CN108976872A - 一种释放负离子远红外除醛抗菌的贝壳粉水性涂料的制备方法 - Google Patents
一种释放负离子远红外除醛抗菌的贝壳粉水性涂料的制备方法 Download PDFInfo
- Publication number
- CN108976872A CN108976872A CN201810617415.1A CN201810617415A CN108976872A CN 108976872 A CN108976872 A CN 108976872A CN 201810617415 A CN201810617415 A CN 201810617415A CN 108976872 A CN108976872 A CN 108976872A
- Authority
- CN
- China
- Prior art keywords
- powder
- infrared
- conch meal
- negative ion
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明具有良好的使用功能，功能成分主要由矿物材料和植物细粉组成。取自天然的矿物材料，研磨到1250目以上细度，结合可释放负离子植物粉，可以释放负离子，具有发射远红外线，除甲醛，杀菌、消毒、祛味、净化空气、镇静、提神醒脑、增强免疫力的功能。具有广泛的应用价值。本发明的配方如下：电气石粉(10.0‑60.0)，贝壳粉(5.0‑20.0)，锐钛型纳米二氧化钛(0.0‑5.0)，伊利石粉(5.0‑15.0)，钙基膨润土(5.0‑15.0)，石英粉(5.0‑20.0)，水洗高岭土(5.0‑20.0)，稀土氧化物(0.1‑2.0)，改性高分子成膜材料(10.0‑30.0)，松枝粉(0.0‑2.0)，柏叶粉(0.0‑2.0)，绿茶粉(0.0‑4.0)，薄荷叶粉(0.0‑2.0)。
Description
技术领域
一种释放负离子远红外除醛抗菌的贝壳粉水性涂料的制备方法，属于生活日用品、化学、化工领域。
发明背景
目前，市场上销售的环保内墙漆，以水性涂料为主，其主要以水，乳液，颜料，填料，添加剂五种成分构成。一般的水性涂料有机溶剂占涂料的10％-15％之间，比非水性涂料对降低污染节省资源效果更显著。
为了实现水性涂料更加安全环保的性能，并且涂料在施工后，对室内其他有可能释放甲醛等污染源如板式家具、厨柜、布艺沙发等也能起到消除甲醛的作用，释放负离子除醛抗菌的内墙涂料是解决这些问题的途径。
释放负离子的电气石、催化剂，除甲醛的贝壳粉、锐钛型纳米二氧化钛等加入涂料中，形成能除甲醛、抗菌、释放负离子远红外的功能涂料，涂料有毒有害物质检测为0，喷涂在墙面上能释放一些负离子，静态负离子浓度在1500ions/cm3以上，满足人体健康生活的需要。抗菌性达到99％以上，甲醛净化性能达80％以上。
表1世界卫生组织提出的空气负离子浓度与人体健康的关系
本发明具有良好的使用功能，功能成分主要由矿物材料和植物细粉组成。取自天然的矿物材料，研磨到1250目以上细度，结合可释放负离子植物粉，可以释放负离子，具有发射远红外线，除甲醛，杀菌、消毒、祛味、净化空气、镇静、提神醒脑、增强免疫力的功能。具有广泛的应用价值。
矿物材料主要取电气石、贝壳粉、锐钛型纳米二氧化钛等，主要功能有：释放负离子、发射远红外线、净化空气、镇静、镇痛、催眠、提神醒脑、降血压、增强免疫力等。
