CN108103661A - It is a kind of can cutting edge lace - Google Patents
It is a kind of can cutting edge lace Download PDFInfo
- Publication number
- CN108103661A CN108103661A CN201810098644.7A CN201810098644A CN108103661A CN 108103661 A CN108103661 A CN 108103661A CN 201810098644 A CN201810098644 A CN 201810098644A CN 108103661 A CN108103661 A CN 108103661A
- Authority
- CN
- China
- Prior art keywords
- lace
- fabric
- cutting edge
- mass parts
- antibacterial
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to it is a kind of can cutting edge lace, belong to lace fabric technical field.It includes several fabric blocks, it is connected between fabric block and fabric block by spinning threadling, wherein each fabric block is interweaved blended form by radial line and weft, and move 3 millimeters in the first latitude direction in the place of edge strand line, again plus one is locked yarn, and the lock yarn is 40D high stretch yarns, and Jacquard is added to do jacquard weave, line is pressed into, obtain can cutting edge lace.The fabric block of lace fabric of the present invention is combined with the hollow-out fabric actual situation for the composition that spins, and enhances the stereovision of fabric, is had good hygroscopicity, gas permeability, is worn soft comfortable, warmth retention property is good, and alkali resistance is strong.The present invention moves 3 millimeters by place elder generation's latitude direction in edge strand line, then adds a lock yarn, and the lock yarn is 40D high stretch yarns, Jacquard is added to do jacquard weave, line is pressed into, allows lace not cutting edge by hand obtained, and is not in the lace of burr after washing.
Description
Technical field
The present invention relates to it is a kind of can cutting edge lace, belong to lace fabric technical field.
Background technology
China is to have become one of main grown place of global lace fabric at present.Although lace fabric has formed multiple
Industry cluster, but still only only a few lace manufacturing enterprise can carry out the production of square silk face fabric at home.Due to tricot machine pair
Cotton yarn production is not suitable with, at present still without ripe square silk face fabric production technology.The more cotton carding lace fabrics of warp knit be with
Cotton yarn is the lace fabric that primary raw material produces on multi-bar warp knitting machine.Square silk face fabric becomes near due to naturally honest style
Year popular garment material is used not only for making women's shoes, woman style bag, headwear, and is widely used in shirt, one-piece dress, skirt
The clothes such as son, suit, full dress.Present lace production equipment and technology are to the bar evenness of yarn material, intensity, elasticity, yarn
Line filoplume has strict requirements, this causes traditional lace fabric most for filament of synthetic fibre such as polyamide fibre, terylene.Tradition
Lace unite since raw material limits, purposes is limited, and existing multi-bar warp knitting machine and production technology are all using chemical fibre as raw material
What performance requirement was researched and developed.Therefore, in the case of using existing production technology, lace surface is carried out by primary raw material of cotton yarn
Material production is present with the problems such as defect rate is high and equipment fault is frequent.It is produced with Jacquard machine, the production technology manufactured from lace is come
Word belongs to woven lace.The lace of this production of machinery is cleaner and tidier, need to only clean before dyeing, but be deposited in cutting edge
Split the phenomenon that, strand easily splits when consumer takes on hand when most of, and if burr needs to wash not
Splitting just needs manual cutting edge, but the cost of manual cutting edge is higher, and recessive risk is higher.
The content of the invention
The defects of present invention is for present in the prior art, manual cutting edge can not be had to cutting edge by providing after one kind is finished, and
It is not in the lace of burr after washing.
The above-mentioned purpose of the present invention can be carried out by the following technical programs：A kind of lace of cutting edge, including several
Fabric block is connected between fabric block and fabric block by spinning threadling, wherein each fabric block by radial line and weft interweave it is blended and
Into, and 3 millimeters are moved in the first latitude direction in the place of edge strand line, then add a lock yarn, the lock yarn is high-elastic for 40D
Silk, Jacquard is added to do jacquard weave, line is pressed into, obtain can cutting edge lace.
Preferably, the 40D high stretch yarns are cut into slices with 100 mass parts polyamide fibres 40,5-10 mass parts sulfite antioxygens
Agent DLTP, 5-8 mass parts sodium metasilicate, 10-15 mass parts dimethyl amide, 5-15 mass parts copper ammonia fiber, 20-30 mass
Part silver molecular sieve, 45-50 mass parts polycaprolactone are made for raw material using POY-DTY techniques.
Preferably, the radial line is woven by antibacterial dacron monofilament.
