CN108084770A - A kind of waterproof putty powder and preparation method thereof - Google Patents
A kind of waterproof putty powder and preparation method thereof Download PDFInfo
- Publication number
- CN108084770A CN108084770A CN201810151189.2A CN201810151189A CN108084770A CN 108084770 A CN108084770 A CN 108084770A CN 201810151189 A CN201810151189 A CN 201810151189A CN 108084770 A CN108084770 A CN 108084770A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- water
- cellulose
- putty
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of waterproof putty powder and preparation method thereof, in terms of parts by weight, including following components：40 55 parts of white cement, 35 50 parts of talcum powder, grey 30 40 parts of calcium, 13 parts of cellulose ether, water-fast 25 parts of rubber powder, 10 15 parts of bentonite, 13 parts of cellulose, 12 parts of hydroxyethyl cellulose, 0.1 0.4 parts of tributyl phosphate.White cement, talcum powder in the invention etc. and additive synergistic effect improve the water proofing property of powder of lacquer putty for use on, and without toxic additive, have fewer environmental impacts, meet the requirement of green product.
Description
Technical field
The present invention relates to a kind of powder of lacquer putty for use on more particularly to a kind of waterproof putty powder and preparation method thereof.
Background technology
Powder of lacquer putty for use on is before paint class is constructed, to the levelling pulverulent material in a kind of surface that construction surface is pre-processed, main purpose
Be the hole for filling construction surface and the curve deviation for correcting construction surface, lay a solid foundation to obtain uniform, smooth lacquer painting, generally by
The compositions such as base-material, filler, water and auxiliary agent.
Existing most of powder of lacquer putty for use on waterproof effects are bad, and the moisture in air or the rainwater when exterior wall uses all can
The using effect of powder of lacquer putty for use on is reduced, influences paint class construction of the later stage to wall, and existing powder of lacquer putty for use on weatherability is poor.
The content of the invention
To solve the above-mentioned problems, it is an object of the present invention to provide a kind of waterproof putty powder and preparation method thereof, solutions
The problem of existing powder of lacquer putty for use on waterproof effect of having determined is bad, while improve the cementability of powder of lacquer putty for use on.
The present invention is using technical solution：
A kind of waterproof putty powder, in terms of parts by weight, including following components：
40-55 parts of white cement, 35-50 parts of talcum powder, grey calcium 30-40 parts, 1-3 parts of cellulose ether, water-fast rubber powder 2-5 parts,
10-15 parts of bentonite, 1-3 parts of cellulose, 1-2 parts of hydroxyethyl cellulose, 0.1-0.4 parts of tributyl phosphate.
By above technical scheme, water-fast rubber powder is added in powder of lacquer putty for use on, there is waterproof, this is because waterproof glue
With bentonitic surface physicochemical work occurs for powder and bentonitic synergistic effect, the surfactant in water-fast rubber powder
With on the one hand the surfactant of water-fast rubber powder is attracted on bentonitic surface, adds its current potential, so as in powder of lacquer putty for use on
Waterproof can preferably be played the role of by making when putty is coated onto on metope, and also improve disperseing, be plasticized, filling out for putty simultaneously
The effect filled and be homogenized, the compound dense micro-structure for making putty of the two, in addition, water-fast rubber powder can be shown with bentonitic introducing
Writing reduces bleeding, so that pore structure is also improved, at the same time, bentonite inherently has good heat resistance, expansion
Property and shrinkage, while there is the effect of water swelling, by itself expanded constituents, voluntarily adaptive compensation blockage effect, reduction are split
The generation of line so as to prevent the infiltration of water, plays the effect of waterproof；Another aspect is that the addition of grey calcium can fill putty structure
Internal gap and defect reduce the quantity of water-fast rubber powder filling gap and defect, water-fast rubber powder are allow fully to wrap up putty,
Connection networking is so easier under the relatively low volume of water-fast rubber powder, the anti-permeability performance of putty is further improved, makes powder of lacquer putty for use on
Effect with waterproof；At the same time, the main component of grey calcium is the mixture of Ca (OH) 2, CaO and a small amount of CaCO3, and grey calcium adds
Enter into powder of lacquer putty for use on, with the coating film forming of powder of lacquer putty for use on, calcium hydroxide (calcium oxide also becomes calcium hydroxide after meeting water) can be with sky
CO2 reactions generation calcium carbonate crystal in gas and generate intensity, and then can be provided for putty powder component in film certain
Caking property, and assign powder of lacquer putty for use on significant water proofing property, and grey calcium is at low cost, for good waterproof performance in powder of lacquer putty for use on.
Preferably, in terms of parts by weight, including following components：45-50 parts of white cement, 40-45 parts of talcum powder, grey calcium 35-
40 parts, 2-3 parts of cellulose ether, water-fast rubber powder 3-4 parts, 12-14 parts of bentonite, 2-3 parts of cellulose, hydroxypropyl methyl cellulose 1-
2 parts, 0.1-0.4 parts of dibutyl ester.
