CN107964784A - A kind of preparation method of embroidery moisture control agent - Google Patents
A kind of preparation method of embroidery moisture control agent Download PDFInfo
- Publication number
- CN107964784A CN107964784A CN201711238709.5A CN201711238709A CN107964784A CN 107964784 A CN107964784 A CN 107964784A CN 201711238709 A CN201711238709 A CN 201711238709A CN 107964784 A CN107964784 A CN 107964784A
- Authority
- CN
- China
- Prior art keywords
- parts
- embroidery
- sodium
- control agent
- good
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
This application discloses a kind of preparation method of embroidery moisture control agent, distilled water, sodium carbonate, coagulator, hydrogen peroxide, propane diols, silicone oil, olive oil, polypropylene glycol diglycidyl ether, sodium benzoate, sodium acetate and polyethylene glycol are weighed；Preparation method is simple, moisture absorbing and sweat releasing, and anti-mold effect is good, and 4 5MPa of tensile strength, resistance to moisture is excellent, favorable anti-corrosion effect；It is glossy, increase gloss, adhesion 1 grade, good corrosion resistance, abrasion resistance 200 400 times, antistatic property is good；Of low cost, 85 95 acarids of water-wash resistance walk quickly and keep away rate 92.5 94.5%, and pliability 1mm, glossiness is good, asepsis environment-protecting；Without formaldehyde, extend embroidery service life, fast drying, fire resistance is good, and anti-microbial property is good, to Escherichia coli bacteriostasis rate 97.5 99.5%, can extensively produce and constantly replace current material.
Description
Technical field
The application belongs to embroidery material field, more particularly to a kind of preparation method of embroidery moisture control agent.
Background technology
Though the ornamental value of Yuan Dynasty's embroidery was made far away from the Song Dynasty, Song Dynasty realistic embroidery reason style is also inherited.In becoming owner of
Former first people, establish in a wide range embroidery office and sieve office throughout the country, and the aesthetic and function of embroidery, more tends to the fine arts.Buddhism theme goes out
It is existing, Tang of Sui is started from, main pattern is Bao Xianghua.Song embroiders solely still famous person's painting and calligraphy, occasionally there is figure of buddha embroidery.First generation ancestral Kublai Khan is in order to no
Determine the monic status of the Confucian school, worship and release Tibetan Buddhist, the worship Buddha at temple wind believed in a religion of Central Plains is revived.
Ming Dynasty's embroidery embroiders the most novel protrude to spill line.The bifilar counting of twisting thread of line embroidery is spilt, it is embroidered by the yarn hole of square hole yarn,
Based on geometry line, or it is equipped with the main flower of flocking.It is to receive the predecessor of line to spill line and embroider, and belongs to the north and embroiders kind, makes tranquil emperor with Ding Imperial Tomb bright filial piety of being unearthed
After spill line and embroider the imperial the ancient philosophers of preesed gold and play exemplified by female's lined dress, it with compenzine, knitting wool, twist thread, wrap stalk line, peacock plumage line, spend 6 kinds of clamp
Line, 12 kinds of skill of handling needles are made, and are the fine work of Ming Dynasty's embroidery.Also Shandong Shandong embroidery, the clothing line of category north embroidery system are embroidered and are collected line and embroider.
Sichuan embroidery, also known as " river embroidery ", refers to the Sichuan using Chengdu as representative and embroiders.The history of Sichuan embroidery is also very long, according to Jin Daichang
Jade earrings《Huayang state will》Described in, the embroidery in another name for Sichuan Province was very well-known at that time, and Sichuan embroidery is arranged side by side with Sichuan brocade, was considered as Sichuan famous product.
The pure ornamental article of Sichuan embroidery is relatively fewer, in the majority with daily necessities, and materials majority is flower, bird, insect, and fish, lucky language and traditional patterns etc. among the people,
Celebrating color is had much, it is embroidered in quilt cover, pillowcase, clothing, footwear and painted screen.Clear middle and later periods, base of the Sichuan embroidery in local tradition embroidery skill and technique
Gu embroidery and the strong point of Suzhou embroidery have been drawn on plinth, has suddenly become one of important commodity embroidery in the whole nation.Sichuan embroidery pin is carefully and neatly done, concordant light
Bright, the Silk Road is clear, is not added with writing on one's behalf, and pattern edge is cut such as knife and is generally too neat, color floridity.
Antibacterial finishing agent is many at present, can be divided mainly into three big species of inorganic, organic and natural antibacterial agent.
In the market is divided into quaternary ammonium salt, organosilicone quaternary ammonium salt, guanidine using organic antibacterial, organic antibacterial is up to
Class, halogen amine compounds, quaternary ammonium salt light yellow liquid have certain penetrating odor, and halogen class does not select generally to be used in weaving above.
