CN107083098A - A kind of powder of lacquer putty for use on and preparation method thereof - Google Patents
A kind of powder of lacquer putty for use on and preparation method thereof Download PDFInfo
- Publication number
- CN107083098A CN107083098A CN201710479702.6A CN201710479702A CN107083098A CN 107083098 A CN107083098 A CN 107083098A CN 201710479702 A CN201710479702 A CN 201710479702A CN 107083098 A CN107083098 A CN 107083098A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- lacquer putty
- clay
- tourmaline
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of powder of lacquer putty for use on, include the raw material of following parts by weight：3~8 parts of sepiolite powder, 15~20 parts of quartz sand, 1~5 part of bamboo charcoal powder, 30~50 parts of Concave-convex clay rod, 13~18 parts of clay, 0.1~0.5 part of carboxymethyl cellulose, 0.2~2 part of tourmaline powder anionic additive, 2~5 parts of photocatalysis antibacterial material, 2~5 parts of mould inhibitor, 1~2 part of colouring agent, 2~3 parts of accelerator.The powder of lacquer putty for use on is while people's traditional performance requirement is met, moreover it is possible to effectively remove formaldehyde and benzene, plays a part of mould proof, release anion and anti-electromagnetic-radiation, removes indoor pollution, is adapted to promote.
Description
Technical field
The invention belongs to building material technical field, and in particular to a kind of powder of lacquer putty for use on and preparation method thereof.
Background technology
With expanding economy, people pass through the dress to indoor environment to indoor requirement more and more higher whether attractive in appearance
Adorn to meet the esthetic requirement of individual, and the environmental pollution caused by interior decoration is increasingly severe.Finishing material and coating are released
Formaldehyde, volatile organic matter benzene and the toluene of releasing, in addition, in interior decoration and renovation process, also using substantial amounts of phenolic aldehyde tree
Fat, the paint of floor furniture, wallpaper, the diluent of coating etc., this kind of material discharges formaldehyde once exposure, causes family to occupy
Concentration of formaldehyde in room air is up to 0.05-2mg/m3.
Putty is the supplementary material in building coating coating process, and its is indispensable.Putty is under coating, its main work(
It can be smooth metope and play adhesive effect between metope basic unit and film, while being also prevented from metope peeling, be cracked, come off
Phenomenon, powder of lacquer putty for use on of the prior art can not effectively remove formaldehyde and electromagnetic radiation, and the air pollution of interior can not be removed again,
Mould proof, release anion and anti-electromagnetic-radiation can not be played a part of, and these air pollutions are very harmful to the mankind..
The content of the invention
The invention provides a kind of powder of lacquer putty for use on and preparation method thereof, the problem of solving in above-mentioned background technology is described greasy
Sub- powder is while people's traditional performance requirement is met, moreover it is possible to effectively remove formaldehyde and benzene, plays mould proof, release anion and anti-
The effect of electromagnetic radiation, removes indoor pollution, is adapted to promote.
In order to solve the problem of prior art is present, adopt the following technical scheme that：
A kind of powder of lacquer putty for use on, includes the raw material of following parts by weight：3~8 parts of sepiolite powder, 15~20 parts of quartz sand, bamboo charcoal powder 1~5
Part, 30~50 parts of Concave-convex clay rod, 13~18 parts of clay, 0.1~0.5 part of carboxymethyl cellulose, tourmaline powder anion add
Plus 0.2~2 part of agent, 2~5 parts of photocatalysis antibacterial material, 2~5 parts of mould inhibitor, 1~2 part of colouring agent, 2~3 parts of accelerator.
It is preferred that, the powder of lacquer putty for use on includes the raw material of following parts by weight：4~6 parts of sepiolite powder, 17~19 parts of quartz sand,
2~4 parts of bamboo charcoal powder, 35~45 parts of Concave-convex clay rod, 15~17 parts of clay, 0.2~0.4 part of carboxymethyl cellulose, tourmaline
1~1.7 part of powder anionic additive, 3~4 parts of photocatalysis antibacterial material, 3~4 parts of mould inhibitor, 1.3~1.7 parts of colouring agent, rush
Enter 2.5~2.8 parts of agent.
It is preferred that, the powder of lacquer putty for use on includes the raw material of following parts by weight：5 parts of sepiolite powder, 18 parts of quartz sand, bamboo charcoal powder 3
Part, 42 parts of Concave-convex clay rod, 16 parts of clay, 0.3 part of carboxymethyl cellulose, 1.5 parts of tourmaline powder anionic additive, light are urged
Change 3.7 parts of anti-biotic material, 3.2 parts of mould inhibitor, 1.5 parts of colouring agent, 2.6 parts of accelerator.
