CN108060611A - A kind of antistatic special release paper and preparation method thereof - Google Patents
A kind of antistatic special release paper and preparation method thereof Download PDFInfo
- Publication number
- CN108060611A CN108060611A CN201711362055.7A CN201711362055A CN108060611A CN 108060611 A CN108060611 A CN 108060611A CN 201711362055 A CN201711362055 A CN 201711362055A CN 108060611 A CN108060611 A CN 108060611A
- Authority
- CN
- China
- Prior art keywords
- parts
- release paper
- paper
- antistatic
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to pulp technology for making paper, especially a kind of antistatic special release paper, raw material is as follows in parts by weight:110 parts of slurry, 5 10 parts of acrylic acid epoxy resin, 12 parts of silicon nitride powder, 6 12 parts of quartz sand, 10 15 parts of vinyon particle, 35 parts of stabilizer, 15 parts of interleaving agent solvent-borne type silicone oil, 3 10 parts of crosslinking agent, 6 12 parts of sizing agent, 5 10 parts of mould release.The invention also discloses a kind of preparation method of antistatic special release paper, the present invention effectively increases the antistatic property and flexibility of release paper.
Description
Technical field
The present invention relates to pulp technology for making paper more particularly to a kind of antistatic special release paper and preparation method thereof.
Background technology
The species of release paper can be basically divided into two major classes:One kind is for producing polyvinyl chloride(PVC)Used for artificial leather
Release paper;Another kind of is production polyurethane(PU)The release paper of use for synthetic leather.Some of which release paper can be used for polyvinyl chloride
Artificial leather can be used for Synthetic Leather.Release paper of the prior art, antistatic effect is poor, and flexibility is not
It is good.
The content of the invention
The purpose of the present invention is to solve shortcoming in the prior art, and the one kind proposed is antistatic special release
Paper and preparation method thereof.
To achieve these goals, present invention employs following technical solutions:
A kind of antistatic special release paper of design, raw material are as follows in parts by weight:110 parts of slurry, acrylic acid epoxy tree
5-10 parts of fat, 1-2 parts of silicon nitride powder, 6-12 parts of quartz sand, 10-15 parts of vinyon particle, 3-5 parts of stabilizer, interleaving agent
1-5 parts of solvent-borne type silicone oil, 3-10 parts of crosslinking agent, 6-12 parts of sizing agent, 5-10 parts of mould release.
Preferably, raw material is as follows in parts by weight:110 parts of slurry, 6-8 parts of acrylic acid epoxy resin, silicon nitride
1-2 parts of powder, 7-11 parts of quartz sand, 12-14 parts of vinyon particle, 3.5-4 parts of stabilizer, interleaving agent solvent-borne type silicone oil 2-4
Part, 5-8 parts of crosslinking agent, 7-10 parts of sizing agent, 5-10 parts of mould release.
Preferably, raw material is as follows in parts by weight:110 parts of slurry, 7 parts of acrylic acid epoxy resin, silicon nitride powder 2
Part, 10 parts of quartz sand, 13 parts of vinyon particle, 4 parts of stabilizer, 3 parts of interleaving agent solvent-borne type silicone oil, 6 parts of crosslinking agent, sizing
8 parts of agent, 8 parts of mould release.
Preferably, mould release is the mixture of silicone oil, palladium calcium carbonate and palm oil.
Preferably, the coating weight of mould release is 1.5h/m2。
The invention also discloses a kind of preparation methods of antistatic special release paper, comprise the following steps:
The preparation of S1, dry page:Slurry is subjected to handsheet in handsheet machine, obtained l Water Paper page is pressed in hydraulic press
It squeezes, pressure 3.5MPa, the squeezing time is 45s;The page obtained after squeezing is dried in vacuum desiccator, dry temperature
It spends for 120 DEG C, drying time 4min obtains dry page;
S2, membrane coating material is prepared:
A1, interleaving agent solvent-borne type silicone oil, vinyon particle are mixed, obtains mixture;
A2, mixture with mixer is stirred, adds crosslinking agent, stabilizer, 1000r stirrings are heated to simultaneously
125-135 DEG C obtains membrane coating material;
S3, lamination:Membrane coating material is obtained into leaching membrane paper by laminating machine die head co-extrusion on dry page, co-extrusion temperature is
240-250 DEG C, back pressure 700-900pa, co-extrusion speed is 100m/min;
S4, sizing:It is glued on the surface of leaching membrane paper with sizing agent by the way of top sizing, is coated one layer by acrylic acid ring
The antistatic layer that oxygen resin, quartz sand mix coats mould release afterwards, finally carries out corona pre-treatment and supercalendering;
S5, drying.
