CN107984828A - 复合卷材及其制备方法 - Google Patents
复合卷材及其制备方法 Download PDFInfo
- Publication number
- CN107984828A CN107984828A CN201711208647.3A CN201711208647A CN107984828A CN 107984828 A CN107984828 A CN 107984828A CN 201711208647 A CN201711208647 A CN 201711208647A CN 107984828 A CN107984828 A CN 107984828A
- Authority
- CN
- China
- Prior art keywords
- layer
- asphalt
- parts
- composite sheet
- sheet material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了复合卷材,以玻纤毡或聚酯毡为增强体,增强体上面涂覆改性沥青层,改性沥青层上表面覆矿物颗粒层,增强体下面涂覆热塑性聚烯烃层;改性沥青胶料层设置在上覆面层和中间胎体层之间;所述改性沥青胶料层由以下重量份的原料组成:沥青50~62份、粉化再生橡胶粉8~10份、废胶粉15~25份、软化油1.5~2.5份。本发明的防水卷材使用寿命长,防水性能和耐老化性能、耐热性能好。
Description
技术领域
本发明属于建筑用化学材料领域,具体涉及复合卷材及其制备方法。
背景技术
自粘防水卷材是一种很有发展前景的新型防水材料。自粘卷材具有不透水性好,低温柔度适应性强,抗变形性能及自愈性好等特点,防水效果良好,而且无需热熔,冷施工,直接铺粘,既提高了施工效率,又消除了火灾隐患,受到了施工、设计与建设单位的高度赞誉。
但就目前的自粘聚合物改性沥青防水卷材来说,其耐热性不高,夏季施工出现了很多问题,在太阳暴晒下卷材表面温度可达到70℃,此时卷材熔化变软,有流淌趋势;并且隔离膜难以揭开,影响施工效率。国家标准规定耐热性要求是70℃无滑动流淌,行业中鲜有耐热性超过70℃的自粘性卷材。
发明内容
本发明要解决的技术问题是提供复合卷材及其制备方法,该卷材使用寿命长,耐高温,适合高温地域使用。
本发明提供的技术方案是提供复合卷材,以玻纤毡或聚酯毡为增强体,增强体上面涂覆改性沥青层,改性沥青层上表面覆矿物颗粒层,增强体下面涂覆热塑性聚烯烃层;
改性沥青胶料层设置在上覆面层和中间胎体层之间;所述改性沥青胶料层由以下重量份的原料组成:沥青50~62份、粉化再生橡胶粉8~10份、废胶粉15~25份、软化油1.5~2.5份。
各层的厚度分别为:增加体厚度为1.0~2.0mm、矿物颗粒层1.0~2.0mm、热塑性聚烯烃层0.6~1.5mm、改性沥青胶料层0.5~1.0mm。
所述改性沥青胶料的制作方法为:现将沥青升温至200~220℃,加入废机油搅拌均匀降温至180~190℃,再加入粉化再生橡胶粉,升温至240~250℃,加入废胶粉,保温搅拌2~3h,再加入软化油继续搅拌0.5~1h,即得改性沥青胶料。
所述沥青为石油沥青和天然湖沥青复配,天然湖沥青占沥青总量的50~100%。
石油沥青的针入度为80~60,软化点为48~55℃,沥青质的含量在15~18%。
所述天然湖沥青的软化点为95~110℃,含有33~38%的多孔矿物质,天然湖沥青中沥青质的含量为38~43%。
本发明还提供了上述复合卷材的制备方法,将各层热压复合,冷却成型,即得。
与现有技术相比,本发明具有以下有益效果:
1)本发明的复合卷材,所用的耐候性改性沥青使用的湖沥青含氮量高,分子量大,含蜡量低,含有活性多孔状的矿物质等特点,赋予沥青卷材具有优异的耐候性、性能稳定性、与矿物粒料的粘附性和优异的阻燃性能。
2)在保证价格不变的基础上,可以显著改善目前沥青卷材老化速度快,矿物粒料易脱落,使用寿命短等问题。
3)液态是由沥青与改性剂的配伍性好,具有良好的蠕变性、自愈性和粘接性,在温度为150℃时,表现出良好的施工性能,可以与基层形成良好的满粘效果,提高了施工效率,降低了高温下气体挥发对环境造成的污染,同时也降低了高温下施工作用带来的安全风险。
具体实施方式
以下具体实施例对本发明作进一步阐述,但不作为对本发明的限定。
实施例1
1)石油沥青的针入度为80,软化点为48℃,沥青质的含量在15%。天然湖沥青的软化点为95℃,含有33%的多孔矿物质,天然湖沥青中沥青质的含量为38%。将石油沥青和天然湖沥青复配,天然湖沥青占沥青总量的50%;