It is preferred that, the mould inhibitor is sodium Diacetate.
It is preferred that, the photocatalysis antibacterial material is TiO2, ZnO, CdS and WO3 mixture.
It is preferred that, the tourmaline powder anionic additive has following methods preparation：Electricity of the selection with negative ion effect
Gas stone, carries out attrition grinding, is then dispersed in water miberal powder, wet grinding, with 1000 mesh filter-cloth filterings, filtration material drying
Afterwards, the tourmaline anion additive is made.
A kind of method for preparing the powder of lacquer putty for use on, comprises the following steps：
（1）The sepiolite powder, quartz sand, bamboo charcoal powder, Concave-convex clay rod, clay, carboxymethyl cellulose are weighed by above-mentioned formula
Element, tourmaline powder anionic additive, photocatalysis antibacterial material, mould inhibitor, colouring agent, accelerator are standby；
（2）Sepiolite powder, quartz sand, bamboo charcoal powder, attapulgite clay and clay are put into stirrer for mixing, distilled water is added,
Mixture is placed in heating stirring in 80~85 DEG C of water-bath, is allowed to be gelatinized, accelerator is added, is completely dissolved it, is made
Dextrin；
（3）Colouring agent and carboxymethyl cellulose, tourmaline powder anionic additive are added in dextrin, in 80~85 DEG C of water
Stirred 30~35 minutes in bath, add photocatalysis antibacterial material and mould inhibitor, it is scattered 20~30 minutes at a high speed, obtain putty slurry
Material；
（4）By powder of lacquer putty for use on slurry drying, its water content is less than 3%, be then ground to powder, cross 500 mesh sieves, obtain described greasy
Sub- powder.
It is preferred that, the scattered speed of the high speed is 1000~1100r/min.
Compared with prior art, it has the advantages that the present invention：
Powder of lacquer putty for use on of the present invention is while people's traditional performance requirement is met, moreover it is possible to effectively removes formaldehyde and benzene, plays
The effect of mould proof, release anion and anti-electromagnetic-radiation, removes indoor pollution, is adapted to promote, specific as follows：
（1）Sepiolite powder, bamboo charcoal powder employed in powder of lacquer putty for use on of the present invention are sorbing materials, can absorb benzene and formaldehyde,
Air is purified, indoor pollution is removed；
（2）Due to the addition of tourmaline anion additive in powder of lacquer putty for use on, so negative aeroion can be produced, ring can be purified
Border air, is conducive to health；
（3）Mould inhibitor in powder of lacquer putty for use on of the present invention is sodium Diacetate, especially right with efficient, wide spectrum anti-mold effect
Aflatoxins has stronger inhibitory action, it by permeating the generations of various enzyme systems in microorganism wall, interference cell,
The growth of more than ten kinds of moldin and various bacteria can efficiently be suppressed and spread；
（4）The anti-biotic material that the present invention is added is photocatalysis antibacterial material, under light irradiation, can just be killed completely in the short time
The microorganism being in contact with it, instant effect, durable, non-secondary pollution.
Embodiment
With reference to specific embodiment, the present invention is expanded on further.These embodiments be merely to illustrate the present invention and without
In limitation the scope of the present invention.
Embodiment 1
The present embodiment is related to a kind of powder of lacquer putty for use on, includes the raw material of following parts by weight：3 parts of sepiolite powder, 15 parts of quartz sand, bamboo charcoal powder
1 part, 30 parts of Concave-convex clay rod, 13 parts of clay, 0.1 part of carboxymethyl cellulose, 0.2 part of tourmaline powder anionic additive, light
2 parts of catalytic antibacterial material, 2 parts of mould inhibitor, 1 part of colouring agent, 2 parts of accelerator.
Wherein, the mould inhibitor is sodium Diacetate.
Wherein, the photocatalysis antibacterial material is TiO2, ZnO, CdS and WO3 mixture.
Wherein, the tourmaline powder anionic additive has following methods preparation：Selection is electric with negative ion effect
Stone, carries out attrition grinding, is then dispersed in water miberal powder, wet grinding, with 1000 mesh filter-cloth filterings, and filtration is expected after drying,
The tourmaline anion additive is made.