And wherein security highest, be also widely used among medical treatment for guanidine.
Earliest cross embroidery is to be embroidered with the silk extracted out from silk cocoon on the fabric of animal fur, later and then by people
For decorating clothing and furniture.Cross embroidery is simple with its embroidery method, appearance noble quality is magnificent, it is exquisite it is elegant, do not have style, quickly in Europe
It is in fashion in the imperial palace of continent, becomes the first choice of royal noble's amusement and recreation, is gradually passed to later among the people.It is widely current in Europe and the U.S.
And the countries and regions such as Asia.By the development of centuries, the basic material of cross embroidery is pure continuous embroider line, special process system
The meshed fabric and design picture proof, the embroidery yarn of a variety of colors of work have all been numbered with number, every width pattern all teacher of being designed by people
Specially treated is made, every design picture proof all makes according to wire size, even very complicated pattern, as long as according to design
The position of picture proof is selected appropriate line to carry out embroidery and can be completed.Since it is the handicraft hobby of an easily-learned easily mastered, more
It is the innovation of art, thus it is popular very extensive, and the people's for being subject to all ages and classes likes.
The content of the invention
The technical problem of solution：
The application is directed to above-mentioned technical problem, there is provided a kind of preparation method of embroidery moisture control agent, solves existing thorn
Embroider with moisture control agent anti-mold effect is poor, glossiness is low and the technical problem such as moisture absorbing and sweat releasing effect difference.
Technical solution：
A kind of preparation method of embroidery moisture control agent, includes the following steps：
The first step：100 parts of distilled water, 10-30 parts of sodium carbonate, 1.5-5.5 parts of coagulator, dioxygen are weighed according to parts by weight proportioning
30-50 parts of water, 5-25 parts of propane diols, 10-30 parts of silicone oil, 15-35 parts of olive oil, 1-5 parts of polypropylene glycol diglycidyl ether, benzene
45-55 parts of 0.8-1.2 parts of sodium formate, 0.5-0.9 parts of sodium acetate and polyethylene glycol；
Second step：Sodium carbonate, sodium benzoate and sodium acetate are put into grinder and grind 10-20min, then input carries temperature
In the reaction kettle of meter, mixer and heating unit, mixer mixing is opened, is warming up to 60-70 DEG C, mixing velocity 220-
280r/min, mixes 30-50min；
3rd step：Propane diols, distilled water and hydrogen peroxide are sequentially added, is warming up to 80-90 DEG C, adjusts mixing velocity to 320-380
R/min, mixes 60-80min, adds surplus stock, is warming up to 100-120 DEG C, puts into sand mill, is sanded after mixing 1-3h
30-50min, is cooled to 30-40 DEG C, after filtering to obtain the final product.
As a preferred technical solution of the present invention：Embroidery is pressed with the raw material of moisture control agent in the first step
Parts by weight proportioning is as follows：100 parts of distilled water, 10 parts of sodium carbonate, 1.5 parts of coagulator, 30 parts of hydrogen peroxide, 5 parts of propane diols, silicone oil
10 parts, 15 parts of olive oil, 1 part of polypropylene glycol diglycidyl ether, 0.8 part of sodium benzoate, 0.5 part of sodium acetate and polyethylene glycol 45
Part.
As a preferred technical solution of the present invention：Embroidery is pressed with the raw material of moisture control agent in the first step
Parts by weight proportioning is as follows：100 parts of distilled water, 30 parts of sodium carbonate, 5.5 parts of coagulator, 50 parts of hydrogen peroxide, 25 parts of propane diols, silicon
30 parts of oil, 35 parts of olive oil, 5 parts of polypropylene glycol diglycidyl ether, 1.2 parts of sodium benzoate, 0.9 part of sodium acetate and polyethylene glycol
55 parts.
As a preferred technical solution of the present invention：Embroidery is pressed with the raw material of moisture control agent in the first step
Parts by weight proportioning is as follows：100 parts of distilled water, 20 parts of sodium carbonate, 3.5 parts of coagulator, 40 parts of hydrogen peroxide, 15 parts of propane diols, silicon
20 parts of oil, 25 parts of olive oil, 3 parts of polypropylene glycol diglycidyl ether, 1 part of sodium benzoate, 0.7 part of sodium acetate and polyethylene glycol 50
Part.
As a preferred technical solution of the present invention：The coagulator uses ammonium sulfate.
