CN107938379A - Luggage low temperature artificial polyvinyl chloride leather of resistance to meander configuration and preparation method thereof - Google Patents
Luggage low temperature artificial polyvinyl chloride leather of resistance to meander configuration and preparation method thereof Download PDFInfo
- Publication number
- CN107938379A CN107938379A CN201711446770.9A CN201711446770A CN107938379A CN 107938379 A CN107938379 A CN 107938379A CN 201711446770 A CN201711446770 A CN 201711446770A CN 107938379 A CN107938379 A CN 107938379A
- Authority
- CN
- China
- Prior art keywords
- polyvinyl chloride
- resistance
- low temperature
- luggage
- chloride leather
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of luggage low temperature artificial polyvinyl chloride leather of resistance to meander configuration and preparation method thereof, which is made of the raw material of following mass percent:25%~35% PVC, 8%~12% PE, 8%~12% PBT, 8%~12% triethylene diamine, 8%~12% propane diols, 8%~12% lime stone, surplus are silane coupler modified clay powders.The raw material of above-mentioned mass percent is put into after being stirred 15 minutes in high-speed mixer, place into material-extruding machine and be heated to 160 DEG C, extruding sheet material after forty minutes is stopped at such a temperature, and it is fitted in the surface of cloth base, foaming processing is finally carried out, the low temperature artificial polyvinyl chloride leather of resistance to meander configuration is just made.The artificial polyvinyl chloride leather produced using the formula and preparation method of invention, has good low-temperature flex resistance energy, can effectively improve the quality of artificial polyvinyl chloride leather leatherware.
Description
Technical field
The present invention relates to a kind of artificial polyvinyl chloride leather and preparation method thereof, is specifically a kind of polyvinyl chloride for luggage
Artificial leather and preparation method thereof.
Background technology
Low-temperature flex resistance is polyvinyl chloride（PVC）One critical nature of artificial leather, low-temperature flex resistance is in very great Cheng
The quality and use scope of PVC leatherware goods can be influenced on degree.By development for many years, China's luggage with PVC artificial leather
Tremendous development is achieved, application percentages of the PVC in box material is also continuously improved.It was predicted that the year two thousand twenty, luggage will with PVC
By 3.22 hundred million square metres in 2016, improve to 6.2 hundred million square metres, growth rate nearly 100%.But tradition P VC, due to the resistance to song of low temperature
Folding endurance is poor, strongly limit the use scope of luggage PVC.Therefore, a kind of low temperature luggage of resistance to meander configuration PVC is developed, is promoted
The use scope of PVC, is of great significance.
The content of the invention
The object of the present invention is to provide a kind of luggage low temperature artificial polyvinyl chloride leather of resistance to meander configuration.
It is a further object of the present invention to provide a kind of preparation method of the luggage low temperature artificial polyvinyl chloride leather of resistance to meander configuration.
To achieve the above object, the technical solution adopted in the present invention is：
The luggage low temperature artificial polyvinyl chloride leather of resistance to meander configuration, it is made of the raw material of following mass percent:25%~35%
PVC, 8%~12% PE, 8%~12% PBT, 8%~12% triethylene diamine, 8%~12% propane diols, 8%~12%
Lime stone, surplus are silane coupler modified clay powders.
The luggage low temperature artificial polyvinyl chloride leather of resistance to meander configuration, it is characterised in that it is by following quality percentage
The raw material composition of ratio:28%~32% PVC, 9%~11% PE, 9%~11% PBT, 9%~11% triethylene diamine, 9%~
11% propane diols, 9%~11% lime stone, surplus are silane coupler modified clay powders.
The luggage low temperature artificial polyvinyl chloride leather of resistance to meander configuration, it is the raw material group by following mass percent
Into:30% PVC, 10% PE, 10% PBT, 10% triethylene diamine, 10% propane diols, 10% lime stone, surplus are silicon
The coupling agent modified clay powders of alkane.
The preparation method of the luggage low temperature artificial polyvinyl chloride leather of resistance to meander configuration is as follows：By the original of above-mentioned mass percent
After material is put into and stir 15 minutes in high-speed mixer, place into material-extruding machine and be heated to 160 DEG C, at such a temperature stop 40 minutes
Extruding sheet material afterwards, and the surface of cloth base is fitted in, foaming processing is finally carried out, the low temperature polyvinyl chloride of resistance to meander configuration people is just made
Fabricate-leather.
Beneficial effects of the present invention：The artificial polyvinyl chloride leather produced using the formula and preparation method of invention, tool
There is good low-temperature flex resistance energy, the quality of artificial polyvinyl chloride leather leatherware can be effectively improved；Compared with conventional method, profit
The artificial polyvinyl chloride leather produced with the formula and preparation method of invention, has the wider array of scope of application.
Embodiment
Embodiment 1
The luggage low temperature artificial polyvinyl chloride leather of resistance to meander configuration, it is made of the raw material of following mass percent:35% PVC,
8% PE, 8% PBT, 8% triethylene diamine, 8% propane diols, 8% lime stone, surplus are glued for silane coupler modified
Native powder.
The preparation method of the luggage low temperature artificial polyvinyl chloride leather of resistance to meander configuration is as follows：By the original of above-mentioned mass percent
After material is put into and stir 15 minutes in high-speed mixer, place into material-extruding machine and be heated to 160 DEG C, at such a temperature stop 40 minutes
Extruding sheet material afterwards, and the surface of cloth base is fitted in, foaming processing is finally carried out, the low temperature polyvinyl chloride of resistance to meander configuration people is just made
Fabricate-leather.