A kind of method for preparing the powder of lacquer putty for use on, comprises the following steps：
（1）The sepiolite powder, quartz sand, bamboo charcoal powder, Concave-convex clay rod, clay, carboxymethyl cellulose are weighed by above-mentioned formula
Element, tourmaline powder anionic additive, photocatalysis antibacterial material, mould inhibitor, colouring agent, accelerator are standby；
（2）Sepiolite powder, quartz sand, bamboo charcoal powder, attapulgite clay and clay are put into stirrer for mixing, distilled water is added,
Mixture is placed in heating stirring in 80 DEG C of water-bath, is allowed to be gelatinized, accelerator is added, is completely dissolved it, gelatinization is made
Liquid；
（3）Colouring agent and carboxymethyl cellulose, tourmaline powder anionic additive are added in dextrin, in 80 DEG C of water-bath
Middle stirring 30 minutes, adds photocatalysis antibacterial material and mould inhibitor, scattered 20 minutes at a high speed, and the scattered speed of the high speed is
1000r/min, obtains powder of lacquer putty for use on slurry；
（4）By powder of lacquer putty for use on slurry drying, its water content is less than 3%, be then ground to powder, cross 500 mesh sieves, obtain described greasy
Sub- powder.
Embodiment 2
The present embodiment is related to a kind of powder of lacquer putty for use on, includes the raw material of following parts by weight：8 parts of sepiolite powder, 20 parts of quartz sand, bamboo charcoal powder
5 parts, 50 parts of Concave-convex clay rod, 18 parts of clay, 0.5 part of carboxymethyl cellulose, 2 parts of tourmaline powder anionic additive, light urges
Change 5 parts of anti-biotic material, 5 parts of mould inhibitor, 2 parts of colouring agent, 3 parts of accelerator.
Wherein, the mould inhibitor is sodium Diacetate.
Wherein, the photocatalysis antibacterial material is TiO2, ZnO, CdS and WO3 mixture.
Wherein, the tourmaline powder anionic additive has following methods preparation：Selection is electric with negative ion effect
Stone, carries out attrition grinding, is then dispersed in water miberal powder, wet grinding, with 1000 mesh filter-cloth filterings, and filtration is expected after drying,
The tourmaline anion additive is made.
A kind of method for preparing the powder of lacquer putty for use on, comprises the following steps：
（1）The sepiolite powder, quartz sand, bamboo charcoal powder, Concave-convex clay rod, clay, carboxymethyl cellulose are weighed by above-mentioned formula
Element, tourmaline powder anionic additive, photocatalysis antibacterial material, mould inhibitor, colouring agent, accelerator are standby；
（2）Sepiolite powder, quartz sand, bamboo charcoal powder, attapulgite clay and clay are put into stirrer for mixing, distilled water is added,
Mixture is placed in heating stirring in 85 DEG C of water-bath, is allowed to be gelatinized, accelerator is added, is completely dissolved it, gelatinization is made
Liquid；
（3）Colouring agent and carboxymethyl cellulose, tourmaline powder anionic additive are added in dextrin, in 85 DEG C of water-bath
Middle stirring 35 minutes, adds photocatalysis antibacterial material and mould inhibitor, scattered 30 minutes at a high speed, and the scattered speed of the high speed is
1100r/min, obtains powder of lacquer putty for use on slurry；
（4）By powder of lacquer putty for use on slurry drying, its water content is less than 3%, be then ground to powder, cross 500 mesh sieves, obtain described greasy
Sub- powder.
Embodiment 3
The present embodiment is related to a kind of powder of lacquer putty for use on, includes the raw material of following parts by weight：4 parts of sepiolite powder, 17 parts of quartz sand, bamboo charcoal powder
2 parts, 35 parts of Concave-convex clay rod, 15 parts of clay, 0.2 part of carboxymethyl cellulose, 1 part of tourmaline powder anionic additive, light urges
Change 3 parts of anti-biotic material, 3 parts of mould inhibitor, 1.3 parts of colouring agent, 2.5 parts of accelerator.
Wherein, the mould inhibitor is sodium Diacetate.
Wherein, the photocatalysis antibacterial material is TiO2, ZnO, CdS and WO3 mixture.
Wherein, the tourmaline powder anionic additive has following methods preparation：Selection is electric with negative ion effect
Stone, carries out attrition grinding, is then dispersed in water miberal powder, wet grinding, with 1000 mesh filter-cloth filterings, and filtration is expected after drying,
The tourmaline anion additive is made.