Beneficial effect：
A kind of preparation method of embroidery moisture control agent of the present invention uses above technical scheme and prior art phase
Than having following technique effect：1st, preparation method is simple, moisture absorbing and sweat releasing, and anti-mold effect is good, tensile strength 4-5MPa, resistance to moisture
Excellent, the favorable anti-corrosion effect of property；2nd, it is glossy, increase gloss, adhesion 1 grade, good corrosion resistance, abrasion resistance 200-400 times, resists quiet
Good electrical property；3rd, of low cost, 85-95 acarid of water-wash resistance walks quickly and keeps away rate 92.5-94.5%, and pliability 1mm, glossiness is good, nothing
Poison ring is protected；4th, without formaldehyde, embroidery service life is extended, fast drying, fire resistance is good, and anti-microbial property is good, and Escherichia coli are pressed down
Bacterium rate 97.5-99.5%, can extensively produce and constantly replace current material.
Embodiment
Embodiment 1:
100 parts of distilled water, 10 parts of sodium carbonate, 1.5 parts of ammonium sulfate, 30 parts of hydrogen peroxide, propane diols 5 are weighed according to parts by weight proportioning
Part, 10 parts of silicone oil, 15 parts of olive oil, 1 part of polypropylene glycol diglycidyl ether, 0.8 part of sodium benzoate, 0.5 part of sodium acetate and poly-
45 parts of ethylene glycol.
Sodium carbonate, sodium benzoate and sodium acetate are put into grinder and grind 10min, then input carries thermometer, stirs
In the reaction kettle for mixing machine and heating unit, mixer mixing is opened, is warming up to 60 DEG C, mixing velocity 220r/min, mixing
30min。
Propane diols, distilled water and hydrogen peroxide are sequentially added, is warming up to 80 DEG C, adjusts mixing velocity to 320 r/min, mixing
60min, adds surplus stock, is warming up to 100 DEG C, is put into after mixing 1h in sand mill, 30min is sanded, and is cooled to 30 DEG C, filtering
Afterwards to obtain the final product.
Preparation method is simple, moisture absorbing and sweat releasing, and anti-mold effect is good, and tensile strength 4MPa, resistance to moisture is excellent, anti-corrosion effect
It is good；It is glossy, increase gloss, adhesion 1 grade, good corrosion resistance, abrasion resistance 200 times, antistatic property is good；It is of low cost, it is resistance to
85 acarids of washing property walk quickly and keep away rate 92.5%, and pliability 1mm, glossiness is good, asepsis environment-protecting；Without formaldehyde, extend embroidery and use the longevity
Life, fast drying, fire resistance is good, and anti-microbial property is good, to Escherichia coli bacteriostasis rate 97.5%, can extensively produce and constantly replace
Current material.
Embodiment 2:
100 parts of distilled water, 30 parts of sodium carbonate, 5.5 parts of ammonium sulfate, 50 parts of hydrogen peroxide, propane diols are weighed according to parts by weight proportioning
25 parts, 30 parts of silicone oil, 35 parts of olive oil, 5 parts of polypropylene glycol diglycidyl ether, 1.2 parts of sodium benzoate, 0.9 part of sodium acetate and
55 parts of polyethylene glycol.
Sodium carbonate, sodium benzoate and sodium acetate are put into grinder and grind 20min, then input carries thermometer, stirs
In the reaction kettle for mixing machine and heating unit, mixer mixing is opened, is warming up to 70 DEG C, mixing velocity 280r/min, mixing
50min。
Propane diols, distilled water and hydrogen peroxide are sequentially added, is warming up to 90 DEG C, adjusts mixing velocity to 380 r/min, mixing
80min, adds surplus stock, is warming up to 120 DEG C, is put into after mixing 3h in sand mill, 50min is sanded, and is cooled to 40 DEG C, filtering
Afterwards to obtain the final product.
Preparation method is simple, moisture absorbing and sweat releasing, and anti-mold effect is good, and tensile strength 4.5MPa, resistance to moisture is excellent, anti-corrosion effect
It is good；It is glossy, increase gloss, adhesion 1 grade, good corrosion resistance, abrasion resistance 300 times, antistatic property is good；It is of low cost, it is resistance to
90 acarids of washing property walk quickly and keep away rate 93.5%, and pliability 1mm, glossiness is good, asepsis environment-protecting；Without formaldehyde, extend embroidery and use the longevity
Life, fast drying, fire resistance is good, and anti-microbial property is good, to Escherichia coli bacteriostasis rate 98.5%, can extensively produce and constantly replace
Current material.
Embodiment 3:
100 parts of distilled water, 20 parts of sodium carbonate, 3.5 parts of ammonium sulfate, 40 parts of hydrogen peroxide, propane diols are weighed according to parts by weight proportioning
15 parts, 20 parts of silicone oil, 25 parts of olive oil, 3 parts of polypropylene glycol diglycidyl ether, 1 part of sodium benzoate, 0.7 part of sodium acetate and poly-
50 parts of ethylene glycol.
