CN103351696A - Waterproof corrosion preventing interior wall putty - Google Patents
Waterproof corrosion preventing interior wall putty Download PDFInfo
- Publication number
- CN103351696A CN103351696A CN2013102546379A CN201310254637A CN103351696A CN 103351696 A CN103351696 A CN 103351696A CN 2013102546379 A CN2013102546379 A CN 2013102546379A CN 201310254637 A CN201310254637 A CN 201310254637A CN 103351696 A CN103351696 A CN 103351696A
- Authority
- CN
- China
- Prior art keywords
- parts
- putty
- powder
- wall putty
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses waterproof corrosion preventing interior wall putty which comprises the following components in parts by weight: 35-45 parts of ash-calcium-powder, 12-14 parts of attapulgite, 6-8 parts of sepiolite powder, 3-5 parts of nano zinc oxide micropowder, 10-14 parts of titanium dioxide, 2-4 parts of HPMC (Hydroxy Propyl Methyl Cellulose), 5-8 parts of polyvinyl alcohol, 1-2 parts of castor oil, 1-3 parts of salad oil, 2-3 parts of latex dry powder and 1-2 parts of a wetting assistant. According to the invention, the interior wall putty is excellent in waterproof and corrosion preventing performance, and meanwhile, the normal performance of the putty can be maintained.
Description
Technical field
The present invention relates to building material technical field, relate in particular to a kind of water-fast anticorrosion inner wall putty.
Background technology
Putty claims again to filler, and is a kind of thick slurry coating material.Be coated with to impose on the priming paint or directly be coated with and impose on the object, in order to remove rugged defective on the coated article surface.Its major function is: 1, remedy Defect Base, levelling: with floating rule blade coating on metope or end face, make it to satisfy the upper requirement to planeness of decoration; Do light: fill said minuscule hole and slit, make it to satisfy the requirement of surface flatness; Cover crackle: bouncing putty can cover the following segmentation crack of 0.5mm.2, the diversified texture of performance or decorative pattern.Such as the tangerine peel decorative pattern, can produce the tangerine peel decorative pattern with the roller coating of garland cylinder; And for example raised pattern is used first spray gun spraying, and then flattens with the light surface roller, can form raised pattern; And other personalized decorative pattern: decorative pattern or the pattern that can form multiple energy personalized requirements with other coating tool; 3, other special purpose such as ceramic tile bond, high-elastic anti-cracking etc.
Except these basic functions, along with the development of decorating and renovating material, and people are to the high request of decorating and renovating material, and people expect that not only putty possesses above-mentioned basic function, also will possess environmental protection, taste removal, antibiotic, anticorrosion etc. function.Water-fast antiseptic property wherein causes people's very big concern in recent years.
Traditional putty is comprised of the fillers such as talcum powder and matrix material, when construction, add and scrape on body of wall after a certain proportion of water mixes, this class putty cohesive strength is low, water tolerance, preservative property are relatively poor, in long-term use procedure, produce easily hollowing, come off, be full of cracks, the phenomenon such as mouldy, surface of wall coating also along with coming off of putty peeling, come off, have influence on the quality of buildings fitting-out work.Some putties take grey calcium powder as main active filler occurred on the market now, grey calcium powder is a kind of air hardening cementitious materials, along with the blade coating of putty, and its main component Ca (OH)
2Meeting and airborne CO
2Reaction generates CaCO
3Crystal and produce intensity, and then in putty layer, can provide certain cohesiveness for other filler components, and give putty layer significant water tolerance; Simultaneously owing to consumed airborne CO
2, can improve indoor Air quality after the application; And the high alkalinity environment that grey calcium powder provides so that mould and microorganism can't survive, can improve the preservative property of putty.But because grey calcium powder adds the phenomenon that thickening can occur putty to, if the too high levels of grey calcium powder, meeting is so that filler is difficult to be distributed to equably in the matrix material, and putty produces caking, affects its construction blade coating; In addition, absorb CO
2After will produce volumetric expansion, this also will cause putty to peel off easily, thereby the consumption of grey calcium powder is lower in the existing putty, this so that the water-fast antiseptic property of this class putty be restricted.
