CN108101440A - A kind of Anti-crack composite cement mortar - Google Patents
A kind of Anti-crack composite cement mortar Download PDFInfo
- Publication number
- CN108101440A CN108101440A CN201711458100.9A CN201711458100A CN108101440A CN 108101440 A CN108101440 A CN 108101440A CN 201711458100 A CN201711458100 A CN 201711458100A CN 108101440 A CN108101440 A CN 108101440A
- Authority
- CN
- China
- Prior art keywords
- parts
- cement mortar
- composite cement
- crack composite
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of Anti-crack composite cement mortars, it is made of the raw material components of following parts by weight:85 95 parts of perlite powder; 20 40 parts of diatomite, 80 100 parts of cement, 15 23 parts of glass bead; 25 parts of calgon; 36 parts of sodium tripolyphosphate, 39 parts of alum, 5 10 parts of tetra calcium aluminoferrite; 16 parts of potassium dihydrogen phosphate; 36 parts of barium metaborate, 15 parts of neopelex, 5 10 parts of postassium hypochlorite; 13 parts of antifoaming agent; 48 parts of polyvinyl alcohol, 6 13 parts of latex powder, 26 parts of retarder; 5 15 parts of aqueous epoxy emulsion; 28 parts of stearic acid, 15 parts of p-aminobenzene sulfonic acid, 13 parts of turpentine oil.Compared with prior art, the Anti-crack composite cement mortar in the present invention has many advantages, such as that effect of prestressed is good, mortar hardness is high, thus substantially increases the performance of cement mortar.
Description
Technical field
The present invention relates to building material technical fields, and in particular to a kind of Anti-crack composite cement mortar.
Background technology
Cement mortar is also known as mortar, is with inorganic coagulation material and fine aggregate and the water Building wood that mix forms in proportion
Material, is chiefly used in building by laying bricks or stones in construction and plastering engineering, to realize building structure and surfacecti proteon, decoration.Traditional mortar material
Material generally comprises cement, water, river sand etc., in order to improve the intensity of building structure screed and crack resistance, can also often fill
Gypsum, lime paste or fibrous reinforcing material.After mortar mixes and in use, should all contain in ash-storage, cement bonded sand in the market
Poor toughness after slurry cures, easily occurs cracking phenomena, causes structure unstable, needs timely to repair when being continuing with, otherwise
It may cause security risk.
The content of the invention
It is an object of the invention to provide a kind of Anti-crack composite cement mortar, which imitates with cracking resistance
The advantages that fruit is good, mortar hardness is high, thus substantially increase the performance of cement mortar.
To achieve the above object, the present invention provides following technical solution:
A kind of Anti-crack composite cement mortar, it is made of the raw material components of following parts by weight:Perlite powder 85-95
Part, 20-40 parts of diatomite, 80-100 parts of cement, 15-23 parts of glass bead, 2-5 parts of calgon, sodium tripolyphosphate 3-6
Part, 3-9 parts of alum, 5-10 parts of tetra calcium aluminoferrite, 1-6 parts of potassium dihydrogen phosphate, 3-6 parts of barium metaborate, detergent alkylate sulphur
Sour sodium 1-5 parts, 5-10 parts of postassium hypochlorite, 1-3 parts of antifoaming agent, 4-8 parts of polyvinyl alcohol, 6-13 parts of latex powder, 2-6 parts of retarder,
5-15 parts of aqueous epoxy emulsion, 2-8 parts of stearic acid, 1-5 parts of p-aminobenzene sulfonic acid, 1-3 parts of turpentine oil.
Preferably, the Anti-crack composite cement mortar is made of the raw material components of following parts by weight:Perlite powder
88 parts, 25 parts of diatomite, 90 parts of cement, 16 parts of glass bead, 3 parts of calgon, 4.5 parts of sodium tripolyphosphate, alum 7
Part, 8 parts of tetra calcium aluminoferrite, 3 parts of potassium dihydrogen phosphate, 5 parts of barium metaborate, 2 parts of neopelex, 9 parts of postassium hypochlorite disappear
1.5 parts of infusion, 6 parts of polyvinyl alcohol, 11 parts of latex powder, 3 parts of retarder, 9 parts of aqueous epoxy emulsion, 4 parts of stearic acid, p-aminophenyl
3 parts of sulfonic acid.
Preferably, the Anti-crack composite cement mortar is made of the raw material components of following parts by weight:Perlite powder
90 parts, 30 parts of diatomite, 85 parts of cement, 18 parts of glass bead, 3 parts of calgon, 3 parts of sodium tripolyphosphate, alum 5
Part, 7 parts of tetra calcium aluminoferrite, 5 parts of potassium dihydrogen phosphate, 4 parts of barium metaborate, 4 parts of neopelex, 5 parts of postassium hypochlorite disappear
1.5 parts of infusion, 6 parts of polyvinyl alcohol, 10 parts of latex powder, 4 parts of retarder, 8 parts of aqueous epoxy emulsion, 6 parts of stearic acid, p-aminophenyl
3 parts of sulfonic acid, 2 parts of turpentine oil.