Preferably, drying process is:After the completion of coating, to be dried rapidly in vacuum desiccator, drying temperature is 120 DEG C,
Drying time 2min, obtains finished product.
Antistatic special release paper of one kind proposed by the present invention and preparation method thereof, advantageous effect is:Present invention addition
The antistatic layer and interleaving agent solvent-borne type silicone oil, vinyon particle that acrylic acid epoxy resin, quartz sand mix
Leaching membrane layer is formed, effectively increases the antistatic property and flexibility of release paper.
Specific embodiment
The technical solution in the embodiment of the present invention is clearly and completely described below, it is clear that described embodiment
Only part of the embodiment of the present invention, instead of all the embodiments.
Embodiment 1
A kind of antistatic special release paper, raw material are as follows in parts by weight:110 parts of slurry, acrylic acid epoxy resin 5
Part, 1 part of silicon nitride powder, 6 parts of quartz sand, 10 parts of vinyon particle, 3 parts of stabilizer, 1 part of interleaving agent solvent-borne type silicone oil are handed over
Join 3 parts of agent, 6 parts of sizing agent, 5 parts of mould release.
Mould release is the mixture of silicone oil, palladium calcium carbonate and palm oil.
The coating weight of mould release is 1.5h/m2。
The invention also discloses a kind of preparation methods of antistatic special release paper, comprise the following steps:
The preparation of S1, dry page:Slurry is subjected to handsheet in handsheet machine, obtained l Water Paper page is pressed in hydraulic press
It squeezes, pressure 3.5MPa, the squeezing time is 45s;The page obtained after squeezing is dried in vacuum desiccator, dry temperature
It spends for 120 DEG C, drying time 4min obtains dry page;
S2, membrane coating material is prepared:
A1, interleaving agent solvent-borne type silicone oil, vinyon particle are mixed, obtains mixture;
A2, mixture with mixer is stirred, adds crosslinking agent, stabilizer, 1000r stirrings are heated to simultaneously
125 DEG C obtain membrane coating material;
S3, lamination:Membrane coating material is obtained into leaching membrane paper by laminating machine die head co-extrusion on dry page, co-extrusion temperature is
240 DEG C, back pressure 700pa, co-extrusion speed is 100m/min;
S4, sizing:It is glued on the surface of leaching membrane paper with sizing agent by the way of top sizing, is coated one layer by acrylic acid ring
The antistatic layer that oxygen resin, quartz sand mix coats mould release afterwards, finally carries out corona pre-treatment and supercalendering;
S5, drying.
Drying process is:It after the completion of coating, is dried rapidly in vacuum desiccator, drying temperature is 120 DEG C, drying time
2min obtains finished product.
Embodiment 2
A kind of antistatic special release paper, raw material are as follows in parts by weight:110 parts of slurry, acrylic acid epoxy resin 6
Part, 7 parts of quartz sand, 12 parts of vinyon particle, 3.5 parts of stabilizer, 2 parts of interleaving agent solvent-borne type silicone oil, 5 parts of crosslinking agent are applied
7 parts of jelly, 5 parts of mould release.
Mould release is the mixture of silicone oil, palladium calcium carbonate and palm oil.
