CN107384529A - A kind of electrically conductive type ultra high temperature lubricating grease and preparation method thereof - Google Patents
A kind of electrically conductive type ultra high temperature lubricating grease and preparation method thereof Download PDFInfo
- Publication number
- CN107384529A CN107384529A CN201710579902.9A CN201710579902A CN107384529A CN 107384529 A CN107384529 A CN 107384529A CN 201710579902 A CN201710579902 A CN 201710579902A CN 107384529 A CN107384529 A CN 107384529A
- Authority
- CN
- China
- Prior art keywords
- high temperature
- lubricating grease
- electrically conductive
- ultra high
- conductive type
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of electrically conductive type ultra high temperature lubricating grease, it is made up of the raw material of following mass fraction:Base oil 20% 75%;Thickening agent 5% 30%;Viscous silicone fluid 5% 35%;Conductive agent 5% 20%;Lubricant 5% 17%;Antioxidant 1% 3%.It can meet the high temperature resistant of plant equipment under some specified conditions, lubrication, anti-oxidant, adhesion requirement the present invention is to provide a kind of ultra high temperature lubricating grease and ensure that the lubricant effect of equipment extends its service life.The present invention is to provide a kind of electrically conductive type ultra high temperature lubricating grease, has good electric conductivity, excellent heat-resisting quantity, lubricity, inoxidizability, structural stability.Overcome heat resistance in existing grease product is poor, do not possess the characteristics of pyroconductivity and solve the problems, such as lubricating grease it is dry and cracked under the high temperature conditions, point oil, hardening, lubricant effect failure etc..
Description
Technical field
The present invention relates to lubriation material technical field, and in particular to a kind of electrically conductive type ultra high temperature lubricating grease and its preparation side
Method.
Background technology
Electrically conductive type lubricating grease is seen as each position that a kind of new electrical material is widely used in electrical device
And certain conduction, drag reduction, anti-corrosion and other effects can be reached on the place of the connecing face of each Power tabs.
Ultra high temperature lubricating grease is a kind of resistance to hot conditions stability inferior, oxidation stability, mechanical stability, extreme pressure mill
The higher lubriation material of requirement such as property, adhesiveness, lubricity.Continuous development plant equipment with the modernization of industry etc. needs to moisten
Sliding position uses heat resistance and the electric conductivity of privileged sites for the requirement more and more higher of lubricating grease to lubricating grease
Higher requirement can be proposed.Softening under the high temperature conditions, point oily, dry and cracked, molten mostly be present in existing ultra high temperature lubricating grease
The behaviors such as change, volatilization, hardening, conductive capability deficiency cause lubricating grease lose lubrication or conduction, drag reduction, save and other effects cause machine
Tool equipment occurs abrasion, sinters, be seizing, can not work, largely repair, and reduces the use longevity of plant equipment and privileged sites
Life etc..Therefore a kind of electrically conductive type ultra high temperature lubricating grease product is produced for industries such as machining, electrical equipment, office instruments
For there is very big demand space.
The content of the invention
The present invention is for problem and shortage existing for lubricating grease in the prior art, there is provided a kind of electrically conductive type superelevation is gentle
Consistent lubricant, mechanical stability is good under the high temperature conditions, antioxygenic property is excellent and production phenomena such as without point oily, dry and cracked, coking
It is raw.The characteristics of protrusion of the lubricating grease be use a kind of viscous silicone fluid substitute the tackifier used in existing lubricating grease with
Make up high-viscosity polymer existing coking, dry and crack problemses under the conditions of 300 DEG C of high temperature above.Can be using viscous silicone fluid
Improve viscosity, prevent point oil in the case of can be with good associativity so that made by high temperature action and silica
Standby lubricating grease has more preferable heat-resisting quantity, lubricity, resists a point oil, anti-chap, without performances such as hardening.
In order to reach above-mentioned purpose, one aspect of the present invention is achieved through the following technical solutions:
A kind of electrically conductive type ultra high temperature lubricating grease, it is characterised in that following quality point is included on the basis of lubricating grease quality
Several raw material compositions:Base oil 20%-75%;Thickening agent 5%-30%;Viscous silicone fluid 5%-35%;Conductive agent;5%-
20%;Lubricant 5%-17%;Antioxidant 1%-3%.
One or more mixtures of the base oil of the present invention in silicone oil, artificial oil, synthesizing ester oil, it is excellent
Elect phenyl silicone oil as.
Thickening agent of the present invention is one or more in silica, boron nitride, graphite, polytetrafluoroethylene (PTFE)
Mixture, preferably silica.
Viscous silicone fluid of the present invention is selected from high viscosity methyl-silicone oil, high viscosity phenyl silicone oil, high viscosity ethyl silicon
Oil etc., preferably high viscosity methyl-silicone oil.
The one kind of conductive agent of the present invention in electrically conductive polyaniline, conductive metal powder, conducting metal oxide
Or a variety of mixtures, preferably electrically conductive polyaniline.
