CN108017291A - A kind of colored glazed glass and preparation method thereof - Google Patents
A kind of colored glazed glass and preparation method thereof Download PDFInfo
- Publication number
- CN108017291A CN108017291A CN201711344410.8A CN201711344410A CN108017291A CN 108017291 A CN108017291 A CN 108017291A CN 201711344410 A CN201711344410 A CN 201711344410A CN 108017291 A CN108017291 A CN 108017291A
- Authority
- CN
- China
- Prior art keywords
- glass
- film
- colored
- glass substrate
- colored glazed
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of colored glazed glass, including glass-base, the side of the glass-base is provided with glazed colour layer, and the opposite side of the glass-base has been provided with Low E film layers；The invention also discloses a kind of production method of colored glazed glass, comprise the following steps：S1：Halftone makes；S2：Halftone；S3：Drying；S4：Baking cooling；S5：It is cleaned and dried.The present invention is by providing colored glazed glass preparation method, chromatography colored glazed glass product can be prepared, the product can prepare different chromatography colored glazed glass products according to the pattern of backboard, chromatography is uniform, be not in that chromatography misplaces or leaks heterochromatic phenomenon, meet that designer's pursuit present invention process higher and higher to colored glaze product is simple, equipment requirement is low, it is workable, there is good society generalization application.
Description
Technical field
The present invention relates to colored glazed glass to make correlative technology field, more particularly to a kind of colored glazed glass and preparation method thereof.
Background technology
Colored glazed glass is by inorganic glaze (also known as ink), using certain technique bat printing to glass surface, low-temperature glaze
Drying processing, high temperature glaze obtain a kind of decorative glasses product by high temperature sintering in glass surface, and high temperature glaze is color
Glaze glass can monolithic use, may be alternatively configured the joint product such as sandwiched product or hollow glass product, and low-temperature glaze colored glaze glass
Glass can not monolithic use, the joint product such as sandwiched product or hollow glass product can only be made, since colored glazed glass has very well
Dicoration, colored glaze product is especially covered, using can be more and more extensive.At present, generally inkjet printing technology molding sleeve is used
Colored glaze glass, although the uniform product of chromatography can also be molded, there is processing charges is excessive and processing efficiency is low
The problem of.Therefore, it is necessary to solve the above problems to invent a kind of colored glazed glass and preparation method thereof.
The content of the invention
It is an object of the invention to provide a kind of colored glazed glass and preparation method thereof, to solve to propose in above-mentioned background technology
The problem of.
To achieve the above object, the present invention provides following technical solution：A kind of colored glazed glass and preparation method thereof, including glass
Glass basic unit, the side of the glass-base are provided with glazed colour layer, and the opposite side of the glass-base has been provided with Low-E film layers,
The production method of the colored glazed glass comprises the following steps：
Step 1：Halftone makes：Film film is layed on silk screen, will along the edge of film film by sealant tape
Film sticker is opened up in the clear area of film film on silk screen, making to form sealing space between film film and silk screen
For the through hole of grafting exhaust tube, by the exhaust tube insertion through hole for connecting vacuum pump and seal, vacuum pump is then turned on, to sealing
Space vacuumizes, and film film is bonded with silk screen, is finally exposed processing to the film film after fitting and silk screen, to obtain the final product
Colored glazed glass halftone；
Step 2：Screen painting：Glass substrate is placed in screen printer, keeps the one side of glass substrate upwardly disposed,
Upper blade and halftone, colored glazed glass halftone is placed on the one side of glass substrate, is then uniformly poured on glaze on halftone,
Using scraper by glaze silk-screen on the one side of glass substrate, colored glaze face is formed on the one side of the glass substrate；
Step 3：Drying：The good glass substrate of silk-screen is sent into drying and processing in dryer, drying temperature 150 °-
Between 180 °；
Step 4：Baking cooling：The glass substrate of drying is put into oven baking, baking time 10min-20min, dries
Roasting temperature is 200 ° -250 °, then will by the glass substrate ventilating and cooling after baking, cooling time 60min-90min；
Step 5：It is cleaned and dried：Glass substrate after cooling is rinsed with clear water, cleaning machine cleaning is placed into, has cleaned
Into rear carry out drying process, drying time 30min-50min, up to colored glazed glass.
Preferably, it is provided with sound insulation glue-line between glass-base and the Low-E film layer.
Preferably, in the step 1, meshcount is 200~300 mesh.
Preferably, in the step 2, glaze is uniformly sufficiently stirred by mixer.
