CN108083722B - 一种具有苏格兰方格布风格的硅藻泥的施工方法 - Google Patents
一种具有苏格兰方格布风格的硅藻泥的施工方法 Download PDFInfo
- Publication number
- CN108083722B CN108083722B CN201711259868.3A CN201711259868A CN108083722B CN 108083722 B CN108083722 B CN 108083722B CN 201711259868 A CN201711259868 A CN 201711259868A CN 108083722 B CN108083722 B CN 108083722B
- Authority
- CN
- China
- Prior art keywords
- powder
- diatom ooze
- construction method
- water
- iron oxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了一种具有苏格兰方格布风格的硅藻泥的施工方法。该施工方法包括批底‑粘贴网格布‑二次批底‑去网格布，收光‑上夹具，擦色‑扫粉‑二次扫粉‑完成。利用本发明的施工方法进行施工后，成品效果美观，富于苏格兰风情，满足了人们对硅藻泥壁材装饰性的要求。并且，本发明提供的硅藻泥中不含有任何对人体有害的物质，不释放甲醛、甲苯、氨气等对人们有害的气体，具有吸附降解甲醛有害气体的功能，还具有调节空气湿度，吸音降噪，防火阻燃等功能。
Description
技术领域
本发明属于建筑装饰装修材料领域，更具体地，涉及一种具有苏格兰方格布风格的硅藻泥的施工方法。
背景技术
硅藻土是一种生物成因的硅质沉积岩，它主要由古代硅藻的遗骸所组成，主要矿物成分为蛋白石及其变种，提纯后的硅藻土具有细腻、松散、质轻、多孔、吸水性和渗透性强的性质，因此越来越受到装修材料行业喜欢。硅藻土具有天然环保，孔隙率大、吸收性强、化学性质稳定、耐磨、耐热等特点，在日常生活中应用越来越广，广泛用于内墙装饰装修壁材、助滤剂、浴室防滑垫，硅藻砖等方面。
苏格兰格子图案历史悠久，在欧美纺织界有这样一种说法，“苏格兰格子，等于一部大英帝国的历史”。在现代服装设计的舞台上，苏格兰格子一直都是被经常运用到的设计元素之一，而且运用的形式与手法也越来越丰富，风格日趋多样化，苏格兰格子继续在苏格兰和英国的其他地方流行起来，苏格兰格子的图案种类和穿着范围也都大大地扩展了。我们仅以最近几年的时装潮流趋势来研判，无论是奔放的“民族风”、刚毅的“军装潮”、硬朗的“工装秀”，还是怀旧的“古着风”，格子衬衣都能与之完美融合。
如果在室内装饰装修时，能巧妙的把苏格兰格子和天花软装等融合在一起，在室内背景墙运用上苏格兰格子风格，那必将是锦上添花，为室内装修，尤其是欧式风格的装修，增加一道亮丽的风景。因此，发明一种具有苏格兰网格布风格的硅藻泥，即能满足环保性的要求，又极富艺术性和美感，满足市场对装饰性的要求。
目前市面上的硅藻泥装饰壁材可以制作出一些常见纹理，但是尚未有苏格兰格子风格的施工方法。
发明内容
本发明的目的在于提供一种具有苏格兰格子风格的特定的硅藻泥的施工方法。
为了实现上述目的，本发明提供一种具有苏格兰方格布风格的硅藻泥的施工方法，该施工方法包括批底-粘贴网格布-二次批底-去网格布，收光-上夹具，擦色-扫粉-二次扫粉-完成；
优选地，该施工方法包括如下步骤：
步骤1：对墙体基层进行处理，涂刮腻子层，使墙体平整；
