CN107987730A - Strong glazing car wax of a kind of electrical insulating property and preparation method thereof - Google Patents
Strong glazing car wax of a kind of electrical insulating property and preparation method thereof Download PDFInfo
- Publication number
- CN107987730A CN107987730A CN201711307155.XA CN201711307155A CN107987730A CN 107987730 A CN107987730 A CN 107987730A CN 201711307155 A CN201711307155 A CN 201711307155A CN 107987730 A CN107987730 A CN 107987730A
- Authority
- CN
- China
- Prior art keywords
- parts
- wax
- electrical insulating
- insulating property
- strong
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of strong glazing car wax of electrical insulating property, including the following raw material according to mass fraction meter：25 parts of palm wax, 5 parts of diatomite, 10 parts of Tissuemat E, 3 parts of silicon Acrylote fluororesin, 0.5 part of essence, 0.5 part of polyethylene oxide, 1 part of nano mica powder, 0.8 part of anti-UV agent, 6 parts of emulsifying agent, 18 parts of solvent naphtha, 2 parts of turpentine oil, 2 parts of montanin wax, 50 parts of water.By above-mentioned technical proposal, the present invention provides the car wax that a kind of electrical insulating property is strong and glossiness is high, water proofing property is excellent, and further provides preparation method.
Description
Technical field
The invention belongs to car wax field, more particularly to a kind of strong glazing car wax of electrical insulating property and its preparation side
Method.
Background technology
With the increasingly lifting of living standard, automobile has entered into huge numbers of families.And the protection for automobile then it is particularly important that,
The electrical insulating property of existing car wax is not high, is easy to cause on car door there are a small amount of electrostatic, brings some potential safety problems.Its
Secondary, in 3-5 days of waxing, the hydrophobicity of car wax just substantially reduces existing car wax, so water resistance has much room for improvement.And
For the place more than strong wind weather, the debris such as rubble, sand, leaf often brings vehicle body damage, causes trickle cut, shadow
Ring the gloss of car body.
The content of the invention
It is an object of the present invention to overcome existing automobile storage the defects of, there is provided a kind of electrical insulating property is strong, water proofing property is strong and
The high car wax of glossiness, thus more suitable for practicality.
The object of the invention to solve the technical problems is realized using following technical scheme.According to proposed by the present invention
A kind of strong glazing car wax of electrical insulating property, including the following raw material according to mass fraction meter：20-30 parts of palm wax, diatomite
3-8 parts, 6-12 parts of Tissuemat E, 2-4 parts of silicon Acrylote fluororesin, 0.3-0.7 parts of essence, 0.3-0.7 parts of polyethylene oxide,
0.5-1.5 parts of nano mica powder, 0.5-1 parts of anti-UV agent, 5-10 parts of emulsifying agent, 15-25 parts of solvent naphtha, 1-3 parts of turpentine oil, illiteracy
1.5-2.5 parts of denier wax, 30-50 parts of water.
A kind of strong glazing car wax of electrical insulating property of the invention, including the following raw material according to mass fraction meter：Palm
25 parts of wax, 5 parts of diatomite, 10 parts of Tissuemat E, 3 parts of silicon Acrylote fluororesin, 0.5 part of essence, 0.5 part of polyethylene oxide, receive
1 part of mica powder of rice, 0.8 part of anti-UV agent, 6 parts of emulsifying agent, 18 parts of solvent naphtha, 2 parts of turpentine oil, 2 parts of montanin wax, 50 parts of water.
The preparation method of the present invention includes the following steps：According to mass fraction, palm wax, Tissuemat E, montanin wax are ground
Be milled to it is powdered, after be heated to melting, melt after under 200-280rpm stir heating, when temperature reaches 75 DEG C -85 DEG C, add
Enter solvent naphtha and turpentine oil, continue to stir under 650rpm-700rpm, after sequentially add diatomite, silicon Acrylote fluororesin,
Polyethylene oxide, nano mica powder are added when being warming up to 90 DEG C -100 DEG C, continues to stir, reduces rotating speed to 300-400rpm, drop
Temperature reduces rotating speed to 300-400rpm, sequentially adds emulsifying agent and 75 DEG C of water to essence and anti-UV agent is added at 40 DEG C -50 DEG C
Emulsified, stirred under 200-300rpm, 70-85min is emulsified, up to the strong glazing car wax of electrical insulating property.
