CN108043168A - 一种c60负离子复合超强空气净化剂及其制备方法 - Google Patents
一种c60负离子复合超强空气净化剂及其制备方法 Download PDFInfo
- Publication number
- CN108043168A CN108043168A CN201711191609.1A CN201711191609A CN108043168A CN 108043168 A CN108043168 A CN 108043168A CN 201711191609 A CN201711191609 A CN 201711191609A CN 108043168 A CN108043168 A CN 108043168A
- Authority
- CN
- China
- Prior art keywords
- parts
- component
- following weight
- weight ratio
- air purifying
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种C60负离子复合超强空气净化剂，包括以下重量比的组分：基质材料610‑790份、功能材料添加剂248‑275份，所述基质材料包括以下重量比的组分：海泡石粉250‑350份、披缕缟石粉180‑220份、硅藻土180‑220份；功能材料添加剂包括以下重量比的组分：电气石粉125‑145份、磁石粉50‑58份、富勒烯C6025‑29份、石墨烯25‑29份、氧化锌13‑14份。采用上述技术方案，根据富勒烯C60的超导特性当电气石电子流入时，富勒烯C60会释放大量负氧离子，在与电气石纳米粉中的分子正极丶负极反应时，也产生大量负氧离子；其次沸石丶硅藻土等多孔质超微细孔具有对空气中苯丶二甲苯、Tv0C等有害气体产生超强吸附功能，並释放负氧离子可以全方位净化居室及乘用车内的空气，更多地在人体保健医养方面发挥辅助作用。
Description
技术领域
本发明涉及绿色环保和空气净化技术领域，具体指一种C60负离子复合超强空气净化剂及其制备方法。
背景技术
目前，随着环境污染的日益加剧，雾霾天气的发生频率也越来越高。雾霾天气是一种大气污染状态，雾霾是对大气中各种悬浮颗粒物含量超标的笼统表述，尤其是PM2.5被认为是造成雾霾天气的“元凶”。
PM2.5是指环境空气中空气动力学当量直径小于等于2.5μm的颗粒物，也称细颗粒物，对人体危害极大。医学临床表明，MP2.5会通过呼吸进入肺部最深处，造成肺部PM2.5沉积，由于细颗粒物表面吸附着大量的有毒有害物质，并可通过呼吸沉积在肺泡，最终造成呼吸系统结构和功能的损害，引发包括哮喘、急慢性支气管炎等疾病。因此，在雾霾天气，人们采取减少户外活动或通过一些防护措施来减少PM2.5对自身的影响，但是研究表明，在室外PM2.5污染的情况下，封闭情况下的室内PM2.5约为室外的80％左右，这样就对室内空间造成很大的污染。
目前市场流通的空气净化剂(器)，多为矿晶复合而成，具有绿色环保低成本与可持续使用的特点，对居室和乘用车内一些残留有毒有害气体，通过物理吸附和化学反应达到净化空气的目的。可是由于这些产品组成的缘故，净化空气的速率及释放负氧离子浓度还不适应于保健医养业方面的需求。
发明内容
本发明的目的在于：提出一种C60负离子复合超强空气净化剂及其制备方法，釆用天然绿色低碳材料和高尖端纳米富勒烯C60+石墨烯双改性材料和纳米天然能量粉经特殊复合工艺制成，具有超强净化空气，並使空气中持久维持 2000-20000个负氧离子/Cm3，发射远红外线和磁力线。
为了解决上述技术问题，本发明的技术方案为：
一种C60负离子复合超强空气净化剂，包括以下重量比的组分：基质材料 610-790份、功能材料添加剂248-275份，所述基质材料包括以下重量比的组分：海泡石粉250-350份、披缕缟石粉180-220份、硅藻土180-220份；所述功能材料添加剂包括以下重量比的组分：电气石粉125-145份、磁石粉50-58份、富勒烯C6025-29份、石墨烯25-29份、氧化锌13-14份。
进一步的，还包括20-40份的粘结材料。
