CN108083853A - A kind of production method of entire body Dali stone ceramic tile - Google Patents
A kind of production method of entire body Dali stone ceramic tile Download PDFInfo
- Publication number
- CN108083853A CN108083853A CN201711046001.XA CN201711046001A CN108083853A CN 108083853 A CN108083853 A CN 108083853A CN 201711046001 A CN201711046001 A CN 201711046001A CN 108083853 A CN108083853 A CN 108083853A
- Authority
- CN
- China
- Prior art keywords
- ceramic tile
- entire body
- production method
- stone ceramic
- glaze
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to ceramic tile manufacture technology field, the production method for providing a kind of entire body Dali stone ceramic tile；The production method of the entire body Dali stone ceramic tile, including：65 75min are fired at a temperature of 1,245 1250 DEG C after applying glaze on green body.The production method is simple, workable, and the entire body artificial marble products excellent quality being prepared by this method, texture is more preferable, and effect is more life-like.
Description
Technical field
The invention belongs to ceramic tile manufacture technology fields, specifically, are related to a kind of production method of entire body Dali stone ceramic tile.
Background technology
Compared to common ceramic tile, entire body Dali stone ceramic tile has the following advantages：Entire body Dali stone ceramic tile is in ceramic tile blank, face
Color, skin texture and lithotome rock stratum qualitative change effect is functionally all ad infinitum approached, texture texture is penetrating stronger；Full solid cloth
Be combined with colour mixture coloring process, entire body marble ceramic tile blank bottom made to accomplish to think and act in one and the same way to overglaze, entire ceramic tile from appoint
What angle and any cutting method are attained by perfect texture and effect are presented, and accomplish real texture entire body；Entire body marble
Tile product is through excessively high tonnage press compression moulding and high-temperature firing, and finished product adobe color and luster is finer and smoother, performance and quality higher；
The natural precious stone material of entire body Dali stone ceramic tile reduction true to nature；Ceramic tile blank is full of soul full of variation texture, product with space, more
It disclosure satisfy that consumer demand.
However, although entire body marble future prospect is become better, also complex in current technique, production cost is higher,
Cognition degree is also limited in terminal market, remains in the budding period of product on the whole.
The content of the invention
For deficiency above-mentioned in the prior art, it is an object of the invention to provide a kind of making of entire body Dali stone ceramic tile
Method, the production method is simple, workable, the entire body artificial marble products excellent quality being prepared by this method, texture
More preferably, effect is more life-like.
In order to achieve the above object, the preferred solution that uses of the present invention is：
A kind of production method of entire body Dali stone ceramic tile, including：In 1245-1250 DEG C of temperature after application glaze on green body
Lower firing 65-75min.
A kind of advantageous effect of the production method of entire body Dali stone ceramic tile provided by the invention is：
The production method of entire body Dali provided in an embodiment of the present invention stone ceramic tile passes through creatively technique between each step
The setting of parameter, coordinated between each parameter so that the effect for the entire body Dali stone ceramic tile being prepared is more life-like, resistance to
Mill property and hardness are also more excellent, and product quality is improved.
Specific embodiment
It, below will be in the embodiment of the present invention to make the purpose, technical scheme and advantage of the embodiment of the present invention clearer
Technical solution be clearly and completely described.The person that is not specified actual conditions in embodiment, builds according to normal condition or manufacturer
The condition of view carries out.Reagents or instruments used without specified manufacturer is the conventional production that can be obtained by commercially available purchase
Product.
A kind of production method of entire body Dali stone ceramic tile provided in an embodiment of the present invention is specifically described below.
The production method of entire body Dali provided in an embodiment of the present invention stone ceramic tile, including：On green body apply glaze after
65-75min is fired at a temperature of 1245-1250 DEG C.Ceramic tile is fired under the temperature time protocols, is conducive to reach in glaze infiltration green body
To lifelike visual effect, while ceramic tile hardness can be improved.
It should be noted that in the present embodiment, the fineness of the blank of green body is 1.5-2mm, and in the range of the fineness, system
Obtain that green body texture is more preferable, and surface is smooth, flatness is more preferable, finer and smoother, beautiful, application glaze is more conducive to, with glaze
It is combined.
Further, flow velocity when blank surveys slurry is conducive to the performance of test blank comprehensively for 25-40s；And preferably, exist
In the present embodiment, the moisture control of green body is 0.05-0.1%, is conducive to improve the hardness of green body.
It should be noted that in the present embodiment, in order to further such that entire body Dali stone ceramic tile is more beautiful forces, apply
The detailed process of glaze includes：Apply a Ceng Di You successively to green body first, then after carrying out stamp, apply a level glaze.
