CN108046724A - A kind of diatomite forming composition with moisture absorbing and preparation method thereof - Google Patents

A kind of diatomite forming composition with moisture absorbing and preparation method thereof Download PDF

Info

Publication number
CN108046724A
CN108046724A CN201711368121.1A CN201711368121A CN108046724A CN 108046724 A CN108046724 A CN 108046724A CN 201711368121 A CN201711368121 A CN 201711368121A CN 108046724 A CN108046724 A CN 108046724A
Authority
CN
China
Prior art keywords
forming composition
diatomite
antiseptic
mixture
moisture absorbing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201711368121.1A
Other languages
Chinese (zh)
Other versions
CN108046724B (en
Inventor
韦仲华
卢发昭
韦睿
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guilin Good Materials And Daily Necessities Co Ltd
Original Assignee
Guilin Good Materials And Daily Necessities Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Guilin Good Materials And Daily Necessities Co Ltd filed Critical Guilin Good Materials And Daily Necessities Co Ltd
Priority to CN201711368121.1A priority Critical patent/CN108046724B/en
Publication of CN108046724A publication Critical patent/CN108046724A/en
Application granted granted Critical
Publication of CN108046724B publication Critical patent/CN108046724B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

A kind of diatomite forming composition with moisture absorbing of the present invention and preparation method thereof, diatomite forming composition is made of diatomite, tourmaline powder, zeolite powder, bamboo charcoal, antiseptic, acrylic resin adhesive, land plaster.The antiseptic of addition is that the inorganic antiseptic obtained on glass is attached to by silver ion, and the safe of the inorganic antiseptic, impatience bacterium, fungistatic effect are notable；Metallic silver and glass under conditions of high temperature anaerobic are uniformly mixed when preparing the antiseptic, metallic silver can be avoided to aoxidize；The mixture of melting is put into low temperature oxygen-free environment when preparing the antiseptic and is cooled to room temperature, the hardness for the antiseptic being prepared can be improved, the roughness on increase antiseptic surface reduces the generation of antiseptic obscission；The suitable tourmaline powder of addition proportioning and zeolite powder can effectively excite the negative oxygen ion in living environment.

Description

A kind of diatomite forming composition with moisture absorbing and preparation method thereof
Technical field
Preparation and applied technical field the present invention relates to diatomite based composites, and in particular to one kind has moisture absorption work( Diatomite forming composition of energy and preparation method thereof.
Background technology
After diatomite is the remains accumulative deposit of ancient times unicellular rudimentary plant diatom, formed by preliminary diagenesis One kind there are porous biological silicalite.It is made of the wall shell of diatom, there is multistage, a large amount of, orderly row on wall shell The micropore of row, and diatomite has the characteristics such as small density, large specific surface area, excellent adsorption, acidproof, alkaline-resisting, insulation, it is unique Surface texture be adapted for use as sorbing material with excellent absorption property, and Chinese diatomite Resource management enriches, It is cheap and easy to get.Diatomite is by unbodied SiO2Composition, and contain a small amount of Fe2O3、CaO、MgO、Al2O3And organic impurities.Diatom Soil is in usually light yellow or light grey, and matter is soft, porous and light.Diatomaceous main component is silicic acid matter, has superfluorescent fiber, porous The characteristics such as matter, ultra tiny boring ratio charcoal it is more go out 5000 to 6000 times.It is super on diatomite when humidity indoors rises Micropore can be in automatic absorption air moisture, stored.If the moisture in room air is reduced, under humidity Drop, diatomite can just come out the water release being stored in ultra micro pore.Diatomite also has the function of to eliminate peculiar smell, protect Hold the effect of indoor cleaning.
At home and abroad there is enterprise to add composite material using diatomite to manufacture various formed combination Tetramunes at present, But also have certain limitation in terms of composition of raw materials and manufacturing process, affect the effect of application.Diatomite formed combination Object is since its moisture absorbing is strong, and the outside face of various products made of diatomite forming composition is easy to grow various bacteriums, no Beneficial to the cleaning for keeping diatomite forming composition product surface.
The content of the invention
In view of the deficiencies of the prior art, the object of the present invention is to provide a kind of making is simple, manufacturing cost is low, is not easy to grow A kind of diatomite forming composition with moisture absorbing of bacterium and preparation method thereof.
What the invention is realized by the following technical scheme：
It is formulated and is：A kind of diatomite forming composition with moisture absorbing, the weight of the diatomite forming composition each component Amount percentage, which forms, is：Diatomite 15%~20%, tourmaline powder 10%~15%, zeolite powder 5%~8%, bamboo charcoal 3%~5%, antiseptic 3%~5%, acrylic resin adhesive 0.1%~1.0%, surplus are land plaster, and the antiseptic is to be attached to glass by silver ion On obtained inorganic antiseptic.
