CN107938384A - A kind of flame retardant nonwoven fabric - Google Patents

A kind of flame retardant nonwoven fabric Download PDF

Info

Publication number
CN107938384A
CN107938384A CN201711124436.1A CN201711124436A CN107938384A CN 107938384 A CN107938384 A CN 107938384A CN 201711124436 A CN201711124436 A CN 201711124436A CN 107938384 A CN107938384 A CN 107938384A
Authority
CN
China
Prior art keywords
weight
parts
fibre
flame retardant
base fabric
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201711124436.1A
Other languages
Chinese (zh)
Inventor
黄�俊
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Huzhou Tai Xin Non-Woven Fabric Co Ltd
Original Assignee
Huzhou Tai Xin Non-Woven Fabric Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Huzhou Tai Xin Non-Woven Fabric Co Ltd filed Critical Huzhou Tai Xin Non-Woven Fabric Co Ltd
Priority to CN201711124436.1A priority Critical patent/CN107938384A/en
Publication of CN107938384A publication Critical patent/CN107938384A/en
Withdrawn legal-status Critical Current

Abstract

The invention discloses a kind of flame retardant nonwoven fabric, carries out in the steps below：A, the polyester fiber of 120 140 parts by weight is sprayed by screw extruding, networking, and milling train flower roller is rolled into base fabric；B, takes the zinc borate mixing of the fire resistance fibre of 18 20 parts by weight, the coir fibre of 10 12 parts by weight, the nanometer pyrophillite of 50 100 parts by weight, the alginate fibre of 15 20 parts by weight, 57 parts by weight, then upper to apply base fabric, by being dried into cloth at a high speed.For the fire retardant of the specific proportioning of the present invention coated in base fabric, drying, technological process is simple and quick, and waste of material is few, can reduce production cost.

Description

A kind of flame retardant nonwoven fabric
Technical field
The present invention relates to a kind of non-woven fabrics, particularly a kind of flame retardant nonwoven fabric.
Background technology
Raw material such as polypropylene due to non-woven fabrics etc. is hydrocarbon class material, and easily burning, makes flame retardant nonwoven fabric at present Process be typically by non-woven fabrics in retardant solution after time of infusion, take out drying, long flow path and be easy to cause resistance Fire the waste of agent solution.
The content of the invention
It is an object of the present invention to provide a kind of flame retardant nonwoven fabric.The present invention has technological process short and saves cost The characteristics of.
Technical scheme：A kind of flame retardant nonwoven fabric, carries out in the steps below：
A, the polyester fiber of 120-140 parts by weight is sprayed by screw extruding, networking, and milling train flower roller is rolled into base fabric；
B, takes the fire resistance fibre of 18-20 parts by weight, the coir fibre of 10-12 parts by weight, the nanometer leaf of 50-100 parts by weight The zinc borate mixing of cured stone, the alginate fibre of 15-20 parts by weight, 5-7 parts by weight, it is then upper to apply base fabric, by being dried at a high speed Cloth.
In foregoing flame retardant nonwoven fabric, the step b, takes the fire resistance fibre of 19 parts by weight, the coconut husk of 11 parts by weight fine The zinc borate mixing of dimension, the nanometer pyrophillite of 75 parts by weight, the alginate fibre of 17 parts by weight, 6 parts by weight, it is then upper to apply base fabric, By being dried into cloth at a high speed.
In foregoing flame retardant nonwoven fabric, the drying temperature is 180-200 DEG C.
Compared with prior art, the fire retardant of the specific proportioning of the present invention is coated in base fabric, drying, technological process letter It is single quick, and waste of material is few, can reduce production cost.The fire retardant of the present invention is made of multiple fiber, strainability Good, good spinnability does not drip slurry, and tinctorial property is good, and grammes per square metre is normal, and tensile strength is high, and softness is good；And antibacterial, fire-retardant, waterproof Effect is good.
Embodiment
With reference to embodiment, the present invention is further illustrated, but is not intended as the foundation limited the present invention.
Embodiment.A kind of flame retardant nonwoven fabric, it is characterised in that carry out in the steps below：
A, the polyester fiber of 120-140 parts by weight is sprayed by screw extruding, networking, and milling train flower roller is rolled into base fabric；
B, takes the fire resistance fibre of 18-20 parts by weight, the coir fibre of 10-12 parts by weight, the nanometer leaf of 50-100 parts by weight The zinc borate mixing of cured stone, the alginate fibre of 15-20 parts by weight, 5-7 parts by weight, it is then upper to apply base fabric, by being dried at a high speed Cloth.
It is preferable to the step b, takes the fire resistance fibre of 19 parts by weight, the coir fibre of 11 parts by weight, 75 parts by weight Nanometer pyrophillite, the alginate fibres of 17 parts by weight, 6 parts by weight zinc borate mixing, it is then upper to apply base fabric, pass through and dry at a high speed Cheng Bu；The drying temperature is 180-200 DEG C.
The fire retardant of the specific proportioning of the present invention is coated in base fabric, and drying, technological process is simple and quick, and material Waste less, production cost can be reduced.The fire retardant of the present invention is made of multiple fiber, and strainability is good, and good spinnability, does not drip Slurry, tinctorial property is good, and grammes per square metre is normal, and tensile strength is high, and softness is good；And antibacterial, fire-retardant, good water-proof effect.

Claims (3)

1. a kind of flame retardant nonwoven fabric, it is characterised in that carry out in the steps below：
A, the polyester fiber of 120-140 parts by weight is sprayed by screw extruding, networking, and milling train flower roller is rolled into base fabric；
B, take the fire resistance fibre of 18-20 parts by weight, the coir fibre of 10-12 parts by weight, 50-100 parts by weight nanometer pyrophillite, The alginate fibre of 15-20 parts by weight, the zinc borate mixing of 5-7 parts by weight, it is then upper to apply base fabric, by being dried into cloth at a high speed.
2. flame retardant nonwoven fabric according to claim 1, it is characterised in that：The step b, takes the fire-retardant fibre of 19 parts by weight Dimension, the alginate fibre of the nanometer pyrophillite of the coir fibre of 11 parts by weight, 75 parts by weight, 17 parts by weight, the zinc borate of 6 parts by weight Mixing, it is then upper to apply base fabric, by being dried into cloth at a high speed.
3. flame retardant nonwoven fabric according to claim 1, it is characterised in that：The drying temperature is 180-200 DEG C.
CN201711124436.1A 2017-11-14 2017-11-14 A kind of flame retardant nonwoven fabric Withdrawn CN107938384A (en)