Preferably, the Anti-crack composite cement mortar is made of the raw material components of following parts by weight:Perlite powder
85 parts, 24 parts of diatomite, 90 parts of cement, 22 parts of glass bead, 3 parts of calgon, 6 parts of sodium tripolyphosphate, alum 9
Part, 6 parts of tetra calcium aluminoferrite, 3 parts of potassium dihydrogen phosphate, 5 parts of barium metaborate, 2 parts of neopelex, 8 parts of postassium hypochlorite disappear
1 part of infusion, 7 parts of polyvinyl alcohol, 12 parts of latex powder, 3 parts of retarder, 8 parts of aqueous epoxy emulsion, 4 parts of stearic acid, p-aminophenyl sulphur
3 parts of acid, 1 part of turpentine oil.
Compared with prior art, the beneficial effects of the invention are as follows:
In addition Anti-crack composite cement mortar in the present invention adds using perlite powder, diatomite and cement as primary raw material
Added with calgon, sodium tripolyphosphate, alum, tetra calcium aluminoferrite, potassium dihydrogen phosphate, barium metaborate, retarder and hard
The chemical constituents such as resin acid, thus make the Anti-crack composite cement mortar in the present invention excellent with good, the mortar hardness height of effect of prestressed etc.
Point substantially increases the performance of cement mortar.
Specific embodiment
With reference to the embodiment technical solution that the present invention will be described in detail, but protection domain is not limited thereto.
Embodiment one:
A kind of Anti-crack composite cement mortar is made of the raw material components of following parts by weight:88 parts of perlite powder, silicon
25 parts of diatomaceous earth, 90 parts of cement, 16 parts of glass bead, 3 parts of calgon, 4.5 parts of sodium tripolyphosphate, 7 parts of alum, iron aluminium
Sour 8 parts of four calcium, 3 parts of potassium dihydrogen phosphate, 5 parts of barium metaborate, 2 parts of neopelex, 9 parts of postassium hypochlorite, antifoaming agent 1.5
Part, 6 parts of polyvinyl alcohol, 11 parts of latex powder, 3 parts of retarder, 9 parts of aqueous epoxy emulsion, 4 parts of stearic acid, p-aminobenzene sulfonic acid 3
Part, 2 parts of turpentine oil.
Embodiment two:
A kind of Anti-crack composite cement mortar is made of the raw material components of following parts by weight:90 parts of perlite powder, silicon
30 parts of diatomaceous earth, 85 parts of cement, 18 parts of glass bead, 3 parts of calgon, 3 parts of sodium tripolyphosphate, 5 parts of alum, iron aluminic acid
Four 7 parts of calcium, 5 parts of potassium dihydrogen phosphate, 4 parts of barium metaborate, 4 parts of neopelex, 5 parts of postassium hypochlorite, antifoaming agent 1.5
Part, 6 parts of polyvinyl alcohol, 10 parts of latex powder, 4 parts of retarder, 8 parts of aqueous epoxy emulsion, 6 parts of stearic acid, p-aminobenzene sulfonic acid 3
Part, 2 parts of turpentine oil.
Embodiment three:
A kind of Anti-crack composite cement mortar is made of the raw material components of following parts by weight:85 parts of perlite powder, silicon
24 parts of diatomaceous earth, 90 parts of cement, 22 parts of glass bead, 3 parts of calgon, 6 parts of sodium tripolyphosphate, 9 parts of alum, iron aluminic acid
Four 6 parts of calcium, 3 parts of potassium dihydrogen phosphate, 5 parts of barium metaborate, 2 parts of neopelex, 8 parts of postassium hypochlorite, 1 part of antifoaming agent,
7 parts of polyvinyl alcohol, 12 parts of latex powder, 3 parts of retarder, 8 parts of aqueous epoxy emulsion, 4 parts of stearic acid, 3 parts of p-aminobenzene sulfonic acid, pine
1 part of fuel-economizing.
Example IV:
A kind of Anti-crack composite cement mortar, it is made of the raw material components of following parts by weight:85 parts of perlite powder,
20 parts of diatomite, 80 parts of cement, 15 parts of glass bead, 2 parts of calgon, 3 parts of sodium tripolyphosphate, 3 parts of alum, iron aluminium
Sour 5 parts of four calcium, 1 part of potassium dihydrogen phosphate, 3 parts of barium metaborate, 1 part of neopelex, 5 parts of postassium hypochlorite, antifoaming agent 1
Part, 4 parts of polyvinyl alcohol, 6 parts of latex powder, 2 parts of retarder, 5 parts of aqueous epoxy emulsion, 2 parts of stearic acid, 1 part of p-aminobenzene sulfonic acid,
1 part of turpentine oil.
Embodiment five:
A kind of Anti-crack composite cement mortar, it is made of the raw material components of following parts by weight:95 parts of perlite powder,
40 parts of diatomite, 100 parts of cement, 23 parts of glass bead, 5 parts of calgon, 6 parts of sodium tripolyphosphate, 9 parts of alum, iron
10 parts of four calcium of aluminic acid, 6 parts of potassium dihydrogen phosphate, 6 parts of barium metaborate, 5 parts of neopelex, 10 parts of postassium hypochlorite, defoaming
3 parts of agent, 8 parts of polyvinyl alcohol, 13 parts of latex powder, 6 parts of retarder, 15 parts of aqueous epoxy emulsion, 8 parts of stearic acid, p-aminophenyl sulphur
5 parts of acid, 3 parts of turpentine oil.
