CN108034222A - A kind of polyurethane clad on forklift hub surface - Google Patents
A kind of polyurethane clad on forklift hub surface Download PDFInfo
- Publication number
- CN108034222A CN108034222A CN201711374923.3A CN201711374923A CN108034222A CN 108034222 A CN108034222 A CN 108034222A CN 201711374923 A CN201711374923 A CN 201711374923A CN 108034222 A CN108034222 A CN 108034222A
- Authority
- CN
- China
- Prior art keywords
- parts
- rubber
- polyurethane
- hub surface
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of polyurethane clad on forklift hub surface, its raw material includes by weight:100 140 parts of polyurethane rubber, 30 40 parts of butadiene-styrene rubber, 10 20 parts of natural rubber, 10 18 parts of nitrile rubber, 5 11 parts of vulcanizing agent, 25 45 parts of powdered whiting, 10 20 parts of graphene, 10 18 parts of nano-bentonite, 48 parts of vulcanization accelerator, 24 parts of pine tar, 24 parts of antiscorching agent, 24 parts of antioxidant, 24 parts of plasticizer, 24 parts of softening agent.The present invention has an excellent wear-resisting property, and suitable for persistently being used under high abrasive conditions, and the adhesive strength between core wheel is high, is not likely to produce sliding friction, while tensile strength height, fire resisting, corrosion-resistant.
Description
Technical field
The present invention relates to polyurethanes technology field, more particularly to a kind of polyurethane clad on forklift hub surface.
Background technology
Fork truck needs crotch stretching to tray bottom in use, is moved integrally under the drive of fork truck wheel,
This bearing capacity to fork truck wheel requires high, and fork truck wheel includes wheel hub and is coated on the polyurethane clad of hub surface, mesh
The preceding wheel hub weight due to 5-10t fork trucks reach more than 40kg, after loading cargo, is manually transported to mounting plate and subsequently
90 ° of turn work of process, its labor intensity is big, and since workpiece quality is big, to the polyurethane clad wear resistance on top layer
It is required that high, there are serious security risk.
The content of the invention
Based on technical problem existing for background technology, the present invention proposes a kind of polyurethane cladding on forklift hub surface
Layer, has excellent wear-resisting property, and suitable for persistently being used under high abrasive conditions, and the adhesive strength between core wheel
Height, is not likely to produce sliding friction, while tensile strength is high, fire resisting, corrosion-resistant.
A kind of polyurethane clad on forklift hub surface proposed by the present invention, its raw material include by weight:Polyurethane
100-140 parts of rubber, 30-40 parts of butadiene-styrene rubber, 10-20 parts of natural rubber, 10-18 parts of nitrile rubber, 5-11 parts of vulcanizing agent, weight
25-45 parts of matter calcium carbonate, 10-20 parts of graphene, 10-18 parts of nano-bentonite, 4-8 parts of vulcanization accelerator, 2-4 parts of pine tar,
2-4 parts of antiscorching agent, 2-4 parts of antioxidant, 2-4 parts of plasticizer, 2-4 parts of softening agent.
Preferably, vulcanizing agent includes by weight:4-8 parts of cumyl peroxide, 1-3 parts of tert-butyl hydroperoxide.
Preferably, vulcanization accelerator includes by weight:2-4 parts of 2- mercapto imidazolines, tetramethylthiuram disulfide
2-4 parts.
With common rubber phase ratio, the present invention has excellent wear-resisting property, and suitable for continuing under high abrasive conditions
Use, and tensile strength is high, it is fire resisting, corrosion-resistant.
The present invention is compounded using polyurethane rubber and butadiene-styrene rubber, natural rubber, nitrile rubber, and synergistic effect, can improve
Adhesive strength between the present invention and core wheel, bond strength is high, is not likely to produce sliding friction, service life is grown, and peroxidating two
Isopropylbenzene, tert-butyl hydroperoxide can promote to form cross-linked network between polyurethane rubber, butadiene-styrene rubber, natural rubber, nitrile rubber
Shape structure, bond strength is high, and wear-resisting property is excellent, and good toughness, and powdered whiting, graphene, nano-bentonite can be abundant
It is dispersed in system, on the basis of polyurethane rubber additive amount is reduced, reduce cost, hardness is high, and wearability is outstanding, makes
The present invention is uniformly and intimately fitted in core surfaces, and composite performance is good, and gained fork truck wheel is corrosion-resistant, wear-resistant, and cost is low
It is honest and clean.