步骤2：将硅藻泥主体材料与水混合搅拌，使硅藻泥浆体均匀、无团聚、无气泡，并将上述浆体静置；
步骤3：待腻子层完全干透后，将其打磨光滑平整，除去浮灰；然后批刮硅藻泥层，批刮厚度为0.5-1mm，待硅藻泥层5成干时，压平收光；
步骤4：将网格布固定在硅藻泥层上，确保网格布各个方向平整自然，无变形；
步骤5：批刮第二遍硅藻泥层；批刮完后，待硅藻泥3-4成干时，用收光刀收光，揭下网格布，待硅藻泥6-7成干时，再收光，使整个平面光滑平整，待8-9成干时，增加收光力度再次收光，以确保硅藻泥的粘结强度，干燥成型后不掉粉；
步骤6：将点料材料和水混合，搅拌均匀，得到点料材料浆体，将镂刻有横竖条纹的模具压在硅藻泥表面，以苏格兰格子的纹路，蘸点料材料浆体沿横纹路/竖纹路擦色，避免盖住竖纹/横纹；
步骤7：将扫粉材料和水混合，搅拌均匀，得到扫粉材料浆体，待点料浆体完全干透，蘸取扫粉材料浆体，沿模具的竖纹路从上到下扫粉或沿模具的横纹路从左到右扫粉；
步骤8：逐个颜色扫，直至全部扫完，拿掉模具，完成整个作业。
作为本发明优选的实施方式，其中，步骤2中，硅藻泥主体材料与水的重量比为1：0.9-1.2；步骤6中，点料材料与水的重量比为1：2.5-3.5，优选为1：3；步骤7中，扫粉材料与水的重量比为1：2.5-3。
经过多年的研究试验，发明人根据苏格兰格子的风格，研制出一种具有苏格兰风情的硅藻泥装饰壁材和施工方法，制作出来的成品美仑美奂，充满异域风情，满足了人们对硅藻泥装饰壁材的要求。
根据本发明一种具体实施方式，所述施工方法包括如下步骤：
步骤1：对墙体基层进行处理，为获得良好的苏格兰风格，墙体必须保证平整，墙体应当整体涂刮一层0.5-1.5mm的防水腻子并涂刷基膜；对于潮湿环境的墙面，必须刷涂专用封闭底漆，对于出现空鼓或裂纹的基底需预先处理；基底材料为同一物质，但有接缝的，需用网格布先贴上接缝；基底材料为不同材料(如水泥墙和木工板墙拼接，水泥墙和石膏板墙拼接，木工板墙和石膏板墙拼接等)，接缝处理就要用的确良布或无纺布，加白胶进行处理然后涂刷批刮防水腻子。刷涂完成后要求整个腻子层光滑、平整，用2米靠尺检测平整度要求误差不超过3mm，垂直度误差不超过3mm，阴阳角误差不超过3mm。
步骤2：将硅藻泥主体材料与水按1：0.9-1.2的比例搅拌均匀，本步骤中要求施工温度不低于5℃。硅藻泥与水混合均匀的方法如下：先在容器中加入30％水，再小心加入所述的硅藻泥，缓慢搅拌10分钟，静置2分钟，加入剩余70％水，静置3分钟后，用电动搅拌器搅拌10-15分钟，静置3-6分钟后，再用电动搅拌器搅拌10-15分钟，确保硅藻泥浆体均匀、无团聚、无气泡；将上述浆体静置10-15分钟。
步骤3：等腻子层完全干透后，用200-800目砂纸将基层打磨光滑平整，用毛刷除去浮灰；然后批刮硅藻泥层，厚度为0.5-1mm，批刮时用抹刀从各个不同的方向涂抹，等硅藻泥层5成干时，用专用抹刀压平收光，收光次数为2-3次。
步骤4：将网格布小心铺在硅藻泥层上，用胶带粘牢，确保各个方向平整，无变形。
步骤5：用批刀批第二遍硅藻泥层，厚度为0.5-1mm；批完后，等硅藻泥3、4成干时，用收光刀轻轻收一遍光。然后小心撕掉胶带，揭下网格布，注意不要带起硅藻泥。等硅藻泥6、7成干时，用收光刀再轻轻收一遍光，使整个平面光滑平整。等8、9成干时，再稍微重力收一遍光，确保硅藻泥的粘结强度，保证干燥成型后不掉粉。
步骤6：将点料调至合适的浓稠度，按照苏格兰格子的纹路打印制作镂空模具，将镂刻有横竖条纹的模具轻轻压在硅藻泥表面，尽量模仿苏格兰格子的纹路，用海藻蘸少量的点料轻轻沿着横纹路擦色，颜色均匀美观，不要太艳丽，以免盖住竖纹。擦2-3遍，等点料颜料完全干透。
