CN107988695A - A kind of low temperature dyeing washs stretch knit fabric and preparation method thereof entirely - Google Patents
A kind of low temperature dyeing washs stretch knit fabric and preparation method thereof entirely Download PDFInfo
- Publication number
- CN107988695A CN107988695A CN201711482791.6A CN201711482791A CN107988695A CN 107988695 A CN107988695 A CN 107988695A CN 201711482791 A CN201711482791 A CN 201711482791A CN 107988695 A CN107988695 A CN 107988695A
- Authority
- CN
- China
- Prior art keywords
- low temperature
- fabric
- temperature dyeing
- washs
- elastic force
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to fabric production technical field, is specially that a kind of low temperature dyeing washs stretch knit fabric and its manufacture method entirely.The low temperature dyeing washs stretch knit fabric entirely, bicomponent filament yarn braiding is selected to form, the bicomponent filament yarn is formed by elastic force composite filament and low temperature dyeing dacron thread and sth. made by twisting, the elastic force composite filament blows to close since PET and PPT is formed, after should being extruded by extruder respectively by PET and PTT through cold wind forms the elastic force composite filament with circular cross-section.Above-mentioned low temperature dyeing polyester knitted fabric, there is excellent pliability, plasticity, wrinkle resistance, chemical resistance, easy dyeing, liking for consumer is firmly got, while there is excellent physicochemical property and processing performance, and cost is low, fabric is changed to the dye of positive ion by original disperse dyes, dyeing under cryogenic conditions is realized, saves the production costs such as a large amount of steam, improves factory's benefit, and gained fabric has soft, the permanent notable feature of elastic force.
Description
Technical field
The invention belongs to fabric production technical field, is specially that a kind of low temperature dyeing washs stretch knit fabric and its manufacture entirely
Method.
Background technology
With the progress in epoch and the further lifting of people's quality of the life, the work(such as comfortable, convenient of the people for clothing
It can require higher and higher, conventional needle knitted fabric cannot meet people to the functional demand of fabric.Poly terephthalic acid second
Diol ester (PET)/polypropylene terephthalate (PTT) belongs to a kind of new high molecular synthetic material, it has excellent
Physicochemical property and processing performance, and cost is low, thus will have in the field such as automobile, electric, household electrical appliances, fiber wide
Application prospect.Especially in fiber art, PET/PTT composite fibres are combine PET and PTT each the advantages of in performance, tool
There are especially excellent pliability, plasticity, gas permeability, wrinkle resistance, chemical resistance, dirt, low static behaviour, easy dyeing, low suction
The advantages that water rate, firmly get liking for consumer.It is understood that clothes loses elasticity, it is easy for deforming and slack and undisciplined, loses it
Carry out example edition.The traditional dyeing process of knitting fabric is under conditions of sizing, adds disperse dyes and passes through high temperature (135 DEG C) high pressure
Dyed, gained fabric feel hard, production cost is high, it is impossible to meet that people are comfortably random, it is convenient and efficient, outdoor activity
Modern way of life.
The content of the invention
In order to solve the problems, such as above-mentioned fabric function and Dyeing Technology, the present invention provides a kind of low temperature dyeing and washs knitting entirely
Fabric and preparation method thereof.
A kind of low temperature dyeing washs stretch knit fabric entirely, selects bicomponent filament yarn braiding to form, the bicomponent filament yarn is by elastic force
Composite filament is formed with low temperature dyeing dacron thread and sth. made by twisting, which should be distinguished since PET and PPT is formed by PET and PTT
Blow to close through cold wind after being extruded by extruder and form the elastic force composite filament with circular cross-section.
Further, elastic force composite filament is 20-100D/15-100F.
Further, mass percent shared by PET and PTT is respectively 10%-90% and 90%- in elastic force composite filament
10%.
Further, low temperature dyeing dacron thread is 20-100D/15-100F, and contains polyethanol.
Further, bicomponent filament yarn 40-200D/30-200F.
A kind of low temperature dyeing washs stretch knit manufacturing method of fabric entirely, manufactures above-mentioned low temperature dyeing and washs elastic needle surface of second order entirely
Material, technological process specific as follows:
1) elastic force composite filament manufactures:Blowing conjunction through cold wind after PET and PTT are extruded by extruder respectively and form has circular cut
The elastic force composite filament in face;
2) fabric manufactures:By weaving set device parameter;
3) dyeing includes successively:It is pre-treatment, low temperature dyeing, washing, low-temperature shaped, above-mentioned obtained fabric is added to
Pre-treatment is carried out in 35-40 DEG C of auxiliary agent cylinder, is subsequently added into the dye of positive ion, temperature is risen to 80-100 DEG C, carries out low temperature dye
Color, dyeing time 30-50min, is then passed through washing and is dehydrated, and by temperature control at 0-45 DEG C, carries out low-temperature shaped.