Sodium carbonate, sodium benzoate and sodium acetate are put into grinder and grind 15min, then input carries thermometer, stirs
In the reaction kettle for mixing machine and heating unit, mixer mixing is opened, is warming up to 65 DEG C, mixing velocity 250r/min, mixing
40min。
Propane diols, distilled water and hydrogen peroxide are sequentially added, is warming up to 85 DEG C, adjusts mixing velocity to 350 r/min, mixing
70min, adds surplus stock, is warming up to 110 DEG C, is put into after mixing 2h in sand mill, 40min is sanded, and is cooled to 35 DEG C, filtering
Afterwards to obtain the final product.
Preparation method is simple, moisture absorbing and sweat releasing, and anti-mold effect is good, and tensile strength 5MPa, resistance to moisture is excellent, anti-corrosion effect
It is good；It is glossy, increase gloss, adhesion 1 grade, good corrosion resistance, abrasion resistance 400 times, antistatic property is good；It is of low cost, it is resistance to
95 acarids of washing property walk quickly and keep away rate 94.5%, and pliability 1mm, glossiness is good, asepsis environment-protecting；Without formaldehyde, extend embroidery and use the longevity
Life, fast drying, fire resistance is good, and anti-microbial property is good, to Escherichia coli bacteriostasis rate 99.5%, can extensively produce and constantly replace
Current material.
Composition all components in above example can be commercially available.
The above embodiments are merely intended to illustrate the present invention rather than to limit it, therefore with the present invention's
Any change in claims suitable implication and scope, should be construed as being included in the scope of the claims.
Claims (5)
1. a kind of preparation method of embroidery moisture control agent, it is characterised in that include the following steps：
The first step：100 parts of distilled water, 10-30 parts of sodium carbonate, 1.5-5.5 parts of coagulator, dioxygen are weighed according to parts by weight proportioning
30-50 parts of water, 5-25 parts of propane diols, 10-30 parts of silicone oil, 15-35 parts of olive oil, 1-5 parts of polypropylene glycol diglycidyl ether, benzene
45-55 parts of 0.8-1.2 parts of sodium formate, 0.5-0.9 parts of sodium acetate and polyethylene glycol；
Second step：Sodium carbonate, sodium benzoate and sodium acetate are put into grinder and grind 10-20min, then input carries temperature
In the reaction kettle of meter, mixer and heating unit, mixer mixing is opened, is warming up to 60-70 DEG C, mixing velocity 220-
280r/min, mixes 30-50min；
3rd step：Propane diols, distilled water and hydrogen peroxide are sequentially added, is warming up to 80-90 DEG C, adjusts mixing velocity to 320-380
R/min, mixes 60-80min, adds surplus stock, is warming up to 100-120 DEG C, puts into sand mill, is sanded after mixing 1-3h
30-50min, is cooled to 30-40 DEG C, after filtering to obtain the final product.
2. the preparation method of embroidery moisture control agent according to claim 1, it is characterised in that：The first step
The raw materials by weight portion proportioning of middle embroidery moisture control agent is as follows：100 parts of distilled water, 10 parts of sodium carbonate, coagulator
1.5 parts, 30 parts of hydrogen peroxide, 5 parts of propane diols, 10 parts of silicone oil, 15 parts of olive oil, 1 part of polypropylene glycol diglycidyl ether, benzoic acid
45 parts of 0.8 part of sodium, 0.5 part of sodium acetate and polyethylene glycol.
3. the preparation method of embroidery moisture control agent according to claim 1, it is characterised in that：The first step
The raw materials by weight portion proportioning of middle embroidery moisture control agent is as follows：100 parts of distilled water, 30 parts of sodium carbonate, coagulator
5.5 parts, 50 parts of hydrogen peroxide, 25 parts of propane diols, 30 parts of silicone oil, 35 parts of olive oil, 5 parts of polypropylene glycol diglycidyl ether, benzene first
55 parts of sour 1.2 parts of sodium, 0.9 part of sodium acetate and polyethylene glycol.
4. the preparation method of embroidery moisture control agent according to claim 1, it is characterised in that：The first step
The raw materials by weight portion proportioning of middle embroidery moisture control agent is as follows：100 parts of distilled water, 20 parts of sodium carbonate, coagulator
3.5 parts, 40 parts of hydrogen peroxide, 15 parts of propane diols, 20 parts of silicone oil, 25 parts of olive oil, 3 parts of polypropylene glycol diglycidyl ether, benzene first
50 parts of sour 1 part of sodium, 0.7 part of sodium acetate and polyethylene glycol.
5. the preparation method of embroidery moisture control agent according to claim 1, it is characterised in that：The coagulator
Using ammonium sulfate.