CN108033732A - A kind of environmentally friendly regeneration concrete for building and preparation method thereof - Google Patents
A kind of environmentally friendly regeneration concrete for building and preparation method thereof Download PDFInfo
- Publication number
- CN108033732A CN108033732A CN201711101951.8A CN201711101951A CN108033732A CN 108033732 A CN108033732 A CN 108033732A CN 201711101951 A CN201711101951 A CN 201711101951A CN 108033732 A CN108033732 A CN 108033732A
- Authority
- CN
- China
- Prior art keywords
- parts
- concrete
- environmentally friendly
- additive
- strontium carbonate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
It is prepared the invention discloses a kind of environmentally friendly regeneration concrete for building and preparation method thereof, including by the raw material of following parts by weight:85 100 parts of Portland cement, 20 30 parts of iron ore waste residue, 10 25 parts of palygorskite, 15 35 parts of rubble, 10 15 parts of nano-pearl rock, 18 25 parts of regenerated coarse aggregate, 10 20 parts of strontium carbonate, 20 25 parts of high tensile strength fiber, 10 15 parts of discarded object calcining material, 10 20 parts of naphthalene water reducer, 5 10 parts of CTF Concrete synergists, 8 15 parts of additive and appropriate amount of water.The present invention is effectively matched using Portland cement, iron ore waste residue, palygorskite, rubble, nano-pearl rock, regenerated coarse aggregate, strontium carbonate, high tensile strength fiber, discarded object calcining material, naphthalene water reducer, obtain a kind of not only there is higher compression strength and flexural strength, and it can be combined well with having concrete, it is not easily to fall off, overall performance is superior, is very suitable for the reinforced concrete for concrete works damage position;Simple production process, is adapted to large-scale production.
Description
Technical field
The present invention relates to Portland cement manufacture technology field, and in particular to a kind of environmentally friendly regeneration coagulation for building
Soil and preparation method thereof.
Background technology
With rapid development of economy, in many big cities in China, the waste that building industry produces has been changed to public hazards.This
A little wastes not only cause environment serious destruction, but also the space of existence is being fought for the mankind, and seriously affect country can
Sustainable development.Therefore, exploitation reduces, recycles and utilizes the new technology of waste material of buildings extremely urgent.
Waste material of buildings is generally by broken concrete, nano-pearl rock brick and ceramic tile, sand and dust, sawdust, plastics and waste paper,
Old metal etc. forms.Broken concrete is typically the maximum part of waste material of buildings, by the broken concrete of crushing and screening
It can be used to the natural aggregate that substitutes in concrete or be used to do the basis of road.This type salvage material is just called
Recycled aggregates.Recycled aggregates have been applied successfully in the building industry of some European and American developed countries, but mainly
Apply on the basis of non-structural concrete and road, the application in structural concrete is limited, usually there was only the thick bone of concrete
The 20% of material is recycled aggregates.Mainly due to recycled aggregates, the intensity compared with natural aggregate is low for this, it is porous and
There is higher water absorption rate.This requires add water in concrete batching to increase its fluidity so as to cause maturing
Contract with dry rate and creep increase.For this difficulty for overcoming recycled aggregates to recycle, concrete research personnel are by research
Have been developed for utilizing the method manufacture concrete partition brick of mechanical pressing and the patented technology of paving block.Study hair at the same time
Now utilization rate of the recycled aggregates in structural concrete can be improved using atmospheric steam maintenance technology.
The characteristics of concrete has abundant raw material, cheap, simple production process, thus make its dosage increasing.
Concrete also has the features such as compression strength is high, and durability is good, and strength grade scope is wide at the same time;These features make it use model
Enclose quite varied, not only used in various civil engineerings, be exactly shipbuilding industry, mechanical industry, the exploitation of ocean, geothermal engineering etc.
;In recent years, with China's high-rise building constantly going into operation, the height of high-rise building is constantly refreshed, its sole plate by
Power state constantly aggravates, and structure is more and more thicker, and strength grade of concrete requires higher and higher, and total gel material content is also increasingly
More, hydration heat of concrete is also with regard to higher, so being easy for the cracking for causing super thick structural concrete.
