CN108003787A - A kind of ceramic coating of resistant to damage - Google Patents
A kind of ceramic coating of resistant to damage Download PDFInfo
- Publication number
- CN108003787A CN108003787A CN201711429771.2A CN201711429771A CN108003787A CN 108003787 A CN108003787 A CN 108003787A CN 201711429771 A CN201711429771 A CN 201711429771A CN 108003787 A CN108003787 A CN 108003787A
- Authority
- CN
- China
- Prior art keywords
- parts
- component
- resistant
- ceramic powder
- damage
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The mass fraction of a kind of ceramic coating of resistant to damage, its component and each component is：10 12 parts of polysiloxane compound, 10 12 parts of acrylic resin, 20 24 parts of ceramic powder, more 58 parts of amine type hardeners；The ceramic powder is the mixing of aluminium oxide and silica, and the mass ratio of the two is 1: (1.2 1.3).Ceramic coating proposed by the present invention employs the polysiloxane compound of inorganic system and the acrylic resin of organic system, combines both specialities, bears dirty, resistant to damage.
Description
Technical field
The invention belongs to Material Field, more particularly to a kind of ceramic coating of resistant to damage.
Background technology
With the development of society, ceramic coating occupies an important position in many fields, and it is subject to many consumers
Accreditation, ceramic use environment is sufficiently complex, especially with high temperature in the environment of, greatly reduce service life, increase
Cost, so traditional ceramic material can not meet increasingly harsh job requirement, exploitation with high temperature resistant, it is corrosion-resistant,
Shock resistance, anti-tired and anti abrasive advanced composite material (ACM) have become the important topic of material science research.
The content of the invention
It is an object of the present invention to propose a kind of ceramic coating of resistant to damage, the technical problem to be solved is that make its tool
There are good abrasion resistance properties, thus more suitable for practicality.
The object of the invention to solve the technical problems is realized using following technical scheme.According to proposed by the present invention
The mass fraction of a kind of ceramic coating of resistant to damage, its component and each component is：10-12 parts of polysiloxane compound, acrylic acid
10-12 parts of resin, 20-24 parts of ceramic powder, more amine type hardeners 5-8 parts；The ceramic powder is the mixed of aluminium oxide and silica
Close, the mass ratio of the two is 1: (1.2-1.3).
The object of the invention to solve the technical problems is also further realized using following technical measures.
The mass fraction of foregoing ceramic coating, its component and each component is：11 parts of polysiloxane compound, acrylic acid tree
11 parts of fat, 22 parts of ceramic powder, more 6 parts of amine type hardeners；The ceramic powder is the mixing of aluminium oxide and silica, the matter of the two
Amount is than being 1: 1.2.
The mass fraction of foregoing ceramic coating, its component and each component is：11 parts of polysiloxane compound, acrylic acid tree
11 parts of fat, 23 parts of ceramic powder, more 7 parts of amine type hardeners；The ceramic powder is the mixing of aluminium oxide and silica, the matter of the two
Amount is than being 1: 1.3.
Ceramic coating proposed by the present invention employs the polysiloxane compound of inorganic system and the acrylic resin of organic system,
Both specialities are combined, are born dirty, resistant to damage.
Described above is only the general introduction of technical solution of the present invention, in order to better understand the technological means of the present invention,
And can be practiced according to the content of specification, and in order to allow the above and other objects, features and advantages of the present invention can
Become apparent, described in detail below especially exemplified by preferred embodiment.
Embodiment
Further to illustrate the present invention to reach the technological means and effect that predetermined goal of the invention is taken, below in conjunction with
Preferred embodiment, to according to a kind of its embodiment of the ceramic coating of resistant to damage proposed by the present invention, structure, feature and its
Effect, describes in detail as after.
Embodiment 1
The mass fraction of a kind of ceramic coating of resistant to damage, its component and each component is：10 parts of polysiloxane compound, third
10 parts of olefin(e) acid resin, 20 parts of ceramic powder, more 5 parts of amine type hardeners；The ceramic powder for aluminium oxide and silica mixing, two
The mass ratio of person is 1: 1.2.
Embodiment 2
The mass fraction of a kind of ceramic coating of resistant to damage, its component and each component is：11 parts of polysiloxane compound, third
11 parts of olefin(e) acid resin, 22 parts of ceramic powder, more 6 parts of amine type hardeners；The ceramic powder for aluminium oxide and silica mixing, two
The mass ratio of person is 1: 1.2.
Embodiment 3
The mass fraction of a kind of ceramic coating of resistant to damage, its component and each component is：11 parts of polysiloxane compound, third
11 parts of olefin(e) acid resin, 23 parts of ceramic powder, more 7 parts of amine type hardeners；The ceramic powder for aluminium oxide and silica mixing, two
The mass ratio of person is 1: 1.3.
Embodiment 4
The mass fraction of a kind of ceramic coating of resistant to damage, its component and each component is：12 parts of polysiloxane compound, third
12 parts of olefin(e) acid resin, 24 parts of ceramic powder, more 8 parts of amine type hardeners；The ceramic powder for aluminium oxide and silica mixing, two
The mass ratio of person is 1: 1.3.
The above described is only a preferred embodiment of the present invention, limitation in any form is not done to the present invention, though
So the present invention is disclosed above with preferred embodiment, but is not limited to the present invention, any to be familiar with this professional technology people
Member, without departing from the scope of the present invention, when the technology contents using the disclosure above make a little change or modification
For the equivalent embodiment of equivalent variations, as long as being the content without departing from technical solution of the present invention, the technical spirit according to the present invention
To any simple modification, equivalent change and modification made for any of the above embodiments, in the range of still falling within technical solution of the present invention.
Claims (3)
1. a kind of ceramic coating of resistant to damage, it is characterised in that the mass fraction of its component and each component is：Silicone
10-12 parts of thing, 10-12 parts of acrylic resin, 20-24 parts of ceramic powder, more amine type hardeners 5-8 parts；The ceramic powder is aluminium oxide
With the mixing of silica, the mass ratio of the two is 1: (1.2-1.3).
2. ceramic coating according to claim 1, it is characterised in that the mass fraction of its component and each component is：Poly- silica
11 parts of hydride compounds, 11 parts of acrylic resin, 22 parts of ceramic powder, more 6 parts of amine type hardeners；The ceramic powder is aluminium oxide and dioxy
The mixing of SiClx, the mass ratio of the two are 1: 1.2.
3. ceramic coating according to claim 1, it is characterised in that the mass fraction of its component and each component is：Poly- silica
11 parts of hydride compounds, 11 parts of acrylic resin, 23 parts of ceramic powder, more 7 parts of amine type hardeners；The ceramic powder is aluminium oxide and dioxy
The mixing of SiClx, the mass ratio of the two are 1: 1.3.