Summary of the invention
The object of the invention is to propose a kind of water-fast anticorrosion inner wall putty, this inner wall putty is water-fast and antiseptic property is excellent, can keep the traditional performance of putty simultaneously.
A kind of water-fast anticorrosion inner wall putty, described inner wall putty is comprised of following component in weight part: grey calcium powder 35-45 part, attapulgite 12-14 part, sepiolite powder 6-8 part, nano oxidized zinc powder 3-5 part, titanium dioxide 10-14 part, HPMC2-4 part, polyvinyl alcohol 5-8 part, Viscotrol C 1-2 part, salad oil 1-3 part, latex dry powder 2-3 part, moistening auxiliary agent 1-2 part.
Preferably, described inner wall putty is comprised of following component in weight part: grey calcium powder 38-42 part, attapulgite 12.5-13.5 part, sepiolite powder 6.5-7.5 part, nano oxidized zinc powder 3.5-4.5 part, titanium dioxide 11-13 part, HPMC2.5-3.5 part, polyvinyl alcohol 6-7 part, Viscotrol C 1.3-1.7 part, salad oil 1.5-2.5 part, latex dry powder 2.3-2.7 part, moistening auxiliary agent 1.3-1.7 part.
Most preferably, described inner wall putty is comprised of following component in weight part: 40 parts of grey calcium powders, 13 parts of attapulgites, 7 parts of sepiolite powders, 4 parts of nano oxidized zinc powders, 12 parts of titanium dioxides, HPMC3 part, 6.5 parts of polyvinyl alcohol, 1.5 parts of Viscotrol C, 2 parts of salad oils, 2.5 parts in latex dry powder, 1.5 parts of moistening auxiliary agents.
The present invention compared with prior art has following beneficial effect: the grey calcium powder that the present invention adds is than height of the prior art, and grey calcium powder itself has water-fast antiseptic property, therefore so that the water-fast antiseptic property of putty guaranteed, the defective that causes for fear of grey calcium powder content height simultaneously, the present invention adds polyvinyl alcohol, Viscotrol C and salad oil, and it is mixed first with grey calcium powder, improved the dispersing property of grey calcium powder.Attapulgite and sepiolite powder and nano oxidized zinc powder have been added in the mud of the present invention, and determined its component content separately on the basis of great many of experiments, attapulgite and sepiolite can absorbing air in and the coating that adjoins and the moisture in the body of wall, the water resistance of height putty, nano oxidized zinc powder helps to improve the antiseptic property of putty simultaneously.
Embodiment
Embodiment one
A kind of water-fast anticorrosion inner wall putty, described inner wall putty is comprised of following component in weight part: 35 parts of grey calcium powders, 14 parts of attapulgites, 6 parts of sepiolite powders, 5 parts of nano oxidized zinc powders, 10 parts of titanium dioxides, HPMC4 part, 5 parts of polyvinyl alcohol, 2 parts of Viscotrol C, 1 part of salad oil, 3 parts in latex dry powder, 1 part of moistening auxiliary agent.
Embodiment two
A kind of water-fast anticorrosion inner wall putty, described inner wall putty is comprised of following component in weight part: 45 parts of grey calcium powders, 12 parts of attapulgites, 8 parts of sepiolite powders, 3 parts of nano oxidized zinc powders, 14 parts of titanium dioxides, HPMC2 part, 8 parts of polyvinyl alcohol, 1 part of Viscotrol C, 3 parts of salad oils, 2 parts in latex dry powder, 2 parts of moistening auxiliary agents.
Embodiment three
A kind of water-fast anticorrosion inner wall putty, described inner wall putty is comprised of following component in weight part: 38 parts of grey calcium powders, 13.5 parts of attapulgites, 6.5 parts of sepiolite powders, 4.5 parts of nano oxidized zinc powders, 11 parts of titanium dioxides, HPMC3.5 part, 6 parts of polyvinyl alcohol, 1.7 parts of Viscotrol C, 1.5 parts of salad oils, 2.7 parts in latex dry powder, 1.3 parts of moistening auxiliary agents.