Embodiment 2
The luggage low temperature artificial polyvinyl chloride leather of resistance to meander configuration, it is made of the raw material of following mass percent:30% PVC,
10% PE, 10% PBT, 10% triethylene diamine, 10% propane diols, 10% lime stone, surplus are silane coupler modified
Clay powders.
The preparation method of the luggage low temperature artificial polyvinyl chloride leather of resistance to meander configuration is as follows：By the original of above-mentioned mass percent
After material is put into and stir 15 minutes in high-speed mixer, place into material-extruding machine and be heated to 160 DEG C, at such a temperature stop 40 minutes
Extruding sheet material afterwards, and the surface of cloth base is fitted in, foaming processing is finally carried out, the low temperature polyvinyl chloride of resistance to meander configuration people is just made
Fabricate-leather.
Embodiment 3
The luggage low temperature artificial polyvinyl chloride leather of resistance to meander configuration, it is made of the raw material of following mass percent:25% PVC,
12% PE, 12% PBT, 12% triethylene diamine, 12% propane diols, 12% lime stone, surplus are silane coupler modified
Clay powders.
The preparation method of the luggage low temperature artificial polyvinyl chloride leather of resistance to meander configuration is as follows：By the original of above-mentioned mass percent
After material is put into and stir 15 minutes in high-speed mixer, place into material-extruding machine and be heated to 160 DEG C, at such a temperature stop 40 minutes
Extruding sheet material afterwards, and the surface of cloth base is fitted in, foaming processing is finally carried out, the low temperature polyvinyl chloride of resistance to meander configuration people is just made
Fabricate-leather.
Embodiment 4
The luggage low temperature artificial polyvinyl chloride leather of resistance to meander configuration, it is characterised in that it is by following mass percent
Raw material forms:32% PVC, 9% PE, 9% PBT, 9% triethylene diamine, 9% propane diols, 9% lime stone, surplus are
Silane coupler modified clay powders.The preparation method of the luggage low temperature artificial polyvinyl chloride leather of resistance to meander configuration is as follows：Will be upper
The raw material for the mass percent stated is put into stirred 15 minutes in high-speed mixer after, place into material-extruding machine and be heated to 160 DEG C,
Extruding sheet material after forty minutes is stopped at this temperature, and is fitted in the surface of cloth base, finally carries out foaming processing, low temperature is just made
The artificial polyvinyl chloride leather of resistance to meander configuration.
Embodiment 5
The luggage low temperature artificial polyvinyl chloride leather of resistance to meander configuration, it is characterised in that it is by following mass percent
Raw material forms:28% PVC, 11% PE, 11% PBT, 11% triethylene diamine, 11% propane diols, 11% lime stone are remaining
Measure as silane coupler modified clay powders.
The preparation method of the luggage low temperature artificial polyvinyl chloride leather of resistance to meander configuration is as follows：By the original of above-mentioned mass percent
After material is put into and stir 15 minutes in high-speed mixer, place into material-extruding machine and be heated to 160 DEG C, at such a temperature stop 40 minutes
Extruding sheet material afterwards, and the surface of cloth base is fitted in, foaming processing is finally carried out, the low temperature polyvinyl chloride of resistance to meander configuration people is just made
Fabricate-leather.
The above is the preferred embodiment of the present invention, cannot limit the right model of the present invention with this certainly
Enclose, it is noted that for those skilled in the art, modify or wait to technical scheme
With replacing, without departure from the protection domain of technical solution of the present invention.
Claims (4)
1. a kind of luggage low temperature artificial polyvinyl chloride leather of resistance to meander configuration, it is characterised in that it is by following mass percent
Raw material forms:25%~35% PVC, 8%~12% PE, 8%~12% PBT, 8%~12% triethylene diamine, 8%~12%
Propane diols, 8%~12% lime stone, surplus are silane coupler modified clay powders.
2. the luggage low temperature artificial polyvinyl chloride leather of resistance to meander configuration according to claim 1, it is characterised in that it be by with
The raw material composition of lower mass percent:28%~32% PVC, 9%~11% PE, 9%~11% PBT, 9%~11% triethylene
Diamines, 9%~11% propane diols, 9%~11% lime stone, surplus are silane coupler modified clay powders.
3. the luggage low temperature artificial polyvinyl chloride leather of resistance to meander configuration according to claim 1 or 2, it is characterised in that：It is
It is made of the raw material of following mass percent:30% PVC, 10% PE, 10% PBT, 10% triethylene diamine, the third of 10%
Glycol, 10% lime stone, surplus are silane coupler modified clay powders.
4. the luggage low temperature artificial polyvinyl chloride leather of resistance to meander configuration according to claims 1 to 3, it is characterised in that：It is made
Preparation Method is as follows：Each raw material is put into by the mass percent after being stirred 15 minutes in high-speed mixer, then put
Enter and 160 DEG C are heated in material-extruding machine, stop extruding sheet material after forty minutes at such a temperature, and be fitted in the surface of cloth base, most
After carry out foaming processing, the low temperature artificial polyvinyl chloride leather of resistance to meander configuration is just made.