Ground-coat enamel is the transition zone be combineding with each other with green body, has stronger adherence, and overglaze rises and covers coated on ground-coat enamel
Background color simultaneously assigns product with the surface of smooth and beautiful appearance and a series of excellent physical and chemical performances.
Stamp is carried out on the You of bottom preferably by 8D ink jet printers, more efficient, flower pattern is more abundant, and ceramic tile obtained should
With more extensively.
In the present embodiment, it is necessary to which explanation, the fineness of glaze is preferably 0.025-0.035mm.The fineness mistake of glaze
Thin to be easy to cause exhaust variation, beginning fusing point is relatively low, is susceptible to glaze paint pin hole；The fineness of glaze is excessively thick to be easy to cause dispersiveness again
Bad, glaze dispersiveness is excellent in the range.
In the present embodiment, the flow velocity for applying Di You is preferably 42-44s.The flow velocity for applying Di You is too high or too low easily
Generate ripple glaze；To ensure the stability of glaze application, the flow velocity for applying overglaze is preferably 62-65s.
In conclusion the entire body Dali stone ceramic tile being prepared by present invention process step, no matter being fallen to ceramic tile
Angle, kerve or trimming processing, the texture thought and acted in one and the same way can be seen by splitting ceramic tile, true to nature in table.
The feature and performance of the present invention are described in further detail with reference to embodiments.
Embodiment 1
The production method for present embodiments providing a kind of entire body Dali stone ceramic tile, including：
Slurry is surveyed under being 25s in flow velocity by the blank that fineness is 1.5mm, the green body that moisture is 0.05% is made；By fineness
It is divided into bottom You and overglaze for the glaze of 0.025mm；Bottom You is applied with the flow velocity of 42s on above-mentioned green body, after stamp, then with 62s
Flow velocity apply a level glaze；Finished product is fired 75min at a temperature of 1245 DEG C after the completion of applying and product is made by glaze.
Embodiment 2
The production method for present embodiments providing a kind of entire body Dali stone ceramic tile, including：
Slurry is surveyed under being 40s in flow velocity by the blank that fineness is 2mm, the green body that moisture is 0.1% is made；It is by fineness
The glaze of 0.035mm is divided into bottom You and overglaze；Bottom You is applied with the flow velocity of 44s on above-mentioned green body, after stamp, then with 65s's
Flow velocity applies a level glaze；Finished product is fired 65min at a temperature of 1250 DEG C after the completion of applying and product is made by glaze.
Embodiment 3
The production method for present embodiments providing a kind of entire body Dali stone ceramic tile, including：
Slurry is surveyed under being 30s in flow velocity by the blank that fineness is 1.8mm, the green body that moisture is 0.08% is made；By fineness
It is divided into bottom You and overglaze for the glaze of 0.03mm；Bottom You is applied with the flow velocity of 43s on above-mentioned green body, after stamp, then with 64s's
Flow velocity applies a level glaze；Finished product is fired 70min at a temperature of 1248 DEG C after the completion of applying and product is made by glaze.
Comparative example 1
The production method that this comparative example provides a kind of entire body Dali stone ceramic tile, including：
Slurry is surveyed under being 20s in flow velocity by the blank that fineness is 1.4mm, the green body that moisture is 0.04% is made；By fineness
It is divided into bottom You and overglaze for the glaze of 0.020mm；Bottom You is applied with the flow velocity of 40s on above-mentioned green body, after stamp, then with 60s
Flow velocity apply a level glaze；Finished product is fired 70min at a temperature of 1200 DEG C after the completion of applying and product is made by glaze.
Comparative example 2
The production method that this comparative example provides a kind of entire body Dali stone ceramic tile, including：
Slurry is surveyed under being 45s in flow velocity by the blank that fineness is 2.2mm, the green body that moisture is 0.15% is made；By fineness
It is divided into bottom You and overglaze for the glaze of 0.04mm；Bottom You is applied with the flow velocity of 45s on above-mentioned green body, after stamp, then with 70s's
Flow velocity applies a level glaze；Finished product is fired 60min at a temperature of 1260 DEG C after the completion of applying and product is made by glaze.
Experimental example 1
The entire body Dali stone ceramic tile that embodiment 1-3 and comparative example 1-2 are prepared is arranged to experimental group 1-5, it will be commercially available
Entire body Dali stone ceramic tile be arranged to experimental group 6；
Water absorption rate test, strength test, thermal shock resistance test, anti-glaze fragility survey are carried out to the sample of experimental group 1-6 respectively
Examination and glossiness test, test result are as shown in table 1：
The performance comparison of the product of 1 experimental group 1-6 of table
From the data in table 1, it can be seen that the water absorption rate for the entire body Dali stone ceramic tile that experimental group 1-5 is provided, intensity, thermal shock resistance resist
Glaze fragility and glossiness are superior to the entire body Dali stone ceramic tile of experimental group 6, and the overall quality of product gets a promotion, which benefits
The creative restriction of each technological parameter, common to act synergistically in each step in the entire body Dali stone ceramic tile preparation process, rises
To the effect for promoting product quality.