本发明还提供了一种C60负离子复合超强空气净化剂，包括以下重量比的组分：基质材料642-718份、功能材料添加剂258-322份，所述基质材料包括以下重量比的组分：海泡石粉194-214份、披缕缟石粉194-214份、硅藻土194-214 份、纳米二氧化钛粉30-38份、薄荷精油30-38份；所述功能材料添加剂包括以下重量比的组分：电气石粉106-126份、磁石粉80-94份、富勒烯C6024-34份、石墨烯29-34份、氧化锌29-34份。
进一步的，还包括20-40份的粘结材料。
本发明还提供了一种C60负离子复合超强空气净化剂，包括以下重量比的组分：基质材料610-690份、功能材料添加剂299-330份，所述基质材料包括以下重量比的组分：海泡石粉280-305份、披缕缟石粉120-140份、尖晶石60-70份、硅藻土150-175份；所述功能材料添加剂包括以下重量比的组分：电气石粉 120-144份、磷酸改性二氧化钛30-36份、富勒烯C6030-36份、氧化石墨烯30-36 份、石墨烯改性活性炭75-90份、氧化锌14-19份。
进一步的，还包括15-25份的粘结材料。
本发明还提供了一种C60负离子复合超强空气净化剂的制备方法，步骤包括；
S1、将上述成分按重量比进行混合粘结；
S2、制成直径为3毫米的颗粒。
本发明具有以下的特点和有益效果：
采用上述技术方案，根据富勒烯C60的超导特性当电气石电子流入时，富勒烯C60会释放大量负氧离子，同时石墨烯超导性，在与电气石纳米粉中的分子正极丶负极反应时，也产生大量负氧离子；其次沸石丶硅藻土等多孔质超微细孔比木炭多5000至6000倍，具有对空气中苯丶二甲苯、Tv0C等有害气体产生超强吸附功能，並释放负氧离子可以全方位净化居室及乘用车内的空气，更多地在人体保健医养方面发挥辅助作用。
具体实施方式
下面对本发明的具体实施方式作进一步说明。在此需要说明的是，对于这些实施方式的说明用于帮助理解本发明，但并不构成对本发明的限定。此外，下面所描述的本发明各个实施方式中所涉及的技术特征只要彼此之间未构成冲突就可以相互组合。
实施例1
本发明提供了一种C60负离子复合超强空气净化剂，包括以下重量比的组分：基质材料610份、功能材料添加剂248份，所述基质材料包括以下重量比的组分：海泡石粉250份、披缕缟石粉180份、硅藻土180份；所述功能材料添加剂包括以下重量比的组分：电气石粉125份、磁石粉50份、富勒烯C6025 份、石墨烯25份、氧化锌13份。
进一步的，还包括20份的粘结材料。
上述技术方案制备而成的C60负离子复合超强空气净化剂，主要针对保健养生场所。
本实施例中，富勒烯C60又称足球烯，是一种超穏定结构的类似足球形的空心圆球状全碳分子，由12个正五边形碳球和20个正六边形碳环组成。其中五边形为碳一碳单键结构，六边形为苯环式结构，不溶于水。C60富勒烯的非线性效应起源于兀电子又C60分子具有非常丰富的氧化还原性质，具有很高的电负性和的较高的电离势。昵称＂纳米王子＂和自由基海绵。因其特殊的笼状分子结构和超强物理化学特质和超导性，本发明采用其亲电子和在外加微电场可产生正极丶负极的优点。
硅藻土是一种硅质沉积岩石，由古代硅藻遗骸所组成。化学硅成分是Si02，占原矿80-94％，並含少量Al203丶Fe203、CaO、Mg0、K20、Na20、P205和有机质。硅藻土的矿物组成主要是蛋白石，其次是水云母丶高岭石和石英丶长石丶黑云母等。硅藻土的密度1.9-2.3g/Cm3、堆密度0.34-0.65g/Cm3、比表面积 40-65m2/g，在电鏡下可以看到特殊多孔构造。
披缕缟石粉是一种具链层状结构的含水富镁硅酸盐。凹凸棒石为主要组分，又常含蒙脱石，海泡石丶蛋白石。披缕缟石粉具有阳离子可交換性，吸水性吸附脱色性:比表面积9.6-36m2/g，pH7.5-9.5。吸湿率在23-27％，有良好粘结能力和质轻韧大，也是放射性物质和有毒气体极好的清除剂。
海泡石是一种誉为“软黄金”耐高温无毒无味无腐且具有较高热穏定性吸附性材料。耐高温性能达1500-1700度，吸收大于自身重量150％的水。有抗辐射的特殊性能。
微纳米级电气石粉/磁石粉(Fe304)：电气石具有圧电性和热电性与磁石的磁性相融后产生负磁场、远紅外线、负氧离子三大生态能量。对人体健康养生发挥重要作用
实施例2
本发明提供了一种C60负离子复合超强空气净化剂，，包括以下重量比的组分：基质材料790份、功能材料添加剂275份，所述基质材料包括以下重量比的组分：海泡石粉350份、披缕缟石粉220份、硅藻土220份；所述功能材料添加剂包括以下重量比的组分：电气石粉145份、磁石粉58份、富勒烯C6029 份、石墨烯29份、氧化锌14份。