The coating weight of mould release is 1.5h/m2。
The invention also discloses a kind of preparation methods of antistatic special release paper, comprise the following steps:
The preparation of S1, dry page:Slurry is subjected to handsheet in handsheet machine, obtained l Water Paper page is pressed in hydraulic press
It squeezes, pressure 3.5MPa, the squeezing time is 45s;The page obtained after squeezing is dried in vacuum desiccator, dry temperature
It spends for 120 DEG C, drying time 4min obtains dry page;
S2, membrane coating material is prepared:
A1, interleaving agent solvent-borne type silicone oil, vinyon particle are mixed, obtains mixture;
A2, mixture with mixer is stirred, adds crosslinking agent, stabilizer, 1000r stirrings are heated to simultaneously
130 DEG C obtain membrane coating material;
S3, lamination:Membrane coating material is obtained into leaching membrane paper by laminating machine die head co-extrusion on dry page, co-extrusion temperature is
242 DEG C, back pressure 750pa, co-extrusion speed is 100m/min;
S4, sizing:It is glued on the surface of leaching membrane paper with sizing agent by the way of top sizing, is coated one layer by acrylic acid ring
The antistatic layer that oxygen resin, quartz sand mix coats mould release afterwards, finally carries out corona pre-treatment and supercalendering;
S5, drying.
Drying process is:It after the completion of coating, is dried rapidly in vacuum desiccator, drying temperature is 120 DEG C, drying time
2min obtains finished product.
Embodiment 3
A kind of antistatic special release paper, raw material are as follows in parts by weight:110 parts of slurry, acrylic acid epoxy resin 7
Part, 10 parts of quartz sand, 13 parts of vinyon particle, 4 parts of stabilizer, 3 parts of interleaving agent solvent-borne type silicone oil, 6 parts of crosslinking agent, sizing
8 parts of agent, 8 parts of mould release.
Mould release is the mixture of silicone oil, palladium calcium carbonate and palm oil.
The coating weight of mould release is 1.5h/m2。
The invention also discloses a kind of preparation methods of antistatic special release paper, comprise the following steps:
The preparation of S1, dry page:Slurry is subjected to handsheet in handsheet machine, obtained l Water Paper page is pressed in hydraulic press
It squeezes, pressure 3.5MPa, the squeezing time is 45s;The page obtained after squeezing is dried in vacuum desiccator, dry temperature
It spends for 120 DEG C, drying time 4min obtains dry page;
S2, membrane coating material is prepared:
A1, interleaving agent solvent-borne type silicone oil, vinyon particle are mixed, obtains mixture;
A2, mixture with mixer is stirred, adds crosslinking agent, stabilizer, 1000r stirrings are heated to simultaneously
132 DEG C obtain membrane coating material;
S3, lamination:Membrane coating material is obtained into leaching membrane paper by laminating machine die head co-extrusion on dry page, co-extrusion temperature is
245 DEG C, back pressure 800pa, co-extrusion speed is 100m/min;
S4, sizing:It is glued on the surface of leaching membrane paper with sizing agent by the way of top sizing, is coated one layer by acrylic acid ring
The antistatic layer that oxygen resin, quartz sand mix coats mould release afterwards, finally carries out corona pre-treatment and supercalendering;
S5, drying.
Drying process is:It after the completion of coating, is dried rapidly in vacuum desiccator, drying temperature is 120 DEG C, drying time
2min obtains finished product.
Embodiment 4
A kind of antistatic special release paper, raw material are as follows in parts by weight:110 parts of slurry, acrylic acid epoxy resin 10
Part, 2 parts of silicon nitride powder, 12 parts of quartz sand, 15 parts of vinyon particle, 5 parts of stabilizer, 5 parts of interleaving agent solvent-borne type silicone oil are handed over
Join 10 parts of agent, 12 parts of sizing agent, 10 parts of mould release.
Mould release is the mixture of silicone oil, palladium calcium carbonate and palm oil.
The coating weight of mould release is 1.5h/m2。
The invention also discloses a kind of preparation methods of antistatic special release paper, comprise the following steps:
The preparation of S1, dry page:Slurry is subjected to handsheet in handsheet machine, obtained l Water Paper page is pressed in hydraulic press
It squeezes, pressure 3.5MPa, the squeezing time is 45s;The page obtained after squeezing is dried in vacuum desiccator, dry temperature
It spends for 120 DEG C, drying time 4min obtains dry page;
S2, membrane coating material is prepared:
A1, interleaving agent solvent-borne type silicone oil, vinyon particle are mixed, obtains mixture;
A2, mixture with mixer is stirred, adds crosslinking agent, stabilizer, 1000r stirrings are heated to simultaneously
135 DEG C obtain membrane coating material;
S3, lamination:Membrane coating material is obtained into leaching membrane paper by laminating machine die head co-extrusion on dry page, co-extrusion temperature is
250 DEG C, back pressure 900pa, co-extrusion speed is 100m/min;
S4, sizing:It is glued on the surface of leaching membrane paper with sizing agent by the way of top sizing, is coated one layer by acrylic acid ring
The antistatic layer that oxygen resin, quartz sand mix coats mould release afterwards, finally carries out corona pre-treatment and supercalendering;
S5, drying.
