CN108948572A - One kind having water proof anti-soil water bed cushion material and preparation method thereof - Google Patents
One kind having water proof anti-soil water bed cushion material and preparation method thereof Download PDFInfo
- Publication number
- CN108948572A CN108948572A CN201810557805.4A CN201810557805A CN108948572A CN 108948572 A CN108948572 A CN 108948572A CN 201810557805 A CN201810557805 A CN 201810557805A CN 108948572 A CN108948572 A CN 108948572A
- Authority
- CN
- China
- Prior art keywords
- agent
- water
- cushion material
- proof anti
- water bed
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses one kind to have water proof anti-soil water bed cushion material and preparation method thereof, it is made of with water proof anti-soil water bed cushion material Corvic, waterproofing agent, toughener, adhesive, halogen-free flame retardants, antistatic agent, anti-fouling agent, peppermint extracting solution and preservative, ingredient percentage are as follows: Corvic 50%~70%；Waterproofing agent 10%~15%.The present invention joined waterproofing agent and anti-fouling agent in formula, and waterproofing agent and anti-fouling agent are respectively by ethylene propylene diene rubber, polymer emulsion of core shell structure, polyurethane, high density polyethylene (HDPE), polypropylene fibre, quartz sand, Petropols, silicate mineral and water-soluble resin waterproofing agent and metal pyridine thioketone compound, polyurethane resin, fluorine silicon resin, silica, organosilicon levelling agent, nano silver, nano zine oxide and coalescing agent composition, the waterproofness and soil resistance of the water bed mattress of this material production can be effectively improved, it brings great convenience for the use of people.
Description
Technical field
The present invention relates to water bed mattress technical fields, specially a kind of to have water proof anti-soil water bed cushion material and its preparation side
Method.
Background technique
Sleep be health this, the healthy bedding for possessing " health, comfortable, beautiful, durable " is to obtain high quality to sleep
Key point, with being constantly progressive for material progress and technical matters, the mattress type that modern people use gradually tends to polynary
Change, mainly has: sping mattress, palm mattress, latex bed mattress, water bed mattress, pneumatic mattress, magnetic mattress etc., wherein water bed mattress is mainly tied
Structure is to fill the water bag of water to be placed among a frame, but its waterproof of existing water bed mattress and antifouling capacity are poor, is the use band of people
It is inconvenient to come, for this purpose, it is proposed that a kind of have water proof anti-soil water bed cushion material.
Summary of the invention
The purpose of the present invention is to provide one kind to have water proof anti-soil water bed cushion material and preparation method thereof, above-mentioned to solve
The problem of being proposed in background technique.
To achieve the above object, the invention provides the following technical scheme: a kind of have water proof anti-soil water bed cushion material, have
Water proof anti-soil water bed cushion material is by Corvic, waterproofing agent, toughener, adhesive, halogen-free flame retardants, antistatic agent, anti-
Dirty agent, peppermint extracting solution and preservative composition, ingredient percentage are as follows: Corvic 50%~70%；Waterproofing agent 10%
~15%；Toughener 5%~10%；Adhesive 3%~5%；Halogen-free flame retardants 3%~8%；Antistatic agent 2%~5%；It is anti-
Dirty agent 5%~8%；Peppermint extracting solution 3%~7%；Preservative 2%~4%.
Preferably, the waterproofing agent is by ethylene propylene diene rubber, polymer emulsion of core shell structure, polyurethane, high-density polyethylene
Alkene, polypropylene fibre, quartz sand, Petropols, silicate mineral and water-soluble resin waterproofing agent composition, ingredient percentage
Are as follows: ethylene propylene diene rubber 10%~15%；Polymer emulsion of core shell structure 3%~7%；Polyurethane 4%~10%；High density is poly-
Ethylene 2%~5%；Polypropylene fibre 1%~3%；Quartz sand 25%~35%；Petropols 2%~4%；Silicate mineral
Matter 50%~65%；Water-soluble resin waterproofing agent 7%~12%.
Preferably, the toughener is by EP rubbers, pentaerythritol stearate, antiaging agent, polyurethane, acrylonitrile-
Butadiene-styrene copolymer, polypropylene fibre and stabilizer composition, ingredient percentage are as follows: EP rubbers 50%~65%；
Pentaerythritol stearate 8%~15%；Antiaging agent 3%~7%；Polyurethane 2%~5%；Acrylonitrile-butadiene-benzene second
Alkene copolymer 25%~35%, polypropylene fibre 5%~9%；Stabilizer 1%~4%.