步骤7：将扫粉和水按比例混合，搅拌均匀至适宜的浓度，然后用软羊毛刷蘸取少量的扫粉，沿模具的竖纹路，从上到下扫上扫粉，扫粉时不要将颜料沾在模具以外的硅藻泥上。一次扫完等扫粉完全干透后，扫下一遍，扫2-3遍，直至达到理想的颜色饱和度。
步骤8：扫完第一种颜色，再扫下一种颜色，第一条竖纹用一种颜色，间隔3-4个竖纹，颜色循环一次。等所有的扫粉扫完，拿掉模具，即完全整个作业。
优选地，所述主体材料包括硅藻土、沸石、凹凸棒土、水洗陶土、海泡石粉、硅灰石粉、纳米氧化锌、金红石型钛白粉、白云石粉、硅藻土负载纳米二氧化钛、保水剂、有机胶凝材料、无机胶凝材料。
所述点料材料包括滑石粉、硅藻土负载纳米二氧化钛、金红石型钛白粉、羟丙基甲基纤维素醚、可再分散胶粉、无机氧化铁颜料。
所述扫粉材料包括可再分散胶粉、硅灰石粉、无机氧化铁颜料。
主体材料的配方保证了整个硅藻泥墙面具有良好的调湿和吸附降解功能，并保证其具有一定的粘结强度，不空鼓，不掉粉。
点料材料通常要求氧化铁颜料色泽鲜艳纯洁无杂质或杂色，优选地，颜料使用前经20000r/min的高速粉碎机进行打碎以保证颜料中没有大颗粒，易混合均匀。
扫粉材料在使整个扫面具有良好的润滑性的同时，保证它具有良好的粘结性和一定的遮盖性。
作为本发明优选的实施方式，其中，
以主体材料的重量为基准，所述主体材料包括硅藻土15-40wt％、沸石5-20wt％、凹凸棒土5-20wt％、水洗陶土5-30wt％、海泡石粉3-15wt％、硅灰石粉3-35wt％、纳米氧化锌0.5-2wt％、金红石型钛白粉3-15wt％、白云石粉3-15wt％、硅藻土负载纳米二氧化钛0.8-2wt％、保水剂：0.5-5wt％、有机胶凝材料1-3wt％、无机胶凝材料10-35wt％。
以点料材料的重量为基准，所述点料材料包括滑石粉60-85wt％、硅藻土负载纳米二氧化钛1-5wt％、金红石型钛白粉1-10wt％、羟丙基甲基纤维素醚0.5-8wt％、可再分散胶粉5-25wt％、无机氧化铁颜料1-10wt％。
以扫粉材料的重量为基准，所述扫粉材料包括可再分散胶粉10-40wt％、硅灰石粉30-80wt％、无机氧化铁颜料3-20wt％。
作为本发明优选的实施方式，其中，滑石粉与可再分散胶粉的重量比为5：1，所述滑石粉的白度≥92，以便使整个扫面在具有良好的润滑性的同时，具有良好的粘结性和一定的遮盖性。
作为本发明优选的实施方式，其中，硅藻土的粒径为300-400目，更优选为325目；沸石的粒径为650-1000目，更优选为800目；凹凸棒土的粒径为350-650目，更优选为800目；水洗陶土的粒径为300-400目，更优选为325目；海泡石粉的粒径为800-1100目，更优选为1000目；硅灰石粉的粒径为800-1100目，纳米氧化锌的粒径为5-15nm，更优选为10nm；金红石型钛白粉的粒径为650-1000目，更优选为800目；白云石粉的粒径为300-400目，滑石粉的粒径为1100-1300目，更优选为1250目；无机氧化铁颜料的粒径为1100-1300目。
硅藻土作为功能材料，具有调节湿度，吸附有害气体甲醛等功效。
沸石作为另外一种功能材料，可提高产品的吸附性能和调湿性能。
凹凸棒土具有纤维状结构，有极优的吸附性，搅拌成型后又有一定粘性，可节省一部分胶凝材料的使用，同时还可以抗开裂。
水洗陶土主要由高岭土、白云母、蒙脱石等组成，其中高岭土具有良好的可塑性和耐火性，使硅藻泥易于搅拌施工，成形后不易变形，同时高岭土耐高温，增强硅藻泥产品的阻燃性；蒙脱石具有吸附性和悬浮性，使用在硅藻泥产品中，可提高硅藻泥搅拌过程中的悬浮性，使产品更易分散均匀，同时延长可施工时间；白云母反射性强，能将产品中的无机颜料光线大部分反射，使产品颜色亮丽。