The content of the invention
To solve the above problems, the present invention provides a kind of environmentally friendly regeneration concrete for building and preparation method thereof.
To achieve the above object, the technical solution taken of the present invention is:
A kind of environmentally friendly regeneration concrete for building and preparation method thereof, including be prepared by the raw material of following parts by weight:It is general
Logical 85-100 parts of portland cement, 20-30 parts of iron ore waste residue, 10-25 parts of palygorskite, 15-35 parts of rubble, nano-pearl rock 10-
15 parts, 18-25 parts of regenerated coarse aggregate, 10-20 parts of strontium carbonate, 20-25 parts of high tensile strength fiber, discarded object calcining material 10-15
Part, 10-20 parts of naphthalene water reducer, 5-10 parts of CTF Concrete synergists, 8-15 parts of additive and appropriate amount of water.
Further, the additive is prepared by the raw material of following parts by weight:9-15 parts of strontium carbonate, dinonyl naphthalene sulphur
6-10 parts sour, 9-14 parts of crospovidone, 3-5 parts of sodium abietate, 2-4 parts of polyacrylamide, 1-3 parts of polyacrylic acid, glucose
Sour sodium 3-5 parts and 2-6 parts of neopelex.
Further, a kind of environmentally friendly regeneration concrete for building, including be prepared by the raw material of following parts by weight:It is general
Logical 88-90 parts of portland cement, 23-28 parts of iron ore waste residue, 15-20 parts of palygorskite, 20-30 parts of rubble, nano-pearl rock 12-14
Part, 20-24 parts of regenerated coarse aggregate, 12-18 parts of strontium carbonate, 21-24 parts of high tensile strength fiber, discarded object calcining material 11-14 parts,
12-19 parts of naphthalene water reducer, 6-8 parts of CTF Concrete synergists, 9-14 parts of additive and appropriate amount of water.
Further, the regenerated coarse aggregate be concrete in building castoff, waste concrete class wall, barren rock material by
Species is sorted by sorting, crush, the aggregate that manufactured particle diameter is 5-32 mm after magnetic separation removal old metal, carboxylate spray
Particle.
Further, a kind of preparation method of environmentally friendly regeneration concrete for building, includes the following steps:
S1, by 9-15 parts of strontium carbonate, 6-10 parts of dinonylnaphthalene sulfonic acid, 9-14 parts of crospovidone, 3-5 parts of sodium abietate, poly- third
2-6 parts of 2-4 parts of acrylamide, 1-3 parts of polyacrylic acid, 3-5 parts of sodium gluconate and neopelex plus water are mixed,
Additive is made;
S2, by 23-28 parts of iron ore waste residue, 15-20 parts of palygorskite, 20-30 parts of rubble, 12-14 parts of nano-pearl rock, the thick bone of regeneration
10-15 parts of 20-24 parts of material and discarded object calcining material are ground into powder, cross 200-220 mesh sieves, after mixing;
S3, by 85-100 parts of Portland cement, 10-20 parts of strontium carbonate, 20-25 parts of high tensile strength fiber, naphthalene system diminishing
10-20 parts of agent, 5-10 parts of CTF Concrete synergists, 8-15 parts of additive and appropriate amount of water are added in mixer and stir 10-
15min, then adds the mixture obtained by step S2 and stirs 20-25min with the speed of 500-900r/min.
Further, mixer mixing speed is 400-500r/min in the step S3, and mixing time is 12 minutes.
The present invention using Portland cement, iron ore waste residue, palygorskite, rubble, nano-pearl rock, regenerated coarse aggregate,
Strontium carbonate, high tensile strength fiber, discarded object calcining material, naphthalene water reducer, CTF Concrete synergists, additive effectively match,
Additive is using strontium carbonate, dinonylnaphthalene sulfonic acid, crospovidone, sodium abietate, polyacrylamide, polyacrylic acid, glucose
Sour sodium and neopelex proportioning;Obtain it is a kind of not only there is higher compression strength and flexural strength, but also can be with
Combined well with concrete, not easily to fall off, overall performance is superior, is very suitable for for concrete works damage position
Reinforced concrete;Cheap, simple production process, is adapted to large-scale production;Regeneration aggregate is made with waste material of buildings and substitutes day
Right aggregate, it is possible to reduce consumption of the construction industry to natural aggregate, so as to reduce the exploitation to natural sand stone, solves natural aggregate
Increasingly deficient and a large amount of sandstones are produced the problems such as being destroyed caused by ecological environment, protect ecological environment, meet sustainable
The requirement of development.By proportion optimizing and rational additive is added, it is difficult to overcome traditional regenerated aggregate concrete slump
With control, the defects of intensity is low.