进一步的，还包括40份的粘结材料。
上述技术方案制备而成的C60负离子复合超强空气净化剂，主要针对保健养生场所。
实施例3
本发明提供了一种C60负离子复合超强空气净化剂，，包括以下重量比的组分：基质材料700份、功能材料添加剂270份，所述基质材料包括以下重量比的组分：海泡石粉300份、披缕缟石粉200份、硅藻土200份；所述功能材料添加剂包括以下重量比的组分：电气石粉135份、磁石粉54份、富勒烯C6027 份、石墨烯27份、氧化锌13.5份。
进一步的，还包括20-40份的粘结材料。
上述技术方案制备而成的C60负离子复合超强空气净化剂，主要针对保健养生场所。
实施例4
本发明还提供了一种C60负离子复合超强空气净化剂，包括以下重量比的组分：基质材料642份、功能材料添加剂258份，所述基质材料包括以下重量比的组分：海泡石粉194份、披缕缟石粉194份、硅藻土194份、纳米二氧化钛粉30份、薄荷精油30份；所述功能材料添加剂包括以下重量比的组分：电气石粉106份、磁石粉80份、富勒烯C6024份、石墨烯24份、氧化锌24份。
进一步的，还包括20份的粘结材料。
上述技术方案制备而成的C60负离子复合超强空气净化剂，主要针对乘车内空气的净化。
实施例5
本发明还提供了一种C60负离子复合超强空气净化剂，包括以下重量比的组分：基质材料718份、功能材料添加剂322份，所述基质材料包括以下重量比的组分：海泡石粉214份、披缕缟石粉214份、硅藻土214份、纳米二氧化钛粉38份、薄荷精油38份；所述功能材料添加剂包括以下重量比的组分：电气石粉126份、磁石粉94份、富勒烯C6034份、石墨烯34份、氧化锌34份。
进一步的，还包括40份的粘结材料。
上述技术方案制备而成的C60负离子复合超强空气净化剂，主要针对乘车内空气的净化。
实施例6
本发明还提供了一种C60负离子复合超强空气净化剂，包括以下重量比的组分：基质材料280份、功能材料添加剂290份，所述基质材料包括以下重量比的组分：海泡石粉204份、披缕缟石粉204份、硅藻土204份、纳米二氧化钛粉34份、薄荷精油34份；所述功能材料添加剂包括以下重量比的组分：电气石粉116份、磁石粉87份、富勒烯C6029份、石墨烯29份、氧化锌29份。
进一步的，还包括30份的粘结材料。
上述技术方案制备而成的C60负离子复合超强空气净化剂，主要针对乘车内空气的净化。
实施例7
本发明还提供了一种C60负离子复合超强空气净化剂，包括以下重量比的组分：基质材料610份、功能材料添加剂299份，所述基质材料包括以下重量比的组分：海泡石粉280份、披缕缟石粉120份、尖晶石60份、硅藻土150份；所述功能材料添加剂包括以下重量比的组分：电气石粉120份、磷酸改性二氧化钛30份、富勒烯C6030份、氧化石墨烯30份、石墨烯改性活性炭75份、氧化锌14份。
进一步的，还包括15份的粘结材料。
上述技术方案制备而成的C60负离子复合超强空气净化剂，主要针对老年养生和幼儿园休闲睡睌或重病号观察期场所。
本发明釆用氧化石墨烯具有超强比表面积2607m2/g，氧化石墨烯又称功能化石墨烯，是石墨烯的含氧化合物，其结构中含有羟基丶羧基等极性基团故带有很强的负电性。硅藻土纳米粉粒径20um复合成氧化石墨烯/硅藻土作为本发明产品制备的重要材料；优点是成本低廉，释放负离子浓度高。
石墨烯攺性活性炭，本发明制备的活性炭比表面积1800-2000m2/g。
上述技术方案制备而成的C60负离子复合超强空气净化剂，主要针对老年养生和幼儿园休闲睡睌或重病号观察期场所。
实施例8
本发明还提供了一种C60负离子复合超强空气净化剂，包括以下重量比的组分：基质材料690份、功能材料添加剂361份，所述基质材料包括以下重量比的组分：海泡石粉305份、披缕缟石粉140份、尖晶石70份、硅藻土175份；所述功能材料添加剂包括以下重量比的组分：电气石粉144份、磷酸改性二氧化钛36份、富勒烯C6036份、氧化石墨烯36份、石墨烯改性活性炭90份、氧化锌19份。
进一步的，还包括25份的粘结材料。
上述技术方案制备而成的C60负离子复合超强空气净化剂，主要针对老年养生和幼儿园休闲睡睌或重病号观察期场所。