A kind of method for preparing the powder of lacquer putty for use on, comprises the following steps：
（1）The sepiolite powder, quartz sand, bamboo charcoal powder, Concave-convex clay rod, clay, carboxymethyl cellulose are weighed by above-mentioned formula
Element, tourmaline powder anionic additive, photocatalysis antibacterial material, mould inhibitor, colouring agent, accelerator are standby；
（2）Sepiolite powder, quartz sand, bamboo charcoal powder, attapulgite clay and clay are put into stirrer for mixing, distilled water is added,
Mixture is placed in heating stirring in 82 DEG C of water-bath, is allowed to be gelatinized, accelerator is added, is completely dissolved it, gelatinization is made
Liquid；
（3）Colouring agent and carboxymethyl cellulose, tourmaline powder anionic additive are added in dextrin, in 82 DEG C of water-bath
Middle stirring 32 minutes, adds photocatalysis antibacterial material and mould inhibitor, scattered 25 minutes at a high speed, and the scattered speed of the high speed is
1050r/min, obtains powder of lacquer putty for use on slurry；
（4）By powder of lacquer putty for use on slurry drying, its water content is less than 3%, be then ground to powder, cross 500 mesh sieves, obtain described greasy
Sub- powder.
Embodiment 4
The present embodiment is related to a kind of powder of lacquer putty for use on, includes the raw material of following parts by weight：6 parts of sepiolite powder, 19 parts of quartz sand, bamboo charcoal powder
4 parts, 45 parts of Concave-convex clay rod, 17 parts of clay, 0.4 part of carboxymethyl cellulose, 1.7 parts of tourmaline powder anionic additive, light
4 parts of catalytic antibacterial material, 4 parts of mould inhibitor, 1.7 parts of colouring agent, 2.8 parts of accelerator.
Wherein, the mould inhibitor is sodium Diacetate.
Wherein, the photocatalysis antibacterial material is TiO2, ZnO, CdS and WO3 mixture.
Wherein, the tourmaline powder anionic additive has following methods preparation：Selection is electric with negative ion effect
Stone, carries out attrition grinding, is then dispersed in water miberal powder, wet grinding, with 1000 mesh filter-cloth filterings, and filtration is expected after drying,
The tourmaline anion additive is made.
A kind of method for preparing the powder of lacquer putty for use on, comprises the following steps：
（1）The sepiolite powder, quartz sand, bamboo charcoal powder, Concave-convex clay rod, clay, carboxymethyl cellulose are weighed by above-mentioned formula
Element, tourmaline powder anionic additive, photocatalysis antibacterial material, mould inhibitor, colouring agent, accelerator are standby；
（2）Sepiolite powder, quartz sand, bamboo charcoal powder, attapulgite clay and clay are put into stirrer for mixing, distilled water is added,
Mixture is placed in heating stirring in 84 DEG C of water-bath, is allowed to be gelatinized, accelerator is added, is completely dissolved it, gelatinization is made
Liquid；
（3）Colouring agent and carboxymethyl cellulose, tourmaline powder anionic additive are added in dextrin, in 84 DEG C of water-bath
Middle stirring 33 minutes, adds photocatalysis antibacterial material and mould inhibitor, scattered 28 minutes at a high speed, and the scattered speed of the high speed is
1000r/min, obtains powder of lacquer putty for use on slurry；
（4）By powder of lacquer putty for use on slurry drying, its water content is less than 3%, be then ground to powder, cross 500 mesh sieves, obtain described greasy
Sub- powder.
Embodiment 5
The present embodiment is related to a kind of powder of lacquer putty for use on, includes the raw material of following parts by weight：5 parts of sepiolite powder, 18 parts of quartz sand, bamboo charcoal powder
3 parts, 42 parts of Concave-convex clay rod, 16 parts of clay, 0.3 part of carboxymethyl cellulose, 1.5 parts of tourmaline powder anionic additive, light
3.7 parts of catalytic antibacterial material, 3.2 parts of mould inhibitor, 1.5 parts of colouring agent, 2.6 parts of accelerator.
Wherein, the mould inhibitor is sodium Diacetate.
Wherein, the photocatalysis antibacterial material is TiO2, ZnO, CdS and WO3 mixture.
Wherein, the tourmaline powder anionic additive has following methods preparation：Selection is electric with negative ion effect
Stone, carries out attrition grinding, is then dispersed in water miberal powder, wet grinding, with 1000 mesh filter-cloth filterings, and filtration is expected after drying,
The tourmaline anion additive is made.