Embodiment
In order to which objects and advantages of the present invention are more clearly understood, the present invention is carried out with reference to embodiments further detailed
Explanation.It should be appreciated that the specific embodiments described herein are merely illustrative of the present invention, it is not intended to limit the present invention.
The present invention includes being prepared by the raw material of following parts by weight:85-100 parts of Portland cement, iron ore waste residue
20-30 parts, 10-25 parts of palygorskite, 15-35 parts of rubble, 10-15 parts of nano-pearl rock, 18-25 parts of regenerated coarse aggregate, strontium carbonate
10-20 parts, 20-25 parts of high tensile strength fiber, discarded object calcining material 10-15 parts, 10-20 parts of naphthalene water reducer, CTF concrete
5-10 parts of synergist, 8-15 parts of additive and appropriate amount of water.
The additive is prepared by the raw material of following parts by weight:9-15 parts of strontium carbonate, 6-10 parts of dinonylnaphthalene sulfonic acid,
9-14 parts of crospovidone, 3-5 parts of sodium abietate, 2-4 parts of polyacrylamide, 1-3 parts of polyacrylic acid, 3-5 parts of sodium gluconate
With 2-6 parts of neopelex.
A kind of environmentally friendly regeneration concrete for building, including be prepared by the raw material of following parts by weight:Normal silicate
88-90 parts of cement, 23-28 parts of iron ore waste residue, 15-20 parts of palygorskite, 20-30 parts of rubble, 12-14 parts of nano-pearl rock, regeneration
20-24 parts of coarse aggregate, 12-18 parts of strontium carbonate, 21-24 parts of high tensile strength fiber, 11-14 parts of discarded object calcining material, naphthalene system subtract
12-19 parts of aqua, 6-8 parts of CTF Concrete synergists, 9-14 parts of additive and appropriate amount of water.
The regenerated coarse aggregate is that concrete, waste concrete class wall, barren rock material in building castoff are sorted by species
By sorting, crush, magnetic separation remove old metal, carboxylate spray after manufactured particle diameter be 5-32 mm particles of aggregates.
A kind of preparation method of environmentally friendly regeneration concrete for building, includes the following steps:
S1, by 9-15 parts of strontium carbonate, 6-10 parts of dinonylnaphthalene sulfonic acid, 9-14 parts of crospovidone, 3-5 parts of sodium abietate, poly- third
2-6 parts of 2-4 parts of acrylamide, 1-3 parts of polyacrylic acid, 3-5 parts of sodium gluconate and neopelex plus water are mixed,
Additive is made;
S2, by 23-28 parts of iron ore waste residue, 15-20 parts of palygorskite, 20-30 parts of rubble, 12-14 parts of nano-pearl rock, the thick bone of regeneration
10-15 parts of 20-24 parts of material and discarded object calcining material are ground into powder, cross 200-220 mesh sieves, after mixing;
S3, by 85-100 parts of Portland cement, 10-20 parts of strontium carbonate, 20-25 parts of high tensile strength fiber, naphthalene system diminishing
10-20 parts of agent, 5-10 parts of CTF Concrete synergists, 8-15 parts of additive and appropriate amount of water are added in mixer and stir 10-
15min, then adds the mixture obtained by step S2 and stirs 20-25min with the speed of 500-900r/min.
Mixer mixing speed is 400-500r/min in the step S3, and mixing time is 12 minutes.