Drying process is:It after the completion of coating, is dried rapidly in vacuum desiccator, drying temperature is 120 DEG C, drying time
2min obtains finished product.
The foregoing is only a preferred embodiment of the present invention, but protection scope of the present invention be not limited thereto,
Any one skilled in the art in the technical scope disclosed by the present invention, technique according to the invention scheme and its
Inventive concept is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.
Claims (7)
1. a kind of antistatic special release paper, which is characterized in that its raw material is as follows in parts by weight:110 parts of slurry, propylene
Sour epoxy resin 5-10 parts, 1-2 parts of silicon nitride powder, 6-12 parts of quartz sand, 10-15 parts of vinyon particle, stabilizer 3-5
Part, 1-5 parts of interleaving agent solvent-borne type silicone oil, 3-10 parts of crosslinking agent, 6-12 parts of sizing agent, 5-10 parts of mould release.
2. the antistatic special release paper of one kind according to claim 1, which is characterized in that its raw material is in parts by weight
It is as follows:110 parts of slurry, 6-8 parts of acrylic acid epoxy resin, 1-2 parts of silicon nitride powder, 7-11 parts of quartz sand, vinyon particle
12-14 parts, 3.5-4 parts of stabilizer, 2-4 parts of interleaving agent solvent-borne type silicone oil, 5-8 parts of crosslinking agent, 7-10 parts of sizing agent, mould release 5-
10 parts.
3. the antistatic special release paper of one kind according to claim 1, which is characterized in that its raw material is in parts by weight
It is as follows:It is 110 parts of slurry, 7 parts of acrylic acid epoxy resin, 2 parts of silicon nitride powder, 10 parts of quartz sand, 13 parts of vinyon particle, steady
Determine 4 parts of agent, 3 parts of interleaving agent solvent-borne type silicone oil, 6 parts of crosslinking agent, 8 parts of sizing agent, 8 parts of mould release.
4. the antistatic special release paper of one kind according to claim 1, it is characterised in that:Mould release is silicone oil, palladium carbon acid
The mixture of calcium and palm oil.
5. the antistatic special release paper of one kind according to claim 1, it is characterised in that:The coating weight of mould release is
1.5h/m2。
6. the preparation method of a kind of antistatic special release paper according to claim 1, which is characterized in that including following step
Suddenly:
The preparation of S1, dry page:Slurry is subjected to handsheet in handsheet machine, obtained l Water Paper page is pressed in hydraulic press
It squeezes, pressure 3.5MPa, the squeezing time is 45s;The page obtained after squeezing is dried in vacuum desiccator, dry temperature
It spends for 120 DEG C, drying time 4min obtains dry page;
S2, membrane coating material is prepared:
A1, interleaving agent solvent-borne type silicone oil, vinyon particle are mixed, obtains mixture;
A2, mixture with mixer is stirred, adds crosslinking agent, stabilizer, 1000r stirrings are heated to simultaneously
125-135 DEG C obtains membrane coating material;
S3, lamination:Membrane coating material is obtained into leaching membrane paper by laminating machine die head co-extrusion on dry page, co-extrusion temperature is
240-250 DEG C, back pressure 700-900pa, co-extrusion speed is 100m/min;
S4, sizing:It is glued on the surface of leaching membrane paper with sizing agent by the way of top sizing, is coated one layer by acrylic acid ring
The antistatic layer that oxygen resin, quartz sand mix coats mould release afterwards, finally carries out corona pre-treatment and supercalendering;
S5, drying.
A kind of 7. preparation method of antistatic special release paper according to claim 1, which is characterized in that drying process
For:It after the completion of coating, is dried rapidly in vacuum desiccator, drying temperature is 120 DEG C, and drying time 2min obtains finished product.