.1~1:0.2~0.6 mixing, and apply
It applies in insulation ceramic tile brick body upper surface；By cobblestone pressing into cement, Mixture with Sand layer upper surface, make cobblestone 1/
4~1/2 expose cement, Mixture with Sand layer；After when 24~72 is small, cement solidification obtains hot spring bathing insulation
Ceramic tile.
The present invention provides a kind of hot spring bathing insulation ceramic tiles and preparation method thereof, have good heat-insulation effect, system
Make the characteristics of simple, of low cost.Insulation ceramic tile brick body is divided into sub- brick body and female brick body by the present invention, is set in female brick body
Five cavitys are put, the thermal insulation material of two kinds of different thermal conductivity coefficients is filled at cavity interval；Hot spring calorie spread once passes through from top to bottom
The thermal insulation material of multilayer difference thermal conductivity coefficient is crossed, hot spring heat is further reduced and is lost in through ceramic tile；Passing through sub- brick body and female brick
Contact level applies acrylic acid adhesive, and sub- brick body and female brick body cementation are determined, and sets pebble layer in brick body upper surface,
Hot spring bathing health care heat insulating ceramic tile and preparation method thereof with outstanding heat-insulated and health-care effect is made.
Description of the drawings
In order to facilitate the understanding of those skilled in the art, the present invention is further illustrated below in conjunction with the accompanying drawings.
Fig. 1 is a kind of structure diagram of hot spring bathing insulation ceramic tile；
Fig. 2 is a kind of brick laying structure schematic diagram of hot spring bathing insulation ceramic tile；
Fig. 3 is a kind of filling brick laying structure schematic diagram of hot spring bathing insulation ceramic tile.
Specific embodiment
The purpose of the present invention can be achieved through the following technical solutions：
A kind of hot spring bathing insulation ceramic tile, referring to Fig. 1-3, including sub- brick body 1, female brick body 2, pebble layer 3；
1 right side of sub- brick body passes on left cementation with female brick body 2 and determines, and sub- 1 left side of brick body is set there are three card convex 4,
Gap is provided among card convex 4；Female 2 right side of brick body is provided with the card slot 5 with the cooperation of sub- 1 left surface of brick body, is set among card slot 5
There is gap, female brick body 2 is internally provided with parallel to bottom surface, and cavity arranged in arrays, and cavity is divided into the first cavity 6, second
Cavity 7, the 3rd cavity 8, the 4th cavity 9, the 5th cavity 10, wherein filled phenolic foam in the second cavity 7, in the 4th cavity 9
Fill glue powder polyphenyl particle；The sub- brick body 1 and female 2 upper surface of brick body are covered with pebble layer 3；
The sub- brick body 1 is identical with 2 thickness of female brick body；
First cavity 6, second cavity 7, the 3rd cavity 8, the 4th cavity 9 and the 5th cavity
10 sizes, shape and spacing are identical；
The height of first cavity 6 is the 1/10~3/20 of 2 thickness of female brick body；
The thickness of the pebble layer 3 is the 1/10~1/5 of 2 thickness of female brick body；
The sub- brick body 1 and female brick body 2 are determined by acrylic acid adhesive cementation.
A kind of hot spring bathing production method of insulation ceramic tile, comprises the following steps：
Step 1: shaping：By the mixing of clay mud and quartz sand, 2 mold of sub- 1 mold of brick body and female brick body is respectively put into
In, compression moulding obtains clay mud layer embryo material；
Step 2: high-temperature firing：Above-mentioned clay mud layer embryo material is put into high temperature furnace, 1 is fired in 900~1000 DEG C of high temperature
~4 it is small when, sub- brick body 1 and female brick body 2 are obtained after taking-up；
Step 3: filling：Phenol formaldehyde foam and glue powder polyphenyl particle are filled respectively to the second cavity 7, the 4th cavity 9,
And it is compacted；
Step 4: close brick：By acrylic acid adhesive even application in the right flank of sub- brick body 1 and the left surface of female brick body 2,
And sub- 1 right flank of brick body and female 2 left surface of brick body contacts and be compacted to fix 24 it is small when, sub- brick body 1 and mother's 2 cementation of brick body
It is fixed, obtain insulation ceramic tile brick body；
Step 5: make pebble layer：By cement, yellow sand and water in mass ratio 1:0.1~1:0.2~0.6 mixing, and apply
It applies in insulation ceramic tile brick body upper surface；By cobblestone pressing into cement, Mixture with Sand layer upper surface, make cobblestone 1/
4~1/2 expose cement, Mixture with Sand layer；After when 24~72 is small, cement solidification obtains hot spring bathing insulation
Ceramic tile.