Preferably, the diatomaceous grain size is 20 μm~25 μm.
Preferably, the grain size of the tourmaline powder is 20 μm~25 μm.
Preferably, the grain size of the land plaster is 20 μm~25 μm.
Preferably, the grain size of the bamboo charcoal is 20 μm~25 μm.
Preferably, the preparation method of the antiseptic be take the mixture of metallic silver and glass be put into temperature for 1400 DEG C~ In 1700 DEG C of agitator tank, then the air in agitator tank all replaced with into nitrogen, 2h~4h is mixed, it will after the completion of stirring Mixture is removed and placed in the oxygen-free environment that temperature is -4 DEG C and is cooled to room temperature, and mixture finally is crushed to 20 μm~25 μ M is to get the antiseptic.
Preparation method is：A kind of preparation method of the diatomite forming composition with moisture absorbing, comprises the following steps：
（1）Diatomite, tourmaline powder, zeolite powder, bamboo charcoal, land plaster are put into container, water is added and is mixed and mixed Object is closed, the proportion of water is 7%~10% in the mixture；
（2）First by step（1）In mixture filtering, take filter residue and be put into silica gel mould and be molded, then by molding mixture It spontaneously dries, obtains forming composition；
（3）First antiseptic is uniformly mixed to obtain mixture with acrylic resin adhesive, then mixture is equably brushed The surface of forming composition obtains diatomite forming composition semi-finished product；
（4）By step（3）In diatomite forming composition semi-finished product spontaneously dry to get the diatom with moisture absorbing Earth forming composition.
Preferably, the step（1）In mixing speed be 500r/min~700r/min.
Preferably, the step（3）The middle brushing thickness equably brushed mixture on forming composition surface is 0.15mm~0.17mm.
Zeolite is a kind of ore, is a kind of natural aluminosilicate acid salt ore, boiling phenomenon can be generated in calcination.With adsorptivity, The performances such as ion exchangeable, catalysis and acidproof heat-proof, therefore it is widely used as adsorbent, ion-exchanger and catalyst, also may be used Drying, purification and sewage disposal for gas etc..
Tourmaline is aluminium, iron, sodium, magnesium, the cyclic structure silicate mineral of lithium characterized by boracic, in black or ash Black, bodkin shape, pencil or radial structure.Tourmaline has special pyroelectricity and piezoelectricity, there is very high Far-infrared spoke Penetrate with anion releasability, and containing there are many trace element beneficial to health, be widely used in drinking water activation, The fields such as air purification, sewage disposal, ceramics, building materials, daily-use chemical industry, electronics, weaving, health treatment, cosmetics.Due to Tourmaline has unique environmental purification function, is combined and a kind of diatomite forming composition with moisture absorbing is made, Its existing certain mechanical strength is made to have good environmental purification function again.
Land plaster, main chemical compositions are the hydrate of calcium sulfate.Dihydrate CaSO4 2H2O are commonly called as gypsum, and half is hydrated Object 2CaSO4 H2O claim the plaster of paris.Plaster of paris powder has plasticity after being mixed with water, but shortly hardens and become gypsum again.Stone Cream, for slurry is made to have the plasticity of construction requirement, need to add in the water consumption of gypsum dosage 60% in mix.Land plaster has Certain adjustable wet, since a large amount of capillary porosities have stronger adsorption capacity to the vapor in air inside plastering, So there is certain adjustment effect to indoor air humidity.
A kind of diatomite forming composition with moisture absorbing of the present invention and preparation method thereof, the antiseptic of addition be by Silver ion is attached to the inorganic antiseptic obtained on glass, and the safe of the inorganic antiseptic, impatience bacterium, fungistatic effect are shown It writes；Metallic silver and glass under conditions of high temperature anaerobic are uniformly mixed when preparing the antiseptic, metallic silver can be avoided to aoxidize, carried The antibacterial effect for the antiseptic that height is prepared；The mixture of melting is put into low temperature oxygen-free environment when preparing the antiseptic and is cooled down Crushed to room temperature, then by mixture, on the one hand metallic silver can be avoided to aoxidize, on the other hand can improve be prepared it is anti- The hardness of microbial inoculum, the roughness on increase antiseptic surface, reduces the generation of antiseptic obscission；It is suitable electrical to add in proportioning Mountain flour and zeolite powder can effectively excite the negative oxygen ion in living environment, increase negative ion concentration in air, are conducive to human body Health；The bamboo charcoal of addition and diatomaceous water absorbing properties are good, can effectively improve the moisture absorbing of diatomite forming composition.