The technique effect and advantage of the present invention：The present invention is provided with Low-E film layers, Low-E film layers pair on colored glazed glass
The characteristic of visible ray high transmission and centering far infrared high reflection, makes itself and simple glass and traditional coated glass phase for building
Than having excellent heat insulation and good translucency；By providing colored glazed glass preparation method, set colored glaze can be prepared
Glass product, the product can prepare different chromatography colored glazed glass products according to the pattern of backboard, and chromatography is uniform, will not go out
Heterochromatic phenomenon is leaked in existing chromatography dislocation, meets designer to the higher and higher pursuit of colored glaze product；Present invention process is simple, if
It is low for requiring, it is workable, there is good society generalization application.
Embodiment
The technical solution in the embodiment of the present invention will be clearly and completely described below, it is clear that described implementation
Example is only part of the embodiment of the present invention, instead of all the embodiments.Based on the embodiments of the present invention, this area is common
Technical staff's all other embodiments obtained without making creative work, belong to the model that the present invention protects
Enclose.
Embodiment 1：
A kind of colored glazed glass and preparation method thereof, including glass-base, the side of the glass-base are provided with glazed colour layer,
The opposite side of the glass-base has been provided with Low-E film layers, and acoustic mastic is provided between glass-base and the Low-E film layer
Layer, the production method of the colored glazed glass comprise the following steps：
Step 1：Halftone makes：Film film is layed on silk screen, will along the edge of film film by sealant tape
Film sticker is opened up in the clear area of film film on silk screen, making to form sealing space between film film and silk screen
For the through hole of grafting exhaust tube, by the exhaust tube insertion through hole for connecting vacuum pump and seal, vacuum pump is then turned on, to sealing
Space vacuumizes, and film film is bonded with silk screen, is finally exposed processing to the film film after fitting and silk screen, to obtain the final product
Colored glazed glass halftone；
Step 2：Screen painting：Glass substrate is placed in screen printer, keeps the one side of glass substrate upwardly disposed,
Upper blade and halftone, colored glazed glass halftone is placed on the one side of glass substrate, is uniformly sufficiently stirred by mixer
Glaze, is then uniformly poured on halftone by glaze, using scraper by glaze silk-screen on the one side of glass substrate, in the glass
Colored glaze face is formed on the one side of glass substrate；
Step 3：Drying：The good glass substrate of silk-screen is sent into drying and processing in dryer, drying temperature 150 ° it
Between；
Step 4：Baking cooling：The glass substrate of drying is put into oven baking, baking time 10min-20min, dries
Roasting temperature is 200 °, then will by the glass substrate ventilating and cooling after baking, cooling time 60min；
Step 5：It is cleaned and dried：Glass substrate after cooling is rinsed with clear water, cleaning machine cleaning is placed into, has cleaned
Into rear carry out drying process, drying time 30min-50mi, up to colored glazed glass.
Embodiment 2：
A kind of colored glazed glass and preparation method thereof, including glass-base, the side of the glass-base are provided with glazed colour layer,
The opposite side of the glass-base has been provided with Low-E film layers, and acoustic mastic is provided between glass-base and the Low-E film layer
Layer, the production method of the colored glazed glass comprise the following steps：
Step 1：Halftone makes：Film film is layed on silk screen, meshcount is 200~300 mesh, passes through sealing
Adhesive tape along the edge of film film by film sticker on silk screen, making to form sealing space between film film and silk screen,
The through hole for grafting exhaust tube is opened up in the clear area of film film, the exhaust tube insertion through hole and close of vacuum pump will be connected
Envelope, is then turned on vacuum pump, sealing space is vacuumized, film film is bonded with silk screen, finally to the film glue after fitting
Piece and silk screen are exposed processing, up to colored glazed glass halftone；
Step 2：Screen painting：Glass substrate is placed in screen printer, keeps the one side of glass substrate upwardly disposed,
Upper blade and halftone, colored glazed glass halftone is placed on the one side of glass substrate, is uniformly sufficiently stirred by mixer
Glaze, is then uniformly poured on halftone by glaze, using scraper by glaze silk-screen on the one side of glass substrate, in the glass
Colored glaze face is formed on the one side of glass substrate；
Step 3：Drying：The good glass substrate of silk-screen is sent into drying and processing in dryer, drying temperature 165 ° it
Between；
Step 4：Baking cooling：The glass substrate of drying is put into oven baking, baking time 15min, baking temperature
For 230 °, then will by baking after glass substrate ventilating and cooling, cooling time 75min；
Step 5：It is cleaned and dried：Glass substrate after cooling is rinsed with clear water, cleaning machine cleaning is placed into, has cleaned
Into rear carry out drying process, drying time 40min, up to colored glazed glass.
