CN108049248A - A kind of heat-insulated glaxin release paper manufacture craft - Google Patents
A kind of heat-insulated glaxin release paper manufacture craft Download PDFInfo
- Publication number
- CN108049248A CN108049248A CN201711362057.6A CN201711362057A CN108049248A CN 108049248 A CN108049248 A CN 108049248A CN 201711362057 A CN201711362057 A CN 201711362057A CN 108049248 A CN108049248 A CN 108049248A
- Authority
- CN
- China
- Prior art keywords
- paper
- coating
- insulated
- heat
- under conditions
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of heat-insulated glaxin release paper manufacture crafts, include the following steps：Selection glassine paper is raw material, glassine paper is again placed on superpressure machine, glassine paper is compressed under conditions of 40 50 degrees Celsius, then the surface flatness of smoothness detection device detection glassine paper is utilized, it will treated glassine paper surface smear insulating moulding coating by coating machine under conditions of placing it in 70 90 degrees Celsius, it will treated glassine paper surface smear mould release by coating machine, then dried under conditions of placing it in 70 90 degrees Celsius, when meeting the requirements to its surface moisture, it need to be drawn off immediately, obtain heat-insulated glaxin release paper.The present invention is while release paper primary characteristic is ensured, additionally it is possible to by heat-insulated performance synthesis to release paper, it be made to possess heat resistance, effectively increase the service life of release paper.
Description
Technical field
The present invention relates to release paper preparing technical field more particularly to a kind of heat-insulated glaxin release paper manufacture crafts.
Background technology
Release paper is also known as barrier paper, separate paper.It is that one kind prevents prepreg adhesion, and prepreg can be protected not contaminated
Separate paper.During wet production prepreg, release paper is placed up and down in prepreg, wherein lower release paper is with prepreg
Winding deposit it is attached wherein, so usually there is the protection of one layer of release paper on prepreg surface.The effect of release paper is to prevent that prepreg is dirty
Dye, and can be provided conveniently for the line on its surface.Another effect of release paper is to prevent the Transverse Cracks of unidirectional pre-immersion material.With
It release paper and uses more and more extensive, also different to its quality requirements, in the prior art, release paper is in higher temperature
Under, chance, which deforms, either melts, it is desirable that affects its quality.For this purpose, we have proposed a kind of heat-insulated Ge Laxin
Release paper manufacture craft.
The content of the invention
The present invention proposes a kind of heat-insulated glaxin release paper manufacture craft, mentioned above in the background art to solve
Problem.
The present invention proposes a kind of heat-insulated glaxin release paper manufacture craft, includes the following steps：
S1：Selection glassine paper is raw material, and glassine paper is placed in cleaning device, is cleaned multiple times, and is completed clear
After washing, it by drying unit is dried, is then placed within spare in gnotobasis；
S2：By treated in S1, glassine paper is again placed on superpressure machine, the plaid matching Racine under conditions of 40-50 degrees Celsius
Body paper is compressed, and in compression process, repeated multiple times compression need to be carried out using superpressure machine, and compression time is 20-30min；
S3：After the completion of being compressed to glassine paper, the surface flatness of glassine paper is detected using smoothness detection device, with
Ensure the uniformity of the smoothness of paper, glossiness, tightness and thickness, improve the presentation quality of paper, if undesirable,
It then needs to repeat second compression again, meet the requirements then spare；
S4：It, will treated lattice by coating machine under conditions of then placing it in 70-90 degrees Celsius after the completion of being compressed in S3
Racine body paper surface smear insulating moulding coating, and the coating of insulating moulding coating needs uniformly, and after the completion of coating, it is utilized drying unit
Stand drying；
S5：After the completion of insulating moulding coating coating in S4, by coating machine will treated glassine paper surface smear mould release,
And the coating of mould release needs uniformly, to be dried under conditions of then placing it in 70-90 degrees Celsius, its surface moisture is accorded with
When conjunction requires, it need to be drawn off immediately, and natural air drying；
S6：After the completion of above-mentioned, the release paper rolled up greatly is cut under conditions of 40-50 degrees Celsius according to customer demand,
As the finished product needed for client, to get to heat-insulated glaxin release paper after being packaged.