Embodiment 1:
A kind of preparation method of environmentally friendly regeneration concrete for building, includes the following steps:
S1, by 11 parts of strontium carbonate, 8 parts of dinonylnaphthalene sulfonic acid, 12 parts of crospovidone, 4 parts of sodium abietate, 3 parts of polyacrylamide,
4 parts of 2 parts of polyacrylic acid, 4 parts of sodium gluconate and neopelex plus water are mixed, and additive is made;
S2, by 25 parts of iron ore waste residue, 18 parts of palygorskite, 24 parts of rubble, 12 parts of nano-pearl rock, 22 parts of regenerated coarse aggregate and discarded
14 parts of thing calcining material is ground into powder, crosses 220 mesh sieves, after mixing;
S3, by 85-100 parts of Portland cement, 18 parts of strontium carbonate, 22 parts of high tensile strength fiber, 15 parts of naphthalene water reducer,
8 parts of CTF Concrete synergists, 11 parts of additive and appropriate amount of water are added in mixer and stir 12min, then add step S2 institutes
The mixture obtained stirs 20-25min with the speed of 600r/min.
Mixer mixing speed is 440r/min in the step S3, and mixing time is 12 minutes.
Embodiment 2:
A kind of preparation method of environmentally friendly regeneration concrete for building, includes the following steps:
S1, by 15 parts of strontium carbonate, 10 parts of dinonylnaphthalene sulfonic acid, 14 parts of crospovidone, 5 parts of sodium abietate, polyacrylamide 4
Part, 3 parts of polyacrylic acid, 5 parts of sodium gluconate and 6 parts of neopelex plus water are mixed, and additive is made;
S2, by 28 parts of iron ore waste residue, 20 parts of palygorskite, 30 parts of rubble, 14 parts of nano-pearl rock, 24 parts of regenerated coarse aggregate and discarded
15 parts of thing calcining material is ground into powder, crosses 220 mesh sieves, after mixing;
S3, by 100 parts of Portland cement, 20 parts of strontium carbonate, 25 parts of high tensile strength fiber, 20 parts of naphthalene water reducer, CTF
10 parts of Concrete synergist, 15 parts of additive and appropriate amount of water are added in mixer and stir 15min, then add obtained by step S2
Mixture 25min is stirred with the speed of 900r/min.
Mixer mixing speed is 500r/min in the step S3, and mixing time is 12 minutes.
Embodiment 3:
A kind of preparation method of environmentally friendly regeneration concrete for building, includes the following steps:
S1, by 9 parts of strontium carbonate, 6 parts of dinonylnaphthalene sulfonic acid, 9 parts of crospovidone, 3 parts of sodium abietate, 2 parts of polyacrylamide, poly-
2 parts of 1 part of acrylic acid, 3 parts of sodium gluconate and neopelex plus water are mixed, and additive is made;
S2, by 23 parts of iron ore waste residue, 15 parts of palygorskite, 20 parts of rubble, 12 parts of nano-pearl rock, 20 parts of regenerated coarse aggregate and discarded
10 parts of thing calcining material is ground into powder, crosses 200 mesh sieves, after mixing;
S3, by 85 parts of Portland cement, 10 parts of strontium carbonate, 20 parts of high tensile strength fiber, 10 parts of naphthalene water reducer, CTF
5 parts of Concrete synergist, 8 parts of additive and appropriate amount of water are added in mixer and stir 10min, then add obtained by step S2
Mixture stirs 20min with the speed of 500r/min.
Mixer mixing speed is 400r/min in the step S3, and mixing time is 12 minutes.
The present invention using Portland cement, iron ore waste residue, palygorskite, rubble, nano-pearl rock, regenerated coarse aggregate,
Strontium carbonate, high tensile strength fiber, discarded object calcining material, naphthalene water reducer, CTF Concrete synergists, additive effectively match,
Additive is using strontium carbonate, dinonylnaphthalene sulfonic acid, crospovidone, sodium abietate, polyacrylamide, polyacrylic acid, glucose
Sour sodium and neopelex proportioning;Obtain it is a kind of not only there is higher compression strength and flexural strength, but also can be with
Combined well with concrete, not easily to fall off, overall performance is superior, is very suitable for for concrete works damage position
Reinforced concrete;Cheap, simple production process, is adapted to large-scale production;Regeneration aggregate is made with waste material of buildings and substitutes day
Right aggregate, it is possible to reduce consumption of the construction industry to natural aggregate, so as to reduce the exploitation to natural sand stone, solves natural aggregate
Increasingly deficient and a large amount of sandstones are produced the problems such as being destroyed caused by ecological environment, protect ecological environment, meet sustainable
The requirement of development.By proportion optimizing and rational additive is added, it is difficult to overcome traditional regenerated aggregate concrete slump
With control, the defects of intensity is low.