Further preferably, the antibacterial dacron monofilament is made by the following method：
Antiseptic and silane coupling agent KH560 are mixed with to obtain pasty slurry, silane coupling agent is starched in paste
Mass fraction in material is 0.8-1.5%；Using the method for double-screw melt blending, pasty slurry and polyester slice are melted
Melt blending and antibacterial section is prepared, wherein, mass fraction of the antiseptic in antibacterial section is 0.05~1%；
Using the method for melt spinning, using antibacterial section as raw material, melt spinning is carried out, through side-blown air cooling, is oiled, the
Drawing-off, winding shaping obtain antibacterial dacron monofilament fibril, and antibacterial dacron monofilament is obtained through second of drawing-off of fibril.
Preferably, the weft is wool fiber, copper ammonia fiber, aethiops vegetabilis fiber blend weave, wherein sheep
Wool fibre, copper ammonia fiber, seaweed Carbon fibe account for weft mass percent 40-60%, 5-20% and 20-55% respectively.
Compared with prior art, the fabric block of lace fabric of the present invention is combined with the hollow-out fabric actual situation for the composition that spins, and is increased
The strong stereovision of fabric, has good hygroscopicity, gas permeability, wears soft comfortable, warmth retention property is good, and alkali resistance is strong.This hair
Bright place elder generation's latitude direction by edge strand line moves 3 millimeters, then adds a lock yarn, and the lock yarn is high-elastic for 40D
Silk, adds Jacquard to do jacquard weave, line is pressed into, and allows lace not cutting edge by hand obtained, and is not in burr after washing
Lace.
Specific embodiment
It is specific embodiments of the present invention below, technical scheme is further described, but the present invention is simultaneously
It is not limited to these embodiments.
Embodiment 1
It is a kind of can cutting edge lace, including several fabric blocks, connected between fabric block and fabric block by spinning threadling, wherein
Each fabric block by radial line and weft interweave it is blended form, and move 3 millimeters in the first latitude direction in the place of edge strand line, then add one
Root lock yarn, the lock yarn be 40D high stretch yarns, Jacquard is added to do jacquard weave, line is pressed into, obtain can cutting edge lace.Institute
The 40D high stretch yarns stated are cut into slices with 100 mass parts polyamide fibres 40,8 mass parts sulfite antioxidant DLTP, 6 mass parts sodium metasilicate,
12 mass parts dimethyl amides, 10 mass parts copper ammonia fiber, 25 mass parts silver molecular sieves, 48 mass parts polycaprolactones are original
Material is made using POY-DTY techniques.
The radial line is woven by antibacterial dacron monofilament, and antibacterial dacron monofilament is made by the following method：By antibacterial
Agent is mixed with to obtain pasty slurry, mass fraction of the silane coupling agent in pasty slurry with silane coupling agent KH560
For 1.2%；Using the method for double-screw melt blending, pasty slurry and polyester slice are carried out melt blending, antibacterial is prepared
Section, wherein, mass fraction of the antiseptic in antibacterial section is 0.5%；Using the method for melt spinning, using antibacterial section as
Raw material carries out melt spinning, through side-blown air cooling, oils, and first time drawing-off, winding shaping obtains antibacterial dacron monofilament fibril,
Antibacterial dacron monofilament is obtained through second of drawing-off of fibril.
The weft is wool fiber, copper ammonia fiber, aethiops vegetabilis fiber blend weave, wherein wool fiber, copper
Ammonia fiber, seaweed Carbon fibe account for weft mass percent 50%, 12% and 38% respectively.
Embodiment 2
It is a kind of can cutting edge lace, including several fabric blocks, connected between fabric block and fabric block by spinning threadling, wherein
Each fabric block by radial line and weft interweave it is blended form, and move 3 millimeters in the first latitude direction in the place of edge strand line, then add one
Root lock yarn, the lock yarn be 40D high stretch yarns, Jacquard is added to do jacquard weave, line is pressed into, obtain can cutting edge lace.Institute
The 40D high stretch yarns stated are cut into slices with 100 mass parts polyamide fibres 40,5 mass parts sulfite antioxidant DLTP, 8 mass parts sodium metasilicate,
10 mass parts dimethyl amides, 15 mass parts copper ammonia fiber, 20 mass parts silver molecular sieves, 50 mass parts polycaprolactones are original
Material is made using POY-DTY techniques.
The radial line is woven by antibacterial dacron monofilament, and antibacterial dacron monofilament is made by the following method：By antibacterial
Agent is mixed with to obtain pasty slurry, mass fraction of the silane coupling agent in pasty slurry with silane coupling agent KH560
For 0.8%；Using the method for double-screw melt blending, pasty slurry and polyester slice are carried out melt blending, antibacterial is prepared
Section, wherein, mass fraction of the antiseptic in antibacterial section is 1%；Using the method for melt spinning, using antibacterial section as original
Material carries out melt spinning, through side-blown air cooling, oils, and first time drawing-off, winding shaping obtains antibacterial dacron monofilament fibril, warp
Second of drawing-off of fibril obtains antibacterial dacron monofilament.