The operation principle of the present invention：
It is raw material that the phenol formaldehyde foam, which has phenolic resin and fire retardant, smoke suppressant, curing agent, foaming agent, ground
Obturator-type rigid foam particle made of broken；Phenol formaldehyde foam has uniform hole-closing structure, and thermal conductivity factor is low, heat-insulating property
It is good；The glue powder polyphenyl particle is gently expected by rubber powder material, granular polystyrene and cement mixing forms, and curing is ground, adhesive polystyrene
Particle has outstanding heat insulating ability；
A plurality of cavities in mother's brick body 2 is set, is filled in the second cavity 7 and the 4th cavity 9 with outstanding heat insulating ability
Phenol formaldehyde foam and glue powder polyphenyl particle, the first cavity 6, the 3rd cavity 8 and the 5th cavity 10 are interior for air, the thermal conductivity coefficient of air
Less than ceramic tile brick body, there is the effect that good trap heat is transferred；
The 3 upper table EDS maps cobblestone of pebble layer is jammed on or when body is by pressure with foot, stimulates the cave of human body sole
Position helps the active essence and blood of people；
The hot spring bathing insulation ceramic tile is caught in by card convex 4 and the cooperation of card slot 5, is suitble to large area paving linking more
Closely, hot spring heat is lost at ceramic tile gap；
For the present invention using five cavitys are set in ceramic tile, the thermal insulating material of two kinds of different thermal conductivity coefficients is filled at cavity interval
Material；Hot spring calorie spread once passes through the thermal insulation material of multilayer difference thermal conductivity coefficient from top to bottom, is further reduced hot spring heat
It is lost in through ceramic tile.
The present invention provides a kind of hot spring bathing insulation ceramic tiles and preparation method thereof, have good heat-insulation effect, system
Make the characteristics of simple, of low cost.Insulation ceramic tile brick body is divided into sub- brick body and female brick body by the present invention, is set in female brick body
Five cavitys are put, the thermal insulation material of two kinds of different thermal conductivity coefficients is filled at cavity interval；Hot spring calorie spread once passes through from top to bottom
The thermal insulation material of multilayer difference thermal conductivity coefficient is crossed, hot spring heat is further reduced and is lost in through ceramic tile；Passing through sub- brick body and female brick
Contact level applies acrylic acid adhesive, and sub- brick body and female brick body cementation are determined, and sets pebble layer in brick body upper surface,
Hot spring bathing health care heat insulating ceramic tile and preparation method thereof with outstanding heat-insulated and health-care effect is made.
More than content is only to structure example of the present invention and explanation, affiliated those skilled in the art couple
Described specific embodiment does various modifications or additions or substitutes in a similar way, without departing from invention
Structure surmounts scope defined in the claims, is within the scope of protection of the invention.
Claims (7)
1. a kind of hot spring bathing insulation ceramic tile, including sub- brick body (1), female brick body (2), pebble layer (3), feature exists
In：
Cementation is passed on left on the right side of the sub- brick body (1) with female brick body (2) to determine, there are three card convexs for setting on the left of sub- brick body (1)
(4), it is provided with gap among card convex (4)；The card slot (5) with the cooperation of sub- brick body (1) left surface is provided on the right side of female brick body (2),
Gap is provided among card slot (5), female brick body (2) is internally provided with parallel to bottom surface, and cavity arranged in arrays, cavity point
For the first cavity (6), the second cavity (7), the 3rd cavity (8), the 4th cavity (9), the 5th cavity (10), wherein the second cavity
(7) interior filled phenolic foam, the interior filling glue powder polyphenyl particle of the 4th cavity (9)；The sub- brick body (1) and female brick body (2) upper table
Face is covered with pebble layer (3).
A kind of 2. hot spring bathing insulation ceramic tile according to claim 1, which is characterized in that the sub- brick body (1)
It is identical with described female brick body (2) thickness.
A kind of 3. hot spring bathing insulation ceramic tile according to claim 1, which is characterized in that first cavity
(6), second cavity (7), the 3rd cavity (8), the 4th cavity (9) and the 5th cavity (10) size, shape
Shape is identical with spacing.
A kind of 4. hot spring bathing insulation ceramic tile according to claim 1, which is characterized in that first cavity
(6) height is the 1/10~3/20 of female brick body (2) thickness.
A kind of 5. hot spring bathing insulation ceramic tile according to claim 1, which is characterized in that the pebble layer
(3) thickness is the 1/10~1/5 of female brick body (2) thickness.
A kind of 6. hot spring bathing insulation ceramic tile according to claim 1, which is characterized in that the sub- brick body (1)
Determined with female brick body (2) by acrylic acid adhesive cementation.
7. a kind of hot spring bathing production method of insulation ceramic tile, which is characterized in that this method comprises the following steps：
Step 1: shaping：By the mixing of clay mud and quartz sand, sub- brick body (1) mold and female brick body (2) mold are respectively put into
In, compression moulding obtains clay mud layer embryo material；
Step 2: high-temperature firing：Above-mentioned clay mud layer embryo material is put into high temperature furnace, 1~4 is fired in 900~1000 DEG C of high temperature
Hour, sub- brick body (1) and female brick body (2) are obtained after taking-up；
Step 3: filling：Phenol formaldehyde foam and glue powder polyphenyl particle are filled respectively to the second cavity (7), the 4th cavity (9),
And it is compacted；
Step 4: close brick：By acrylic acid adhesive even application in the right flank of sub- brick body (1) and the left surface of female brick body (2),
And sub- brick body (1) right flank and female brick body (2) left surface contacts and be compacted to fix 24 it is small when, sub- brick body (1) and mother's brick body (2)
Cementation is determined, and obtains insulation ceramic tile brick body；
Step 5: make pebble layer：By cement, yellow sand and water in mass ratio 1:0.1~1:0.2~0.6 mixing, and be coated in
Insulation ceramic tile brick body upper surface；By cobblestone pressing into cement, Mixture with Sand layer upper surface, make cobblestone 1/4~
1/2 exposes cement, Mixture with Sand layer；After when 24~72 is small, cement solidification obtains hot spring bathing insulation porcelain
Brick.