The above is only the preferred embodiment of the present invention, it is noted that for the ordinary skill people of the art
For member, without departing from the principle of the present invention, some improvements and modifications can also be made, these improvements and modifications also should
It is considered as protection scope of the present invention.
Claims (6)
1. a kind of environmentally friendly regeneration concrete for building, it is characterised in that including being prepared by the raw material of following parts by weight:It is general
Logical 85-100 parts of portland cement, 20-30 parts of iron ore waste residue, 10-25 parts of palygorskite, 15-35 parts of rubble, nano-pearl rock 10-
15 parts, 18-25 parts of regenerated coarse aggregate, 10-20 parts of strontium carbonate, 20-25 parts of high tensile strength fiber, discarded object calcining material 10-15
Part, 10-20 parts of naphthalene water reducer, 5-10 parts of CTF Concrete synergists, 8-15 parts of additive and appropriate amount of water.
A kind of 2. environmentally friendly regeneration concrete for building according to claim 1, it is characterised in that the additive by with
The raw material of lower parts by weight is prepared:9-15 parts of strontium carbonate, 6-10 parts of dinonylnaphthalene sulfonic acid, 9-14 parts of crospovidone, rosin
Sour sodium 3-5 parts, 2-4 parts of polyacrylamide, 1-3 parts of polyacrylic acid, 3-5 parts of sodium gluconate and neopelex 2-6
Part.
3. a kind of environmentally friendly regeneration concrete for building according to claim 1, it is characterised in that including by following weight
The raw material of part is prepared:88-90 parts of Portland cement, 23-28 parts of iron ore waste residue, 15-20 parts of palygorskite, rubble 20-
30 parts, 12-14 parts of nano-pearl rock, 20-24 parts of regenerated coarse aggregate, 12-18 parts of strontium carbonate, 21-24 parts of high tensile strength fiber,
11-14 parts of discarded object calcining material, 12-19 parts of naphthalene water reducer, 6-8 parts of CTF Concrete synergists, 9-14 parts of additive and water are fitted
Amount.
A kind of 4. environmentally friendly regeneration concrete for building according to claim 1, it is characterised in that the regenerated coarse aggregate
It is that concrete in building castoff, waste concrete class wall, barren rock material are sorted by species and removed by sorting, broken, magnetic separation
The particles of aggregates that manufactured particle diameter is 5-32 mm after old metal, carboxylate spray.
A kind of 5. preparation method of environmentally friendly regeneration concrete for building according to claim 1, it is characterised in that including
Following steps:
S1, by 9-15 parts of strontium carbonate, 6-10 parts of dinonylnaphthalene sulfonic acid, 9-14 parts of crospovidone, 3-5 parts of sodium abietate, poly- third
2-6 parts of 2-4 parts of acrylamide, 1-3 parts of polyacrylic acid, 3-5 parts of sodium gluconate and neopelex plus water are mixed,
Additive is made;
S2, by 23-28 parts of iron ore waste residue, 15-20 parts of palygorskite, 20-30 parts of rubble, 12-14 parts of nano-pearl rock, the thick bone of regeneration
10-15 parts of 20-24 parts of material and discarded object calcining material are ground into powder, cross 200-220 mesh sieves, after mixing;
S3, by 85-100 parts of Portland cement, 10-20 parts of strontium carbonate, 20-25 parts of high tensile strength fiber, naphthalene system diminishing
10-20 parts of agent, 5-10 parts of CTF Concrete synergists, 8-15 parts of additive and appropriate amount of water are added in mixer and stir 10-
15min, then adds the mixture obtained by step S2 and stirs 20-25min with the speed of 500-900r/min.
6. the preparation method of a kind of environmentally friendly regeneration concrete for building according to claim 5, it is characterised in that described
Mixer mixing speed is 400-500r/min in step S3, and mixing time is 12 minutes.