Preferably, the adhesive be high temperature resistant cement, and high temperature resistant cement preparation process the following steps are included:
1., add water in reaction kettle, and heat water to 80~90 DEG C, then natural terpene resins, stone are added into reaction kettle
Oleoresin and naphthenic oil, and continue 15~30min of stirring；
2., reaction kettle is heated to 110~130 DEG C, then into reaction kettle be added natural rubber, petroleum SBS rubber, rubber promote
Agent, sodium benzoate and viscosity- increasing agent, and continue 20~40min of stirring；
3., antioxidant, hydroxymethyl cellulose, nanometer calcium carbonate and latex powder be added in mixed liquor 2., and continue stirring until
Mixeding liquid temperature is identical as room temperature in reaction kettle.
Preferably, the halogen-free flame retardants is by guanyl-urea-phosphate, water-soluble poly ammonium phosphate, core-shell structure polymer cream
Liquid, ammonium molybdate, silica solution, sodium pyrophosphate and expanded perlite composition, ingredient percentage are as follows: guanyl-urea-phosphate 25%~
35%；Water-soluble poly ammonium phosphate 10%~15%；Polymer emulsion of core shell structure 10%~15%；Ammonium molybdate 3%~7%；Silicon
Colloidal sol 20%~30%；Sodium pyrophosphate 1%~3%；Expanded perlite 7%~15%.
Preferably, the antistatic agent is by epoxy resin, vulcanizing activator, water-soluble poly ammonium phosphate, fatty alcohol polyoxy second
Alkene ether, phenyl salicylate, ethoxylated alkylamine, softening agent and tetrabutyl titanate composition, ingredient percentage are as follows: epoxy resin
50~65%；Vulcanizing activator 5~10%；Water-soluble poly ammonium phosphate 8~15%；Fatty alcohol polyoxyethylene ether 3~7%；Bigcatkin willow
Acid phenenyl ester 2~5%；Ethoxylated alkylamine 15~25%；Softening agent 10~15%；Tetrabutyl titanate 4~6%.
Preferably, the anti-fouling agent by metal pyridine thioketone compound, polyurethane resin, fluorine silicon resin, silica,
Organosilicon levelling agent, nano silver, nano zine oxide and coalescing agent composition, ingredient percentage are as follows: metal pyridine thioketone
Close object 70%~80%；Polyurethane resin 5%~8%；Fluorine silicon resin 10%~15%；Silica 1 %~3%；Organosilicon
Levelling agent 2%~4%；Nano silver 3%~7%；Nano zine oxide 4%~6%；Coalescing agent 2%~6%.
Preferably, the peppermint extracting solution is made of base oil, Peppermint essential oil, borneol essential oil and sweet orange oil, ingredient
Percentage are as follows: base oil 25%~35%；Peppermint essential oil 30%~40%；Borneol essential oil 20%~30%；Sweet orange oil 10%
~20%.
Preferably, preparation method includes the following steps:
A, Corvic, waterproofing agent, toughener, adhesive, halogen-free flame retardants, antistatic agent, anti-fouling agent, peppermint are extracted
Liquid and preservative are added to high-speed mixer mixing according to the ingredient percentage of regulation；
B, it is added to melt blending in double screw extruder after mixing to squeeze out, and controls extruder temperature at 180~220 DEG C
In range；
C, mixture is expressed into the mold of water bed mattress, and mold is put into heat in steam box and steams 1~1.5h, steamer temperature control
System is within the scope of 100~120 DEG C；
D, demoulding, cleaning, disinfection；
E, it is packed and stored after the assay was approved.
Compared with prior art, beneficial effects of the present invention are as follows:
1, the present invention joined waterproofing agent and anti-fouling agent in formula, and waterproofing agent and anti-fouling agent respectively by ethylene propylene diene rubber,
Polymer emulsion of core shell structure, polyurethane, high density polyethylene (HDPE), polypropylene fibre, quartz sand, Petropols, silicate mineral
Matter and water-soluble resin waterproofing agent and metal pyridine thioketone compound, fluorine silicon resin, silica, have polyurethane resin
Machine silicon levelling agent, nano silver, nano zine oxide and coalescing agent composition, can effectively improve the waterproof of the water bed mattress of this material production
Property and soil resistance, bring great convenience for the use of people.
