CN108070938A - Ice is felt well wrap yarn and its production method - Google Patents
Ice is felt well wrap yarn and its production method Download PDFInfo
- Publication number
- CN108070938A CN108070938A CN201711285610.0A CN201711285610A CN108070938A CN 108070938 A CN108070938 A CN 108070938A CN 201711285610 A CN201711285610 A CN 201711285610A CN 108070938 A CN108070938 A CN 108070938A
- Authority
- CN
- China
- Prior art keywords
- yarn
- ice
- fiber
- felt well
- well
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
It feels well wrap yarn and its production method the present invention provides ice, which includes heart yarn and outsourcing yarn, and heart yarn is spandex thread, and outsourcing yarn is felt well yarn for jade fiber, Basho fiber and ice made of ramee, and the ice is felt well yarn winding spandex thread and coating spandex silk.Outsourcing yarn of the present invention is felt well yarn for jade fiber, Basho fiber and ice made of ramee, has rapid diffusion body heat, sweat dissipation, ice is accelerated to feel well ventilative good characteristic, dress has preferably nice and cool pro-skin comfort, and application market is wide.
Description
Technical field
The invention belongs to textile technology field more particularly to wrap yarn and its production methods.
Background technology
Wrap yarn is a kind of yarn of new structure, it be using long filament or staple fiber as yarn core, outsourcing another kind long filament or
Staple fiber sliver.Wrap yarn be widely used in high-grade underwear, silk stocking, jeans, high-grade suit fabric, etc. products production.
At present, popular ice fabric of feeling well is mostly chemical synthetic fiber on the market, has sweat absorption and flash drying, but pro-skin comfort
It is poor.
The content of the invention
The present invention provides ice and feels well wrap yarn, and ice is felt well ventilative, and pro-skin is comfortable, and the present invention also provides its production methods.
The present invention is achieved through the following technical solutions:
Ice is felt well wrap yarn, and including heart yarn and outsourcing yarn, the heart yarn is spandex thread, and outsourcing yarn is jade fiber, bajiao banana is fine
Ice made of dimension and ramee is felt well yarn, and the ice is felt well yarn winding spandex thread and coating spandex silk.
The wrap yarn includes following components in percentage by weight:Spandex thread 35-45%, jade fiber 20-30%, bajiao banana
Fiber 14-20%, ramee 20-25%.
Preferably, the fiber number of the jade fiber is 5-8D, length 51-76mm.
Above-mentioned ice is felt well the production method of wrap yarn:Comprise the following steps:
(1) by jade fiber, Basho fiber and ramee respectively successively through grabbing cotton, mixed cotton, opener, coiled, cotton carding,
Head and and two and after half ripe bar is made, three and half ripe bars are made through last mixing in doubling step, Roving Frames, spinning process and winding procedure
Ice is felt well yarn;
(2) using spandex thread as heart yarn, yarn is felt well as outsourcing silk using ice, spandex filament drafting, ice feel well Yarn twisting cladding, winding
Wrap yarn is made;
(3) taken out after wrap yarn being put into 50-55 DEG C of insulated building inside holding 5-6h, natural cooling.
The preparation method of the Basho fiber is as follows:Bajiao banana cane, which passes through, to be impregnated, squeezes, washing, being dehydrated, at biological enzyme
It manages, wash, be dehydrated, shake up, dry, be made;
The cellulase treatment is immersed in for bajiao banana stem fiber in the treatment fluid of 18-20 times of weight, in the treatment fluid
Cellulase is 1-1.5wt%, and pectase 0.3-0.5wt%, treatment fluid temperature is 40-50 DEG C, and the pH value for the treatment of fluid is 3-5
Processing time is 60-70min.
The beneficial effects are mainly as follows following:
Outsourcing yarn of the present invention is felt well yarn for jade fiber, Basho fiber and ice made of ramee, has rapid diffusion
Body heat, accelerate sweat dissipation, ice are felt well ventilative good characteristic, and dress has preferably nice and cool pro-skin comfort, and application market is wide.
