CN102329446A - Transparent starch-based degradable agricultural mulching film composite material - Google Patents
Transparent starch-based degradable agricultural mulching film composite material Download PDFInfo
- Publication number
- CN102329446A CN102329446A CN 201110207085 CN201110207085A CN102329446A CN 102329446 A CN102329446 A CN 102329446A CN 201110207085 CN201110207085 CN 201110207085 CN 201110207085 A CN201110207085 A CN 201110207085A CN 102329446 A CN102329446 A CN 102329446A
- Authority
- CN
- China
- Prior art keywords
- parts
- starch
- mixed
- agricultural mulching
- based degradable
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a transparent starch-based degradable agricultural mulching film composite material and a preparation process thereof. The composite material is characterized by comprising the following components in parts by weight: 85-95 parts of anhydrous sodium sulfate, 18-33 parts of corn starch, 1-1.8 parts of surface treating agent, 3-8 parts of polyolefin elastomer (POE), 55-65 parts of linear low density polyethylene (LLDPE) and 1-3 parts of polyisobutylene. The composite material disclosed by the invention has good dispersibility, maintains the original longitudinal and lateral tension properties, and has good promotion value.
Description
Technical field
The present invention relates to the plastic material technical field, relate to a kind of starch-based agricultural mulching transparent composite and preparation technology thereof in particular.
Background technology
New LDPE (film grade) degree Vilaterm (LDPE) is a kind of plastic material, and it is fit to the various moulding processs of thermoplastic molding's processing, and forming process property is good.The LDPE main application is to make film product, also is used for injection-molded item, medical apparatus, medicine and packaging material for food, blowing slush molding goods.Linear low density polyethylene (LLDPE); Be that ethene and a small amount of high alpha-olefin (like butene-1, hexene-1, octene-1, tetramethyl-amylene-1 etc.) are under catalyst action; Through a kind of multipolymer that high pressure or low-pressure polymerization form, density is between 0.915~0.940 gram/cubic centimetre.At present, traditional LDPE exists anti-environment capacity poor, and especially resistance to elevated temperatures is poor; Be used under the agricultural mulching surrounding medium and be easy to brittle cracking, and shrinking percentage is big, toughness and rigidity can not well be unified; Can not keep original performance to pulling force in length and breadth, can not degrade, not meet environmental requirement.
Summary of the invention
The object of the invention is exactly a kind of not only good dispersibility that provides for the deficiency that solves prior art, keeps original performance to pulling force in length and breadth, and has the starch-based degradable agricultural mulching transparent composite of environment-friendly function.
Another object of the present invention provides a kind of preparation technology of starch-based degradable agricultural mulching transparent composite.
The present invention adopts following technical solution to realize above-mentioned purpose: a kind of starch-based degradable agricultural mulching transparent composite is characterized in that its component and part by weight umber ratio comprise:
SODIUM SULPHATE ANHYDROUS 99PCT 85-95 part (particle diameter 1800-2200 order)
W-Gum 18-22 part (particle diameter 1400-1600 order)
Surface treatment agent 1-1.8 part
POE 3-8 part
LLDPE 55-65 part
Polyisobutene 1-3 part.
As further specifying of such scheme: the component of said matrix material and part by weight umber are preferred:
90 parts of SODIUM SULPHATE ANHYDROUS 99PCTs
20 parts of W-Gums
1.5 parts of surface treatment agents
5 parts of POE
60 parts of LLDPE
2 parts of polyisobutene.
Said surface treatment agent is dedicated modified dose an of starch.
A kind of preparation technology of starch-based degradable agricultural mulching transparent composite is characterized in that it comprises the steps:
A, elder generation are added in horizontal double helical ribbon mixer with SODIUM SULPHATE ANHYDROUS 99PCT and W-Gum, and the heating middling speed was mixed 25-35 minute;
B, add surface treatment agent, mixed at high speed 10-20 minute;
C, add POE and LLDPE, mixed at high speed 8-15 minute;
D, through the screw rod feeder, the mass transport that mixes is to continuous Banbury mixer material storage tank;
E, through the powder metering feeding machine, feeding is to continuous Banbury mixer;
F, polyisobutene is added to the liquid meter feeding machine, feeding is to continuous Banbury mixer;
G, extruding pelletization;
E, finished product packing.
In said process step a process, said mixed powder water cut < 2%, mixed 20 minutes by the heating middling speed.
In the mixed at high speed process of said process step b, mixed at high speed 15 minutes, treatment agent is wanted complete coated powder.
In said process step c process, mixed at high speed 10 minutes.