Preferably, the mould release in S5 be thermosol, oiliness acrylate pressure sensitive adhesive, food-grade silicone oil, stabilizer it is mixed
Liquid is closed, and the weight ratio of thermosol, oiliness acrylate pressure sensitive adhesive, food-grade silicone oil, stabilizer is 1：1：0.5：0.1.
The present invention also provides a kind of insulating moulding coating, the formula of raw material by weight is as follows：30-40 parts of acrylic emulsion,
20-30 parts of styrene-acrylic emulsion, 12-16 parts of neopelex, 12-16 parts of polyvinyl alcohol, 6-9 parts of dispersant, coalescents
6-9 parts.
The present invention also provides a kind of preparation processes of insulating moulding coating, are as follows：
Blender is chosen, and acrylic emulsion, styrene-acrylic emulsion, neopelex and polyvinyl alcohol are inserted into blender
It is interior, be mixed under conditions of 70-90 degrees Celsius, treat it after mixing, again thereto add dispersant with into
Film auxiliary agent carries out mixing 20-30min, takes out after finishing again, to get to heat-insulated painting after its temperature is recovered to room temperature
Material.
Preferably, in acrylic emulsion, styrene-acrylic emulsion, neopelex and polyvinyl alcohol placement process,
It need to be stirred in real time.
A kind of heat-insulated glaxin release paper manufacture craft proposed by the present invention, advantageous effect are：The heat-insulated Ge La
Pungent release paper manufacture craft is when preparing release paper, while release paper primary characteristic is ensured, additionally it is possible to by heat-insulated performance
In synthesis to release paper, it is made to possess heat resistance, effectively increases the service life of release paper, add it uses model
It encloses, is suitble to promote on a large scale.
Specific embodiment
With reference to specific embodiment, the present invention will be further described.
Embodiment 1
The present invention proposes a kind of heat-insulated glaxin release paper manufacture craft, includes the following steps：
S1：Selection glassine paper is raw material, and glassine paper is placed in cleaning device, is cleaned multiple times, and is completed clear
After washing, it by drying unit is dried, is then placed within spare in gnotobasis；
S2：By treated in S1, glassine paper is again placed on superpressure machine, and plaid matching Racine is former under conditions of 40 degrees Celsius
Paper is compressed, and in compression process, repeated multiple times compression need to be carried out using superpressure machine, and compression time is 20min；
S3：After the completion of being compressed to glassine paper, the surface flatness of glassine paper is detected using smoothness detection device, with
Ensure the uniformity of the smoothness of paper, glossiness, tightness and thickness, improve the presentation quality of paper, if undesirable,
It then needs to repeat second compression again, meet the requirements then spare；
S4：After the completion of being compressed in S3, by coating machine, by treated, lattice are drawn under conditions of then placing it in 70 degrees Celsius
Pungent body paper surface smear insulating moulding coating, and the coating of insulating moulding coating needs uniformly, it is after the completion of coating, it is quiet using drying unit
Put drying；
S5：After the completion of insulating moulding coating coating in S4, by coating machine will treated glassine paper surface smear mould release,
And the coating of mould release needs uniformly, to be dried under conditions of then placing it in 70 degrees Celsius, meet its surface moisture
It is required that when, it need to be drawn off immediately, and natural air drying；
S6：After the completion of above-mentioned, the release paper rolled up greatly is cut under conditions of 40 degrees Celsius according to customer demand, is become
Finished product needed for client, to get to heat-insulated glaxin release paper after being packaged.
Mould release in S5 is thermosol, oiliness acrylate pressure sensitive adhesive, food-grade silicone oil, the mixed liquor of stabilizer, and
Thermosol, oiliness acrylate pressure sensitive adhesive, food-grade silicone oil, the weight ratio of stabilizer are 1：1：0.5：0.1.
The present invention also provides a kind of insulating moulding coating, the formula of raw material by weight is as follows：30 parts of acrylic emulsion, phenylpropyl alcohol
20 parts of lotion, 12 parts of neopelex, 12 parts of polyvinyl alcohol, 6 parts of dispersant, 6 parts of coalescents.
