CN107916070A - A kind of high temperature resistant composite coating - Google Patents
A kind of high temperature resistant composite coating Download PDFInfo
- Publication number
- CN107916070A CN107916070A CN201711328044.7A CN201711328044A CN107916070A CN 107916070 A CN107916070 A CN 107916070A CN 201711328044 A CN201711328044 A CN 201711328044A CN 107916070 A CN107916070 A CN 107916070A
- Authority
- CN
- China
- Prior art keywords
- parts
- high temperature
- resistant composite
- composite coating
- temperature resistant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of high temperature resistant composite coating, belong to coating material production technical field.The high temperature resistant composite coating of the present invention is prepared by the raw material of following mass parts:55 ~ 85 parts of epoxy modified silicone resin, 14 ~ 30 parts of azodicarbonamide, 9 ~ 18 parts of β types alumina nano powder, 8 ~ 17 parts of butyl glycol ether, 15 parts of boron carbide, 3 10 parts of carborundum, 2 ~ 5 parts of boron phosphide, levelling agent BYK3334 ~ 12 part, 1 ~ 4 part of wetting agent BZ100,2 ~ 6 parts of pigment, 150 ~ 300 parts of deionized water.The environment friendly heat resistant composite coating of the present invention, using the raw material of environment-friendly type, the material components such as boron nitride, carborundum are added in proportioning, improve the resistance to elevated temperatures of coating, its film has the characteristics that to be not easy bubble under high temperature, hardens, cracks, and the problem of be not easy chromogenic loose colour, floating.
Description
Technical field
The invention belongs to coating material production technical field, and in particular to a kind of high temperature resistant composite coating.
Background technology
High-temperature resistant coating, also known as heat-resisting paint, generally refer to more than 200 DEG C, paint film is non-discolouring, does not depart from, and remains to protect
The coating of appropriate physical mechanical property is held, the particularity that making protected object can normally play a role in hot environment applies
Material.High-temperature resistant coating is generally made of heat-resistant polymer, color stuffing, solvent and auxiliary agent.With other high temperature oxidation corrosion resistance hands
The advantages that section is compared, and high-temperature resistant coating is good with its large-area construction processing performance, and cost is low, significant effect is subject to the green grass or young crops of people
Look at, have been widely used for the surface protection of high temperature applicationss.
At home in recent years, high-temperature resistant coating also becomes one of key industry with fastest developing speed in China's chemical field.It has
Have wide application, easy to use, energy-saving benefit is high, significantly puies forward many features such as commercial production levels, with expanding economy and
The progress of science and technology, coating are increasingly valued by people, and become the industry of a great industrial value and prospect.With boat
The industries such as sky, space flight, automobile and weapons develop rapidly, and high-temperature resistant coating is in space flight and aviation, petroleum and petrochemical industry, metallurgy, electric power, army
Team system and etc. field extensive use, since chimney air flue, high-temperature vapour pipeline, heat exchanger, high temperature furnace, high temperature desulfurizing are set
Standby, petroleum and petrochemical industry cracking equipment, engine components and exhaust pipe anti-corrosion, then the performance requirement for metal material is more next
It is higher, not only need the operation under the temperature in use of higher and more stringent corrosive environment.With the continuous hair of industrial technology
Exhibition, high-temperature resistant coating purposes expand day by day.
The content of the invention
The present invention provides a kind of high temperature resistant composite coating.
To solve above technical problem, the present invention uses following technical scheme:A kind of high temperature resistant composite coating, by following matter
It is prepared by the raw material for measuring part:55 ~ 85 parts of epoxy modified silicone resin, 14 ~ 30 parts of azodicarbonamide, β types alumina nano powder 9
~ 18 parts, 8 ~ 17 parts of butyl glycol ether, 1-5 parts of boron carbide, 3-10 parts of carborundum, 2 ~ 5 parts of boron phosphide, levelling agent BYK333 4 ~ 12
Part, 1 ~ 4 part of wetting agent BZ100,2 ~ 6 parts of pigment, 150 ~ 300 parts of deionized water.
Preferably, the mass fraction of the raw material is as follows:68 parts of epoxy modified silicone resin, azodicarbonamide 27
Part, 10 parts of β types alumina nano powder, 17 parts of butyl glycol ether, 3 parts of boron carbide, 10 parts of carborundum, 4 parts of boron phosphide, levelling agent
10 parts of BYK333,3 parts of wetting agent BZ100,5 parts of pigment, 220 parts of deionized water.
Preferably, the mass fraction of the raw material is as follows:62 parts of epoxy modified silicone resin, azodicarbonamide 19
Part, 11 parts of β types alumina nano powder, 8 parts of butyl glycol ether, 5 parts of boron carbide, 5 parts of carborundum, 5 parts of boron phosphide, levelling agent
8 parts of BYK333,2 parts of wetting agent BZ100,6 parts of pigment, 300 parts of deionized water.
