CN108085111A - A kind of preparation method of clean type film lubrication agent - Google Patents
A kind of preparation method of clean type film lubrication agent Download PDFInfo
- Publication number
- CN108085111A CN108085111A CN201711409109.0A CN201711409109A CN108085111A CN 108085111 A CN108085111 A CN 108085111A CN 201711409109 A CN201711409109 A CN 201711409109A CN 108085111 A CN108085111 A CN 108085111A
- Authority
- CN
- China
- Prior art keywords
- clean type
- lubrication agent
- preparation
- type film
- film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of preparation methods of clean type film lubrication agent, belong to technical field of lubricant.Technical scheme main points are：A kind of preparation method of clean type film lubrication agent, the raw material matched by following weight percent are uniformly mixed and are made at room temperature：Perfluoropolyether 20%~30%, Ultra-low molecular weight polytetrafluoroethylene PTFE particle 15%~25%, polyimides 5%~8%, surplus is fluorocarbon solvent.The use temperature range of clean type film lubrication agent produced by the present invention is wide, can be used at 60 DEG C~260 DEG C；Film forming speed is fast, good leveling property, and 10~15s forms dried layer film；Film layer insulation is non-conductive；Film layer does not flow diffusion, does not adsorb dust particle；The erosion of waterproof and other liquid；To use environment without destruction, nontoxic plurality of advantages.
Description
Technical field
The invention belongs to technical field of lubricant, and in particular to a kind of preparation method of clean type film lubrication agent.
Background technology
In electric appliance and electronic equipment, precision instrument, clock and watch, musical instrument, automobile etc., it is necessary to which a kind of clean, is pollution-free, no
The conductive and significant lubricant of lubricating action, this lubricant can penetrate into and with reference to metal, paper, wood, glass, rubber etc. its
The surface of its overwhelming majority forms the film of one layer of non-pickup to prevent to stick and then reduce friction, it should have good
Thermal stability and chemical stability.It applies in electronic device, energy self-assembling formation insulating layer prevents conduction.Existing product is applicable in
Scope face is narrow, and it is therefore necessary to develop one kind there is clean type, lubricity, insulating properties, temperature tolerance, security and film forming uniformly to have
All multifunctional film lubrication agent.
The content of the invention
The technical problem to be solved by the present invention is to provide a kind of clean type films simple for process, formula is reasonable and environmental-friendly
The preparation method of lubricant.
It is of the invention to adopt the following technical scheme that solve above-mentioned technical problem, a kind of preparation side of clean type film lubrication agent
Method, it is characterised in that the raw material matched by following weight percent is uniformly mixed and is made at room temperature：Perfluoropolyether 20%~
30%th, Ultra-low molecular weight polytetrafluoroethylene (PTFE)（PTFE）Particle 15%~25%, polyimides 5%~8%, surplus are fluorocarbon solvent.
Further preferably, the preparation method of the clean type film lubrication agent, it is characterised in that matched by following weight percent
Raw material be uniformly mixed and be made at room temperature：Perfluoropolyether 30%, Ultra-low molecular weight polytetrafluoroethylene (PTFE)（PTFE）Particle
25%th, polyimides 5%, surplus are fluorocarbon solvent.
Further preferably, the perfluoroalkyl polyether is distillate of the boiling point at 240~260 DEG C, and the molecular weight of polyimides is 300
~400.
Perfluoropolyether used in the present invention is distillate of the boiling point at 240~260 DEG C, has good high and low temperature,
It is non-combustible, the advantages of nontoxic and low volatility；Ultra-low molecular weight polytetrafluoroethylene (PTFE)（PTFE）Particle is that tetrafluoroethene is aggregated anti-
A kind of speciality polymer material of prepared by answering has the advantages that high temperature resistant, low temperature resistant, strong alkali-acid resistance, high lubrication and nontoxic.
Polyimides for molecular weight in the range of 300~400, have good wear resistence and high temperatures and certain adhesiveness, favorably
In the lasting holding of lubricant film layer.
The present invention has the following advantages compared with prior art：Clean type film lubrication agent produced by the present invention, has the advantage that
More, the scope of application is wide, disclosure satisfy that the needs of all trades and professions such as electronic equipment, mechanical equipment, automobile, precision instrument, universal
By force.Use temperature range is wide, can be used at -60 DEG C~260 DEG C；Film forming speed is fast, good leveling property, and 10~15s forms dried layer
Film；Film layer insulation is non-conductive；Film layer does not flow diffusion, does not adsorb dust particle；The erosion of waterproof and other liquid；To using
Environment is without destruction, nontoxic plurality of advantages.
Specific embodiment
The above of the present invention is described in further details by the following examples, but this should not be interpreted as to this
The scope for inventing above-mentioned theme is only limitted to following embodiment, and all technologies realized based on the above of the present invention belong to this hair
Bright scope.
Embodiment
1st, by 23kg perfluoropolyether, 15kg Ultra-low molecular weight polytetrafluoroethylene (PTFE)（PTFE）Particle, 5kg polyimides, 57kg
Fluorocarbon solvent is uniformly mixed obtained clean type film lubrication agent at room temperature.
2nd, by 23kg perfluoropolyether, 20kg Ultra-low molecular weight polytetrafluoroethylene (PTFE)（PTFE）Particle, 5kg polyimides, 52kg
Fluorocarbon solvent is uniformly mixed obtained clean type film lubrication agent at room temperature.
3rd, by 29kg perfluoropolyether, 15kg Ultra-low molecular weight polytetrafluoroethylene (PTFE)（PTFE）Particle, 8kg polyimides, 48kg
Fluorocarbon solvent is uniformly mixed obtained clean type film lubrication agent at room temperature.
The use temperature range of clean type film lubrication agent is wide made from above-described embodiment, can make at -60 DEG C~260 DEG C
With；Film forming speed is fast, good leveling property, and 10~15s forms dried layer film；Film layer insulation is non-conductive；Film layer does not flow diffusion, does not inhale
Attached dust particle；The erosion of waterproof and other liquid；To use environment without destruction, nontoxic plurality of advantages.
Have been shown and described above the basic principle of the present invention, main feature and advantage, do not depart from spirit of the invention and
On the premise of scope, the present invention also has various changes and modifications, these changes and improvements both fall within claimed invention
Scope.
Claims (3)
1. a kind of preparation method of clean type film lubrication agent, it is characterised in that the raw material matched by following weight percent is at room temperature
It is uniformly mixed and is made：Perfluoropolyether 20%~30%, Ultra-low molecular weight polytetrafluoroethylene PTFE particle 15%~25%, polyamides
Imines 5%~8%, surplus are fluorocarbon solvent.
2. the preparation method of clean type film lubrication agent according to claim 1, it is characterised in that matched somebody with somebody by following weight percent
The raw material of ratio is uniformly mixed and is made at room temperature：Perfluoropolyether 30%, Ultra-low molecular weight polytetrafluoroethylene PTFE particle
25%th, polyimides 5%, surplus are fluorocarbon solvent.
3. the preparation method of the face washing mud according to claim 1 for high-efficiency cleaning face, it is characterised in that：The fluorine
Polyethers is distillate of the boiling point at 240~260 DEG C, and the molecular weight of polyimides is 300~400.