CN107974198A - A kind of environment friendly heat resistant composite coating - Google Patents
A kind of environment friendly heat resistant composite coating Download PDFInfo
- Publication number
- CN107974198A CN107974198A CN201711327374.4A CN201711327374A CN107974198A CN 107974198 A CN107974198 A CN 107974198A CN 201711327374 A CN201711327374 A CN 201711327374A CN 107974198 A CN107974198 A CN 107974198A
- Authority
- CN
- China
- Prior art keywords
- parts
- heat resistant
- resistant composite
- composite coating
- environment friendly
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of environment friendly heat resistant composite coating, belong to coating material production technical field.The environment friendly heat resistant composite coating of the present invention is prepared by the raw material of following mass parts：60 ~ 85 parts of epoxy modified silicone resin, 9 ~ 18 parts of azodicarbonamide, 6 ~ 12 parts of spherical ceramic micro mist, 4 ~ 11 parts of dihydro aluminum phosphate, 15 parts of boron nitride, 3 10 parts of carborundum, 4 ~ 12 parts of levelling agent PW336,3 ~ 9 parts of Gluten, 2 ~ 11 parts of wetting agent PE100,3 ~ 13 parts of pigment, 40 ~ 80 parts of deionized water.The environment friendly heat resistant composite coating of the present invention, using the raw material of environment-friendly type, the material components such as boron nitride, carborundum are added in proportioning, improve the resistance to elevated temperatures of coating, its film has the characteristics that to be not easy bubble under high temperature, hardens, cracks, and the problem of be not easy chromogenic loose colour, floating.
Description
Technical field
The invention belongs to coating material production technical field, and in particular to a kind of environment friendly heat resistant composite coating.
Background technology
High-temperature resistant coating, also known as heat-resisting paint, generally refer to more than 200 DEG C, paint film is non-discolouring, does not depart from, and remains to protect
The coating of appropriate physical mechanical property is held, the particularity that making protected object can normally play a role in hot environment applies
Material.High-temperature resistant coating is generally made of heat-resistant polymer, color stuffing, solvent and auxiliary agent.With other high temperature oxidation corrosion resistance hands
The advantages that section is compared, and high-temperature resistant coating is good with its large-area construction processing performance, and cost is low, significant effect is subject to the green grass or young crops of people
Look at, have been widely used for the surface protection of high temperature applicationss.
At home in recent years, high-temperature resistant coating also becomes one of key industry with fastest developing speed in China's chemical field, it has
Have wide application, easy to use, energy-saving benefit is high, significantly puies forward many features such as commercial production levels, with expanding economy and
The progress of science and technology, coating are increasingly valued by people, and become the industry of a great industrial value and prospect.With boat
The industries such as sky, space flight, automobile and weapons develop rapidly, and high-temperature resistant coating is in space flight and aviation, petroleum and petrochemical industry, metallurgy, electric power, army
Team system and etc. field extensive use, since chimney air flue, high-temperature vapour pipeline, heat exchanger, high temperature furnace, high temperature desulfurizing are set
Standby, petroleum and petrochemical industry cracking equipment, engine components and exhaust pipe anti-corrosion, then the performance requirement for metal material is more next
It is higher, not only need the operation under the temperature in use of higher and more stringent corrosive environment.
The content of the invention
The present invention provides a kind of environment friendly heat resistant composite coating, to solve, high-temperature resistant coating persistence is poor, preparation process
The problem of excessively complicated, volatile matter can cause environmental pollution.
To solve above technical problem, the present invention uses following technical scheme：A kind of environment friendly heat resistant composite coating, by with
It is prepared by the raw material of lower mass parts：60 ~ 85 parts of epoxy modified silicone resin, 9 ~ 18 parts of azodicarbonamide, spherical ceramic micro mist 6
~ 12 parts, 4 ~ 11 parts of dihydro aluminum phosphate, 1-5 parts of boron nitride, 3-10 parts of carborundum, 4 ~ 12 parts of levelling agent PW336, Gluten 3 ~ 9
Part, 2 ~ 11 parts of wetting agent PE100,3 ~ 13 parts of pigment, 40 ~ 80 parts of deionized water.
Preferably, the mass fraction of the raw material is as follows：75 parts of epoxy modified silicone tree, 12 parts of azodicarbonamide,
8 parts of spherical ceramic micro mist, 8 parts of dihydro aluminum phosphate, 4 parts of boron nitride, 6 parts of carborundum, 4 parts of levelling agent PW336,9 parts of Gluten,
10 parts of wetting agent PE100,10 parts of pigment, 80 parts of deionized water.
Preferably, the mass fraction of the raw material is as follows：85 parts of epoxy modified silicone resin, azodicarbonamide 18
Part, 6 parts of spherical ceramic micro mist, 11 parts of dihydro aluminum phosphate, 5 parts of boron nitride, 10 parts of carborundum, 4 parts of levelling agent PW336, Gluten
39 parts, 11 parts of wetting agent PE100,13 parts of pigment, 70 parts of deionized water.