植物细粉是特有芳香物质的植物，选取针叶植物的叶、颈，草本植物的花、叶、根、树皮、果实、种子、树脂等，干燥研磨。具有净化空气、杀菌、提供细胞营养。平衡身心灵、增强免疫力等功效。
负离子在公园、郊区田野、海滨、湖泊、瀑布附近和森林中含量较多。因此，当人们进入上述场地的时候，头脑清新，呼吸舒畅和爽快。进入嘈杂拥挤的人群，或进入空调房内，则使人感觉闷热、呼吸不畅等。
发明内容
本发明的要点在于选择合适的组分，将各种成分合理混配。
本发明的配方如下：电气石粉(10.0-60.0)，贝壳粉(5.0-20.0)，锐钛型纳米二氧化钛(0.0-5.0)，伊利石粉(5.0-15.0)，钙基膨润土(5.0-15.0)，石英粉(5.0-20.0)，水洗高岭土(5.0-20.0)，稀土氧化物(0.1-2.0)，改性高分子成膜材料(10.0-30.0)，松枝粉(0.0-2.0)，柏叶粉(0.0-2.0)，绿茶粉(0.0-4.0)，薄荷叶粉(0.0-2.0)。
1.电气石(白色托玛琳)粉：Tourmaline(托玛琳)也称电气石-碧玺，化学组成：
(Na，Ca)(Mg，Fe)3B3Al6Si6(O，OH，F)，呈三方/六方晶系，结晶习性：柱状、三方柱、六方柱、三方单锥，集合体呈放射状、束状、棒状。玻璃光泽，透明至不透明，硬度7-7.5，比重3.0-3.2折射率1.62-1.64，双折射：0.018～0.040，通常为0.020。
电气石是极为复杂的硼铝硅酸盐。它具有生物电作用，碧玺表面流动着微电流，可以调节和补充人体的生物电从而达到抗辐射的作用，这样就可以起到保健的作用了。
电气石具有释放负离子的作用，而负离子具有杀灭病菌及净化空气的作用，而人体自身产生的负离子远远达不到人体的需求。
电气石有远红外线功能，远红外线可以改善人体的血液循环，有利于促进人体的新陈代谢，保持机体的正常能量活动，能够提高肌体的免疫力，增强组织的再生能力，因此非常有助于人体的保健。
2.贝壳粉，是用贝壳打成的粉，含有甲壳素，而甲壳素能够分解中和甲醛。而硅藻泥是古代藻类化石通过一系列物理加工而成的墙面涂料，只能吸附甲醛不能分解甲醛，因此贝壳粉比硅藻泥除醛效果明显很多。
3.锐钛型纳米二氧化钛，颗粒小至纳米级，可大大提高光催化率。在紫外光的照射下，锐钛型纳米二氧化钛其价带电子被激发到导带，形成了电子和空穴与吸附于其表面的)O2、H2O以及无机物，降解速度快，无二次污染，可广泛应用于空气净化、污水处理和工业催化等。
4.伊利石粉：伊利石是常见的一种黏土矿物，常由白云母，钾长石风化而成，并产于泥质岩中，或由其他矿物蚀变形成。
5.钙基膨润土：该产品为白色或灰白色粉末，不溶于水、油和有机溶剂。由于具有较大的有效孔容，因而有很强的吸附能力和吸附容量。无毒，热稳定性好、过滤速度快，带油率低。其作为催化剂、粘结剂、脱色剂、吸附剂、增稠剂、触变剂、而广泛应用于化工、冶金球团、铸造、钻井、石棉保温材料中作为粘结剂；放射性废物吸收剂等领域。
6.石英粉：石英砂是一种坚硬、耐磨、化学性能稳定的硅酸盐矿物，其主要矿物成分是SiO2，石英砂的颜色为乳白色、或无色半透明状，硬度7，性脆无解理，贝壳状断口，油脂光泽，密度为2.65g/cm3，堆积密度(20-200目为1.5)，其化学、热学和机械性能具有明显的异向性，不溶于酸，微溶于KOH溶液，熔点1650℃。从矿山开采出的石英石经加工后，一般细度在120目以下(小于120目)的产品称石英砂。超过120目的产品称为石英粉，可提高涂料的耐候性。
7.水洗高岭土：具有白度高，颗粒细小，比表面积高的特点。在水性基或油性基体系中均有良好的分散性和悬浮性，并能提高涂料的光洁度，PH值7。
