CN108059339A - A kind of explosion-proof beer bottle manufacturing technology - Google Patents
A kind of explosion-proof beer bottle manufacturing technology Download PDFInfo
- Publication number
- CN108059339A CN108059339A CN201610986144.8A CN201610986144A CN108059339A CN 108059339 A CN108059339 A CN 108059339A CN 201610986144 A CN201610986144 A CN 201610986144A CN 108059339 A CN108059339 A CN 108059339A
- Authority
- CN
- China
- Prior art keywords
- bottle
- glass
- parison
- explosion
- finishing die
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to the production fields of Bottle ＆ Can, refer in particular to a kind of explosion-proof beer bottle manufacturing technology, SiO266.8%Al2O38%Fe2O30.6%CaO7.5%MgO1.8%Na2O14.8%BaO0.5%C r2O30.1%, the glass for meeting forming quality requirement is fused into through 1580 DEG C, using osculum press-and-blow process into technology, i.e., glass gob feed blocker → be pressed into parison → parison is overturn to finishing die → reheat → finishing die vacuumize assist formation → blowing eventually → clamp bottle to cooling bench finished product.There is more sufficient reheat time using the technique, end is so contributed to blow in rear Bottle ＆ Can wall, and glass temperature is equal, and the beer bottle that this composition makes can keep good mechanical strength.
Description
Technical field
The present invention relates to the production fields of Bottle ＆ Can, refer in particular to a kind of explosion-proof beer bottle manufacturing technology.
Background technology
Beer consumption is in great demand in drinks ranking No. 1 in the world at present, but thing followed beer glass bottle
Frequent explosion causes the safety problem of people increasing every year, a kind of national patent publication number CN1171425A " vial explosions
The secondary production addition organic chemical composition of protective agent ", first, cost of labor increases, two are detrimental to environmental protection.
The content of the invention
It is an object of the invention to overcome the deficiencies of the prior art and provide technical solution it is as follows：A kind of explosion-proof beer is provided
Bottle manufacturing technology, by weight percentage：SiO266.8%Al2O38%Fe2O30.6%CaO7.5%MgO1.8%Na2O14.8%
BaO0.5%Cr2O30.1%.Present invention process of glass by, it is molten magnificent into the glass for meeting forming quality requirement through 1560 DEG C
Glass, using osculum press-and-blow process into technology, i.e., glass gob feed blocker → be pressed into parison → parison overturn to finishing die →
Reheat → finishing die vacuumizes assist formation → blow → clamp bottle eventually to cooling bench.During using the technique with more sufficiently reheating
Between, end is so contributed to blow, and rear bottle is equal with glass temperature in tank skin, and the beer bottle made of this composition can keep good
Mechanical strength.
The positive effect of the present invention is：SiO2 is substituted with part AL2O3, hardness, density, elasticity and the viscosity of glass increase
Greatly, coefficient of thermal expansion reduces, and increases beer bottle intensity by improving content in glass, adds safety coefficient.
Specific embodiment
Invention is further elaborated with reference to a preferred embodiment, by weight percentage：SiO266.8%
Al2O38%Fe2O30.6%CaO7.5%MgO1.8%Na2O14.8%BaO0.5%Cr2O30.1%, present invention glass production by
Technique, through 1560 DEG C of molten China into the glass for meeting forming quality requirement, using essay press-and-blow process into technology, i.e. glass gob is fed
Blocker → be pressed into parison → parison is overturn to finishing die → reheats → and finishing die vacuumizes assist formation → blowing eventually → and clamps bottle
To cooling bench, finished product.There is more sufficient reheat time using the technique, so contribute to blow rear bottle eventually with glass in tank skin
Glass temperature is uniform, and the beer bottle made of this composition can keep good mechanical strength.
Claims (2)
1. a kind of explosion-proof beer bottle manufacturing technology, it is characterised in that：By weight percentage, SiO266.8%Al2O38%
Fe2O30.6%CaO7.5%MgO1.8%Na2O14.8%BaO0.5%Cr2O30.1%。
2. according to right 1, it is characterised in that：Present invention process of glass by, it is molten magnificent into meeting into through 1580 DEG C
The glass of shape quality requirement, using osculum press-and-blow process into technology, i.e., glass gob feeds blocker → be pressed into parison → parison
Overturning to finishing die → reheat → finishing die vacuumizes assist formation → blowing eventually → and clamps bottle to cooling bench, finished product.