海泡石粉是天然存在的比表面积最大的天然无机非金属矿，其孔隙丰富，吸水性强，且由于大多数孔为大孔结构，吸附水分子在环境湿度降低时可以释放出来，因此可以增大放湿量，放湿性能优越，另外，加水具粘性和可塑性，干燥后收缩小，不会产生裂纹。
金红石型钛白粉的白度在97以上，无结团及团聚现象，遮盖力好，使用后增加物料的柔和度，使材料成形后有光泽。
纳米氧化锌起到了防霉抗菌的作用。
硅藻土负载纳米二氧化钛，可通过光催化作用分解甲醛等有害物质。
保水剂在水中溶解后在物料表面形成一层润滑膜，提高硅藻泥在施工过程中的流动性和滑爽性；由于自身含有较多亲水基团，使砂浆中的水分不易失去，延长可施工时间。
有机胶凝材料可提高硅藻泥的柔性并有较长的开放时间，可改善硅藻泥粘附性可塑性、耐磨性，成膜的聚合物树脂作为增强材料分布于整个砂浆体系中，从而增加了砂浆的内聚力。
无机胶凝材料保证硅藻泥具有良好粘结性能和强度。
滑石粉具有润滑性、遮盖力良好、柔软、光泽好、吸附力强等优良性能。
作为本发明优选的实施方式，所述无机氧化铁颜料选自氧化铁黄、氧化铁红、氧化铁黑、氧化铁绿、氧化铁棕、氧化铁宝蓝、氧化铁群青、氧化铁大红中的至少一种。
作为本发明优选的实施方式，所述保水剂选自甲基纤维素醚、乙基纤维素醚、羟丙基甲基纤维素醚和羟乙基甲基纤维素醚中的至少一种。
作为本发明优选的实施方式，所述有机胶凝材料包括生物质胶粉和/或聚乙烯醇。
生物质胶粉是一种高粘性胶粉，采用植物材料制造，系天然环保产品，具有高强力的粘贴力。该胶粉是采用欧洲天然植物纤维原料，经高分子萃取物制造而成的粘胶制品，是建筑装饰业粘胶产品中少有的可生物降解，完全无毒、无害，绿色环保的健康型产品，其粘度高，能有效提高硅藻泥粘接力，防止墙体开裂、掉粉等。
作为本发明优选的实施方式，所述无机胶凝材料选自白水泥、灰钙粉、石膏粉和水玻璃中的至少一种。
发明人经过潜心的研究试验，发现为了使硅藻泥呈现出苏格兰格子的风格，第一个关键点在于硅藻泥的配方组成；第二个关键点在于施工工艺，特别是硅藻泥的小方格和扫粉组成的大方格的比例，该比例为1：(6-7)时施工效果最佳，指长度比；第三个关键点在于点料和扫粉的颜色搭配；第四个关键点在于扫粉的颜色间隔和相互搭配，这些因素都会影响最终施工出来的效果。
综上，利用本发明的硅藻泥配方及施工方法进行施工后，能够得到呈现苏格兰格子的硅藻泥壁材，成品效果美观，富于苏格兰风情，满足了人们对硅藻泥壁材装饰性的要求。并且，本发明提供的硅藻泥中不含有任何对人体有害的物质，不释放甲醛、甲苯、氨气等对人们有害的气体，具有吸附降解甲醛有害气体的功能，还具有调节空气湿度，吸音降噪，防火阻燃等功能。
本发明的其它特征和优点将在随后具体实施方式部分予以详细说明。
具体实施方式
下面将更详细地描述本发明的优选实施方式。虽然以下描述了本发明的优选实施方式，然而应该理解，可以以各种形式实现本发明而不应被这里阐述的实施方式所限制。相反，提供这些实施方式是为了使本发明更加透彻和完整，并且能够将本发明的范围完整地传达给本领域的技术人员。
实施例1-3所采用的施工方法包括如下步骤：
步骤1：对墙体基层进行处理，为获得良好的苏格兰风格，墙体必须保证平整，墙体应当整体涂刮一层0.5-1.5mm的防水腻子并涂刷基膜；对于潮湿环境的墙面，必须刷涂专用封闭底漆，对于出现空鼓或裂纹的基底需预先处理；基底材料为同一物质，但有接缝的，需用网格布先贴上接缝；基底材料为不同材料(如水泥墙和木工板墙拼接，水泥墙和石膏板墙拼接，木工板墙和石膏板墙拼接等)，接缝处理就要用的确良布或无纺布，加白胶进行处理然后涂刷批刮防水腻子。刷涂完成后要求整个腻子层光滑、平整，用2米靠尺检测平整度要求误差不超过3mm，垂直度误差不超过3mm，阴阳角误差不超过3mm。