2)所述改性沥青胶料层由以下重量份的原料组成:上述复配沥青50份、粉化再生橡胶粉8份、废胶粉15份、软化油1.5份。
3)先将上述复配沥青升温至200℃,加入废机油搅拌均匀降温至180℃,再加入粉化再生橡胶粉,升温至240℃,加入废胶粉,保温搅拌2h,再加入软化油继续搅拌0.5h,即得改性沥青胶料。
4)以玻纤毡或聚酯毡为增强体,增强体上面涂覆改性沥青层,改性沥青层上表面覆矿物颗粒层,增强体下面涂覆热塑性聚烯烃层;增加体厚度为1.0mm、矿物颗粒层1.0mm、热塑性聚烯烃层0.6mm、改性沥青胶料层0.5mm,即为防水卷材。
实施例2
1)天然湖沥青的软化点为110℃,含有38%的多孔矿物质,天然湖沥青中沥青质的含量为43%。
2)所述改性沥青胶料层由以下重量份的原料组成:天然湖沥青62份、粉化再生橡胶粉10份、废胶粉25份、软化油2.5份。
3)先将天然湖沥青升温至220℃,加入废机油搅拌均匀降温至190℃,再加入粉化再生橡胶粉,升温至250℃,加入废胶粉,保温搅拌3h,再加入软化油继续搅拌1h,即得改性沥青胶料。
4)以玻纤毡或聚酯毡为增强体,增强体上面涂覆改性沥青层,改性沥青层上表面覆矿物颗粒层,增强体下面涂覆热塑性聚烯烃层;增加体厚度为2.0mm、矿物颗粒层2.0mm、热塑性聚烯烃层1.5mm、改性沥青胶料层1.0mm,即为防水卷材。
实施例3
1)石油沥青的针入度为70,软化点为50℃,沥青质的含量在16%。天然湖沥青的软化点为105℃,含有35%的多孔矿物质,天然湖沥青中沥青质的含量为40%。将石油沥青和天然湖沥青复配,天然湖沥青占沥青总量的80%;
2)所述改性沥青胶料层由以下重量份的原料组成:上述复配沥青58份、粉化再生橡胶粉9份、废胶粉20份、软化油2份。
3)先将上述复配沥青升温至210℃,加入废机油搅拌均匀降温至185℃,再加入粉化再生橡胶粉,升温至245℃,加入废胶粉,保温搅拌2.5h,再加入软化油继续搅拌0.8h,即得改性沥青胶料。
4)以玻纤毡或聚酯毡为增强体,增强体上面涂覆改性沥青层,改性沥青层上表面覆矿物颗粒层,增强体下面涂覆热塑性聚烯烃层;增加体厚度为1.5mm、矿物颗粒层1.5mm、热塑性聚烯烃层1.2mm、改性沥青胶料层0.8mm,即为防水卷材。
实施例4
1)石油沥青的针入度为80,软化点为55℃,沥青质的含量在15%。天然湖沥青的软化点为110℃,含有33%的多孔矿物质,天然湖沥青中沥青质的含量为43%。将石油沥青和天然湖沥青复配,天然湖沥青占沥青总量的50%;
2)所述改性沥青胶料层由以下重量份的原料组成:上述复配沥青62份、粉化再生橡胶粉8份、废胶粉25份、软化油1.5份。
3)先将上述复配沥青升温至220℃,加入废机油搅拌均匀降温至180℃,再加入粉化再生橡胶粉,升温至250℃,加入废胶粉,保温搅拌2h,再加入软化油继续搅拌1h,即得改性沥青胶料。
4)以玻纤毡或聚酯毡为增强体,增强体上面涂覆改性沥青层,改性沥青层上表面覆矿物颗粒层,增强体下面涂覆热塑性聚烯烃层;增加体厚度为1.0mm、矿物颗粒层2.0mm、热塑性聚烯烃层0.6mm、改性沥青胶料层1.0mm,即为防水卷材。
Claims (7)
1.复合卷材,其特征在于:以玻纤毡或聚酯毡为增强体,增强体上面涂覆改性沥青层,改性沥青层上表面覆矿物颗粒层,增强体下面涂覆热塑性聚烯烃层;
改性沥青胶料层设置在上覆面层和中间胎体层之间;所述改性沥青胶料层由以下重量份的原料组成:沥青50~62份、粉化再生橡胶粉8~10份、废胶粉15~25份、软化油1.5~2.5份。
2.根据权利要求1所述的复合卷材,其特征在于:各层的厚度分别为:增加体厚度为1.0~2.0mm、矿物颗粒层1.0~2.0mm、热塑性聚烯烃层0.6~1.5mm、改性沥青胶料层0.5~1.0mm。
3.根据权利要求1所述的复合卷材,其特征在于:所述改性沥青胶料的制作方法为:现将沥青升温至200~220℃,加入废机油搅拌均匀降温至180~190℃,再加入粉化再生橡胶粉,升温至240~250℃,加入废胶粉,保温搅拌2~3h,再加入软化油继续搅拌0.5~1h,即得改性沥青胶料。
4.根据权利要求1所述的复合卷材,其特征在于:所述沥青为石油沥青和天然湖沥青复配,天然湖沥青占沥青总量的50~100%。
5.根据权利要求4所述的复合卷材,其特征在于:石油沥青的针入度为80~60,软化点为48~55℃,沥青质的含量在15~18%。
6.根据权利要求4所述的复合卷材,其特征在于:所述天然湖沥青的软化点为95~110℃,含有33~38%的多孔矿物质,天然湖沥青中沥青质的含量为38~43%。
7.权利要求1~6中任一项所述的复合卷材的制备方法,其特征在于:将各层热压复合,冷却成型,即得。