CN108059756A - A kind of polyethylene filling master batch - Google Patents
A kind of polyethylene filling master batch Download PDFInfo
- Publication number
- CN108059756A CN108059756A CN201711474588.4A CN201711474588A CN108059756A CN 108059756 A CN108059756 A CN 108059756A CN 201711474588 A CN201711474588 A CN 201711474588A CN 108059756 A CN108059756 A CN 108059756A
- Authority
- CN
- China
- Prior art keywords
- master batch
- polyethylene
- ldpe
- filling master
- low density
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to plastics to prepare adjuvant technical field, more particularly, to a kind of polyethylene filling master batch.It includes following components by weight percent, calcium carbonate:80‑123;Low density polyethylene (LDPE):11‑26;Three oleoyl isopropyl titanates:0.5‑2.1;Calcium stearate:1.0‑2.6;White oil:1.5‑3.2;Titanium dioxide:1.2‑3.8;Stearic acid:0.1‑0.7;Paraffin:0.2‑1.1.
Description
Technical field
The invention belongs to plastics to prepare adjuvant technical field, more particularly, to a kind of polyethylene filling master batch.
Background technology
The resin Composition or base-material being dispersed therein in masterbatch system reinforced plastics by fiber or other reinforcing materials.Composite wood
Continuous phase in material claims masterbatch or base-material.
Plastic matrix is that plastic additive super quantity is attached in resin and manufactured condensation product;Manufacture plastic products
When, it is not necessary to this kind of plastic additive is added, and need to only add in corresponding masterbatch.Thus, it is world today's plastic additive
One of main form of application.Its advantage is:It is simple for process, it is easy to use, production automation is easy to implement, improves work life
Yield, and environmental pollution is avoided, the cleaning for being conducive to workers ' health is carried out production strictly in line with rules and regulations.
Masterbatch is made of vector resin, filler and various auxiliary agents.The limit of auxiliary agent or the content of filler ratio in masterbatch
Requirement in actual plastic products wants high several times to more than ten times.In molding process, it is necessary to according to related group in masterbatch
The amount added in is needed in the content and actual product divided, adjusts the proportioning of masterbatch and matrix resin.Masterbatch can be generally divided into general
Logical filling master batch (abbreviation filling master batch) and functional masterbatch, such as color masterbatch, anti-droplet masterbatch.The key component of filling master batch
It is filler, is mainly used for the machine-shaping of polyolefin (polyethylene and polypropylene), also known as polyolefin packing material.
Polyolefin packing material is by powdery inorganic filler and random polypropylene, low density polyethylene (LDPE), powdered polypropylene etc.
Vector resin, the manufactured filling master batch through the coupled action of coupling agent.Polyethylene filling master batch formula is matched somebody with somebody, and is added in toughening, is increased
Strong agent compared with traditional filler parent granule, has good fluidity and impact flexibility, and scattered effect is mixed with polyethylene and polypropylene
Fruit is very prominent, is especially suitable for the product more demanding to elongation.Polyolefin packing material is by powdery inorganic filler and nothing
The vector resins such as isotactic polypropylene, low density polyethylene (LDPE), powdered polypropylene, through the coupled action of coupling agent, manufactured filling is female
Material.
The content of the invention
For this reason, it may be necessary to provide a kind of polyethylene filling master batch.
To achieve the above object, the present invention adopts the following technical scheme that:
A kind of polyethylene filling master batch, it includes following components by weight percent,
Calcium carbonate:80-123;
Low density polyethylene (LDPE):11-26;
Three oleoyl isopropyl titanates:0.5-2.1;
Calcium stearate:1.0-2.6;
White oil:1.5-3.2;
Titanium dioxide:1.2-3.8;
Stearic acid:0.1-0.7;
Paraffin:0.2-1.1.
The technical program further optimizes, described
Calcium carbonate:100;
Low density polyethylene (LDPE):20;
Three oleoyl isopropyl titanates:1.3;
Calcium stearate:2;
White oil:2.6;
Titanium dioxide:2.6;
Stearic acid:0.6;
Paraffin:0.8.
The technical program further optimizes, described
Calcium carbonate:113;
Low density polyethylene (LDPE):16;
Three oleoyl isopropyl titanates:1.1;
Calcium stearate:1.5;
White oil:1.9;
Titanium dioxide:2.3;
Stearic acid:0.3;
Paraffin:0.6.
The technical program further optimizes, described
Calcium carbonate:112;
Low density polyethylene (LDPE):21;
Three oleoyl isopropyl titanates:0.9;
Calcium stearate:2.1;
White oil:3.0;
Titanium dioxide:2.1;
Stearic acid:0.7;
Paraffin:0.9.
The technical program further optimizes, described
Calcium carbonate:95;
Low density polyethylene (LDPE):23;
Three oleoyl isopropyl titanates:1.6;
Calcium stearate:2.2;
White oil:2.9;
Titanium dioxide:3.2;
Stearic acid:0.5;
Paraffin:1.0.
To improve the intensity of fleut, low density polyethylene (LDPE) can be used and make vector resin, addition is usually filler
1/4-1/5, the resin for preferably selecting melt index (MI) larger, mobility are much better.
Low density polyethylene (LDPE) (ldpe) is also commonly known as:Polyethylene from high pressure process is milky ball-point pen type particle.Nontoxic, tasteless,
Odorless, mattness, density is 0.916~0.930.Property is relatively soft, and softening point is 105~120o, has good prolong
Stretching property, electrical insulating property, but it is mechanical strength, poor every moist, gas barrier properties and solvent resistance, and molecular structure is not regular enough, crystallinity
(60~80%) are low, and crystalline melt point (108~126 DEG C) is relatively low.