步骤2：将硅藻泥主体材料与水按1：0.9-1.2的比例搅拌均匀，本步骤中要求施工温度不低于5℃。硅藻泥与水混合均匀的方法如下：先在容器中加入30％水，再小心加入所述的硅藻泥，缓慢搅拌10分钟，静置2分钟，加入剩余70％水，静置3分钟后，用电动搅拌器搅拌10-15分钟，静置3-6分钟后，再用电动搅拌器搅拌10-15分钟，确保硅藻泥浆体均匀、无团聚、无气泡；将上述浆体静置10-15分钟。
步骤3：批刮硅藻泥层，等腻子层完全干透后，用200-800目砂纸将基层打磨光滑平整，用毛刷除去浮灰；然后批刮硅藻泥层，厚度为0.5-1mm，批刮时用抹刀从各个不同的方向涂抹，等硅藻泥层5成干时，用专用抹刀压平收光，收光次数为2-3次。
步骤4：将网格布小心铺在硅藻泥层上，用胶带粘牢，确保各个方向平整自然，无变形。
步骤5：用批刀批第二遍硅藻泥层，厚度为0.5-1mm；批完后，等硅藻泥3、4成干时，用收光刀轻轻收一遍光。然后小心撕掉胶带，揭下网格布，注意不要带起硅藻泥。等硅藻泥6、7成干时，用收光刀再轻轻收一遍光，使整个平面光滑平整。等8、9成干时，再稍微重力收一遍光，确保硅藻泥的粘结强度，保证干燥成型后不掉粉。
步骤6：将点料调至合适的浓稠度，按照苏格兰格子的纹路打印制作镂空模具，将镂刻有横竖条纹的模具轻轻压在硅藻泥表面，尽量模仿苏格兰格子的纹路，用海藻蘸少量的点料轻轻沿着横纹路擦色，颜色均匀美观，不要太艳丽，以免盖住竖纹。擦2-3遍，等点料颜料完全干透。
步骤7：将扫粉和水按比例混合，搅拌均匀至适宜的浓度，然后用软羊毛刷蘸取少量的扫粉，沿模具的竖纹路，从上到下扫上扫粉，扫粉时不要将颜料沾在模具以外的硅藻泥上。一次扫完等扫粉完全干透后，扫下一遍，扫2-3遍，直至达到理想的颜色饱和度。
步骤8：扫完第一种颜色，再扫下一种颜色，第一条竖纹用一种颜色，间隔3-4个竖纹，颜色循环一次。等所有的扫粉扫完，拿掉模具，即完全整个作业。
实施例1：
以主体材料的重量为基准，主体材料包括：
主体材料与水的重量比为1：1
以点料材料的重量为基准，点料材料包括
点料材料与水的重量比为1：3
扫粉配方：
扫粉材料与水的重量比为1：2.5
实施例2：
主体配方：
主体材料与水的重量比为0.9：1
点料配方：
点料材料与水的重量比为1：3
扫粉配方：
扫粉材料与水的重量比为1：3
实施例3：
主体配方：
主体材料与水的重量比为1.2：1
点料配方：
点料材料与水的重量比为1：3
扫粉配方：
扫粉材料与水的重量比为1：2.5
以上已经描述了本发明的各实施例，上述说明是示例性的，并非穷尽性的，并且也不限于所披露的各实施例。在不偏离所说明的各实施例的范围和精神的情况下，对于本技术领域的普通技术人员来说许多修改和变更都是显而易见的。
Claims (9)
1.一种具有苏格兰方格布风格的硅藻泥的施工方法，其特征在于，该施工方法包括批底-粘贴网格布-二次批底-去网格布，收光-上夹具，擦色-扫粉-二次扫粉-完成；
步骤1：对墙体基层进行处理，涂刮腻子层，使墙体平整；
步骤2：将硅藻泥主体材料与水混合搅拌，使硅藻泥浆体均匀、无团聚、无气泡，并将上述浆体静置；
步骤3：待腻子层完全干透后，将其打磨光滑平整，除去浮灰；然后批刮硅藻泥层，批刮厚度为0.5-1mm，待硅藻泥层5成干时，压平收光；
步骤4：将网格布固定在硅藻泥层上，确保网格布各个方向平整自然，无变形；