Preferably, the mass fraction of the raw material is as follows:76 parts of epoxy modified silicone resin, azodicarbonamide 25
Part, 17 parts of β types alumina nano powder, 15 parts of butyl glycol ether, 1 part of boron carbide, 8 parts of carborundum, 2 parts of boron phosphide, levelling agent
7 parts of BYK333,1 part of wetting agent BZ100,3 parts of pigment, 180 parts of deionized water.
The environment friendly heat resistant composite coating of the present invention, using the raw material of environment-friendly type, adds boron nitride, carborundum in proportioning
Deng material component, the resistance to elevated temperatures of coating is improved, its film has the characteristics that to be not easy bubble under high temperature, hardens, cracks, and not
The problem of easy chromogenic loose colour, floating.
Embodiment
Below by more specific embodiment, the present invention will be described.For ease of more fully understanding the present invention, by following
Example is illustrated, these examples belong to protection scope of the present invention, but do not limit the scope of the invention.
A kind of high temperature resistant composite coating of embodiment 1, is prepared by the raw material of following mass parts:The mass fraction of the raw material is such as
Under:68 parts of epoxy modified silicone resin, 27 parts of azodicarbonamide, 10 parts of β types alumina nano powder, butyl glycol ether 17
Part, 3 parts of boron carbide, 10 parts of carborundum, 4 parts of boron phosphide, 10 parts of levelling agent BYK333,3 parts of wetting agent BZ100,5 parts of pigment,
220 parts of deionized water.
A kind of high temperature resistant composite coating of embodiment 2, is prepared by the raw material of following mass parts:The mass fraction of the raw material is such as
Under:62 parts of epoxy modified silicone resin, 19 parts of azodicarbonamide, 11 parts of β types alumina nano powder, 8 parts of butyl glycol ether,
5 parts of boron carbide, 5 parts of carborundum, 5 parts of boron phosphide, 8 parts of levelling agent BYK333,2 parts of wetting agent BZ100,6 parts of pigment, deionization
300 parts of water.
A kind of high temperature resistant composite coating of embodiment 3, is prepared by the raw material of following mass parts:Epoxy modified silicone resin 76
Part, 25 parts of azodicarbonamide, 17 parts of β types alumina nano powder, 15 parts of butyl glycol ether, 1 part of boron carbide, 8 parts of carborundum, phosphorus
Change 2 parts of boron, 7 parts of levelling agent BYK333,1 part of wetting agent BZ100,3 parts of pigment, 1 part of deionized water 180 part, 3 parts of pigment, go
180 parts of ionized water.2 parts of boron phosphide, 7 parts of levelling agent BYK333,1 part of wetting agent BZ100,3 parts of pigment, 180 parts of deionized water.
Claims (4)
1. a kind of high temperature resistant composite coating, it is characterised in that prepared by the raw material of following mass parts:Epoxy modified silicone resin
55 ~ 85 parts, 14 ~ 30 parts of azodicarbonamide, 9 ~ 18 parts of β types alumina nano powder, 8 ~ 17 parts of butyl glycol ether, boron carbide 1-5
Part, 3-10 parts of carborundum, 2 ~ 5 parts of boron phosphide, 4 ~ 12 parts of levelling agent BYK333,1 ~ 4 part of wetting agent BZ100,2 ~ 6 parts of pigment,
150 ~ 300 parts of deionized water.
2. high temperature resistant composite coating according to claim 1, it is characterised in that the mass fraction of the raw material is as follows:Ring
68 parts of oxygen modified organic silicone resin, 27 parts of azodicarbonamide, 10 parts of β types alumina nano powder, 17 parts of butyl glycol ether, carbonization
3 parts of boron, 10 parts of carborundum, 4 parts of boron phosphide, 10 parts of levelling agent BYK333,3 parts of wetting agent BZ100,5 parts of pigment, deionized water
220 parts.
3. high temperature resistant composite coating according to claim 1, it is characterised in that the mass fraction of the raw material is as follows:Ring
62 parts of oxygen modified organic silicone resin, 19 parts of azodicarbonamide, 11 parts of β types alumina nano powder, 8 parts of butyl glycol ether, carbonization
5 parts of boron, 5 parts of carborundum, 5 parts of boron phosphide, 8 parts of levelling agent BYK333,2 parts of wetting agent BZ100,6 parts of pigment, deionized water
300 parts.
4. high temperature resistant composite coating according to claim 1, it is characterised in that the mass fraction of the raw material is as follows:Ring
76 parts of oxygen modified organic silicone resin, 25 parts of azodicarbonamide, 17 parts of β types alumina nano powder, 15 parts of butyl glycol ether, carbonization
1 part of boron, 8 parts of carborundum, 2 parts of boron phosphide, 7 parts of levelling agent BYK333,1 part of wetting agent BZ100,3 parts of pigment, deionized water
180 parts.