Specific embodiment
With reference to embodiment, present disclosure is further illustrated.It should be appreciated that the implementation of the present invention is not limited to
In the following examples, the accommodation in any form and/or change made to the present invention fall within the scope of the present invention.
In the present invention, if not refering in particular to, all parts, percentage are unit of weight, and all equipment and raw material etc. are equal
It is commercially available or the industry is common.Method in following embodiments is the routine of this field unless otherwise instructed
Method.
Embodiment 1
Ice is felt well wrap yarn, and including heart yarn and outsourcing yarn, the heart yarn is spandex thread, and outsourcing yarn is jade fiber, bajiao banana is fine
Ice made of dimension and ramee is felt well yarn, spandex thread 40%, jade fiber 25%, Basho fiber 15%, ramee 20%;
The ice is felt well yarn winding spandex thread and coating spandex silk.
Above-mentioned ice is felt well the production method of wrap yarn:Comprise the following steps:
(1) preparation method of Basho fiber is as follows:Bajiao banana cane by immersion, squeezing, washing, dehydration, cellulase treatment,
It washes, be dehydrated, shake up, dry, be made;
The cellulase treatment is immersed in for bajiao banana stem fiber in the treatment fluid of 18 times of weight, fiber in the treatment fluid
Plain enzyme is 1.5wt%, and pectase 0.4wt%, treatment fluid temperature is 45 DEG C, and the pH value for the treatment of fluid is 3, and processing time is
70min。
(2) by jade fiber, Basho fiber and ramee respectively successively through grabbing cotton, mixed cotton, opener, coiled, cotton carding,
Head and and two and after half ripe bar is made, three and half ripe bars are made through last mixing in doubling step, Roving Frames, spinning process and winding procedure
Ice is felt well yarn;
The fiber number of jade fiber is 5-8D, and length 51-76mm is bought by Shangyu Honjoy Co., Ltd..
The key step parameter of jade fiber:
Opener main technologic parameters:Cylinder speed 500r/min;Feeding roller 8r/min;Fan 1100r/min;
Cotton carding main technologic parameters:Cylinder-Flat Gauge 0.25*0.23*0.2*0.2*0.23mm;Cylinder speed 380r/
min;Licker-in speed 650r/min;Doffer speed 23r/min;Cover plate speed 98mm/min;
Head and main technologic parameters:Combined roots 5;First break draft 1.3;Total draft multiple:4.9;Roller gauge 7*15mm;
Two and main technologic parameters:Combined roots 8;First break draft 1.7;Total draft multiple:8.5;Roller gauge 7*15mm;
The key step parameter of Basho fiber:
Opener main technologic parameters:Cylinder speed 420r/min;Feeding roller 8r/min;Fan 1300r/min;
Cotton carding main technologic parameters:Cylinder-Flat Gauge 0.3*0.23*0.25*0.2*0.23mm;Cylinder speed 300r/
min;Licker-in speed 580r/min;Doffer speed 18r/min;Cover plate speed 80mm/min;
Head and main technologic parameters:Combined roots 5;First break draft 1.1;Total draft multiple:3.8;Roller gauge 6*15mm;
Two and main technologic parameters:Combined roots 8;First break draft 1.6;Total draft multiple:7.5;Roller gauge 6*15mm;
The key step parameter of ramee:
Opener main technologic parameters:Cylinder speed 500r/min;Feeding roller 9r/min;Fan 1200r/min;
Cotton carding main technologic parameters:Cylinder-Flat Gauge 0.28*0.25*0.23*0.2*0.23mm;Cylinder speed 350r/
min;Licker-in speed 620r/min;Doffer speed 19r/min;Cover plate speed 90mm/min;
Head and main technologic parameters:Combined roots 5;First break draft 1.2;Total draft multiple:4.8;Roller gauge 6*15mm;
Two and main technologic parameters:Combined roots 8;First break draft 1.5;Total draft multiple:7.5;Roller gauge 6*15mm;
Above-mentioned end mixing in doubling step main technologic parameters:First break draft 1.6;Total draft multiple:8.1;Roller gauge 5*17mm;
Roving Frames main technologic parameters:Twist factor 85, gauge 27*37mm, Pullin performances:5.9*1.3 front roller speed
200r/min;
Spinning process main technologic parameters:Twist factor 320, gauge 19*30mm, Pullin performances:24*1.2, front roller speed
204r/min。
(3) using spandex thread as heart yarn, yarn is felt well as outsourcing silk using ice, spandex filament drafting, ice feel well Yarn twisting cladding, winding
Wrap yarn is made;
(4) taken out after wrap yarn being put into 50 DEG C of insulated building inside holding 5.5h, natural cooling.