Antioxidant of the present invention is selected from Diphenylsilanediol.
One or more mixing of the lubricant of the present invention in boron nitride, polytetrafluoroethylene (PTFE), silica gel, graphite
Thing.
Second aspect of the present invention provides the preparation method of above-mentioned electrically conductive type ultra high temperature lubricating grease, and it comprises the following steps:
(1) take base oil add normal-pressure reaction kettle in and start to warm up while stirring add thickening agent and be warming up to 120 DEG C-
150 DEG C or so, the reaction time is 30min-120min or so.
(2) continue heat up stirring reaction to 180 DEG C -200 DEG C or so start simultaneously at addition viscous silicone fluid, antioxygen
Agent, lubricant, conductive agent, stirring reaction 60min-120min or so, finally it is cooled to 90 DEG C -120 DEG C or so;
(3) mixture obtained above is cooled down, homogeneous/grinding, filtering can obtain a kind of electrically conductive type superelevation
Temperature lubricating grease.
A kind of electrically conductive type ultra high temperature lubricating grease of the present invention, its outstanding feature are using viscous silicone fluid come instead of existing
There are the tackifier added in ultra high temperature lubricating grease preparation process.Because the tackifier in existing ultra high temperature lubricating grease are mostly
The coking of grease product, dry and cracked and point oily phenomenon generation can be caused under its hot conditions more than 300 DEG C of high polymer;
So the present invention is by adding high viscosity methyl-silicone oil, preferably the prepared one kind of combination can with the progress of silica thickening agent
Conductivity type ultra high temperature lubricating grease can tolerate 300 degree of high temperature above, have excellent inoxidizability, structure stability, lubricity, chemistry
Stability, electric conductivity etc..Superhigh temperature conductive grease prepared by the present invention without obvious dropping point, tortoise does not occur under the high temperature conditions
Split, divide phenomena such as oil, hardening.
Embodiment
The following examples are that the present invention is expanded on further, but present disclosure not limited to this.Explanation of the invention
Embodiment in book is only used for that the present invention will be described, and it does not play restriction effect to protection scope of the present invention.This
The protection domain of invention is only defined by the claims, those skilled in the art institute on the basis of embodiment disclosed by the invention
Any omission, replacement or the modification made fall within protection scope of the present invention.
Example 1
The electrically conductive type ultra high temperature lubricating grease is prepared using component as described below:Based on the gross mass of lubricating grease, benzene
Base silicone oil:35%;High viscosity methyl-silicone oil:35%;Silica:6%;Graphite:11.5%;Boron nitride:4.5%;Conduction is poly-
Aniline:7%;Diphenylsilanediol:1%.
A kind of preparation method of electrically conductive type ultra high temperature lubricating grease of the present invention is as follows:
(1) take phenyl silicone oil to add in normal-pressure reaction kettle and start to warm up and add SiO 2 powder while stirring to heating
To 120 DEG C -150 DEG C or so, the reaction time is 30min-120min or so,
(2) stirring reaction that continues to heat up starts simultaneously at addition high viscosity methyl-silicone oil, two to 180 DEG C -200 DEG C or so
Phenyl dihydroxy base silane, graphite, boron nitride, electrically conductive polyaniline, stirring reaction 60min-120min or so, are finally cooled to 90
DEG C -120 DEG C or so;
(3) grease product obtained above is cooled down, homogeneous/grinding, filtering can obtain a kind of electrically conductive type
Ultra high temperature lubricating grease.
Example 2
The electrically conductive type ultra high temperature lubricating grease is prepared using component as described below:Based on the gross mass of lubricating grease, benzene
Base silicone oil:62%;High viscosity methyl-silicone oil:9%;Silica:7%;Graphite:10.5%;Boron nitride:3%;Metal aoxidizes
Thing:7%;Diphenylsilanediol:1.5%.
A kind of preparation method of electrically conductive type ultra high temperature lubricating grease of the present invention is as follows:
(1) take phenyl silicone oil to add in normal-pressure reaction kettle and start to warm up and add SiO 2 powder while stirring to heating
To 120 DEG C -150 DEG C or so, the reaction time is 30min-120min or so,
(2) stirring reaction that continues to heat up starts simultaneously at addition high viscosity methyl-silicone oil, two to 180 DEG C -200 DEG C or so
Phenyl dihydroxy base silane, graphite, boron nitride, metal oxide, stirring reaction 60min-120min or so, are finally cooled to 90
DEG C -120 DEG C or so,
(3) grease product obtained above is cooled down, homogeneous/grinding, filtering can obtain a kind of electrically conductive type
Ultra high temperature lubricating grease.
Example 3
The electrically conductive type ultra high temperature lubricating grease is prepared using component as described below:Based on the gross mass of lubricating grease, benzene
Base silicone oil:60%;High viscosity methyl-silicone oil:9%;Silica:9%;Graphite:14%;Electrically conductive polyaniline:7%;Diphenyl two
Silicol:1%.