Preferably, the mass fraction of the raw material is as follows：60 parts of epoxy modified silicone resin, 9 parts of azodicarbonamide,
12 parts of spherical ceramic micro mist, 4 parts of dihydro aluminum phosphate, 1 part of boron nitride, 10 parts of carborundum, 4 parts of levelling agent PW336, Gluten 6
Part, 9 parts of wetting agent PE100,8 parts of pigment, 76 parts of deionized water.
The environment friendly heat resistant composite coating of the present invention, using the raw material of environment-friendly type, adds boron nitride, carborundum in proportioning
Deng material component, the resistance to elevated temperatures of coating is improved, its film has the characteristics that to be not easy bubble under high temperature, hardens, cracks, and not
The problem of easy chromogenic loose colour, floating.
Embodiment
Below by more specific embodiment, the present invention will be described.For ease of more fully understanding the present invention, by following
Example is illustrated, these examples belong to protection scope of the present invention, but do not limit the scope of the invention.
A kind of environment friendly heat resistant composite coating of embodiment 1, is prepared by the raw material of following mass parts：Epoxy modified silicone
75 parts of tree, 12 parts of azodicarbonamide, 8 parts of spherical ceramic micro mist, 8 parts of dihydro aluminum phosphate, 4 parts of boron nitride, 6 parts of carborundum, stream
Flat 4 parts of agent PW336,9 parts of Gluten, 10 parts of wetting agent PE100,10 parts of pigment, 80 parts of deionized water.
A kind of environment friendly heat resistant composite coating of embodiment 2, is prepared by the raw material of following mass parts：Epoxy modified silicone
85 parts of resin, 18 parts of azodicarbonamide, 6 parts of spherical ceramic micro mist, 11 parts of dihydro aluminum phosphate, 5 parts of boron nitride, carborundum 10
Part, 4 parts of levelling agent PW336,39 parts of Gluten, 11 parts of wetting agent PE100,13 parts of pigment, 70 parts of deionized water.
A kind of environment friendly heat resistant composite coating of embodiment 3, is prepared by the raw material of following mass parts：Epoxy modified silicone
60 parts of resin, 9 parts of azodicarbonamide, 12 parts of spherical ceramic micro mist, 4 parts of dihydro aluminum phosphate, 1 part of boron nitride, 10 parts of carborundum,
4 parts of levelling agent PW336,6 parts of Gluten, 9 parts of wetting agent PE100,8 parts of pigment, 76 parts of deionized water.
Claims (4)
1. a kind of environment friendly heat resistant composite coating, it is characterised in that prepared by the raw material of following mass parts：Epoxy modified silicone
60 ~ 85 parts of resin, 9 ~ 18 parts of azodicarbonamide, 6 ~ 12 parts of spherical ceramic micro mist, 4 ~ 11 parts of dihydro aluminum phosphate, boron nitride 1-5
Part, 3-10 parts of carborundum, 4 ~ 12 parts of levelling agent PW336,3 ~ 9 parts of Gluten, 2 ~ 11 parts of wetting agent PE100,3 ~ 13 parts of pigment,
40 ~ 80 parts of deionized water.
2. environment friendly heat resistant composite coating according to claim 1, it is characterised in that the mass fraction of the raw material is such as
Under：75 parts of epoxy modified silicone tree, 12 parts of azodicarbonamide, 8 parts of spherical ceramic micro mist, 8 parts of dihydro aluminum phosphate, boron nitride
4 parts, 6 parts of carborundum, 4 parts of levelling agent PW336,9 parts of Gluten, 10 parts of wetting agent PE100,10 parts of pigment, deionized water 80
Part.
3. environment friendly heat resistant composite coating according to claim 1, it is characterised in that the mass fraction of the raw material is such as
Under：85 parts of epoxy modified silicone resin, 18 parts of azodicarbonamide, 6 parts of spherical ceramic micro mist, 11 parts of dihydro aluminum phosphate, nitrogen
Change 5 parts of boron, 10 parts of carborundum, 4 parts of levelling agent PW336,39 parts of Gluten, 11 parts of wetting agent PE100,13 parts of pigment, go from
Sub- 70 parts of water.
4. environment friendly heat resistant composite coating according to claim 1, it is characterised in that the mass fraction of the raw material is such as
Under：60 parts of epoxy modified silicone resin, 9 parts of azodicarbonamide, 12 parts of spherical ceramic micro mist, 4 parts of dihydro aluminum phosphate, nitridation
1 part of boron, 10 parts of carborundum, 4 parts of levelling agent PW336,6 parts of Gluten, 9 parts of wetting agent PE100,8 parts of pigment, deionized water 76
Part.