Embodiment four
A kind of water-fast anticorrosion inner wall putty, described inner wall putty is comprised of following component in weight part: 42 parts of grey calcium powders, 12.5 parts of attapulgites, 7.5 parts of sepiolite powders, 3.5 parts of nano oxidized zinc powders, 13 parts of titanium dioxides, HPMC2.5 part, 7 parts of polyvinyl alcohol, 1.3 parts of Viscotrol C, 2.5 parts of salad oils, 2.3 parts in latex dry powder, 1.7 parts of moistening auxiliary agents.
Embodiment five
A kind of water-fast anticorrosion inner wall putty, described inner wall putty is comprised of following component in weight part: 40 parts of grey calcium powders, 13 parts of attapulgites, 7 parts of sepiolite powders, 4 parts of nano oxidized zinc powders, 12 parts of titanium dioxides, HPMC3 part, 6.5 parts of polyvinyl alcohol, 1.5 parts of Viscotrol C, 2 parts of salad oils, 2.5 parts in latex dry powder, 1.5 parts of moistening auxiliary agents.
The grey calcium powder that the present invention adds is than height of the prior art, and grey calcium powder itself has water-fast antiseptic property, therefore so that the water-fast antiseptic property of putty guaranteed, the defective that causes for fear of grey calcium powder content height simultaneously, the present invention adds polyvinyl alcohol, Viscotrol C and salad oil, and it is mixed first with grey calcium powder, improved the dispersing property of grey calcium powder.Attapulgite and sepiolite powder and nano oxidized zinc powder have been added in the mud of the present invention, and determined its component content separately on the basis of great many of experiments, attapulgite and sepiolite can absorbing air in and the coating that adjoins and the moisture in the body of wall, the water resistance of height putty, nano oxidized zinc powder helps to improve the antiseptic property of putty simultaneously.
With reference to JG/T3049-1998 technical indicator putty of the present invention is carried out performance test, the result shows that aforesaid combination and consumption proportion can make putty composition of the present invention have good application property, water tolerance, preservative property, pure white property, and it is very low to reach desirable effect and cost.
Claims (3)
1. a water-fast anticorrosion inner wall putty is characterized in that described inner wall putty is comprised of following component in weight part: grey calcium powder 35-45 part, attapulgite 12-14 part, sepiolite powder 6-8 part, nano oxidized zinc powder 3-5 part, titanium dioxide 10-14 part, HPMC2-4 part, polyvinyl alcohol 5-8 part, Viscotrol C 1-2 part, salad oil 1-3 part, latex dry powder 2-3 part, moistening auxiliary agent 1-2 part.
2. water-fast anticorrosive putty as claimed in claim 1 is characterized in that, described inner wall putty is comprised of following component in weight part: grey calcium powder 38-42 part, attapulgite 12.5-13.5 part, sepiolite powder 6.5-7.5 part, nano oxidized zinc powder 3.5-4.5 part, titanium dioxide 11-13 part, HPMC2.5-3.5 part, polyvinyl alcohol 6-7 part, Viscotrol C 1.3-1.7 part, salad oil 1.5-2.5 part, latex dry powder 2.3-2.7 part, moistening auxiliary agent 1.3-1.7 part.
3. water-fast anticorrosive putty as claimed in claim 2 is characterized in that, described inner wall putty is comprised of following component in weight part: 40 parts of grey calcium powders, 13 parts of attapulgites, 7 parts of sepiolite powders, 4 parts of nano oxidized zinc powders, 12 parts of titanium dioxides, HPMC3 part, 6.5 parts of polyvinyl alcohol, 1.5 parts of Viscotrol C, 2 parts of salad oils, 2.5 parts in latex dry powder, 1.5 parts of moistening auxiliary agents.