2, present invention adds halogen-free flame retardants, anti-flammability and the smoke amount in burning that this material can be effectively improved
It is small, do not generate toxic, corrosive gas, antistatic agent can reduce the electrostatic content of this water bed mattress, improve this water bed mattress sleep
Comfort level, while peppermint extracting solution can make this water bed mattress have peppermint fragrance, be conducive to alleviate human-body fatigue, improve sleep
Quality.
Detailed description of the invention
Fig. 1 is ingredient table schematic diagram of the present invention.
Specific embodiment
Following will be combined with the drawings in the embodiments of the present invention, and technical solution in the embodiment of the present invention carries out clear, complete
Site preparation description, it is clear that described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.It is based on
Embodiment in the present invention, it is obtained by those of ordinary skill in the art without making creative efforts every other
Embodiment shall fall within the protection scope of the present invention.
Referring to Fig. 1, a kind of have water proof anti-soil water bed cushion material, have water proof anti-soil water bed cushion material by polyvinyl chloride
Resin, waterproofing agent, toughener, adhesive, halogen-free flame retardants, antistatic agent, anti-fouling agent, peppermint extracting solution and preservative composition,
Its ingredient percentage are as follows: Corvic 50%~70%；Waterproofing agent 10%~15%；Toughener 5%~10%；Adhesive
3%~5%；Halogen-free flame retardants 3%~8%；Antistatic agent 2%~5%；Anti-fouling agent 5%~8%；Peppermint extracting solution 3%~
7%；Preservative 2%~4%.
Waterproofing agent is fine by ethylene propylene diene rubber, polymer emulsion of core shell structure, polyurethane, high density polyethylene (HDPE), polypropylene
Dimension, quartz sand, Petropols, silicate mineral and water-soluble resin waterproofing agent composition, ingredient percentage are as follows: EPDM
Rubber 10%~15%；Polymer emulsion of core shell structure 3%~7%；Polyurethane 4%~10%；High density polyethylene (HDPE) 2%~
5%；Polypropylene fibre 1%~3%；Quartz sand 25%~35%；Petropols 2%~4%；Silicate mineral 50%~
65%；Water-soluble resin waterproofing agent 7%~12%.
Toughener is by EP rubbers, pentaerythritol stearate, antiaging agent, polyurethane, acrylonitrile-butadiene-benzene second
Alkene copolymer, polypropylene fibre and stabilizer composition, ingredient percentage are as follows: EP rubbers 50%~65%；Pentaerythrite is hard
Resin acid ester 8%~15%；Antiaging agent 3%~7%；Polyurethane 2%~5%；Acrylonitrile-butadiene-phenylethylene copolymer
25%~35%, polypropylene fibre 5%~9%；Stabilizer 1%~4%.
Adhesive is high temperature resistant cement, and high temperature resistant cement preparation process the following steps are included:
1., add water in reaction kettle, and heat water to 80~90 DEG C, then natural terpene resins, stone are added into reaction kettle
Oleoresin and naphthenic oil, and continue 15~30min of stirring；
2., reaction kettle is heated to 110~130 DEG C, then into reaction kettle be added natural rubber, petroleum SBS rubber, rubber promote
Agent, sodium benzoate and viscosity- increasing agent, and continue 20~40min of stirring；
3., antioxidant, hydroxymethyl cellulose, nanometer calcium carbonate and latex powder be added in mixed liquor 2., and continue stirring until
Mixeding liquid temperature is identical as room temperature in reaction kettle.
Halogen-free flame retardants is by guanyl-urea-phosphate, water-soluble poly ammonium phosphate, polymer emulsion of core shell structure, ammonium molybdate, silicon
Colloidal sol, sodium pyrophosphate and expanded perlite composition, ingredient percentage are as follows: guanyl-urea-phosphate 25%~35%；Water-soluble poly
Ammonium phosphate 10%~15%；Polymer emulsion of core shell structure 10%~15%；Ammonium molybdate 3%~7%；Silica solution 20%~
30%；Sodium pyrophosphate 1%~3%；Expanded perlite 7%~15%.
Antistatic agent is by epoxy resin, vulcanizing activator, water-soluble poly ammonium phosphate, fatty alcohol polyoxyethylene ether, salicylic acid
Phenyl ester, ethoxylated alkylamine, softening agent and tetrabutyl titanate composition, ingredient percentage are as follows: epoxy resin 50~65%；Sulphur
Change activating agent 5~10%；Water-soluble poly ammonium phosphate 8~15%；Fatty alcohol polyoxyethylene ether 3~7%；Phenyl salicylate 2~
5%；Ethoxylated alkylamine 15~25%；Softening agent 10~15%；Tetrabutyl titanate 4~6%.