8.稀土氧化物：稀土氧化物的带隙能较大，可在其禁带中引入杂质能级，减小禁带宽度，使价带中的电子接受波长较大的光激发后，先跃迁到杂质能级，通过再一次吸收能量，由杂质能级跃迁至导带，这样就降低了受激所需的能量，从而实现光催化剂的光谱响应范围向可见光区移动这一目标，使催化物活性得到提高。
9.改性高分子成膜材料：是成膜的基料，决定了漆膜的主要功能。
制做方法：
(1)矿物材料经破碎-研磨-球磨等，达到1250目细度备用。
(2)植物干燥粉碎达到200目以上备用。
(3)生产工艺过程，首先投入水、分散剂和其他助剂投入分散罐中，搅拌均匀后在搅拌下再投入矿物、植物填料，加入多种填料时，按先投入密度较小的、吸水量较大、粒径较细的填料的顺序进行，投料速度要和浆液混合情况一致，全部粉料投后，应用工艺水彻底清洗罐内壁，搅拌至混匀。
(4)本发明具有以下优点：1)适用于室内墙面涂刷涂料时使用；2)能够长期持续释放负离子、远红外，较好地净化空气、祛除异味、杀灭病菌，并且起到平静心情、提神醒脑、增强人体免疫力的效果；3)由纯天然原料制成，对人体安全无毒，对环境无污染；4)具有良好的使用性能，且使用方便，可以进行广泛的应用推广。
Claims (7)
1.一种释放负离子远红外除醛抗菌的贝壳粉水性涂料的制备方法，其特征在于，属于生活日用品、化学、化工领域。
2.一种释放负离子远红外除醛抗菌的贝壳粉水性涂料的制备方法，其特征在于，功能成分主要由矿物材料和植物细粉组成。取自天然的矿物材料，研磨到1250目以上细度，结合可释放负离子植物粉，可以释放负离子，具有发射远红外线，除甲醛，杀菌、消毒、祛味、净化空气、镇静、提神醒脑、增强免疫力的功能。
3.一种释放负离子远红外除醛抗菌的贝壳粉水性涂料的制备方法，其特征在于，本发明使用的矿物材料主要取电气石、贝壳粉、锐钛型纳米二氧化钛等，主要功能有：释放负离子、发射远红外线、净化空气、镇静、镇痛、催眠、提神醒脑、降血压、增强免疫力等。
4.一种释放负离子远红外除醛抗菌的贝壳粉水性涂料的制备方法，其特征在于，植物细粉是特有芳香物质的植物，选取针叶植物的叶、颈，草本植物的花、叶、根、树皮、果实、种子、树脂等，干燥研磨。具有净化空气、杀菌、提供细胞营养。平衡身心灵、增强免疫力等功效。
5.一种释放负离子远红外除醛抗菌的贝壳粉水性涂料的制备方法，其特征在于，矿物材料经破碎-研磨-球磨等，达到1250目细度，植物干燥粉碎达到200目以上。
6.一种释放负离子远红外除醛抗菌的贝壳粉水性涂料的制备方法，其特征在于，生产工艺过程，首先投入水、分散剂和其他助剂投入分散罐中，搅拌均匀后在搅拌下再投入矿物、植物填料，加入多种填料时，按先投入密度较小的、吸水量较大、粒径较细的填料的顺序进行，投料速度要和浆液混合情况一致，全部粉料投后，应用工艺水彻底清洗罐内壁，搅拌至混匀。
7.一种释放负离子远红外除醛抗菌的贝壳粉水性涂料的制备方法，其特征在于，电气石粉(10.0-60.0)，贝壳粉(5.0-20.0)，锐钛型纳米二氧化钛(0.0-5.0)，伊利石粉(5.0-15.0)，钙基膨润土(5.0-15.0)，石英粉(5.0-20.0)，水洗高岭土(5.0-20.0)，稀土氧化物(0.1-2.0)，改性高分子成膜材料(10.0-30.0)，松枝粉(0.0-2.0)，柏叶粉(0.0-2.0)，绿茶粉(0.0-4.0)，薄荷叶粉(0.0-2.0)。得到一种释放负离子、远红外去味除甲醛的贝壳粉水性涂料，可有效去甲醛等有害气体、去除异味、释放负离子、远红外的环保健康涂料。