Preferably, the preparation method of the strong glazing car wax of electrical insulating property of the present invention, includes the following steps：According to quality
Number, palm wax, Tissuemat E, montanin wax are ground to it is powdered, after be heated to melting, melt after under 240rpm stir rise
Temperature, when temperature reaches 80 DEG C, adds solvent naphtha and turpentine oil, continues to stir under 675rpm, after sequentially add diatomite, third
Olefin(e) acid fluosilicic resin, adds polyethylene oxide, nano mica powder when being warming up to 95 DEG C, continues to stir, reduction rotating speed to 350rpm,
Essence and anti-UV agent are added when being cooled to 45 DEG C, rotating speed is reduced to 350rpm, sequentially adds emulsifying agent and 75 DEG C of water carries out breast
Change, stirred under 250rpm, 80min is emulsified, up to the strong glazing car wax of electrical insulating property.
By above-mentioned technical proposal, car wax proposed by the present invention compared with prior art, its antistatic property, insulating properties,
Water proofing property greatly improves；Secondly fine handling scratches can be filled up completely, play the high effect of glossiness.
Described above is only the general introduction of technical solution of the present invention, in order to better understand the technological means of the present invention, and
It can be practiced according to the content of specification, and to allow the above and other objects, features and advantages of the present invention can be brighter
It is aobvious understandable, described in detail below especially exemplified by preferred embodiment.
Embodiment
Further to illustrate the present invention to reach the technological means and effect that predetermined goal of the invention is taken, below in conjunction with
Preferred embodiment, to strong according to a kind of electrical insulating property proposed by the present invention its embodiment of glazing car wax, structure, spy
Sign and its effect, describe in detail as after.
Embodiment one
A kind of strong glazing car wax of electrical insulating property of the invention, including the following raw material according to mass fraction meter：Palm
25 parts of wax, 5 parts of diatomite, 10 parts of Tissuemat E, 3 parts of silicon Acrylote fluororesin, 0.5 part of essence, 0.5 part of polyethylene oxide, receive
1 part of mica powder of rice, 0.8 part of anti-UV agent, 6 parts of emulsifying agent, 18 parts of solvent naphtha, 2 parts of turpentine oil, 2 parts of montanin wax, 50 parts of water.
The preparation method of the present embodiment, includes the following steps：According to mass fraction, by palm wax, Tissuemat E, montanin wax
Be ground to it is powdered, after be heated to melting, melt after under 240rpm stir heating, when temperature reaches 80 DEG C, add solvent
Oil and turpentine oil, continue to stir under 675rpm, after sequentially add diatomite, silicon Acrylote fluororesin, add when being warming up to 95 DEG C
Enter polyethylene oxide, nano mica powder, continue to stir, reduce rotating speed to 350rpm, essence and anti-UV are added when being cooled to 45 DEG C
Agent, reduces rotating speed to 350rpm, sequentially adds emulsifying agent and 75 DEG C of water is emulsified, stirred under 250rpm, emulsified
80min, up to the strong glazing car wax of electrical insulating property.
Embodiment two
A kind of strong glazing car wax of electrical insulating property of the invention, including the following raw material according to mass fraction meter：Palm
20 parts of wax, 3 parts of diatomite, 6 parts of Tissuemat E, 2 parts of silicon Acrylote fluororesin, 0.3 part of essence, polyethylene oxide 0.3 part, nanometer
0.5 part of mica powder, 0.5 part of anti-UV agent, 5 parts of emulsifying agent, 15 parts of solvent naphtha, 1 part of turpentine oil, 1.5 parts of montanin wax, 30 parts of water.
The preparation method of the present embodiment, includes the following steps：According to mass fraction, by palm wax, Tissuemat E, montanin wax
Be ground to it is powdered, after be heated to melting, melt after under 200rpm stir heating, when temperature reaches 75 DEG C, add solvent
Oil and turpentine oil, continue to stir under 650rpmrpm, after sequentially add diatomite, silicon Acrylote fluororesin, when being warming up to 90 DEG C
Polyethylene oxide, nano mica powder are added, continues to stir, rotating speed is reduced to 300rpm, essence is added when being cooled to 40 DEG C and is resisted
UV agent, reduces rotating speed to 300rpm, sequentially adds emulsifying agent and 75 DEG C of water is emulsified, stirred under 200rpm, emulsified
70min, up to the strong glazing car wax of electrical insulating property.
