CN107619546A - A kind of heat resistance plastic floor and preparation method thereof - Google Patents
A kind of heat resistance plastic floor and preparation method thereof Download PDFInfo
- Publication number
- CN107619546A CN107619546A CN201610547278.XA CN201610547278A CN107619546A CN 107619546 A CN107619546 A CN 107619546A CN 201610547278 A CN201610547278 A CN 201610547278A CN 107619546 A CN107619546 A CN 107619546A
- Authority
- CN
- China
- Prior art keywords
- plastic floor
- heat resistance
- roller
- corvic
- polyphthalamide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of heat resistance plastic floor and preparation method thereof, it is made up of the raw material of following parts by weight：Corvic 45 65, polyphthalamide 20 40, cellulose acetate propionate 15 30, epoxidized linseed oil 8 16, dual polyethylene dimethyl silicone polymer 48, four basic lead sulphates 36, aluminium dihydrogen tripolyphosphate 10 15, volcanic ash 16 24, husky rope wax 58, butyl acetoxystearate 7 10, granite waste material 15 20, tri trimellitate (2 ethylhexyl) 14 22.The present invention is polymer blended using Corvic and polyphthalamide, cellulose acetate propionate, dual polyethylene dimethyl silicone polymer, butyl acetoxystearate, tri trimellitate (2 ethylhexyl) etc., and the inorganic raw materials such as aluminium dihydrogen tripolyphosphate, volcanic ash, granite waste material are filled, obtained plastic floor has hot excellent moisture-resistant, dimensional stability, chemical stability, weatherability and durability.
Description
Background technology
The present invention relates to a kind of plastic floor and preparation method thereof, and in particular to a kind of heat resistance plastic floor and its preparation
Method.
Background technology
In modern society, the kind of floor decorative material is more and more, from traditional cement mortar surface to generally slaughtering light
Terrazzo floor, then emerged in an endless stream to floor tile, granite, timber floor, new material.Wherein plastic floor is because with deadweight
The advantages that small, speed of application is fast, and impression quality is good, and color is various, and walking is comfortable, anti-skidding, is widely used in kindergarten, guest
Many fields such as shop, hospital, office buildings, house, airport, gymnasium, railway station.In recent years, it is quick with industrial technology
Development and people's living standards continue to improve, to the performance requirement more and more higher of plastic floor.But traditional plastic floor
There are still moisture-resistant it is hot poor the shortcomings that, can not meet the needs of market.
The content of the invention
For above shortcomings in the prior art, the technical problems to be solved by the invention are to provide a kind of heat resistance
Plastic floor and preparation method thereof.
The technical problems to be solved by the invention are achieved by the following technical solution：
A kind of heat resistance plastic floor, is made up of the raw material of following parts by weight：Corvic 45-65, poly- phthalyl
Amine 20-40, cellulose acetate propionate 15-30, epoxidized linseed oil 8-16, dual polyethylene dimethyl silicone polymer 4-8, four alkali formula sulphur
Lead plumbate 3-6, aluminium dihydrogen tripolyphosphate 10-15, volcanic ash 16-24, husky rope wax 5-8, butyl acetoxystearate 7-10, Hua Gang
Rock waste material 15-20, tri trimellitate (2- ethylhexyls) 14-22.
A kind of preparation method of heat resistance plastic floor, comprises the following steps：
（1）By Corvic, polyphthalamide, cellulose acetate propionate, epoxidized linseed oil, four basic lead sulphates,
Husky rope wax the mixed at high speed 8-12min at 70-80 DEG C, sequentially adds aluminium dihydrogen tripolyphosphate, volcano in high-speed mixer
Ash, granite waste material, dual polyethylene dimethyl silicone polymer, butyl acetoxystearate, tri trimellitate (2- ethyl hexyls
Ester) etc. raw material, the high-speed stirred 7-10min at 110-120 DEG C, be then transferred in cooling and stirring machine, stirring material temperature be down to 45-55
DEG C when, discharging；
（2）Compound obtained above is added in plasticator, it is thin logical 7-9 times to beat triangle bag, pulling-on piece；
（3）The sheet material for post-tensioning of plasticating is transported on tri-roll press machine and rolled, the roller temperature of three rollers is respectively from top to bottom
190-210 DEG C, 200-220 DEG C, 185-205 DEG C, the speed ratio of the second roller and the first roller is controlled in 1.09-1.17, third roll
The speed ratio of second roller is in 1.05-1.08；
（4）The trimming after the sheet material rolled is cooled to normal temperature, it is finished product to examine qualified.
Beneficial effects of the present invention：
The present invention is using Corvic and polyphthalamide, cellulose acetate propionate, dual polyethylene poly dimethyl silicon
Oxygen alkane, butyl acetoxystearate, tri trimellitate (2- ethylhexyls) etc. are polymer blended, and fill tripolyphosphate dihydro
The inorganic raw materials such as aluminium, volcanic ash, granite waste material, obtained plastic floor have hot excellent moisture-resistant, dimensional stability, change
Learn stability, weatherability and durability.