Embodiment 2
Ice is felt well wrap yarn, and including heart yarn and outsourcing yarn, the heart yarn is spandex thread, and outsourcing yarn is jade fiber, bajiao banana is fine
Ice made of dimension and ramee is felt well yarn, spandex thread 37%, jade fiber 28%, Basho fiber 14%, ramee 21%;
The ice is felt well yarn winding spandex thread and coating spandex silk.
Above-mentioned ice is felt well the production method of wrap yarn:Comprise the following steps:
(1) preparation method of Basho fiber is as follows:Bajiao banana cane by immersion, squeezing, washing, dehydration, cellulase treatment,
It washes, be dehydrated, shake up, dry, be made;
The cellulase treatment is immersed in for bajiao banana stem fiber in the treatment fluid of 19 times of weight, fiber in the treatment fluid
Plain enzyme is 1.2wt%, and pectase 0.3wt%, treatment fluid temperature is 40 DEG C, and the pH value for the treatment of fluid is 4, and processing time is
65min。
(2) by jade fiber, Basho fiber and ramee respectively successively through grabbing cotton, mixed cotton, opener, coiled, cotton carding,
Head and and two and after half ripe bar is made, three and half ripe bars are made through last mixing in doubling step, Roving Frames, spinning process and winding procedure
Ice is felt well yarn;
The fiber number of jade fiber is 5-8D, and length 51-76mm is bought by Shangyu Honjoy Co., Ltd..
The key step parameter of jade fiber:
Opener main technologic parameters:Cylinder speed 450r/min;Feeding roller 8r/min;Fan 1200r/min;
Cotton carding main technologic parameters:Cylinder-Flat Gauge 0.25*0.23*0.2*0.2*0.23mm;Cylinder speed 380r/
min;Licker-in speed 650r/min;Doffer speed 23r/min;Cover plate speed 98mm/min;
Head and main technologic parameters:Combined roots 5;First break draft 1.3;Total draft multiple:4.9;Roller gauge 7*15mm;
Two and main technologic parameters:Combined roots 8;First break draft 1.7;Total draft multiple:8.5;Roller gauge 7*15mm;
The key step parameter of Basho fiber:
Opener main technologic parameters:Cylinder speed 420r/min;Feeding roller 8r/min;Fan 1300r/min;
Cotton carding main technologic parameters:Cylinder-Flat Gauge 0.3*0.23*0.25*0.2*0.23mm;Cylinder speed 300r/
min;Licker-in speed 580r/min;Doffer speed 18r/min;Cover plate speed 80mm/min;
Head and main technologic parameters:Combined roots 5;First break draft 1.1;Total draft multiple:3.8;Roller gauge 6*15mm;
Two and main technologic parameters:Combined roots 8;First break draft 1.6;Total draft multiple:7.5;Roller gauge 6*15mm;
The key step parameter of ramee:
Opener main technologic parameters:Cylinder speed 500r/min;Feeding roller 9r/min;Fan 1200r/min;
Cotton carding main technologic parameters:Cylinder-Flat Gauge 0.28*0.25*0.23*0.2*0.23mm;Cylinder speed 350r/
min;Licker-in speed 620r/min;Doffer speed 19r/min;Cover plate speed 90mm/min;
Head and main technologic parameters:Combined roots 5;First break draft 1.2;Total draft multiple:4.8;Roller gauge 6*15mm;
Two and main technologic parameters:Combined roots 8;First break draft 1.5;Total draft multiple:7.5;Roller gauge 6*15mm;
Above-mentioned end mixing in doubling step main technologic parameters:First break draft 1.6;Total draft multiple:8.1;Roller gauge 5*17mm;
Roving Frames main technologic parameters:Twist factor 85, gauge 27*37mm, Pullin performances:5.9*1.3 front roller speed
200r/min;
Spinning process main technologic parameters:Twist factor 320, gauge 19*30mm, Pullin performances:24*1.2, front roller speed
204r/min。
(3) using spandex thread as heart yarn, yarn is felt well as outsourcing silk using ice, spandex filament drafting, ice feel well Yarn twisting cladding, winding
Wrap yarn is made;
(4) taken out after wrap yarn being put into 50 DEG C of insulated building inside holding 6h, natural cooling.