The present invention also provides a kind of preparation processes of insulating moulding coating, are as follows：
Blender is chosen, and acrylic emulsion, styrene-acrylic emulsion, neopelex and polyvinyl alcohol are inserted into blender
It is interior, it is mixed under conditions of 70 degrees Celsius, treats it after mixing, addition dispersant is helped with film forming thereto again
Agent carries out mixing 20min, takes out after finishing again, to get to insulating moulding coating after its temperature is recovered to room temperature.
In acrylic emulsion, styrene-acrylic emulsion, neopelex and polyvinyl alcohol placement process, need to its into
Row stirring in real time.
Embodiment 2
The present invention proposes a kind of heat-insulated glaxin release paper manufacture craft, includes the following steps：
S1：Selection glassine paper is raw material, and glassine paper is placed in cleaning device, is cleaned multiple times, and is completed clear
After washing, it by drying unit is dried, is then placed within spare in gnotobasis；
S2：By treated in S1, glassine paper is again placed on superpressure machine, and plaid matching Racine is former under conditions of 44 degrees Celsius
Paper is compressed, and in compression process, repeated multiple times compression need to be carried out using superpressure machine, and compression time is 24min；
S3：After the completion of being compressed to glassine paper, the surface flatness of glassine paper is detected using smoothness detection device, with
Ensure the uniformity of the smoothness of paper, glossiness, tightness and thickness, improve the presentation quality of paper, if undesirable,
It then needs to repeat second compression again, meet the requirements then spare；
S4：After the completion of being compressed in S3, by coating machine, by treated, lattice are drawn under conditions of then placing it in 75 degrees Celsius
Pungent body paper surface smear insulating moulding coating, and the coating of insulating moulding coating needs uniformly, it is after the completion of coating, it is quiet using drying unit
Put drying；
S5：After the completion of insulating moulding coating coating in S4, by coating machine will treated glassine paper surface smear mould release,
And the coating of mould release needs uniformly, to be dried under conditions of then placing it in 75 degrees Celsius, meet its surface moisture
It is required that when, it need to be drawn off immediately, and natural air drying；
S6：After the completion of above-mentioned, the release paper rolled up greatly is cut under conditions of 44 degrees Celsius according to customer demand, is become
Finished product needed for client, to get to heat-insulated glaxin release paper after being packaged.
Mould release in S5 is thermosol, oiliness acrylate pressure sensitive adhesive, food-grade silicone oil, the mixed liquor of stabilizer, and
Thermosol, oiliness acrylate pressure sensitive adhesive, food-grade silicone oil, the weight ratio of stabilizer are 1：1：0.5：0.1.
The present invention also provides a kind of insulating moulding coating, the formula of raw material by weight is as follows：34 parts of acrylic emulsion, phenylpropyl alcohol
24 parts of lotion, 13 parts of neopelex, 13 parts of polyvinyl alcohol, 7 parts of dispersant, 7 parts of coalescents.
The present invention also provides a kind of preparation processes of insulating moulding coating, are as follows：
Blender is chosen, and acrylic emulsion, styrene-acrylic emulsion, neopelex and polyvinyl alcohol are inserted into blender
It is interior, it is mixed under conditions of 75 degrees Celsius, treats it after mixing, addition dispersant is helped with film forming thereto again
Agent carries out mixing 24min, takes out after finishing again, to get to insulating moulding coating after its temperature is recovered to room temperature.
In acrylic emulsion, styrene-acrylic emulsion, neopelex and polyvinyl alcohol placement process, need to its into
Row stirring in real time.
Embodiment 3
The present invention proposes a kind of heat-insulated glaxin release paper manufacture craft, includes the following steps：
S1：Selection glassine paper is raw material, and glassine paper is placed in cleaning device, is cleaned multiple times, and is completed clear
After washing, it by drying unit is dried, is then placed within spare in gnotobasis；
S2：By treated in S1, glassine paper is again placed on superpressure machine, and plaid matching Racine is former under conditions of 48 degrees Celsius
Paper is compressed, and in compression process, repeated multiple times compression need to be carried out using superpressure machine, and compression time is 28min；
S3：After the completion of being compressed to glassine paper, the surface flatness of glassine paper is detected using smoothness detection device, with
Ensure the uniformity of the smoothness of paper, glossiness, tightness and thickness, improve the presentation quality of paper, if undesirable,
It then needs to repeat second compression again, meet the requirements then spare；
S4：After the completion of being compressed in S3, by coating machine, by treated, lattice are drawn under conditions of then placing it in 85 degrees Celsius
Pungent body paper surface smear insulating moulding coating, and the coating of insulating moulding coating needs uniformly, it is after the completion of coating, it is quiet using drying unit
Put drying；
S5：After the completion of insulating moulding coating coating in S4, by coating machine will treated glassine paper surface smear mould release,
And the coating of mould release needs uniformly, to be dried under conditions of then placing it in 85 degrees Celsius, meet its surface moisture
It is required that when, it need to be drawn off immediately, and natural air drying；
S6：After the completion of above-mentioned, the release paper rolled up greatly is cut under conditions of 48 degrees Celsius according to customer demand, is become
Finished product needed for client, to get to heat-insulated glaxin release paper after being packaged.