Preferably, in terms of parts by weight, including following components：50 parts of white cement, 40 parts of talcum powder, grey 35 parts of calcium, fiber
Plain 2 parts of ether, water-fast 3 parts of rubber powder, 13 parts of bentonite, 2 parts of cellulose, 2 parts of hydroxypropyl methyl cellulose, 0.3 part of dimeticone.
Preferably, the thickener includes any one in hydroxypropyl methyl cellulose, hydroxyethyl cellulose.
Preferably, the antifoaming agent includes any one in dimeticone, dibutyl ester, tributyl phosphate.
Preferably, the preparation method of the powder of lacquer putty for use on comprises the following steps：
1) by white cement, talcum powder, grey calcium, cellulose ether, water-fast rubber powder, bentonite, cellulose, thickener, antifoaming agent
It carries out plus water is thoroughly mixed uniformly；
2) packed for standby use can be carried out by the material of mixing being dried by putty powder drier.
Based on described above, compared with prior art, the present invention having the advantages that：
(1) bentonite and water-fast rubber powder are added in powder of lacquer putty for use on, it can by the effect between bentonite and water-fast rubber powder
The water resistance of powder of lacquer putty for use on is effectively improved, so as to make powder of lacquer putty for use on that there is very high waterproof to imitate by the interaction between each component
Fruit.
(2) the grey calcium added in powder of lacquer putty for use on makes putty during coating film forming, calcium hydroxide and air in grey calcium
In the calcium carbonate of carbon dioxide reaction generation make putty that there is higher intensity, and then can be powder of lacquer putty for use in putty film
Component provides certain caking property.
(3) plasticizer in the putty powder component of the application effectively increases the adhesion strength of powder of lacquer putty for use on, so as to reduce
The additive amount of moisture, and then the drying time of powder of lacquer putty for use on is reduced, improve work efficiency.
(4) harmful substance is not contained in the putty powder component of the application, to work during industrial production and decorations
Actual bodily harm will not be caused by making personnel, and not can cause environmental pollution.
Specific embodiment
In order to which those skilled in the art is made to more fully understand technical scheme, with reference to specific embodiment pair
The present invention is described in further detail.
Embodiment 1
A kind of waterproof putty powder, in terms of parts by weight, including following components：
40 parts of white cement, 35 parts of talcum powder, grey 30 parts of calcium, 1 part of cellulose ether, water-fast 2 parts of rubber powder, 10 parts of bentonite are fine
1 part of dimension element, 1 part of thickener, 0.1 part of antifoaming agent.
Its preparation method comprises the following steps：
1) by white cement, talcum powder, grey calcium, cellulose ether, water-fast rubber powder, bentonite, cellulose, thickener, antifoaming agent
It carries out plus water is thoroughly mixed uniformly.
It 2) can packed for standby use after the material of mixing is dried by putty powder drier.
Embodiment 2
A kind of waterproof putty powder, in terms of parts by weight, including following components：
55 parts of white cement, 50 parts of talcum powder, grey 40 parts of calcium, 3 parts of cellulose ether, water-fast 5 parts of rubber powder, 15 parts of bentonite are fine
3 parts of dimension element, 2 parts of thickener, 0.4 part of antifoaming agent.
Its preparation method comprises the following steps：
1) by white cement, talcum powder, grey calcium, cellulose ether, water-fast rubber powder, bentonite, cellulose, thickener, antifoaming agent
It carries out plus water is thoroughly mixed uniformly.
It 2) can packed for standby use after the material of mixing is dried by putty powder drier.
Embodiment 3
A kind of waterproof putty powder, in terms of parts by weight, including following components：
45 parts of white cement, 40 parts of talcum powder, grey 35 parts of calcium, 2 parts of cellulose ether, water-fast 3 parts of rubber powder, 12 parts of bentonite are fine
2 parts of dimension element, 1 part of thickener, 0.1 part of antifoaming agent.
Its preparation method comprises the following steps：
1) by white cement, talcum powder, grey calcium, cellulose ether, water-fast rubber powder, bentonite, cellulose, thickener, antifoaming agent
It carries out plus water is thoroughly mixed uniformly.
It 2) can packed for standby use after the material of mixing is dried by putty powder drier.
Embodiment 4
A kind of waterproof putty powder, in terms of parts by weight, including following components：
50 parts of white cement, 45 parts of talcum powder, grey 40 parts of calcium, 3 parts of cellulose ether, water-fast 4 parts of rubber powder, 14 parts of bentonite are fine
3 parts of dimension element, 2 parts of thickener, 0.4 part of antifoaming agent.