The water absorption rate for the entire body Dali stone ceramic tile that experimental group 1-3 is provided, intensity, thermal shock resistance, anti-glaze fragility and glossiness
The entire body Dali stone ceramic tile of experimental group 4 and 5 is superior to, the further table of the result shows using provided in an embodiment of the present invention each
The tile product being prepared in process parameters range has more excellent physical property.
Experimental example 2
The entire body Dali stone ceramic tile that embodiment 1-3 and comparative example 1-2 are prepared is arranged to experimental group 1-5, it will be commercially available
Entire body Dali stone ceramic tile be arranged to experimental group 6；
The surface quality of observation experiment group 1-6：Every group of experimental group takes 100 pieces of products, and 0.8 meter of distant place of vertical product is seen
Examine whether product stain, pin hole occurs, two tone colour, lack flower, collapse the defects of angle, chipping and occur, and statistical probability, experimental group 1-6
The defects of probability be shown in Table 2：
The defects of 2 experimental group 1-6 of table probability
| Experimental group | 1 | 2 | 3 | 4 | 5 | 6 |
| Shortage probability (%) | 2% | 2% | 1% | 4% | 5% | 8% |
From the data in table 2, it can be seen that the defects of experimental group 1-5 probability, less than experimental group 6, and no more than 5%, which benefits
The creative restriction of each technological parameter, common to act synergistically in each step in the stone ceramic tile preparation process of entire body Dali, plays
Promote the effect of product quality.
The defects of experimental group 1-3, probability was less than experimental group 4 and 5, should the result shows that, using provided in an embodiment of the present invention each
The tile product being prepared in process parameters range has more excellent surface property.
Experimental example 3
The entire body Dali stone ceramic tile that embodiment 1-3 and comparative example 1-2 are prepared is arranged to experimental group 1-5, it will be commercially available
Entire body Dali stone ceramic tile be arranged to experimental group 6；
The section texture of observation experiment group 1-6, the wherein product of experimental group 1-3 have the texture thought and acted in one and the same way, experimental group
There is situations such as not deep enough in 4-6 section textures；The result further illustrates, is joined using each technique provided in an embodiment of the present invention
The tile product being prepared in number scope is more inside and outside consistent, and true to nature in table, quality is relatively reliable.
In conclusion the production method of entire body Dali provided by the present invention stone ceramic tile is simple, and it is workable, by the party
The entire body artificial marble products excellent quality that method is prepared, texture is more preferable, and effect is more life-like.
Embodiments described above is part of the embodiment of the present invention, instead of all the embodiments.The reality of the present invention
The detailed description for applying example is not intended to limit the scope of claimed invention, but is merely representative of the selected implementation of the present invention
Example.Based on the embodiments of the present invention, those of ordinary skill in the art are obtained without creative efforts
Every other embodiment, belongs to the scope of protection of the invention.
Claims (9)
1. a kind of production method of entire body Dali stone ceramic tile, which is characterized in that including：In 1245- after application glaze on green body
65-75min is fired at a temperature of 1250 DEG C.
2. the production method of entire body Dali according to claim 1 stone ceramic tile, which is characterized in that make the base of the green body
The fineness of material is 1.5-2mm.
3. the production method of entire body Dali according to claim 2 stone ceramic tile, which is characterized in that the blank is surveyed when starching
Flow velocity is 25-40s.
4. the production method of entire body Dali according to claim 2 stone ceramic tile, which is characterized in that the moisture of the green body contains
It measures as 0.05-0.1%.
5. the production method of entire body Dali according to claim 1 stone ceramic tile, which is characterized in that the application bag of the glaze
It includes：Apply a Ceng Di You and a level glaze successively to the green body.
6. the production method of entire body Dali according to claim 5 stone ceramic tile, which is characterized in that the application of the glaze is also
Including：To the after-applied overglaze of the Di You stamp.
7. the production method of entire body Dali according to claim 1 stone ceramic tile, which is characterized in that the fineness of the glaze is
0.025-0.035mm。
8. the production method of entire body Dali according to claim 5 stone ceramic tile, which is characterized in that apply the stream of the bottom You
Speed is 42-44s.
9. the production method of entire body Dali according to claim 5 stone ceramic tile, which is characterized in that apply the stream of the overglaze
Speed is 62-65s.