Embodiment three
A kind of strong glazing car wax of electrical insulating property, including the following raw material according to mass fraction meter：30 parts of palm wax, silicon
8 parts of diatomaceous earth, 12 parts of Tissuemat E, 4 parts of silicon Acrylote fluororesin, 0.7 part of essence, 0.7 part of polyethylene oxide, nano mica powder
1.5 parts, 1 part of anti-UV agent, 10 parts of emulsifying agent, 25 parts of solvent naphtha, 3 parts of turpentine oil, 2.5 parts of montanin wax, 50 parts of water.
The preparation method of the present embodiment, includes the following steps：According to mass fraction, by palm wax, Tissuemat E, montanin wax
Be ground to it is powdered, after be heated to melting, melt after under 280rpm stir heating, when temperature reaches 85 DEG C, add solvent
Oil and turpentine oil, continue to stir under 700rpm, after sequentially add diatomite, silicon Acrylote fluororesin, add when being warming up to 100 DEG C
Enter polyethylene oxide, nano mica powder, continue to stir, reduce rotating speed to 400rpm, essence and anti-UV are added when being cooled to 50 DEG C
Agent, reduces rotating speed to 400rpm, sequentially adds emulsifying agent and 75 DEG C of water is emulsified, stirred under 300rpm, emulsified
85min, up to the strong glazing car wax of electrical insulating property.
In use, first that automobile washing is clean, then with cock skin cloth then the vehicle body wiped clean of full car is dipped in sponge
Taking small part and wiping polishing machine can be used to be polished after full car, 15 minutes.It is very convenient, save expense.
The above described is only a preferred embodiment of the present invention, any person skilled in the art is not departing from
In the range of technical solution of the present invention, the technical spirit according to the present invention is to any simple modification made for any of the above embodiments, equivalent
Change and modification, in the range of still falling within technical solution of the present invention.
Claims (3)
1. the strong glazing car wax of a kind of electrical insulating property, it is characterised in that including the following raw material according to mass fraction meter：Palm
25 parts of wax, 5 parts of diatomite, 10 parts of Tissuemat E, 3 parts of silicon Acrylote fluororesin, 0.5 part of essence, 0.5 part of polyethylene oxide, receive
1 part of mica powder of rice, 0.8 part of anti-UV agent, 6 parts of emulsifying agent, 18 parts of solvent naphtha, 2 parts of turpentine oil, 2 parts of montanin wax, 50 parts of water.
2. the preparation method of the strong glazing car wax of electrical insulating property according to claim 1, it is characterised in that including as follows
Step：According to mass fraction, palm wax, Tissuemat E, montanin wax are ground to it is powdered, after be heated to melting, melt after
Heating is stirred under 200-280rpm, when temperature reaches 75 DEG C -85 DEG C, solvent naphtha and turpentine oil are added, in 650rpm-700rpm
Under continue to stir, after sequentially add diatomite, silicon Acrylote fluororesin, added when being warming up to 90 DEG C -100 DEG C polyethylene oxide,
Nano mica powder, continues to stir, and reduces rotating speed to 300-400rpm, essence and anti-UV agent, drop are added when being cooled to 40 DEG C -50 DEG C
The slow-speed of revolution sequentially adds emulsifying agent and 75 DEG C of water is emulsified, stirred under 200-300rpm, emulsified to 300-400rpm
70-85min, up to the strong glazing car wax of electrical insulating property.
3. the preparation method of the strong glazing car wax of electrical insulating property according to claim 2, it is characterised in that including as follows
Step：According to mass fraction, palm wax, Tissuemat E, montanin wax are ground to it is powdered, after be heated to melting, melt after
Heating is stirred under 240rpm, when temperature reaches 80 DEG C, solvent naphtha and turpentine oil is added, continues to stir under 675rpm, after according to
Secondary addition diatomite, silicon Acrylote fluororesin, add polyethylene oxide, nano mica powder when being warming up to 95 DEG C, continue to stir, drop
The slow-speed of revolution adds essence and anti-UV agent to 350rpm when being cooled to 45 DEG C, reduces rotating speed to 350rpm, sequentially add emulsifying agent and
75 DEG C of water is emulsified, and is stirred under 250rpm, 80min is emulsified, up to the strong glazing car wax of electrical insulating property.