Embodiment 3：
A kind of colored glazed glass and preparation method thereof, including glass-base, the side of the glass-base are provided with glazed colour layer,
The opposite side of the glass-base has been provided with Low-E film layers, and acoustic mastic is provided between glass-base and the Low-E film layer
Layer, the production method of the colored glazed glass comprise the following steps：
Step 1：Halftone makes：Film film is layed on silk screen, meshcount is 300 mesh, passes through sealant tape edge
The edge of film film by film sticker on silk screen, making to form sealing space between film film and silk screen, in the film
The clear area of film opens up the through hole for grafting exhaust tube, by the exhaust tube insertion through hole for connecting vacuum pump and seals, then
Vacuum pump is opened, sealing space is vacuumized, film film is bonded with silk screen, finally to the film film and silk screen after fitting
Processing is exposed, up to colored glazed glass halftone；
Step 2：Screen painting：Glass substrate is placed in screen printer, keeps the one side of glass substrate upwardly disposed,
Upper blade and halftone, colored glazed glass halftone is placed on the one side of glass substrate, is uniformly sufficiently stirred by mixer
Glaze, is then uniformly poured on halftone by glaze, using scraper by glaze silk-screen on the one side of glass substrate, in the glass
Colored glaze face is formed on the one side of glass substrate；
Step 3：Drying：The good glass substrate of silk-screen is sent into drying and processing in dryer, drying temperature 180 ° it
Between；
Step 4：Baking cooling：The glass substrate of drying is put into oven baking, baking time 20min, baking temperature
For 250 °, then will by baking after glass substrate ventilating and cooling, cooling time 90min；
Step 5：It is cleaned and dried：Glass substrate after cooling is rinsed with clear water, cleaning machine cleaning is placed into, has cleaned
Into rear carry out drying process, drying time 50min, up to colored glazed glass.
Colored glazed glass can be made in three groups of embodiments more than, wherein colored glazed glass made from second group of embodiment is imitated
Fruit is best, and the present invention can prepare chromatography colored glazed glass product, which can basis by providing colored glazed glass preparation method
The pattern of backboard prepares different chromatography colored glazed glass products, and chromatography is uniform, is not in that chromatography misplaces or leaks heterochromatic show
As meeting designer to the higher and higher pursuit of colored glaze product.
Finally it should be noted that：The foregoing is only a preferred embodiment of the present invention, is not intended to limit the invention,
Although the present invention is described in detail with reference to the foregoing embodiments, for those skilled in the art, it still may be used
To modify to the technical solution described in foregoing embodiments, or equivalent substitution is carried out to which part technical characteristic,
Within the spirit and principles of the invention, any modification, equivalent replacement, improvement and so on, should be included in the present invention's
Within protection domain.
Claims (4)
- A kind of 1. colored glazed glass and preparation method thereof, it is characterised in that：Including glass-base, the side of the glass-base is set There is glazed colour layer, the opposite side of the glass-base has been provided with Low-E film layers, and the production method of the colored glazed glass includes following step Suddenly：Step 1：Halftone makes：Film film is layed on silk screen, by sealant tape along the edge of film film by the film Sticker is opened up in the clear area of film film and is used on silk screen, making to form sealing space between film film and silk screen The through hole of grafting exhaust tube, by the exhaust tube insertion through hole for connecting vacuum pump and seals, vacuum pump is then turned on, to sealing space Vacuumize, film film is bonded with silk screen, processing finally is exposed to the film film after fitting and silk screen, up to colored glaze Glass halftone；Step 2：Screen painting：Glass substrate is placed in screen printer, keeps the one side of glass substrate upwardly disposed, above scrapes Knife and halftone, colored glazed glass halftone is placed on the one side of glass substrate, is then uniformly poured on glaze on halftone, is utilized Glaze silk-screen on the one side of glass substrate, is formed colored glaze face by scraper on the one side of the glass substrate；Step 3：Drying：The good glass substrate of silk-screen is sent into drying and processing in dryer, drying temperature 150 ° -180 ° it Between；Step 4：Baking cooling：The glass substrate of drying is put into oven baking, baking time 10min-20min, baking temperature Spend for 200 ° -250 °, then will by baking after glass substrate ventilating and cooling, cooling time 60min-90min；Step 5：It is cleaned and dried：Glass substrate after cooling is rinsed with clear water, cleaning machine cleaning is placed into, after the completion of cleaning Processing, drying time 30min-50min, up to colored glazed glass is dried.
- A kind of 2. colored glazed glass according to claim 1 and preparation method thereof, it is characterised in that：The glass-base with Sound insulation glue-line is provided between Low-E film layers.
- A kind of 3. colored glazed glass according to claim 1 and preparation method thereof, it is characterised in that：In the step 1, silk Mesh number is 200~300 mesh.
- A kind of 4. colored glazed glass according to claim 1 and preparation method thereof, it is characterised in that：In the step 2, lead to Cross mixer and uniformly sufficiently stir glaze.