A kind of method for preparing the powder of lacquer putty for use on, comprises the following steps：
（1）The sepiolite powder, quartz sand, bamboo charcoal powder, Concave-convex clay rod, clay, carboxymethyl cellulose are weighed by above-mentioned formula
Element, tourmaline powder anionic additive, photocatalysis antibacterial material, mould inhibitor, colouring agent, accelerator are standby；
（2）Sepiolite powder, quartz sand, bamboo charcoal powder, attapulgite clay and clay are put into stirrer for mixing, distilled water is added,
Mixture is placed in heating stirring in 81 DEG C of water-bath, is allowed to be gelatinized, accelerator is added, is completely dissolved it, gelatinization is made
Liquid；
（3）Colouring agent and carboxymethyl cellulose, tourmaline powder anionic additive are added in dextrin, in 81 DEG C of water-bath
Middle stirring 34 minutes, adds photocatalysis antibacterial material and mould inhibitor, scattered 25 minutes at a high speed, and the scattered speed of the high speed is
1080r/min, obtains powder of lacquer putty for use on slurry；
（4）By powder of lacquer putty for use on slurry drying, its water content is less than 3%, be then ground to powder, cross 500 mesh sieves, obtain described greasy
Sub- powder.
The specific embodiment of the present invention is described above.It is to be appreciated that the invention is not limited in above-mentioned
Particular implementation, those skilled in the art can make various deformations or amendments within the scope of the claims, this not shadow
Ring the substantive content of the present invention.
Claims (8)
1. a kind of powder of lacquer putty for use on, it is characterised in that include the raw material of following parts by weight：3~8 parts of sepiolite powder, quartz sand 15~20
Part, 1~5 part of bamboo charcoal powder, 30~50 parts of Concave-convex clay rod, 13~18 parts of clay, 0.1~0.5 part of carboxymethyl cellulose, electrically
0.2~2 part of stone flour anionic additive, 2~5 parts of photocatalysis antibacterial material, 2~5 parts of mould inhibitor, 1~2 part of colouring agent, promotion
2~3 parts of agent.
2. powder of lacquer putty for use on according to claim 1, it is characterised in that include the raw material of following parts by weight：Sepiolite powder 4~6
Part, 17~19 parts of quartz sand, 2~4 parts of bamboo charcoal powder, 35~45 parts of Concave-convex clay rod, 15~17 parts of clay, carboxymethyl cellulose
0.2~0.4 part, 1~1.7 part of tourmaline powder anionic additive, 3~4 parts of photocatalysis antibacterial material, 3~4 parts of mould inhibitor,
1.3~1.7 parts of toner, 2.5~2.8 parts of accelerator.
3. powder of lacquer putty for use on according to claim 1, it is characterised in that include the raw material of following parts by weight：5 parts of sepiolite powder,
18 parts of quartz sand, 3 parts of bamboo charcoal powder, 42 parts of Concave-convex clay rod, 16 parts of clay, 0.3 part of carboxymethyl cellulose, tourmaline powder bear from
Sub- 1.5 parts of additive, 3.7 parts of photocatalysis antibacterial material, 3.2 parts of mould inhibitor, 1.5 parts of colouring agent, 2.6 parts of accelerator.
4. powder of lacquer putty for use on according to claim 1, it is characterised in that the mould inhibitor is sodium Diacetate.
5. powder of lacquer putty for use on according to claim 1, it is characterised in that the photocatalysis antibacterial material be TiO2, ZnO, CdS and
WO3 mixture.
6. volume powder of lacquer putty for use on according to claim 1, it is characterised in that the tourmaline powder anionic additive has following methods
Prepare：Tourmaline of the selection with negative ion effect, carries out attrition grinding, is then dispersed in water miberal powder, wet grinding, uses
1000 mesh filter-cloth filterings, after filtration material is dried, are made the tourmaline anion additive.
7. a kind of method for preparing any one of claim 1~6 powder of lacquer putty for use on, it is characterised in that comprise the following steps：
（1）The sepiolite powder, quartz sand, bamboo charcoal powder, Concave-convex clay rod, clay, carboxymethyl cellulose are weighed by above-mentioned formula
Element, tourmaline powder anionic additive, photocatalysis antibacterial material, mould inhibitor, colouring agent, accelerator are standby；
（2）Sepiolite powder, quartz sand, bamboo charcoal powder, attapulgite clay and clay are put into stirrer for mixing, distilled water is added,
Mixture is placed in heating stirring in 80~85 DEG C of water-bath, is allowed to be gelatinized, accelerator is added, is completely dissolved it, is made
Dextrin；
（3）Colouring agent and carboxymethyl cellulose, tourmaline powder anionic additive are added in dextrin, in 80~85 DEG C of water
Stirred 30~35 minutes in bath, add photocatalysis antibacterial material and mould inhibitor, it is scattered 20~30 minutes at a high speed, obtain putty slurry
Material；
（4）By powder of lacquer putty for use on slurry drying, its water content is less than 3%, be then ground to powder, cross 500 mesh sieves, obtain described greasy
Sub- powder.
8. preparation method according to claim 7, it is characterised in that the scattered speed of the high speed is 1000~1100r/
min。