步骤5：批刮第二遍硅藻泥层；批刮完后，待硅藻泥3-4成干时，用收光刀收光，揭下网格布，待硅藻泥6-7成干时，再收光，使整个平面光滑平整，待8-9成干时，增加收光力度再次收光，以确保硅藻泥的粘结强度，干燥成型后不掉粉；
步骤6：将点料材料和水混合，搅拌均匀，得到点料材料浆体，将镂刻有横竖条纹的模具压在硅藻泥表面，以苏格兰格子的纹路，蘸点料材料浆体沿横纹路/竖纹路擦色，避免盖住竖纹/横纹；
步骤7：将扫粉材料和水混合，搅拌均匀，得到扫粉材料浆体，待点料浆体完全干透，蘸取扫粉材料浆体，沿模具的竖纹路从上到下扫粉或沿模具的横纹路从左到右扫粉；
步骤8：逐个颜色扫，直至全部扫完，拿掉模具，完成整个作业。
2.根据权利要求1所述的施工方法，其中，步骤2中，硅藻泥主体材料与水的重量比为1：0.9-1.2；步骤6中，点料材料与水的重量比为1：2.5-3.5步骤7中，扫粉材料与水的重量比为1：2.5-3。
3.根据权利要求1所述的施工方法，其中，步骤8中，扫完第一种颜色，再扫下一种颜色，第一条竖纹用一种颜色，间隔3-4个竖纹，颜色循环一次。
4.根据权利要求1所述的施工方法，其中，
所述主体材料包括硅藻土、沸石、凹凸棒土、水洗陶土、海泡石粉、硅灰石粉、纳米氧化锌、金红石型钛白粉、白云石粉、硅藻土负载纳米二氧化钛、保水剂、有机胶凝材料、无机胶凝材料；
所述点料材料包括滑石粉、硅藻土负载纳米二氧化钛、金红石型钛白粉、羟丙基甲基纤维素醚、可再分散胶粉、无机氧化铁颜料；
所述扫粉材料包括可再分散胶粉、硅灰石粉、无机氧化铁颜料。
5.根据权利要求4所述的施工方法，其中，
以主体材料的重量为基准，所述主体材料包括硅藻土15-40wt％、沸石5-20wt％、凹凸棒土5-20wt％、水洗陶土5-30wt％、海泡石粉3-15wt％、硅灰石粉3-35wt％、纳米氧化锌0.5-2wt％、金红石型钛白粉3-15wt％、白云石粉3-15wt％、硅藻土负载纳米二氧化钛0.8-2wt％、保水剂：0.5-5wt％、有机胶凝材料1-3wt％、无机胶凝材料10-35wt％；
以点料材料的重量为基准，所述点料材料包括滑石粉60-85wt％、硅藻土负载纳米二氧化钛1-5wt％、金红石型钛白粉1-10wt％、羟丙基甲基纤维素醚0.5-8wt％、可再分散胶粉5-25wt％、无机氧化铁颜料1-10wt％；
以扫粉材料的重量为基准，所述扫粉材料包括可再分散胶粉10-40wt％、硅灰石粉30-80wt％、无机氧化铁颜料3-20wt％。
6.根据权利要求4或5所述的施工方法，其中，滑石粉与可再分散胶粉的重量比为5：1，所述滑石粉的白度≥92。
7.根据权利要求4或5所述的施工方法，其中，硅藻土的粒径为300-400目，沸石的粒径为650-1000目，凹凸棒土的粒径为350-650目，水洗陶土的粒径为300-400目，海泡石粉的粒径为800-1100目，硅灰石粉的粒径为800-1100目，纳米氧化锌的粒径为5-15nm，金红石型钛白粉的粒径为650-1000目，白云石粉的粒径为300-400目，滑石粉的粒径为1100-1300目；无机氧化铁颜料的粒径为1100-1300目。
8.根据权利要求4或5所述的施工方法，其中，所述无机氧化铁颜料选自氧化铁黄、氧化铁红、氧化铁黑、氧化铁绿、氧化铁棕、氧化铁宝蓝、氧化铁群青、氧化铁大红中的至少一种。
9.根据权利要求4或5所述的施工方法，其中，所述保水剂选自甲基纤维素醚、乙基纤维素醚、羟丙基甲基纤维素醚和羟乙基甲基纤维素醚中的至少一种；所述有机胶凝材料包括生物质胶粉和/或聚乙烯醇；所述无机胶凝材料选自白水泥、灰钙粉、石膏粉和水玻璃中的至少一种。