Further, device parameter is controlled into yarn tension and controlled in 2-5g, fabric line length in 30-35cm/100 pins, fabric
Grammes per square metre is controlled in 180 ± 5g/m2。
Further, auxiliary formula:Pure glacial acetic acid HAc 0.5g/L, sodium acetate 0.5g/L, Disperse Leveler HTN 0.5g/
L, treasured HB226 1.0g/L in bath, chelant diffusant DM1016 0.5g/L.
Further, dye of positive ion formula:Disperse yellow brown SW-W 0.43%o.w.f, disperse black WF-HB4.3%
O.w.f, dispersed ruby HW-4BS 0.2%o.w.f.
Further, 0.6-1.0 DEG C of the heating rate of low temperature dyeing/min.
Low temperature dyeing polyester knitted fabric prepared by the present invention, using elastic force composite filament and low temperature dyeing dacron thread and is twisted with the fingers
Into long filament braiding form, wherein elastic force composite filament is with PET and PTT in long filament production process, passes through two different extruding
Machine is extruded in the bicomponent filament yarn by cooling down wind and forming altogether.The bicomponent filament yarn have excellent pliability, plasticity,
The advantages that wrinkle resistance, chemical resistance, easy dyeing, firmly get liking for consumer, while has excellent physicochemical property and processing
Performance, and cost is low.Gained fabric is changed to cation dye by varying the colouring method of terylene by original disperse dyes
Material, realizes dyeing under cryogenic conditions, saves the production costs such as a large amount of steam, improves factory's benefit, and gained fabric
With soft, the permanent notable feature of elastic force.
Brief description of the drawings
Fig. 1 is the cross section structure of elastic force composite filament;
Fig. 2 is the upper machine cam chart through knitting device;
Fig. 3 is to manufacture the process flow chart that low temperature dyeing washs elastic fabric entirely.
Embodiment
Embodiment one:
A kind of low temperature dyeing washs stretch knit fabric entirely, selects 28D/18F elastic force composite filament to be washed with 72D/86F low temperature dyeings
The synthetic fibre silk and 100D/104F long filaments being twisted, braiding form;Wherein, the elastic force composite filament is to be produced with PET and PTT in long filament
During, extruded by two different extruders, pass through the bicomponent filament yarn for cooling down wind and forming altogether, bicomponent filament yarn tool
There are excellent pliability, plasticity, wrinkle resistance, chemical resistance, easy dyeing.PET is 28% in elastic force composite filament,
PTT is 72%.
With reference to shown in Fig. 2, low temperature dyeing polyester knitted fabric of the present invention uses common single side weft-knitting large circle machine, upper machine triangle
As shown in Fig. 2, in Fig. 2, ∧ represents lopping for arrangement.Weaving parameter setting avoids the irregular production of tension force to be 5g into yarn tension
Setation pin and horizontal stripe, fabric line length are 30cm/100 pins, and fabric grammes per square metre is 175g/m2。
Above-mentioned obtained fabric is added in 40 DEG C of auxiliary agent cylinder and carries out pre-treatment, is subsequently added into the dye of positive ion, by temperature
Degree rises to 80 DEG C by 0.6 DEG C/min, carries out low temperature dyeing, dyeing time 35min, by washing and being dehydrated, cools the temperature to
45 DEG C, carry out low-temperature shaped.
Above-mentioned auxiliary formula:Pure glacial acetic acid HAc 0.5g/L, sodium acetate 0.5g/L, Disperse Leveler HTN0.5g/L, in bath
Precious HB226 1.0g/L, chelant diffusant DM1016 0.5g/L.
Above-mentioned dye of positive ion formula:Disperse yellow brown SW-W 0.43%o.w.f, disperse black WF-HB4.3%o.w.f, point
Dissipate carbuncle HW-4BS 0.2%o.w.f.
Embodiment two:
A kind of low temperature dyeing washs stretch knit fabric entirely, selects 50D/36F elastic force composite filament to be washed with 50D/72F low temperature dyeings
The synthetic fibre silk and 105D/108F long filaments being twisted, braiding form;Wherein, the elastic force composite filament is to be produced with PET and PTT in long filament
During, extruded by two different extruders, pass through the bicomponent filament yarn for cooling down wind and forming altogether, bicomponent filament yarn tool
There are excellent pliability, plasticity, wrinkle resistance, chemical resistance, easy dyeing.PET is 50% in elastic force composite filament,
PTT is 50%.