A kind of preparation method of electrically conductive type ultra high temperature lubricating grease of the present invention is as follows:
(1) take phenyl silicone oil to add in normal-pressure reaction kettle and start to warm up and add SiO 2 powder while stirring to heating
To 120 DEG C -150 DEG C or so, the reaction time is 30min-120min or so,
(2) stirring reaction that continues to heat up starts simultaneously at addition high viscosity methyl-silicone oil, two to 180 DEG C -200 DEG C or so
Phenyl dihydroxy base silane, graphite, boron nitride, electrically conductive polyaniline, stirring reaction 60min-120min or so, are finally cooled to 90
DEG C -120 DEG C or so,
(3) grease product obtained above is cooled down, homogeneous/grinding, filtering can obtain a kind of electrically conductive type
Ultra high temperature lubricating grease.
Example 4
The electrically conductive type ultra high temperature lubricating grease is prepared using component as described below:Based on the gross mass of lubricating grease, benzene
Base silicone oil:59%;High viscosity methyl-silicone oil:12%;Silica:7%;Boron nitride:3%;Polytetrafluoroethylene (PTFE):10.5%;Lead
Conducting polyaniline:7%;Diphenylsilanediol:1.5%.
A kind of preparation method of electrically conductive type ultra high temperature lubricating grease of the present invention is as follows:
(1) take phenyl silicone oil to add in normal-pressure reaction kettle and start to warm up and add SiO 2 powder while stirring to heating
To 120 DEG C -150 DEG C or so, the reaction time is 30min-120min or so,
(2) stirring reaction that continues to heat up starts simultaneously at addition high viscosity methyl-silicone oil, two to 180 DEG C -200 DEG C or so
Phenyl dihydroxy base silane, polytetrafluoroethylene (PTFE), boron nitride, electrically conductive polyaniline, stirring reaction 60min-120min or so, finally cool
To 90 DEG C -120 DEG C or so,
(3) grease product obtained above is cooled down, homogeneous/grinding, filtering can obtain a kind of electrically conductive type
Ultra high temperature lubricating grease.
Properties of product measure acquired results are as follows prepared by the present invention:
The foregoing examples are merely illustrative of the technical concept and features of the invention, its object is to allow the person skilled in the art to be
Present disclosure can be understood and implemented according to this, it is not intended to limit the scope of the present invention.It is all smart according to the present invention
The equivalent transformation or modification that refreshing essence is done, should all be included within the scope of the present invention.
Claims (8)
1. a kind of electrically conductive type ultra high temperature lubricating grease, it is characterised in that it is made up of the raw material of following mass fraction:Base oil
20%-75%;Thickening agent 5%-30%;Viscous silicone fluid 5%-35%;Conductive agent;5%-20%;Lubricant 5%-17%;It is anti-
Oxygen agent 1%-3%.
2. electrically conductive type ultra high temperature lubricating grease according to claim 1, it is characterised in that the base oil be selected from silicone oil,
One or more mixtures in artificial oil, synthesizing ester oil.
3. electrically conductive type ultra high temperature lubricating grease according to claim 1, it is characterised in that described thickening agent is selected from dioxy
One or more mixtures in SiClx, boron nitride, graphite, polytetrafluoroethylene (PTFE).
4. electrically conductive type ultra high temperature lubricating grease according to claim 1, it is characterised in that described viscous silicone fluid is selected from
High viscosity methyl-silicone oil, high viscosity phenyl silicone oil, high viscosity ethyl silicon oil.
5. electrically conductive type ultra high temperature lubricating grease according to claim 1, it is characterised in that described conductive agent is selected from conduction
One or more mixtures in polyaniline, conductive metal powder, conducting metal oxide.
6. electrically conductive type ultra high temperature lubricating grease according to claim 1, it is characterised in that described lubricant is selected from nitridation
One or more mixtures in boron, polytetrafluoroethylene (PTFE), silica gel, graphite.
7. a kind of electrically conductive type ultra high temperature lubricating grease according to right 1, it is characterised in that described antioxidant is diphenyl
Dihydroxy base silane.
8. preparing a kind of preparation method of electrically conductive type ultra high temperature lubricating grease as described in claim 1-7, it includes following step
Suddenly:
(1) take base oil to add in normal-pressure reaction kettle and start to warm up and add thickening agent while stirring and be warming up to 120 DEG C -150
DEG C or so, the reaction time is 30min-120min or so.
(2) continue heat up stirring reaction to 180 DEG C -200 DEG C or so start simultaneously at addition viscous silicone fluid, antioxidant, profit
Lubrication prescription, conductive agent, stirring reaction 60min-120min or so, finally it is cooled to 90 DEG C -120 DEG C or so;
(3) mixture obtained above is cooled down, homogeneous/grinding, to can obtain a kind of electrically conductive type superelevation gentle for filtering
Consistent lubricant.