CN108059444A - 一种家用地砖防滑陶瓷 - Google Patents

一种家用地砖防滑陶瓷 Download PDF

Info

Publication number
CN108059444A
CN108059444A CN201610980896.3A CN201610980896A CN108059444A CN 108059444 A CN108059444 A CN 108059444A CN 201610980896 A CN201610980896 A CN 201610980896A CN 108059444 A CN108059444 A CN 108059444A
Authority
CN
China
Prior art keywords
parts
floor tile
family expenses
skid
resistance ceramic
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610980896.3A
Other languages
English (en)
Inventor
宋德红
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201610980896.3A priority Critical patent/CN108059444A/zh
Publication of CN108059444A publication Critical patent/CN108059444A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种家用地砖防滑陶瓷，包含以下质量份数的原料：高岭土30‑35份，膨胀珍珠岩10‑14份，氧化铁2‑5份，羟基磷灰石8‑10份，硼氢化锂5‑7份，三乙酰氧基硼氢化钠4‑6份，金红石型钛白粉4‑8份，石英粉10‑14份，蛏子王壳粉12‑16份，硼玻璃4‑7份，硅藻土8‑9份，玻璃纤维12‑13份，碳纤维5‑8份，白云2‑6份，氮化硼2‑5份，辛基酚聚氧乙烯醚4‑5份。本发明防滑能力强，高强度、硬度及耐磨性。

Description

一种家用地砖防滑陶瓷
技术领域
本发明涉及无机非金属材料技术领域，尤其涉及一种家用地砖防滑陶瓷。
背景技术
防滑地砖是一种陶瓷地板砖，正面有褶皱条纹或凹凸点，以增加地板砖面与人体脚底或鞋底的摩擦力，防止打滑摔倒。瓷砖在沾水后防滑能力大大减弱，并非所有瓷砖沾水后均能防滑，若家中有小孩或老人家，将威胁到他们的自身的安全。
发明内容
为解决上述存在的问题，本发明提供一种防滑能力强，高强度、硬度及耐磨性的家用地砖防滑陶瓷。
本发明解决上述技术问题采用的技术方案为：一种家用地砖防滑陶瓷，包含以下质量份数的原料：
高岭土30-35份，膨胀珍珠岩10-14份，氧化铁2-5份，羟基磷灰石8-10份，硼氢化锂5-7份，三乙酰氧基硼氢化钠4-6份，金红石型钛白粉4-8份，石英粉10-14份，蛏子王壳粉12-16份，硼玻璃4-7份，硅藻土8-9份，玻璃纤维12-13份，碳纤维5-8份，白云2-6份，氮化硼2-5份，辛基酚聚氧乙烯醚4-5份。
上述的家用地砖防滑陶瓷，包含以下质量份数的原料：
高岭土33份，膨胀珍珠岩12份，氧化铁4份，羟基磷灰石9份，硼氢化锂6份，三乙酰氧基硼氢化钠5份，金红石型钛白粉6份，石英粉12份，蛏子王壳粉14 份，硼玻璃6份，硅藻土8.5份，玻璃纤维12.6份，碳纤维7份，白云4份，氮化硼3份，辛基酚聚氧乙烯醚4.4份。
本发明的有益效果在于：针对瓷砖沾水后防滑较差，本发明防滑能力强，高强度、硬度及耐磨性。
具体实施方式
下面结合具体实施例对本发明做进一步详细说明。
实施例1
一种家用地砖防滑陶瓷，包含以下质量份数的原料：
高岭土30份，膨胀珍珠岩10份，氧化铁2份，羟基磷灰石8份，硼氢化锂5份，三乙酰氧基硼氢化钠4份，金红石型钛白粉4份，石英粉10份，蛏子王壳粉12份，硼玻璃4份，硅藻土8份，玻璃纤维12份，碳纤维5份，白云2份，氮化硼2份，辛基酚聚氧乙烯醚4份。
实施例2
一种家用地砖防滑陶瓷，包含以下质量份数的原料：
高岭土33份，膨胀珍珠岩12份，氧化铁4份，羟基磷灰石9份，硼氢化锂6份，三乙酰氧基硼氢化钠5份，金红石型钛白粉6份，石英粉12份，蛏子王壳粉14 份，硼玻璃6份，硅藻土8.5份，玻璃纤维12.6份，碳纤维7份，白云4份，氮化硼3份，辛基酚聚氧乙烯醚4.4份。
实施例3
一种家用地砖防滑陶瓷，包含以下质量份数的原料：
高岭土35份，膨胀珍珠岩14份，氧化铁5份，羟基磷灰石10份，硼氢化锂7份，三乙酰氧基硼氢化钠6份，金红石型钛白粉8份，石英粉14份，蛏子王壳粉16份，硼玻璃7份，硅藻土9份，玻璃纤维13份，碳纤维8份，白云6份，氮化硼5份，辛基酚聚氧乙烯醚5份。
上述虽然对本发明的具体实施方式进行了描述，但并非对本发明保护范围的限制，所属领域技术人员应该明白，在本发明的技术方案的基础上，本领域技术人员不需要付出创造性劳动即可做出的各种修改或变形仍在本发明的保护范围以内。

Claims (2)

1.一种家用地砖防滑陶瓷，其特征在于：包含以下质量份数的原料：
高岭土30-35份，膨胀珍珠岩10-14份，氧化铁2-5份，羟基磷灰石8-10份，硼氢化锂5-7份，三乙酰氧基硼氢化钠4-6份，金红石型钛白粉4-8份，石英粉10-14份，蛏子王壳粉12-16份，硼玻璃4-7份，硅藻土8-9份，玻璃纤维12-13份，碳纤维5-8份，白云2-6份，氮化硼2-5份，辛基酚聚氧乙烯醚4-5份。
2.根据权利要求1所述的家用地砖防滑陶瓷，其特征在于：包含以下质量份数的原料：
高岭土33份，膨胀珍珠岩12份，氧化铁4份，羟基磷灰石9份，硼氢化锂6份，三乙酰氧基硼氢化钠5份，金红石型钛白粉6份，石英粉12份，蛏子王壳粉14 份，硼玻璃6份，硅藻土8.5份，玻璃纤维12.6份，碳纤维7份，白云4份，氮化硼3份，辛基酚聚氧乙烯醚4.4份。
CN201610980896.3A 2016-11-08 2016-11-08 一种家用地砖防滑陶瓷 Pending CN108059444A (zh)