Specific embodiment
The following examples can help those skilled in the art that the present invention is more fully understood, but cannot be with any Mode limits the present invention.
Embodiment 1：Prepare diatomite forming composition
It is formulated and is：A kind of diatomite forming composition with moisture absorbing, the weight of the diatomite forming composition each component Amount percentage, which forms, is：Diatomite 15%, tourmaline powder 10%, zeolite powder 5%, bamboo charcoal 3%, antiseptic 3%, acrylic resin gluing Agent 0.1%, surplus are land plaster, and antiseptic is that the inorganic antiseptic obtained on glass is attached to by silver ion, diatomaceous grain size For 20 μm, the grain size of tourmaline powder is 20 μm, and the grain size of land plaster is 20 μm, and the grain size of bamboo charcoal is 20 μm, the preparation of antiseptic Method is that the mixture of metallic silver and glass is taken to be put into the agitator tank that temperature is 1400 DEG C, then the air in agitator tank is whole Nitrogen is replaced with, 2h is mixed, mixture is removed and placed in the oxygen-free environment that temperature is -4 DEG C after the completion of stirring and is cooled down To room temperature, mixture is finally crushed to 20 μm to get antiseptic.
Preparation method is：A kind of preparation method of the diatomite forming composition with moisture absorbing, comprises the following steps：
（1）Diatomite, tourmaline powder, zeolite powder, bamboo charcoal, land plaster are put into container, water is added and is mixed and mixed Close object, the speed of mixing is 500r/min, and the proportion of water is 7% in mixture；
（2）First by step（1）In mixture filtering, take filter residue and be put into silica gel mould and be molded, then by molding mixture It spontaneously dries, obtains forming composition；
（3）First antiseptic is uniformly mixed to obtain mixture with acrylic resin adhesive, then mixture is equably brushed The surface of forming composition, brushing thickness are 0.15mm, obtain diatomite forming composition semi-finished product；
（4）By step（3）In diatomite forming composition semi-finished product spontaneously dry to get the diatom with moisture absorbing Earth forming composition.
Embodiment 2：Prepare diatomite forming composition
It is formulated and is：A kind of diatomite forming composition with moisture absorbing, the weight of the diatomite forming composition each component Amount percentage, which forms, is：Diatomite 20%, tourmaline powder 15%, zeolite powder 8%, bamboo charcoal 5%, antiseptic 5%, acrylic resin gluing Agent 1.0%, surplus are land plaster, and antiseptic is that the inorganic antiseptic obtained on glass is attached to by silver ion, diatomaceous grain size For 25 μm, the grain size of tourmaline powder is 25 μm, and the grain size of land plaster is 25 μm, and the grain size of bamboo charcoal is 25 μm, the preparation of antiseptic Method is that the mixture of metallic silver and glass is taken to be put into the agitator tank that temperature is 1700 DEG C, then the air in agitator tank is whole Nitrogen is replaced with, 4h is mixed, mixture is removed and placed in the oxygen-free environment that temperature is -4 DEG C after the completion of stirring and is cooled down To room temperature, mixture is finally crushed to 25 μm to get antiseptic.
Preparation method is：A kind of preparation method of the diatomite forming composition with moisture absorbing, comprises the following steps：
（1）Diatomite, tourmaline powder, zeolite powder, bamboo charcoal, land plaster are put into container, water is added and is mixed and mixed Close object, the speed of mixing is 700r/min, and the proportion of water is 10% in mixture；
（2）First by step（1）In mixture filtering, take filter residue and be put into silica gel mould and be molded, then by molding mixture It spontaneously dries, obtains forming composition；
（3）First antiseptic is uniformly mixed to obtain mixture with acrylic resin adhesive, then mixture is equably brushed The surface of forming composition, brushing thickness are 0.17mm, obtain diatomite forming composition semi-finished product；
（4）By step（3）In diatomite forming composition semi-finished product spontaneously dry to get the diatom with moisture absorbing Earth forming composition.