Embodiment 3
Ice is felt well wrap yarn, and including heart yarn and outsourcing yarn, the heart yarn is spandex thread, and outsourcing yarn is jade fiber, bajiao banana is fine
Ice made of dimension and ramee is felt well yarn, spandex thread 36%, jade fiber 24%, Basho fiber 20%, ramee 20%;
The ice is felt well yarn winding spandex thread and coating spandex silk.
Above-mentioned ice is felt well the production method of wrap yarn:Comprise the following steps:
(1) preparation method of Basho fiber is as follows:Bajiao banana cane by immersion, squeezing, washing, dehydration, cellulase treatment,
It washes, be dehydrated, shake up, dry, be made;
The cellulase treatment is immersed in for bajiao banana stem fiber in the treatment fluid of 20 times of weight, fiber in the treatment fluid
Plain enzyme is 1wt%, and pectase 0.5wt%, treatment fluid temperature is 50 DEG C, and the pH value for the treatment of fluid is 5, processing time 60min.
(2) by jade fiber, Basho fiber and ramee respectively successively through grabbing cotton, mixed cotton, opener, coiled, cotton carding,
Head and and two and after half ripe bar is made, three and half ripe bars are made through last mixing in doubling step, Roving Frames, spinning process and winding procedure
Ice is felt well yarn;
The fiber number of jade fiber is 5-8D, and length 51-76mm is bought by Shangyu Honjoy Co., Ltd..
The key step parameter of jade fiber:
Opener main technologic parameters:Cylinder speed 450r/min;Feeding roller 8r/min;Fan 1200r/min;
Cotton carding main technologic parameters:Cylinder-Flat Gauge 0.25*0.23*0.2*0.2*0.23mm;Cylinder speed 400r/
min;Licker-in speed 700r/min;Doffer speed 23r/min;Cover plate speed 98mm/min;
Head and main technologic parameters:Combined roots 5;First break draft 1.3;Total draft multiple:4.9;Roller gauge 7*15mm;
Two and main technologic parameters:Combined roots 8;First break draft 1.7;Total draft multiple:8.5;Roller gauge 7*15mm;
The key step parameter of Basho fiber:
Opener main technologic parameters:Cylinder speed 390r/min;Feeding roller 8r/min;Fan 1300r/min;
Cotton carding main technologic parameters:Cylinder-Flat Gauge 0.3*0.23*0.25*0.2*0.23mm;Cylinder speed 300r/
min;Licker-in speed 580r/min;Doffer speed 18r/min;Cover plate speed 80mm/min;
Head and main technologic parameters:Combined roots 5;First break draft 1.1;Total draft multiple:3.8;Roller gauge 6*15mm;
Two and main technologic parameters:Combined roots 8;First break draft 1.6;Total draft multiple:7.5;Roller gauge 6*15mm;
The key step parameter of ramee:
Opener main technologic parameters:Cylinder speed 500r/min;Feeding roller 9r/min;Fan 1200r/min;
Cotton carding main technologic parameters:Cylinder-Flat Gauge 0.28*0.25*0.23*0.2*0.23mm;Cylinder speed 350r/
min;Licker-in speed 620r/min;Doffer speed 19r/min;Cover plate speed 90mm/min;
Head and main technologic parameters:Combined roots 5;First break draft 1.2;Total draft multiple:4.8;Roller gauge 6*15mm;
Two and main technologic parameters:Combined roots 8;First break draft 1.5;Total draft multiple:7.5;Roller gauge 6*15mm;
Above-mentioned end mixing in doubling step main technologic parameters:First break draft 1.6;Total draft multiple:8.1;Roller gauge 5*17mm;