With reference to shown in Fig. 2, low temperature dyeing polyester knitted fabric of the present invention uses common single side weft-knitting large circle machine, upper machine triangle
As shown in Fig. 2, in Fig. 2, ∧ represents lopping for arrangement.Weaving parameter setting avoids the irregular production of tension force to be 5g into yarn tension
Setation pin and horizontal stripe, fabric line length are 32cm/100 pins, and fabric grammes per square metre is 180g/m2。
Above-mentioned obtained fabric is added in 40 DEG C of auxiliary agent cylinder and carries out pre-treatment, is subsequently added into the dye of positive ion, by temperature
Degree rises to 85 DEG C by 0.7 DEG C/min, carries out low temperature dyeing, dyeing time 40min, by washing and being dehydrated, cools the temperature to
45 DEG C, carry out low-temperature shaped.
Above-mentioned auxiliary formula:Pure glacial acetic acid HAc 0.5g/L, sodium acetate 0.5g/L, Disperse Leveler HTN0.5g/L, in bath
Precious HB226 1.0g/L, chelant diffusant DM1016 0.5g/L.
Above-mentioned dye of positive ion formula:Disperse yellow brown SW-W 0.43%o.w.f, disperse black WF-HB4.3%o.w.f, point
Dissipate carbuncle HW-4BS 0.2%o.w.f.
The preferred embodiment of the present invention is above are only, but the design concept of the present invention is not limited thereto, all profits
The change of unsubstantiality is carried out to the present invention with this design, the behavior for invading the scope of the present invention should all be belonged to.
Claims (10)
1. a kind of low temperature dyeing washs stretch knit fabric entirely, it is characterised in that:Bicomponent filament yarn braiding is selected to form, the compound length
Silk is formed by elastic force composite filament and low temperature dyeing dacron thread and twisting with the fingers, the elastic force composite filament since PET and PPT is formed, should by PET and
PTT blows to close after being extruded by extruder respectively through cold wind forms the elastic force composite filament with circular cross-section.
2. low temperature dyeing according to claim 1 washs stretch knit fabric entirely, it is characterised in that:The elastic force composite filament is
20-100D/15-100F。
3. low temperature dyeing according to claim 1 washs stretch knit fabric entirely, it is characterised in that:In the elastic force composite filament
Mass percent shared by PET and PTT is respectively 10%-90% and 90%-10%.
4. low temperature dyeing according to claim 1 washs stretch knit fabric entirely, it is characterised in that:The low temperature dyeing terylene
Silk is 20-100D/15-100F, and contains polyethanol.
5. low temperature dyeing according to claim 1 washs stretch knit fabric entirely, it is characterised in that:The bicomponent filament yarn is
40-200D/30-200F。
6. a kind of low temperature dyeing washs stretch knit manufacturing method of fabric entirely, it is characterised in that described in the manufacturing claims 1
A kind of low temperature dyeing washs stretch knit fabric, technological process specific as follows entirely:
1) elastic force composite filament manufactures:Blow to close through cold wind after PET and PTT are extruded by extruder respectively and form with circular cross-section
Elastic force composite filament;
2) fabric manufactures:By weaving set device parameter;
3) dyeing includes successively:It is pre-treatment, low temperature dyeing, washing, low-temperature shaped, above-mentioned obtained fabric is added to 35-
Pre-treatment is carried out in 40 DEG C of auxiliary agent cylinder, is subsequently added into the dye of positive ion, temperature is risen to 80-100 DEG C, carries out low temperature dyeing,
Dyeing time is 30-50min, is then passed through washing and is dehydrated, and by temperature control at 0-45 DEG C, is carried out low-temperature shaped.
7. low temperature dyeing according to claim 6 washs stretch knit manufacturing method of fabric entirely, it is characterised in that:The equipment
Parameter is controlled into yarn tension and controlled in 2-5g, the control of fabric line length in 30-35cm/100 pins, fabric grammes per square metre in 180 ± 5g/m2。
8. low temperature dyeing according to claim 6 washs stretch knit manufacturing method of fabric entirely, it is characterised in that the auxiliary agent
Formula:Pure glacial acetic acid HAc 0.5g/L, sodium acetate 0.5g/L, Disperse Leveler HTN 0.5g/L, treasured HB226 1.0g/L in bath,
Chelant diffusant DM1016 0.5g/L.
9. low temperature dyeing according to claim 6 washs stretch knit manufacturing method of fabric entirely, it is characterised in that it is described sun from
Sub- dye formulation:Disperse yellow brown SW-W 0.43%o.w.f, disperse black WF-HB 4.3%o.w.f, dispersed ruby HW-4BS
0.2%o.w.f.
10. low temperature dyeing according to claim 6 washs stretch knit manufacturing method of fabric entirely, it is characterised in that:It is described low
0.6-1.0 DEG C of heating rate/min of temperature dyeing.