Embodiment
In the following, technical scheme is described in detail by specific embodiment.
Embodiment 1
A kind of polyurethane clad on forklift hub surface, its raw material include:Polyurethane rubber 100kg, butadiene-styrene rubber
40kg, natural rubber 10kg, nitrile rubber 18kg, vulcanizing agent 5kg, powdered whiting 45kg, graphene 10kg, nano-bentonite
18kg, vulcanization accelerator 4kg, pine tar 4kg, antiscorching agent 2kg, antioxidant 4kg, plasticizer 2kg, softening agent 4kg.
Vulcanizing agent includes:Cumyl peroxide 4kg, tert-butyl hydroperoxide 3kg.Vulcanization accelerator includes:2- mercaptan
Base imidazoline 2kg, tetramethylthiuram disulfide 4kg.
Embodiment 2
A kind of polyurethane clad on forklift hub surface, its raw material include:Polyurethane rubber 140kg, butadiene-styrene rubber 30-
Kg, natural rubber 20kg, nitrile rubber 10kg, vulcanizing agent 11kg, powdered whiting 25kg, graphene 20kg, nano-bentonite
10kg, vulcanization accelerator 8kg, pine tar 2kg, antiscorching agent 4kg, antioxidant 2kg, plasticizer 4kg, softening agent 2kg.
Vulcanizing agent includes:Cumyl peroxide 8kg, tert-butyl hydroperoxide 1kg.Vulcanization accelerator includes:2- mercaptan
Base imidazoline 4kg, tetramethylthiuram disulfide 2kg.
Embodiment 3
A kind of polyurethane clad on forklift hub surface, its raw material include:Polyurethane rubber 110kg, butadiene-styrene rubber
37kg, natural rubber 12kg, nitrile rubber 16kg, vulcanizing agent 6kg, powdered whiting 40kg, graphene 12kg, nano-bentonite
16kg, vulcanization accelerator 5kg, pine tar 3.5kg, antiscorching agent 2.5kg, antioxidant 3.5kg, plasticizer 2.5kg, softening agent
3.5kg。
Vulcanizing agent includes:Cumyl peroxide 5kg, tert-butyl hydroperoxide 2.5kg.Vulcanization accelerator includes:2- sulphur
Alcohol radical imidazoline 2.5kg, tetramethylthiuram disulfide 3.5kg.
Embodiment 4
A kind of polyurethane clad on forklift hub surface, its raw material include:Polyurethane rubber 130kg, butadiene-styrene rubber
33kg, natural rubber 18kg, nitrile rubber 12kg, vulcanizing agent 8kg, powdered whiting 30kg, graphene 18kg, nano-bentonite
12kg, vulcanization accelerator 7kg, pine tar 2.5kg, antiscorching agent 3.5kg, antioxidant 2.5kg, plasticizer 3.5kg, softening agent
2.5kg。
Vulcanizing agent includes:Cumyl peroxide 7kg, tert-butyl hydroperoxide 1.5kg.Vulcanization accelerator includes:2- sulphur
Alcohol radical imidazoline 3.5kg, tetramethylthiuram disulfide 2.5kg.
The foregoing is only a preferred embodiment of the present invention, but protection scope of the present invention be not limited thereto,
Any one skilled in the art the invention discloses technical scope in, technique according to the invention scheme and its
Inventive concept is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.
Claims (3)
1. a kind of polyurethane clad on forklift hub surface, it is characterised in that its raw material includes by weight:Polyurethane rubber
100-140 parts, 30-40 parts of butadiene-styrene rubber, 10-20 parts of natural rubber, 10-18 parts of nitrile rubber, 5-11 parts of vulcanizing agent, heavy carbon
Sour calcium 25-45 parts, 10-20 parts of graphene, 10-18 parts of nano-bentonite, 4-8 parts of vulcanization accelerator, 2-4 parts of pine tar is anti-scorch
2-4 parts of agent, 2-4 parts of antioxidant, 2-4 parts of plasticizer, 2-4 parts of softening agent.
2. the polyurethane clad on forklift hub surface according to claim 1, it is characterised in that vulcanizing agent wraps by weight
Include:4-8 parts of cumyl peroxide, 1-3 parts of tert-butyl hydroperoxide.
3. the polyurethane clad on forklift hub surface according to claim 1, it is characterised in that vulcanization accelerator is by weight
Part includes:2-4 parts of 2- mercapto imidazolines, 2-4 parts of tetramethylthiuram disulfide.