Mould release in S5 is thermosol, oiliness acrylate pressure sensitive adhesive, food-grade silicone oil, the mixed liquor of stabilizer, and
Thermosol, oiliness acrylate pressure sensitive adhesive, food-grade silicone oil, the weight ratio of stabilizer are 1：1：0.5：0.1.
The present invention also provides a kind of insulating moulding coating, the formula of raw material by weight is as follows：37 parts of acrylic emulsion, phenylpropyl alcohol
27 parts of lotion, 15 parts of neopelex, 15 parts of polyvinyl alcohol, 8 parts of dispersant, 8 parts of coalescents.
The present invention also provides a kind of preparation processes of insulating moulding coating, are as follows：
Blender is chosen, and acrylic emulsion, styrene-acrylic emulsion, neopelex and polyvinyl alcohol are inserted into blender
It is interior, it is mixed under conditions of 85 degrees Celsius, treats it after mixing, addition dispersant is helped with film forming thereto again
Agent carries out mixing 27min, takes out after finishing again, to get to insulating moulding coating after its temperature is recovered to room temperature.
In acrylic emulsion, styrene-acrylic emulsion, neopelex and polyvinyl alcohol placement process, need to its into
Row stirring in real time.
Embodiment 4
The present invention proposes a kind of heat-insulated glaxin release paper manufacture craft, includes the following steps：
S1：Selection glassine paper is raw material, and glassine paper is placed in cleaning device, is cleaned multiple times, and is completed clear
After washing, it by drying unit is dried, is then placed within spare in gnotobasis；
S2：By treated in S1, glassine paper is again placed on superpressure machine, and plaid matching Racine is former under conditions of 50 degrees Celsius
Paper is compressed, and in compression process, repeated multiple times compression need to be carried out using superpressure machine, and compression time is 30min；
S3：After the completion of being compressed to glassine paper, the surface flatness of glassine paper is detected using smoothness detection device, with
Ensure the uniformity of the smoothness of paper, glossiness, tightness and thickness, improve the presentation quality of paper, if undesirable,
It then needs to repeat second compression again, meet the requirements then spare；
S4：After the completion of being compressed in S3, by coating machine, by treated, lattice are drawn under conditions of then placing it in 90 degrees Celsius
Pungent body paper surface smear insulating moulding coating, and the coating of insulating moulding coating needs uniformly, it is after the completion of coating, it is quiet using drying unit
Put drying；
S5：After the completion of insulating moulding coating coating in S4, by coating machine will treated glassine paper surface smear mould release,
And the coating of mould release needs uniformly, to be dried under conditions of then placing it in 90 degrees Celsius, meet its surface moisture
It is required that when, it need to be drawn off immediately, and natural air drying；
S6：After the completion of above-mentioned, the release paper rolled up greatly is cut under conditions of 50 degrees Celsius according to customer demand, is become
Finished product needed for client, to get to heat-insulated glaxin release paper after being packaged.
Mould release in S5 is thermosol, oiliness acrylate pressure sensitive adhesive, food-grade silicone oil, the mixed liquor of stabilizer, and
Thermosol, oiliness acrylate pressure sensitive adhesive, food-grade silicone oil, the weight ratio of stabilizer are 1：1：0.5：0.1.