The beneficial effect that the present invention adopts above-mentioned technical solution to reach is:
1, matrix material of the present invention is pressed original LDPE production technique on the blown film machine, fully ordinary production.
2, good dispersibility keeps original performance to pulling force in length and breadth.
3, reach environment-friendly function.
Embodiment
A kind of starch-based degradable agricultural mulching of the present invention transparent composite is characterized in that, its component and part by weight umber ratio comprise:
SODIUM SULPHATE ANHYDROUS 99PCT 85-95 part (particle diameter 2000 orders)
W-Gum 18-22 part (particle diameter 1500 orders)
Surface treatment agent 1-1.8 part
POE 3-8 part
LLDPE 55-65 part
Polyisobutene 1-3 part.
Present embodiment is preferred, 90 parts of SODIUM SULPHATE ANHYDROUS 99PCTs
20 parts of W-Gums
1.5 parts of surface treatment agents (dedicated modified dose of Nanjing Jin Laiwang JL-G02FX-P type starch)
5 parts of POE (Mitsui 810)
60 parts of LLDPE (Maoming petrochemical industry 7042)
2 parts of polyisobutene (Korea S PB2400).
The preparation technology of starch-based degradable agricultural mulching transparent composite, its process step is rapid as follows:
1, earlier SODIUM SULPHATE ANHYDROUS 99PCT and W-Gum are added in horizontal double helical ribbon mixer, the heating middling speed was mixed 30 minutes, reached the combination drying effect, water cut < 2%;
2, add surface treatment agent, mixed at high speed 15 minutes, the complete coated powder of treatment agent;
3, add POE and LLDPE, mixed at high speed 10 minutes, each component distributes and mixes;
4, through the screw rod feeder, the mass transport that mixes is to continuous Banbury mixer material storage tank;
5, through the powder metering feeding machine, feeding is to continuous Banbury mixer;
6, polyisobutene is added to the liquid meter feeding machine, feeding is to continuous Banbury mixer;
7, extruding pelletization;
8, finished product packing.
Above-described only is preferred implementation of the present invention, should be pointed out that for the person of ordinary skill of the art, under the prerequisite that does not break away from the invention design, can also make some distortion and improvement, and these all belong to protection scope of the present invention.
Claims (7)
1. a starch-based degradable agricultural mulching transparent composite is characterized in that, its component and part by weight umber ratio comprise:
SODIUM SULPHATE ANHYDROUS 99PCT 85-95 part,
W-Gum 18-22 part,
Surface treatment agent 1-1.8 part,
POE 3-8 part,
LLDPE 55-65 part,
Polyisobutene 1-3 part.
2. a kind of starch-based degradable agricultural mulching transparent composite according to claim 1 is characterized in that, the particle diameter 1800-2200 order of said SODIUM SULPHATE ANHYDROUS 99PCT, the particle diameter 1400-1600 order of W-Gum.
3. a kind of starch-based degradable agricultural mulching transparent composite according to claim 1 and 2 is characterized in that the component of said matrix material and part by weight umber are preferred:
90 parts of SODIUM SULPHATE ANHYDROUS 99PCTs,
20 parts of W-Gums,
1.5 parts of surface treatment agents,
5 parts of POE,
60 parts of LLDPE,
2 parts of polyisobutene.
4. the preparation technology of a starch-based degradable agricultural mulching transparent composite is characterized in that it comprises the steps:
A, elder generation are added in horizontal double helical ribbon mixer with SODIUM SULPHATE ANHYDROUS 99PCT and W-Gum, and the heating middling speed was mixed 25-35 minute;
B, add surface treatment agent, mixed at high speed 10-20 minute;
C, add POE and LLDPE, mixed at high speed 8-15 minute;
D, through the screw rod feeder, the mass transport that mixes is to continuous Banbury mixer material storage tank;
E, through the powder metering feeding machine, feeding is to continuous Banbury mixer;
F, polyisobutene is added to the liquid meter feeding machine, feeding is to continuous Banbury mixer;
G, extruding pelletization;
E, finished product packing.
5. the preparation technology of starch-based degradable agricultural mulching transparent composite according to claim 4 is characterized in that, in said process step a process, said mixed powder water cut < 2%, mixed 20 minutes by the heating middling speed.
6. the preparation technology of starch-based degradable agricultural mulching transparent composite according to claim 4, in the mixed at high speed process of said process step b, mixed at high speed 15 minutes, treatment agent is wanted complete coated powder.
7. the preparation technology of starch-based degradable agricultural mulching transparent composite according to claim 4, in said process step c process, mixed at high speed 10 minutes.