CN107955945A - A kind of anti-corrosion mobile phone shell metal conditioner - Google Patents
A kind of anti-corrosion mobile phone shell metal conditioner Download PDFInfo
- Publication number
- CN107955945A CN107955945A CN201711034018.3A CN201711034018A CN107955945A CN 107955945 A CN107955945 A CN 107955945A CN 201711034018 A CN201711034018 A CN 201711034018A CN 107955945 A CN107955945 A CN 107955945A
- Authority
- CN
- China
- Prior art keywords
- parts
- mobile phone
- phone shell
- corrosion
- metal conditioner
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
A kind of anti-corrosion mobile phone shell metal conditioner, it is characterized in that, including each component of following parts by weight is prepared：2 12 parts of castor oil, 5 10 parts of paraffin, 26 parts of diphenylamines, 10 25 parts of polyvinyl alcohol, 16 parts of triterpene soap base, 28 parts of terephthalic acid (TPA), 0.5 3 parts of Chinese holly edge acid sodium, 2 10 parts of metallic zinc, 3 15 parts of chitosan, 5 17 parts of aluminium oxide, 19 parts of sodium pyrophosphate, 5 15 parts of deionized water.Mobile phone metal-back surface conditioning agent produced by the present invention, for example slim degree of cell phone appearance fineness, cruel degree of dazzling etc. can be improved, metallic mobile phone shell after applying the present invention has the advantages that texture is good, intensity is high, in wear-resisting property, oxidation resistance, antiseptic and rustproof etc., occupies absolute predominance.Cost of the present invention is low, safe to use, environmentally safe, is conducive to promote the use of well.
Description
Technical field
The invention belongs to field of metal surface treatment technology, specifically, is related to a kind of anti-corrosion mobile phone shell metal surface
Inorganic agent.
Background technology
Metal conditioner refers to the general name for the chemical agent that various processing are carried out to metal surface.Metal is at processing, place
Different degrees of oxidation, corrosion etc. often occur during reason and use, reduces the use longevity of metal material or hardware
Life, therefore, it is necessary to handle metal surface, increases its anti-oxidant, erosion-resisting ability, prolongs the service life.Application is
The common technology of Treatment of Metal Surface, phosphatization can produce substantial amounts of phosphorus-containing wastewater in coating process, and need in strong acid or
Carried out under strong alkaline condition, the health and environment to people cause greatly to endanger.
As the requirement of cell phone appearance fineness is higher and higher, such as slim degree, cruel degree of dazzling, metallic mobile phone shell is in mobile phone
Apparent use is also more and more.Metallic mobile phone shell has the advantages that texture is good, intensity is high, but it there are wearability
Can be poor, oxidation resistance is weak, easy corrosion the problems such as, therefore it is commercially difficult to occupy advantage.Therefore, it is badly in need of a kind of to ring
Border is pollution-free, does not damage human body health, abrasion-proof corrosion-proof, the good mobile phone shell metal conditioner of oxidation resistance.
The content of the invention
The present invention is in view of the above shortcomings of the prior art, there is provided a kind of anti-corrosion mobile phone shell metal conditioner.
The technical scheme is that：A kind of anti-corrosion mobile phone shell metal conditioner, it is characterized in that, including it is following heavy
The each component of amount part is prepared：2-12 parts of castor oil, 5-10 parts of paraffin, 2-6 parts of diphenylamines, 10-25 parts of polyvinyl alcohol, triterpene
1-6 parts of soap base, 2-8 parts of terephthalic acid (TPA), 0.5-3 parts of Chinese holly edge acid sodium, 2-10 parts of metallic zinc, 3-15 parts of chitosan, aluminium oxide 5-
17 parts, 1-9 parts of sodium pyrophosphate, 5-15 parts of deionized water.
The polyvinyl alcohol is 15-20 parts.
The Chinese holly edge acid sodium is 1-1.5 parts.
Described terephthalic acid (TPA) 4-6 parts.
Mobile phone metal-back surface conditioning agent produced by the present invention, can improve cell phone appearance fineness for example slim degree, extremely degree of dazzling
Deng, metallic mobile phone shell after applying the present invention has the advantages that texture is good, intensity is high, wear-resisting property, oxidation resistance,
It is antiseptic and rustproof etc., occupy absolute predominance.Cost of the present invention is low, safe to use, environmentally safe, is conducive to push away well
It is wide to use.