实施例9
本发明还提供了一种C60负离子复合超强空气净化剂，包括以下重量比的组分：基质材料650份、功能材料添加剂330份，所述基质材料包括以下重量比的组分：海泡石粉292.5份、披缕缟石粉130份、尖晶石65份、硅藻土162.5 份；所述功能材料添加剂包括以下重量比的组分：电气石粉132份、磷酸改性二氧化钛33份、富勒烯C6033份、氧化石墨烯33份、石墨烯改性活性炭82.5 份、氧化锌16.5份。
进一步的，还包括20份的粘结材料。
上述技术方案制备而成的C60负离子复合超强空气净化剂，主要针对老年养生和幼儿园休闲睡睌或重病号观察期场所。
实施例10
本发明还提供了一种C60负离子复合超强空气净化剂的制备方法，步骤包括；
S1、将上述成分按重量比进行混合粘结；
S2、制成直径为3毫米的颗粒。
上述步骤S1中具体的还包括：
关键材料1的制备
硅藻土的制备，硅藻土矿经提纯筛选得到本发明产品需要的质量标准，经研碎机研磨颗粒直径至30微米左右；
然后将氧化石墨烯置入去离子水中超声分散4小时多40分钟，达到浓度为 0.9毫克每毫升至1.0毫克每毫升的氧化石墨烯水溶液；
然后把把标准化处理过的硅藻土干粉放入容器内，
随后把去离子水氧化石墨烯溶液倒入容器内，经特殊搅拌器混合均匀，成为漿糊状为止。
再把其容器移入60度干燥箱内蒸发水份后荻得氧化石墨烯包裹的硅藻土粉；
关键材料2的制备，只要指的是石墨烯改性竹炭活性炭材质或者椰壳活性炭。
先把竹炭转变为活性炭材料，纯度达到百分之九十九点九。
备置去离子水，把上述活性炭倒入去离子中，並用搅拌器搅拌均匀成糊状止；
按份额千分之一比例(1：1000)将备好的石墨烯分散洒入盛有去离子水和活性炭粉呈糊状物质中
把盛有石墨烯和活性炭的容器移入烘房，並用搅拌器搅拌均匀，直至出现颗粒止；
检查颗粒质量，符合巜石墨烯包裹活性炭质量标准》。
具体的，步骤S2根据实际需求，可以采用常温模具压制(颗粒径3毫米)或者釆用高温压制煅烧结方法。
以上对本发明的实施方式作了详细说明，但本发明不限于所描述的实施方式。对于本领域的技术人员而言，在不脱离本发明原理和精神的情况下，对这些实施方式包括部件进行多种变化、修改、替换和变型，仍落入本发明的保护范围内。
Claims (7)
1.一种C60负离子复合超强空气净化剂，其特征在于，包括以下重量比的组分：基质材料610-790份、功能材料添加剂248-275份，所述基质材料包括以下重量比的组分：海泡石粉250-350份、披缕缟石粉180-220份、硅藻土180-220份；所述功能材料添加剂包括以下重量比的组分：电气石粉125-145份、磁石粉50-58份、富勒烯C6025-29份、石墨烯25-29份、氧化锌13-14份。
2.根据权利要求1所述的一种C60负离子复合超强空气净化剂，其特征在于，还包括20-40份的粘结材料。
3.一种C60负离子复合超强空气净化剂，其特征在于，包括以下重量比的组分：基质材料642-718份、功能材料添加剂258-322份，所述基质材料包括以下重量比的组分：海泡石粉194-214份、披缕缟石粉194-214份、硅藻土194-214份、纳米二氧化钛粉30-38份、薄荷精油30-38份；所述功能材料添加剂包括以下重量比的组分：电气石粉106-126份、磁石粉80-94份、富勒烯C6024-34份、石墨烯24-34份、氧化锌24-34份。
4.根据权利要求3所述的一种C60负离子复合超强空气净化剂，其特征在于，还包括20-40份的粘结材料。
5.一种C60负离子复合超强空气净化剂，其特征在于，包括以下重量比的组分：基质材料610-690份、功能材料添加剂299-361份，所述基质材料包括以下重量比的组分：海泡石粉280-305份、披缕缟石粉120-140份、尖晶石60-70份、硅藻土150-175份；所述功能材料添加剂包括以下重量比的组分：电气石粉120-144份、磷酸改性二氧化钛30-36份、富勒烯C6030-36份、氧化石墨烯30-36份、石墨烯改性活性炭75-90份、氧化锌14-19份。
6.根据权利要求5所述的一种C60负离子复合超强空气净化剂，其特征在于，还包括15-25份的粘结材料。
7.一种根据权利要求1至6所述的C60负离子复合超强空气净化剂的制备方法，其特征在于，步骤包括；
S1、将上述成分按重量比进行混合粘结；
S2、制成直径为3毫米的颗粒。