Anti-fouling agent is by metal pyridine thioketone compound, polyurethane resin, fluorine silicon resin, silica, organosilicon levelling
Agent, nano silver, nano zine oxide and coalescing agent composition, ingredient percentage are as follows: metal pyridine thioketone compound 70%~
80%；Polyurethane resin 5%~8%；Fluorine silicon resin 10%~15%；Silica 1 %~3%；Organosilicon levelling agent 2%~
4%；Nano silver 3%~7%；Nano zine oxide 4%~6%；Coalescing agent 2%~6%.
Peppermint extracting solution is made of base oil, Peppermint essential oil, borneol essential oil and sweet orange oil, ingredient percentage are as follows: base
Plinth oil 25%~35%；Peppermint essential oil 30%~40%；Borneol essential oil 20%~30%；Sweet orange oil 10%~20%.
Preparation method includes the following steps:
A, Corvic, waterproofing agent, toughener, adhesive, halogen-free flame retardants, antistatic agent, anti-fouling agent, peppermint are extracted
Liquid and preservative are added to high-speed mixer mixing according to the ingredient percentage of regulation；
B, it is added to melt blending in double screw extruder after mixing to squeeze out, and controls extruder temperature at 180~220 DEG C
In range；
C, mixture is expressed into the mold of water bed mattress, and mold is put into heat in steam box and steams 1~1.5h, steamer temperature control
System is within the scope of 100~120 DEG C；
D, demoulding, cleaning, disinfection；
E, it is packed and stored after the assay was approved.
In use, joined waterproofing agent and anti-fouling agent in formula, and waterproofing agent and anti-fouling agent are respectively by ethylene-propylene-diene monomer
Glue, polymer emulsion of core shell structure, polyurethane, high density polyethylene (HDPE), polypropylene fibre, quartz sand, Petropols, silicate mine
Substance and water-soluble resin waterproofing agent and metal pyridine thioketone compound, polyurethane resin, fluorine silicon resin, silica,
Organosilicon levelling agent, nano silver, nano zine oxide and coalescing agent composition, can effectively improve the anti-of the water bed mattress of this material production
Aqueous and soil resistance brings great convenience for the use of people, joined halogen-free flame retardants, can effectively improve the resistance of this material
Combustion property and burning when smoke amount is small, does not generate toxic, corrosive gas, the electrostatic that antistatic agent can reduce this water bed mattress contains
Amount improves the comfort level of this water bed mattress sleep, while peppermint extracting solution can make this water bed mattress have the fragrance of peppermint, be conducive to
Alleviate human-body fatigue, improves sleep quality.
It although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
A variety of variations, modification, replacement can be carried out to these embodiments without departing from the principles and spirit of the present invention by understanding
And modification, the scope of the present invention is defined by the appended.
Claims (9)
1. one kind has water proof anti-soil water bed cushion material, it is characterised in that: have water proof anti-soil water bed cushion material by polyvinyl chloride
Resin, waterproofing agent, toughener, adhesive, halogen-free flame retardants, antistatic agent, anti-fouling agent, peppermint extracting solution and preservative composition,
Its ingredient percentage are as follows: Corvic 50%~70%；Waterproofing agent 10%~15%；Toughener 5%~10%；Adhesive
3%~5%；Halogen-free flame retardants 3%~8%；Antistatic agent 2%~5%；Anti-fouling agent 5%~8%；Peppermint extracting solution 3%~
7%；Preservative 2%~4%.
2. according to claim 1 a kind of with water proof anti-soil water bed cushion material, it is characterised in that: the waterproofing agent is by three
First EP rubbers, polymer emulsion of core shell structure, polyurethane, high density polyethylene (HDPE), polypropylene fibre, quartz sand, Petropols,
Silicate mineral and water-soluble resin waterproofing agent composition, ingredient percentage are as follows: ethylene propylene diene rubber 10%~15%；Nucleocapsid
Structural polymer lotion 3%~7%；Polyurethane 4%~10%；High density polyethylene (HDPE) 2%~5%；Polypropylene fibre 1%~
3%；Quartz sand 25%~35%；Petropols 2%~4%；Silicate mineral 50%~65%；Water-soluble resin waterproofing agent
7%~12%.