Embodiment six:
A kind of Anti-crack composite cement mortar, it is made of the raw material components of following parts by weight:85 parts of perlite powder,
28 parts of diatomite, 100 parts of cement, 22 parts of glass bead, 5 parts of calgon, 5 parts of sodium tripolyphosphate, 8 parts of alum, iron
7 parts of four calcium of aluminic acid, 3 parts of potassium dihydrogen phosphate, 5 parts of barium metaborate, 4 parts of neopelex, 6 parts of postassium hypochlorite, antifoaming agent 1
Part, 6 parts of polyvinyl alcohol, 11 parts of latex powder, 4 parts of retarder, 13 parts of aqueous epoxy emulsion, 5 parts of stearic acid, p-aminobenzene sulfonic acid 2
Part, 1.6 parts of turpentine oil.
Finally illustrate, the above embodiments are merely illustrative of the technical solutions of the present invention and it is unrestricted, although with reference to compared with
The present invention is described in detail in good embodiment, it will be understood by those of ordinary skill in the art that, it can be to the skill of the present invention
Art scheme is modified or replaced equivalently, and without departing from the objective and scope of the technical program, should all be covered in the present invention
Right among.
Claims (4)
1. a kind of Anti-crack composite cement mortar, which is characterized in that it is made of the raw material components of following parts by weight:Perlite
85-95 parts of powder, 20-40 parts of diatomite, 80-100 parts of cement, 15-23 parts of glass bead, 2-5 parts of calgon, trimerization phosphorus
Sour sodium 3-6 parts, 3-9 parts of alum, 5-10 parts of tetra calcium aluminoferrite, 1-6 parts of potassium dihydrogen phosphate, 3-6 parts of barium metaborate, dodecane
1-5 parts of base benzene sulfonic acid sodium salt, 5-10 parts of postassium hypochlorite, 1-3 parts of antifoaming agent, 4-8 parts of polyvinyl alcohol, 6-13 parts of latex powder, retarder
2-6 parts, 5-15 parts of aqueous epoxy emulsion, 2-8 parts of stearic acid, 1-5 parts of p-aminobenzene sulfonic acid, 1-3 parts of turpentine oil.
2. a kind of Anti-crack composite cement mortar according to claim 1, it is characterised in that:The Anti-crack composite cement mortar
It is made of the raw material components of following parts by weight:88 parts of perlite powder, 25 parts of diatomite, 90 parts of cement, glass bead 16
Part, 3 parts of calgon, 4.5 parts of sodium tripolyphosphate, 7 parts of alum, 8 parts of tetra calcium aluminoferrite, 3 parts of potassium dihydrogen phosphate, inclined boron
Sour 5 parts of barium, 2 parts of neopelex, 9 parts of postassium hypochlorite, 1.5 parts of antifoaming agent, 6 parts of polyvinyl alcohol, 11 parts of latex powder are delayed
Solidifying 3 parts of agent, 9 parts of aqueous epoxy emulsion, 4 parts of stearic acid, 3 parts of p-aminobenzene sulfonic acid, 2 parts of turpentine oil.
3. a kind of Anti-crack composite cement mortar according to claim 1, it is characterised in that:The Anti-crack composite cement mortar
It is made of the raw material components of following parts by weight:90 parts of perlite powder, 30 parts of diatomite, 85 parts of cement, glass bead 18
Part, 3 parts of calgon, 3 parts of sodium tripolyphosphate, 5 parts of alum, 7 parts of tetra calcium aluminoferrite, 5 parts of potassium dihydrogen phosphate, metaboric acid
4 parts of barium, 4 parts of neopelex, 5 parts of postassium hypochlorite, 1.5 parts of antifoaming agent, 6 parts of polyvinyl alcohol, 10 parts of latex powder, slow setting
4 parts of agent, 8 parts of aqueous epoxy emulsion, 6 parts of stearic acid, 3 parts of p-aminobenzene sulfonic acid, 2 parts of turpentine oil.
4. a kind of Anti-crack composite cement mortar according to claim 1, it is characterised in that:The Anti-crack composite cement mortar
It is made of the raw material components of following parts by weight:85 parts of perlite powder, 24 parts of diatomite, 90 parts of cement, glass bead 22
Part, 3 parts of calgon, 6 parts of sodium tripolyphosphate, 9 parts of alum, 6 parts of tetra calcium aluminoferrite, 3 parts of potassium dihydrogen phosphate, metaboric acid
5 parts of barium, 2 parts of neopelex, 8 parts of postassium hypochlorite, 1 part of antifoaming agent, 7 parts of polyvinyl alcohol, 12 parts of latex powder, retarder
3 parts, 8 parts of aqueous epoxy emulsion, 4 parts of stearic acid, 3 parts of p-aminobenzene sulfonic acid, 1 part of turpentine oil.