Embodiment 3：Prepare diatomite forming composition
It is formulated and is：A kind of diatomite forming composition with moisture absorbing, the weight of the diatomite forming composition each component Amount percentage, which forms, is：Diatomite 17%, tourmaline powder 12%, zeolite powder 6%, bamboo charcoal 4%, antiseptic 4%, acrylic resin gluing Agent 0.6%, surplus are land plaster, and antiseptic is that the inorganic antiseptic obtained on glass is attached to by silver ion, diatomaceous grain size For 22 μm, the grain size of tourmaline powder is 22 μm, and the grain size of land plaster is 22 μm, and the grain size of bamboo charcoal is 22 μm, the preparation of antiseptic Method is that the mixture of metallic silver and glass is taken to be put into the agitator tank that temperature is 1500 DEG C, then the air in agitator tank is whole Nitrogen is replaced with, 3h is mixed, mixture is removed and placed in the oxygen-free environment that temperature is -4 DEG C after the completion of stirring and is cooled down To room temperature, mixture is finally crushed to 22 μm to get antiseptic.
Preparation method is：A kind of preparation method of the diatomite forming composition with moisture absorbing, comprises the following steps：
（1）Diatomite, tourmaline powder, zeolite powder, bamboo charcoal, land plaster are put into container, water is added and is mixed and mixed Close object, the speed of mixing is 600r/min, and the proportion of water is 8% in mixture；
（2）First by step（1）In mixture filtering, take filter residue and be put into silica gel mould and be molded, then by molding mixture It spontaneously dries, obtains forming composition；
（3）First antiseptic is uniformly mixed to obtain mixture with acrylic resin adhesive, then mixture is equably brushed The surface of forming composition, brushing thickness are 0.16mm, obtain diatomite forming composition semi-finished product；
（4）By step（3）In diatomite forming composition semi-finished product spontaneously dry to get the diatom with moisture absorbing Earth forming composition.
Embodiment 4
It is formulated and is：A kind of diatomite forming composition with moisture absorbing, the weight of the diatomite forming composition each component Amount percentage, which forms, is：Diatomite 17%, tourmaline powder 12%, zeolite powder 6%, bamboo charcoal 4%, antiseptic 4%, acrylic resin gluing Agent 0.6%, surplus are land plaster, and antiseptic is that the inorganic antiseptic obtained on glass is attached to by silver ion, diatomaceous grain size For 22 μm, the grain size of tourmaline powder is 22 μm, and the grain size of land plaster is 22 μm, and the grain size of bamboo charcoal is 22 μm, the preparation of antiseptic Method is that the mixture of metallic silver and glass is taken to be put into the agitator tank that temperature is 1500 DEG C, then the air in agitator tank is whole Nitrogen is replaced with, 3h is mixed, mixture is removed and placed in room temperature and the environment of anaerobic after the completion of stirring and is cooled to room Mixture is finally crushed to 22 μm to get antiseptic by temperature.
Preparation method is：A kind of preparation method of the diatomite forming composition with moisture absorbing, comprises the following steps：
（1）Diatomite, tourmaline powder, zeolite powder, bamboo charcoal, land plaster are put into container, water is added and is mixed and mixed Close object, the speed of mixing is 600r/min, and the proportion of water is 8% in mixture；
（2）First by step（1）In mixture filtering, take filter residue and be put into silica gel mould and be molded, then by molding mixture It spontaneously dries, obtains forming composition；
（3）First antiseptic is uniformly mixed to obtain mixture with acrylic resin adhesive, then mixture is equably brushed The surface of forming composition, brushing thickness are 0.16mm, obtain diatomite forming composition semi-finished product；
（4）By step（3）In diatomite forming composition semi-finished product spontaneously dry to get the diatom with moisture absorbing Earth forming composition.
Comparative example 1
It is formulated and is：A kind of diatomite forming composition with moisture absorbing, the weight of the diatomite forming composition each component Amount percentage, which forms, is：It is diatomite 17%, tourmaline powder 12%, bamboo charcoal 4%, antiseptic 4%, acrylic resin adhesive 0.6%, remaining It measures as land plaster, antiseptic is that the inorganic antiseptic obtained on glass is attached to by silver ion, and diatomaceous grain size is 22 μm, electricity The grain size of gas mountain flour is 22 μm, and the grain size of land plaster is 22 μm, and the grain size of bamboo charcoal is 22 μm, and the preparation method of antiseptic is to take gold The mixture for belonging to silver and glass is put into the agitator tank that temperature is 1500 DEG C, then the air in agitator tank is all replaced with nitrogen 3h is mixed in gas, and mixture is removed and placed in the oxygen-free environment that temperature is -4 DEG C after the completion of stirring and is cooled to room temperature, most Mixture is crushed to 22 μm to get antiseptic afterwards.