Embodiment
Embodiment 1
A kind of heat resistance plastic floor, by following weight（kg）Raw material be made：Corvic 45, polyphthalamide
20th, cellulose acetate propionate 15, epoxidized linseed oil 8, dual polyethylene dimethyl silicone polymer 4, four basic lead sulphates 3, trimerization phosphorus
Acid dihydride aluminium 10, volcanic ash 16, husky rope wax 5, butyl acetoxystearate 7, granite waste material 15, tri trimellitate (2- second
The own ester of base) 14.
A kind of preparation method of heat resistance plastic floor, comprises the following steps：
（1）By Corvic, polyphthalamide, cellulose acetate propionate, epoxidized linseed oil, four basic lead sulphates,
Husky rope wax the mixed at high speed 8-12min at 70-80 DEG C, sequentially adds aluminium dihydrogen tripolyphosphate, volcano in high-speed mixer
Ash, granite waste material, dual polyethylene dimethyl silicone polymer, butyl acetoxystearate, tri trimellitate (2- ethyl hexyls
Ester) etc. raw material, the high-speed stirred 7-10min at 110-120 DEG C, be then transferred in cooling and stirring machine, stirring material temperature be down to 45-55
DEG C when, discharging；
（2）Compound obtained above is added in plasticator, it is thin logical 7-9 times to beat triangle bag, pulling-on piece；
（3）The sheet material for post-tensioning of plasticating is transported on tri-roll press machine and rolled, the roller temperature of three rollers is respectively from top to bottom
190-210 DEG C, 200-220 DEG C, 185-205 DEG C, the speed ratio of the second roller and the first roller is controlled in 1.09-1.17, third roll
The speed ratio of second roller is in 1.05-1.08；
（4）The trimming after the sheet material rolled is cooled to normal temperature, it is finished product to examine qualified.
Embodiment 2
A kind of heat resistance plastic floor, by following weight（kg）Raw material be made：Corvic 55, polyphthalamide
30th, cellulose acetate propionate 25, epoxidized linseed oil 12, dual polyethylene dimethyl silicone polymer 6, four basic lead sulphates 4, trimerization phosphorus
Acid dihydride aluminium 12, volcanic ash 20, husky rope wax 7, butyl acetoxystearate 9, granite waste material 17, tri trimellitate (2- second
The own ester of base) 18.
Preparation method is the same as embodiment 1.
Embodiment 3
A kind of heat resistance plastic floor, by following weight（kg）Raw material be made：Corvic 65, polyphthalamide
40th, cellulose acetate propionate 30, epoxidized linseed oil 16, dual polyethylene dimethyl silicone polymer 8, four basic lead sulphates 6, trimerization phosphorus
Acid dihydride aluminium 15, volcanic ash 24, husky rope wax 8, butyl acetoxystearate 10, granite waste material 20, tri trimellitate (2- second
The own ester of base) 22.
Preparation method is the same as embodiment 1.
The performance test results of plastic floor are as shown in the table made from above-described embodiment 1-3.
Claims (2)
1. a kind of heat resistance plastic floor, it is characterised in that be made up of the raw material of following parts by weight：Corvic 45-65,
Polyphthalamide 20-40, cellulose acetate propionate 15-30, epoxidized linseed oil 8-16, dual polyethylene dimethyl silicone polymer
4-8, four basic lead sulphate 3-6, aluminium dihydrogen tripolyphosphate 10-15, volcanic ash 16-24, husky rope wax 5-8, acetoxyl group stearic acid
Butyl ester 7-10, granite waste material 15-20, tri trimellitate (2- ethylhexyls) 14-22.
2. the preparation method of heat resistance plastic floor according to claim 1, it is characterised in that comprise the following steps：
（1）By Corvic, polyphthalamide, cellulose acetate propionate, epoxidized linseed oil, four basic lead sulphates,
Husky rope wax the mixed at high speed 8-12min at 70-80 DEG C, sequentially adds aluminium dihydrogen tripolyphosphate, volcano in high-speed mixer
Ash, granite waste material, dual polyethylene dimethyl silicone polymer, butyl acetoxystearate, tri trimellitate (2- ethyl hexyls
Ester) etc. raw material, the high-speed stirred 7-10min at 110-120 DEG C, be then transferred in cooling and stirring machine, stirring material temperature be down to 45-55
DEG C when, discharging；
（2）Compound obtained above is added in plasticator, it is thin logical 7-9 times to beat triangle bag, pulling-on piece；
（3）The sheet material for post-tensioning of plasticating is transported on tri-roll press machine and rolled, the roller temperature of three rollers is respectively from top to bottom
190-210 DEG C, 200-220 DEG C, 185-205 DEG C, the speed ratio of the second roller and the first roller is controlled in 1.09-1.17, third roll
The speed ratio of second roller is in 1.05-1.08；
（4）The trimming after the sheet material rolled is cooled to normal temperature, it is finished product to examine qualified.