Roving Frames main technologic parameters:Twist factor 85, gauge 27*37mm, Pullin performances:5.9*1.3 front roller speed
200r/min;
Spinning process main technologic parameters:Twist factor 320, gauge 19*30mm, Pullin performances:24*1.2, front roller speed
204r/min。
(3) using spandex thread as heart yarn, yarn is felt well as outsourcing silk using ice, spandex filament drafting, ice feel well Yarn twisting cladding, winding
Wrap yarn is made;
(4) taken out after wrap yarn being put into 55 DEG C of insulated building inside holding 5h, natural cooling.
Although inventor has done technical scheme more detailed elaboration and has enumerated, it should be understood that right
For the those skilled in the art of this field one, modification is made to above-described embodiment or uses equivalent alternative solution, this
It is it is clear that these made without departing from theon the basis of the spirit of the present invention are changed or changed to those skilled in the art
Into belonging to the scope of protection of present invention.
Claims (5)
- The wrap yarn 1. ice is felt well, it is characterised in that:Including heart yarn and outsourcing yarn, the heart yarn is spandex thread, and outsourcing yarn is fine for jade Ice made of dimension, Basho fiber and ramee is felt well yarn, and the ice is felt well yarn winding spandex thread and coating spandex silk.
- The wrap yarn 2. ice as described in claim 1 is felt well, it is characterised in that:The wrap yarn includes the group of following weight percent Point:Spandex thread 35-45%, jade fiber 20-30%, Basho fiber 14-20%, ramee 20-25%.
- The wrap yarn 3. ice as claimed in claim 2 is felt well, it is characterised in that:The fiber number of the jade fiber is 5-8D, and length is 51-76mm。
- The production method of wrap yarn 4. ice as claimed in claim 2 is felt well, it is characterised in that:Comprise the following steps:(1) by jade fiber, Basho fiber and ramee respectively successively by grabbing cotton, mixed cotton, opener, coiled, cotton carding, head simultaneously With two and after half ripe bar is made, three and half ripe bars are made ice through last mixing in doubling step, Roving Frames, spinning process and winding procedure and feel well Yarn;(2) using spandex thread as heart yarn, yarn is felt well as outsourcing silk using ice, spandex filament drafting, ice are felt well Yarn twisting cladding, and winding is made Wrap yarn;(3) taken out after wrap yarn being put into 50-55 DEG C of insulated building inside holding 5-6h, natural cooling.
- The preparation process of wrap yarn 5. ice as claimed in claim 4 is felt well, it is characterised in that:The preparation method of the Basho fiber It is as follows:Bajiao banana cane by immersions, squeezing, washing, dehydration, cellulase treatment, washing, be dehydrated, shake up, drying, it is obtained;The cellulase treatment is immersed in for bajiao banana stem fiber in the treatment fluid of 18-20 times of weight, fiber in the treatment fluid Plain enzyme is 1-1.5wt%, and pectase 0.3-0.5wt%, treatment fluid temperature is 40-50 DEG C, and the pH value for the treatment of fluid is 3-5 processing Time is 60-70min.