The weft is wool fiber, copper ammonia fiber, aethiops vegetabilis fiber blend weave, wherein wool fiber, copper
Ammonia fiber, seaweed Carbon fibe account for weft mass percent 40%, 20% and 40% respectively.
Embodiment 3
It is a kind of can cutting edge lace, including several fabric blocks, connected between fabric block and fabric block by spinning threadling, wherein
Each fabric block by radial line and weft interweave it is blended form, and move 3 millimeters in the first latitude direction in the place of edge strand line, then add one
Root lock yarn, the lock yarn be 40D high stretch yarns, Jacquard is added to do jacquard weave, line is pressed into, obtain can cutting edge lace.Institute
The 40D high stretch yarns stated are cut into slices with 100 mass parts polyamide fibres 40,10 mass parts sulfite antioxidant DLTP, 5 mass parts silicic acid
Sodium, 15 mass parts dimethyl amides, 5 mass parts copper ammonia fiber, 30 mass parts silver molecular sieves, 45 mass parts polycaprolactones are
Raw material is made using POY-DTY techniques.
The radial line is woven by antibacterial dacron monofilament, and antibacterial dacron monofilament is made by the following method：By antibacterial
Agent is mixed with to obtain pasty slurry, mass fraction of the silane coupling agent in pasty slurry with silane coupling agent KH560
For 1.5%；Using the method for double-screw melt blending, pasty slurry and polyester slice are carried out melt blending, antibacterial is prepared
Section, wherein, mass fraction of the antiseptic in antibacterial section is 0.05%；Using the method for melt spinning, cut into slices with antibacterial
For raw material, melt spinning is carried out, through side-blown air cooling, is oiled, first time drawing-off, winding shaping obtains antibacterial dacron monofilament original
Fibre obtains antibacterial dacron monofilament through second of drawing-off of fibril.
The weft is wool fiber, copper ammonia fiber, aethiops vegetabilis fiber blend weave, wherein wool fiber, copper
Ammonia fiber, seaweed Carbon fibe account for weft mass percent 60%, 5% and 35% respectively.
Above example is merely to illustrate technical scheme rather than limiting the scope of the invention, although ginseng
The present invention is explained in detail according to preferred embodiment, it will be understood by those of ordinary skill in the art that, it can be to the present invention's
Technical solution is modified or replaced equivalently, without departing from the spirit and scope of technical solution of the present invention.
Claims (5)
1. it is a kind of can cutting edge lace, which is characterized in that including several fabric blocks, pass through spinning threadling between fabric block and fabric block
Connection, wherein each fabric block by radial line and weft interweave it is blended form, and move 3 millis in the first latitude direction in the place of edge strand line
Rice, then add a lock yarn, the lock yarn is 40D high stretch yarns, and Jacquard is added to do jacquard weave, line is pressed into, obtaining can cutting edge
Lace.
2. it is according to claim 1 can cutting edge lace, which is characterized in that the 40D high stretch yarns with 100 mass parts brocade
Synthetic fibre 40 is cut into slices, 5-10 mass parts sulfite antioxidant DLTP, 5-8 mass parts sodium metasilicate, two acyl of 10-15 mass parts dimethyl
Amine, 5-15 mass parts copper ammonia fiber, 20-30 mass parts silver molecular sieve, 45-50 mass parts polycaprolactone use POY- for raw material
DTY techniques are made.
3. it is according to claim 1 can cutting edge lace, which is characterized in that the radial line is woven by antibacterial dacron monofilament
It forms.
4. it is according to claim 3 can cutting edge lace, which is characterized in that the antibacterial dacron monofilament is by the following method
It is made：
Antiseptic and silane coupling agent KH560 are mixed with to obtain pasty slurry, silane coupling agent is in pasty slurry
Mass fraction be 0.8-1.5%；Using the method for double-screw melt blending, pasty slurry and polyester slice melt altogether
It is mixed that antibacterial section is prepared, wherein, mass fraction of the antiseptic in antibacterial section is 0.05~1%；
Using the method for melt spinning, using antibacterial section as raw material, melt spinning is carried out, through side-blown air cooling, is oiled, for the first time
Drawing-off, winding shaping obtain antibacterial dacron monofilament fibril, and antibacterial dacron monofilament is obtained through second of drawing-off of fibril.
5. it is according to claim 1 can cutting edge lace, which is characterized in that the weft is wool fiber, cuprammonium is fine
Dimension, aethiops vegetabilis fiber blend weave, and wherein wool fiber, copper ammonia fiber, seaweed Carbon fibe account for weft quality percentage respectively
Than 40-60%, 5-20% and 20-55%.