Preparation method is：A kind of preparation method of the diatomite forming composition with moisture absorbing, comprises the following steps：
（1）Diatomite, tourmaline powder, bamboo charcoal, land plaster are put into container, water is added and is mixed to obtain mixture, is mixed The speed of stirring is closed as 600r/min, the proportion of water is 8% in mixture；
（2）First by step（1）In mixture filtering, take filter residue and be put into silica gel mould and be molded, then by molding mixture It spontaneously dries, obtains forming composition；
（3）First antiseptic is uniformly mixed to obtain mixture with acrylic resin adhesive, then mixture is equably brushed The surface of forming composition, brushing thickness are 0.16mm, obtain diatomite forming composition semi-finished product；
（4）By step（3）In diatomite forming composition semi-finished product spontaneously dry to get the diatom with moisture absorbing Earth forming composition.
The following table 1 provides intermediate product antiseptic made from embodiment 1-4 and comparative example 1 and the diatomite with moisture absorbing The performance measurement result of forming composition.
Table 1
From intermediate product antiseptic made from upper table embodiment 1-4 and comparative example 1 and with moisture absorbing diatom earth forming group The performance measurement result of object, a kind of diatomite forming composition with moisture absorbing of the present invention and preparation method thereof are closed, is prepared Well, moisture sorption effect is strong for the sterilization of obtained diatomite forming composition, and anion production is high, and antiseptic surface roughness is not easy greatly It comes off from diatomite forming composition surface.
Although above the present invention is described in detail with a general description of the specific embodiments, On the basis of the present invention, it can be made some modifications or improvements, this will be apparent to those skilled in the art.Cause This, these modifications or improvements, belong to the scope of protection of present invention without departing from theon the basis of the spirit of the present invention.

Claims (9)

  1. A kind of 1. diatomite forming composition with moisture absorbing, which is characterized in that the diatomite forming composition each group The weight percent divided forms：Diatomite 15%~20%, tourmaline powder 10%~15%, zeolite powder 5%~8%, bamboo charcoal 3%~5%, Antiseptic 3%~5%, acrylic resin adhesive 0.1%~1.0%, surplus are land plaster, and the antiseptic is adhered to by silver ion In the inorganic antiseptic obtained on glass.
  2. A kind of 2. diatomite forming composition with moisture absorbing according to claim 1, which is characterized in that the silicon The grain size of diatomaceous earth is 20 μm~25 μm.
  3. A kind of 3. diatomite forming composition with moisture absorbing according to claim 1, which is characterized in that the electricity The grain size of gas mountain flour is 20 μm~25 μm.
  4. A kind of 4. diatomite forming composition with moisture absorbing according to claim 1, which is characterized in that the stone The grain size of cream powder is 20 μm~25 μm.
  5. A kind of 5. diatomite forming composition with moisture absorbing according to claim 1, which is characterized in that the bamboo The grain size of charcoal is 20 μm~25 μm.
  6. 6. a kind of diatomite forming composition with moisture absorbing according to claim 1, which is characterized in that described anti- The preparation method of microbial inoculum is that the mixture of metallic silver and glass is taken to be put into the agitator tank that temperature is 1400 DEG C~1700 DEG C, will be stirred The air mixed in tank all replaces with nitrogen, remixes stirring 2h~4h, mixture is removed and placed in temperature after the completion of stirring To be cooled to room temperature in -4 DEG C of oxygen-free environment, mixture is finally crushed to 20 μm~25 μm to get the antiseptic.
  7. 7. a kind of preparation side of diatomite forming composition with moisture absorbing in claim 1-6 described in any one Method, which is characterized in that comprise the following steps：
    （1）Diatomite, tourmaline powder, zeolite powder, bamboo charcoal, land plaster are put into container, water is added and is mixed and mixed Object is closed, the proportion of water is 7%~10% in the mixture；
    （2）First by step（1）In mixture filtering, take filter residue and be put into silica gel mould and be molded, then by molding mixture It spontaneously dries, obtains forming composition；
    （3）First antiseptic is uniformly mixed to obtain mixture with acrylic resin adhesive, then mixture is equably brushed The surface of forming composition obtains diatomite forming composition semi-finished product；
    （4）By step（3）In diatomite forming composition semi-finished product spontaneously dry to get the diatom with moisture absorbing Earth forming composition.
  8. 8. a kind of preparation method of diatomite forming composition with moisture absorbing according to claim 7, feature It is, the step（1）In mixing speed be 500r/min~700r/min.
  9. 9. a kind of preparation method of diatomite forming composition with moisture absorbing according to claim 6, feature It is, the step（3）The middle brushing thickness equably brushed mixture on forming composition surface be 0.15mm~ 0.17mm。
CN201711368121.1A 2017-12-18 2017-12-18 Diatomite molding composition with moisture absorption function and preparation method thereof Active CN108046724B (en)