3. according to claim 1 a kind of with water proof anti-soil water bed cushion material, it is characterised in that: the toughener is by second
Third rubber, pentaerythritol stearate, antiaging agent, polyurethane, acrylonitrile-butadiene-phenylethylene copolymer, polypropylene fibre
It is formed with stabilizer, ingredient percentage are as follows: EP rubbers 50%~65%；Pentaerythritol stearate 8%~15%；It is anti-old
Agent 3%~7%；Polyurethane 2%~5%；Acrylonitrile-butadiene-phenylethylene copolymer 25%~35%, polypropylene fibre
5%~9%；Stabilizer 1%~4%.
4. according to claim 1 a kind of with water proof anti-soil water bed cushion material, it is characterised in that: the adhesive is resistance to
High temperature glue, and high temperature resistant cement preparation process the following steps are included:
1., add water in reaction kettle, and heat water to 80~90 DEG C, then natural terpene resins, stone are added into reaction kettle
Oleoresin and naphthenic oil, and continue 15~30min of stirring；
2., reaction kettle is heated to 110~130 DEG C, then into reaction kettle be added natural rubber, petroleum SBS rubber, rubber promote
Agent, sodium benzoate and viscosity- increasing agent, and continue 20~40min of stirring；
3., antioxidant, hydroxymethyl cellulose, nanometer calcium carbonate and latex powder be added in mixed liquor 2., and continue stirring until
Mixeding liquid temperature is identical as room temperature in reaction kettle.
5. according to claim 1 a kind of with water proof anti-soil water bed cushion material, it is characterised in that: the halogen-free flame retardants
By guanyl-urea-phosphate, water-soluble poly ammonium phosphate, polymer emulsion of core shell structure, ammonium molybdate, silica solution, sodium pyrophosphate and expansion
Perlite composition, ingredient percentage are as follows: guanyl-urea-phosphate 25%~35%；Water-soluble poly ammonium phosphate 10%~15%；Core
Shell structure polymer emulsion 10%~15%；Ammonium molybdate 3%~7%；Silica solution 20%~30%；Sodium pyrophosphate 1%~3%；
Expanded perlite 7%~15%.
A kind of there is water proof anti-soil water bed cushion material 6. according to claim 1, it is characterised in that: the antistatic agent by
Epoxy resin, vulcanizing activator, water-soluble poly ammonium phosphate, fatty alcohol polyoxyethylene ether, phenyl salicylate, ethoxylated alkyl
Amine, softening agent and tetrabutyl titanate composition, ingredient percentage are as follows: epoxy resin 50~65%；Vulcanizing activator 5~10%；
Water-soluble poly ammonium phosphate 8~15%；Fatty alcohol polyoxyethylene ether 3~7%；Phenyl salicylate 2~5%；Ethoxylated alkylamine
15~25%；Softening agent 10~15%；Tetrabutyl titanate 4~6%.
7. according to claim 1 a kind of with water proof anti-soil water bed cushion material, it is characterised in that: the anti-fouling agent is by gold
Belong to pyrithione class compound, polyurethane resin, fluorine silicon resin, silica, organosilicon levelling agent, nano silver, nano oxidized
Zinc and coalescing agent composition, ingredient percentage are as follows: metal pyridine thioketone compound 70%~80%；Polyurethane resin 5%
~8%；Fluorine silicon resin 10%~15%；Silica 1 %~3%；Organosilicon levelling agent 2%~4%；Nano silver 3%~
7%；Nano zine oxide 4%~6%；Coalescing agent 2%~6%.
8. according to claim 1 a kind of with water proof anti-soil water bed cushion material, it is characterised in that: the peppermint extracting solution
It is made of base oil, Peppermint essential oil, borneol essential oil and sweet orange oil, ingredient percentage are as follows: base oil 25%~35%；Peppermint
Essential oil 30%~40%；Borneol essential oil 20%~30%；Sweet orange oil 10%~20%.
9. a kind of preparation method with water proof anti-soil water bed cushion material according to any one of claims 1 to 8, feature
Be: preparation method includes the following steps:
A, Corvic, waterproofing agent, toughener, adhesive, halogen-free flame retardants, antistatic agent, anti-fouling agent, peppermint are extracted
Liquid and preservative are added to high-speed mixer mixing according to the ingredient percentage of regulation；
B, it is added to melt blending in double screw extruder after mixing to squeeze out, and controls extruder temperature at 180~220 DEG C
In range；
C, mixture is expressed into the mold of water bed mattress, and mold is put into heat in steam box and steams 1~1.5h, steamer temperature control
System is within the scope of 100~120 DEG C；
D, demoulding, cleaning, disinfection；
E, it is packed and stored after the assay was approved.