Embodiment
Embodiment 1
A kind of anti-corrosion mobile phone shell metal conditioner, including each component of following parts by weight are prepared：Castor oil 2-12
Part, 5-10 parts of paraffin, 2-6 parts of diphenylamines, 10-25 parts of polyvinyl alcohol, 1-6 parts of triterpene soap base, 2-8 parts of terephthalic acid (TPA), Chinese holly edge
Sour sodium 0.5-3 parts, 2-10 parts of metallic zinc, 3-15 parts of chitosan, 5-17 parts of aluminium oxide, 1-9 parts of sodium pyrophosphate, deionized water 5-15
Part.
Embodiment 2
A kind of anti-corrosion mobile phone shell metal conditioner, including each component of following parts by weight are prepared：2 parts of castor oil,
5 parts of paraffin, 2 parts of diphenylamines, 10 parts of polyvinyl alcohol, 1 part of triterpene soap base, 2 parts of terephthalic acid (TPA), 0.5 part of Chinese holly edge acid sodium, metallic zinc
2 parts, 3 parts of chitosan, 5 parts of aluminium oxide, 1 part of sodium pyrophosphate, 5 parts of deionized water.
Embodiment 3
A kind of anti-corrosion mobile phone shell metal conditioner, including each component of following parts by weight are prepared：12 parts of castor oil,
10 parts of paraffin, 6 parts of diphenylamines, 25 parts of polyvinyl alcohol, 6 parts of triterpene soap base, 8 parts of terephthalic acid (TPA), 3 parts of Chinese holly edge acid sodium, metallic zinc
10 parts, 15 parts of chitosan, 17 parts of aluminium oxide, 9 parts of sodium pyrophosphate, 15 parts of deionized water.
Embodiment 4
A kind of anti-corrosion mobile phone shell metal conditioner, including each component of following parts by weight are prepared：5 parts of castor oil,
6 parts of paraffin, 4 parts of diphenylamines, 12 parts of polyvinyl alcohol, 5 parts of triterpene soap base, 2 parts of terephthalic acid (TPA), 1 part of Chinese holly edge acid sodium, metallic zinc 5
Part, 5 parts of chitosan, 12 parts of aluminium oxide, 5 parts of sodium pyrophosphate, 9 parts of deionized water.
Embodiment 5
A kind of anti-corrosion mobile phone shell metal conditioner, including each component of following parts by weight are prepared：3 parts of castor oil,
6 parts of paraffin, 3 parts of diphenylamines, 15 parts of polyvinyl alcohol, 2 parts of triterpene soap base, 2 parts of terephthalic acid (TPA), 1.5 parts of Chinese holly edge acid sodium, metallic zinc
6 parts, 8 parts of chitosan, 12 parts of aluminium oxide, 3 parts of sodium pyrophosphate, 8 parts of deionized water.
Claims (4)
1. a kind of anti-corrosion mobile phone shell metal conditioner, it is characterized in that, including each component of following parts by weight is prepared：
2-12 parts of castor oil, 5-10 parts of paraffin, 2-6 parts of diphenylamines, 10-25 parts of polyvinyl alcohol, 1-6 parts of triterpene soap base, terephthalic acid (TPA)
2-8 parts, 0.5-3 parts of Chinese holly edge acid sodium, 2-10 parts of metallic zinc, 3-15 parts of chitosan, 5-17 parts of aluminium oxide, 1-9 parts of sodium pyrophosphate, go
5-15 parts of ionized water.
2. a kind of anti-corrosion mobile phone shell metal conditioner according to claim 1, it is characterized in that, the polyvinyl alcohol
For 15-20 parts.
3. a kind of anti-corrosion mobile phone shell metal conditioner according to claim 1, it is characterized in that, the Chinese holly edge acid sodium
For 1-1.5 parts.
4. a kind of anti-corrosion mobile phone shell metal conditioner according to claim 1, it is characterized in that, the terephthaldehyde
It is 4-6 parts sour.