The present invention also provides a kind of insulating moulding coating, the formula of raw material by weight is as follows：40 parts of acrylic emulsion, phenylpropyl alcohol
30 parts of lotion, 16 parts of neopelex, 16 parts of polyvinyl alcohol, 9 parts of dispersant, 9 parts of coalescents.
The present invention also provides a kind of preparation processes of insulating moulding coating, are as follows：
Blender is chosen, and acrylic emulsion, styrene-acrylic emulsion, neopelex and polyvinyl alcohol are inserted into blender
It is interior, it is mixed under conditions of 90 degrees Celsius, treats it after mixing, addition dispersant is helped with film forming thereto again
Agent carries out mixing 30min, takes out after finishing again, to get to insulating moulding coating after its temperature is recovered to room temperature.
In acrylic emulsion, styrene-acrylic emulsion, neopelex and polyvinyl alcohol placement process, need to its into
Row stirring in real time.
The foregoing is only a preferred embodiment of the present invention, but protection scope of the present invention be not limited thereto,
Any one skilled in the art in the technical scope disclosed by the present invention, technique according to the invention scheme and its
Inventive concept is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.
Claims (5)
1. a kind of heat-insulated glaxin release paper manufacture craft, which is characterized in that comprise the following steps：
S1：Selection glassine paper is raw material, and glassine paper is placed in cleaning device, is cleaned multiple times, and is completed clear
After washing, it by drying unit is dried, is then placed within spare in gnotobasis；
S2：By treated in S1, glassine paper is again placed on superpressure machine, the plaid matching Racine under conditions of 40-50 degrees Celsius
Body paper is compressed, and in compression process, repeated multiple times compression need to be carried out using superpressure machine, and compression time is 20-30min；
S3：After the completion of being compressed to glassine paper, the surface flatness of glassine paper is detected using smoothness detection device, with
Ensure the uniformity of the smoothness of paper, glossiness, tightness and thickness, improve the presentation quality of paper, if undesirable,
It then needs to repeat second compression again, meet the requirements then spare；
S4：It, will treated lattice by coating machine under conditions of then placing it in 70-90 degrees Celsius after the completion of being compressed in S3
Racine body paper surface smear insulating moulding coating, and the coating of insulating moulding coating needs uniformly, and after the completion of coating, it is utilized drying unit
Stand drying；
S5：After the completion of insulating moulding coating coating in S4, by coating machine will treated glassine paper surface smear mould release,
And the coating of mould release needs uniformly, to be dried under conditions of then placing it in 70-90 degrees Celsius, its surface moisture is accorded with
When conjunction requires, it need to be drawn off immediately, and natural air drying；
S6：After the completion of above-mentioned, the release paper rolled up greatly is cut under conditions of 40-50 degrees Celsius according to customer demand,
As the finished product needed for client, to get to heat-insulated glaxin release paper after being packaged.
2. a kind of heat-insulated glaxin release paper manufacture craft according to claim 1, it is characterised in that：In S5 from
Type agent is thermosol, oiliness acrylate pressure sensitive adhesive, food-grade silicone oil, the mixed liquor of stabilizer, and thermosol, oiliness propylene acid fracturing
Quick glue, food-grade silicone oil, the weight ratio of stabilizer are 1：1：0.5：0.1.
3. a kind of insulating moulding coating according to claim 1, which is characterized in that the formula of its raw material by weight is as follows：Propylene
30-40 parts of yogurt liquid, 20-30 parts of styrene-acrylic emulsion, 12-16 parts of neopelex, 12-16 parts of polyvinyl alcohol, dispersant
6-9 parts, 6-9 parts of coalescents.
4. a kind of preparation process of insulating moulding coating according to claim 3, which is characterized in that be as follows：
Blender is chosen, and acrylic emulsion, styrene-acrylic emulsion, neopelex and polyvinyl alcohol are inserted into blender
It is interior, be mixed under conditions of 70-90 degrees Celsius, treat it after mixing, again thereto add dispersant with into
Film auxiliary agent carries out mixing 20-30min, takes out after finishing again, to get to heat-insulated painting after its temperature is recovered to room temperature
Material.
5. a kind of heat-insulated glaxin release paper manufacture craft according to claim 4, it is characterised in that：In propylene yogurt
In liquid, styrene-acrylic emulsion, neopelex and polyvinyl alcohol placement process, it need to be stirred in real time.