Its preparation method comprises the following steps：
1) by white cement, talcum powder, grey calcium, cellulose ether, water-fast rubber powder, bentonite, cellulose, thickener, antifoaming agent
It carries out plus water is thoroughly mixed uniformly.
It 2) can packed for standby use after the material of mixing is dried by putty powder drier.
Embodiment 5
A kind of waterproof putty powder, in terms of parts by weight, including following components：
50 parts of white cement, 40 parts of talcum powder, grey 35 parts of calcium, 2 parts of cellulose ether, water-fast 3 parts of rubber powder, 13 parts of bentonite are fine
2 parts of dimension element, 2 parts of thickener, 0.3 part of antifoaming agent.
Its preparation method comprises the following steps：
1) by white cement, talcum powder, grey calcium, cellulose ether, water-fast rubber powder, bentonite, cellulose, thickener, antifoaming agent
It carries out plus water is thoroughly mixed uniformly.
It 2) can packed for standby use after the material of mixing is dried by putty powder drier.
Water absorption test is detected according to the regulation of GB/T 9278.
Adhesion strength test is detected according to JC/T298-2010 standards.
Coefficient of permeability test is detected according to JB/T 25993-2010 standards.
Table 1, embodiment 1-5 Data Detection tables
Comparative example 1
The main distinction of comparative example 1 and embodiment 5 is that comparative example 1 does not contain bentonite, other with 5 phase of embodiment
Together.
Comparative example 2
The main distinction of comparative example 2 and embodiment 5 is that comparative example 1 does not contain resistance to rubber powder, other with 5 phase of embodiment
Together.
Comparative example 3
The main distinction of comparative example 3 and embodiment 5 is that comparative example 1 does not contain resistance to rubber powder and bentonite, other with reality
It is identical to apply example 5.
Table 2, comparative example 1-3 Data Detection tables
| Test event | Comparative example 1 | Comparative example 2 | Comparative example 3 |
| Water absorption (%) | 5.9 | 6.2 | 5.7 |
| Adhesive strength (mpa) | 1.05 | 1.08 | 1.03 |
| Coefficient of permeability (mm/s) | 0.92 | 0.89 | 0.97 |
It can draw to draw a conclusion by above-mentioned experiment：Bentonite is added in powder of lacquer putty for use on and water-fast rubber powder greatly reduces
The water absorption of powder of lacquer putty for use on makes powder of lacquer putty for use on have good water proofing property, while improves the cementability of putty, avoids putty from wall
It comes off on body.
It the above is only the preferred embodiment of the present invention, it is noted that above-mentioned preferred embodiment is not construed as pair
The limitation of invention, protection scope of the present invention should be subject to claim limited range.For the general of the art
For logical technical staff, without departing from the spirit and scope of the present invention, several improvements and modifications can also be made, these improvement
Protection scope of the present invention is also should be regarded as with retouching.
Claims (6)
1. a kind of waterproof putty powder, which is characterized in that in terms of parts by weight, including following components：
40-55 parts of white cement, 35-50 parts of talcum powder, grey calcium 30-40 parts, 1-3 parts of cellulose ether, water-fast rubber powder 2-5 parts, swelling
It is 10-15 parts native, 1-3 parts of cellulose, 1-2 parts of thickener, 0.1-0.4 parts of antifoaming agent.
2. a kind of waterproof putty powder according to claim 1, which is characterized in that in terms of parts by weight, including following components：
45-50 parts of white cement, 40-45 parts of talcum powder, grey calcium 35-40 parts, 2-3 parts of cellulose ether, water-fast rubber powder 3-4 parts, swelling
It is 12-14 parts native, 2-3 parts of cellulose, 1-2 parts of thickener, 0.1-0.4 parts of antifoaming agent.
3. a kind of waterproof putty powder according to claim 2, which is characterized in that in terms of parts by weight, including following components：
50 parts of white cement, 40 parts of talcum powder, grey 35 parts of calcium, 2 parts of cellulose ether, water-fast 3 parts of rubber powder, 13 parts of bentonite, cellulose 2
Part, 2 parts of thickener, 0.3 part of antifoaming agent.
4. according to a kind of waterproof putty powder described in claim 1-3 any one, which is characterized in that the thickener includes hydroxyl
Any one in propyl methocel, hydroxyethyl cellulose.
5. according to a kind of waterproof putty powder described in claim 1-3 any one, which is characterized in that the antifoaming agent includes two
Any one in first silicone oil, dibutyl ester, tributyl phosphate.
A kind of 6. preparation method of claim 1-5 any one of them waterproof putty powders, which is characterized in that the preparation method
Comprise the following steps：
1) white cement, talcum powder, grey calcium, cellulose ether, water-fast rubber powder, bentonite, cellulose, thickener, antifoaming agent are carried out
Water is added to be thoroughly mixed uniformly；
2) packed for standby use can be carried out by the material of mixing being dried by putty powder drier.