The melt flow rate (MFR) of ldpe generally not lower than 1.5, the higher inherent quality for being more conducive to improve masterbatch of index,
It is low in order to which the scattered and mobility for improving polyolefin masterbatch can add in appropriate random poly- third powder or a certain proportion of oligomer
Polymers includes:Low molecular weight polyethylene, ethylene waxes, thick shape, sheet oligomer plurality of specifications.Inside and outside lubrication is used in masterbatch production
Agent, be with animal oil make stearic acid and paraffin, dosage the former should control within 0.7% and the latter 1.1%.
Specific embodiment
For the technology contents of technical solution, construction feature, the objects and the effects are described in detail, below in conjunction with specific reality
Example is applied to be explained in detail.
A kind of polyethylene filling master batch, it includes following components by weight percent,
Calcium carbonate:80-123;
Low density polyethylene (LDPE):11-26;
Three oleoyl isopropyl titanates:0.5-2.1;
Calcium stearate:1.0-2.6;
White oil:1.5-3.2;
Titanium dioxide:1.2-3.8;
Stearic acid:0.1-0.7;
Paraffin:0.2-1.1.
Embodiment one
A kind of polyethylene filling master batch, it includes following components by weight percent, described
Calcium carbonate:100;
Low density polyethylene (LDPE):20;
Three oleoyl isopropyl titanates:1.3;
Calcium stearate:2;
White oil:2.6;
Titanium dioxide:2.6;
Stearic acid:0.6;
Paraffin:0.8.
Embodiment two
A kind of polyethylene filling master batch, it includes following components by weight percent, described
Calcium carbonate:113;
Low density polyethylene (LDPE):16;
Three oleoyl isopropyl titanates:1.1;
Calcium stearate:1.5;
White oil:1.9;
Titanium dioxide:2.3;
Stearic acid:0.3;
Paraffin:0.6.
Embodiment three
A kind of polyethylene filling master batch, it includes following components by weight percent, described
Calcium carbonate:112;
Low density polyethylene (LDPE):21;
Three oleoyl isopropyl titanates:0.9;
Calcium stearate:2.1;
White oil:3.0;
Titanium dioxide:2.1;
Stearic acid:0.7;
Paraffin:0.9.
Example IV
A kind of polyethylene filling master batch, it includes following components by weight percent, described
Calcium carbonate:95;
Low density polyethylene (LDPE):23;
Three oleoyl isopropyl titanates:1.6;
Calcium stearate:2.2;
White oil:2.9;
Titanium dioxide:3.2;
Stearic acid:0.5;
Paraffin:1.0.
It should be noted that herein, relational terms such as first and second and the like are used merely to a reality
Body or operation are distinguished with another entity or operation, are deposited without necessarily requiring or implying between these entities or operation
In any this actual relation or order.Moreover, term " comprising ", "comprising" or its any other variant are intended to
Non-exclusive inclusion, so that process, method, article or terminal device including a series of elements not only include those
Element, but also including other elements that are not explicitly listed or further include as this process, method, article or end
The intrinsic element of end equipment.In the absence of more restrictions, limited by sentence " including ... " or " including ... "
Element, it is not excluded that also there are other elements in the process including the element, method, article or terminal device.This
Outside, herein, " being more than ", " being less than ", " being more than " etc. are interpreted as not including this number;" more than ", " following ", " within " etc. understandings
It is to include this number.
Although the various embodiments described above are described, those skilled in the art once know basic wound
The property made concept can then make these embodiments other change and modification, so the foregoing is merely the embodiment of the present invention,
Not thereby the scope of patent protection of the present invention, every equivalent structure made using present specification or equivalent are limited
Flow converts, and is directly or indirectly used in other related technical areas, is similarly included in the patent protection model of the present invention
Within enclosing.
Claims (5)
1. a kind of polyethylene filling master batch, which is characterized in that it includes following components by weight percent,
Calcium carbonate:80-123;
Low density polyethylene (LDPE):11-26;
Three oleoyl isopropyl titanates:0.5-2.1;
Calcium stearate:1.0-2.6;
White oil:1.5-3.2;
Titanium dioxide:1.2-3.8;
Stearic acid:0.1-0.7;
Paraffin:0.2-1.1.
2. polyethylene filling master batch as described in claim 1, which is characterized in that described
Calcium carbonate:100;
Low density polyethylene (LDPE):20;
Three oleoyl isopropyl titanates:1.3;
Calcium stearate:2;
White oil:2.6;
Titanium dioxide:2.6;
Stearic acid:0.6;
Paraffin:0.8.
3. polyethylene filling master batch as described in claim 1, which is characterized in that described
Calcium carbonate:113;
Low density polyethylene (LDPE):16;
Three oleoyl isopropyl titanates:1.1;
Calcium stearate:1.5;
White oil:1.9;
Titanium dioxide:2.3;
Stearic acid:0.3;
Paraffin:0.6.
4. polyethylene filling master batch as described in claim 1, which is characterized in that described
Calcium carbonate:112;
Low density polyethylene (LDPE):21;
Three oleoyl isopropyl titanates:0.9;
Calcium stearate:2.1;
White oil:3.0;
Titanium dioxide:2.1;
Stearic acid:0.7;
Paraffin:0.9.
5. polyethylene filling master batch as described in claim 1, which is characterized in that described
Calcium carbonate:95;
Low density polyethylene (LDPE):23;
Three oleoyl isopropyl titanates:1.6;
Calcium stearate:2.2;
White oil:2.9;
Titanium dioxide:3.2;
Stearic acid:0.5;
Paraffin:1.0.