CN107936762A - Water-base epoxy texture coating - Google Patents
Water-base epoxy texture coating Download PDFInfo
- Publication number
- CN107936762A CN107936762A CN201711186998.9A CN201711186998A CN107936762A CN 107936762 A CN107936762 A CN 107936762A CN 201711186998 A CN201711186998 A CN 201711186998A CN 107936762 A CN107936762 A CN 107936762A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- texture coating
- base epoxy
- component
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of water-base epoxy texture coating, including AB components：The raw material of component A includes by weight：60 80 parts of epoxy resin, 12 16 parts of reactive diluent GGE, 2.5 3 parts of ether acetates, 40 60 parts of deionized water, 80 90 parts of talcum powder, 60 80 parts of barium sulfate, 0.2 0.5 parts of DISPERBYK 194N；The raw material of B component includes by weight：10 18 parts of triethylene tetramine, 10 20 parts of absolute ethyl alcohol, 10 18 parts of diethylenetriamine, 0.2 0.5 parts of levelling agent, 0.2 0.7 parts of wetting dispersing agent, 0.1 0.6 parts of defoamer.The water-base epoxy texture coating of the present invention has environmental protection, wearability is good, clean mark is beautiful, chemical resistance is good, suitable for a variety of occasions.
Description
Technical field
The invention belongs to paint field, and in particular to a kind of water-base epoxy texture coating.
Background technology
Water paint is the trend of following paint development, wherein aqueous epoxide resin paint is due to it due to cheap, environmentally friendly
Excellent characteristic, be one of water paint kind with fastest developing speed, and the coating for developing aqueous wear-resistant and beauty substitutes oiliness
Wear-resistant paint has a vast market prospect.
The content of the invention
It is an object of the invention to provide a kind of water-base epoxy texture coating, has environmental protection, wearability is good, clean mark is beautiful
See, chemical resistance is good, suitable for a variety of occasions.
To achieve the above object, the present invention adopts the following technical scheme that：
A kind of water-base epoxy texture coating, including AB components：The raw material of component A includes by weight：Epoxy resin 60-80
Part, 12-16 parts of reactive diluent GGE, 2.5-3 parts of ether acetates, 40-60 parts of deionized water, 80-90 parts of talcum powder, sulfuric acid
60-80 parts of barium, 0.2-0.5 parts of DISPERBYK-194N；
The raw material of B component includes by weight：10-18 parts of triethylene tetramine, 10-20 parts of absolute ethyl alcohol, diethylenetriamine 10-
18 parts, 0.2-0.5 parts of levelling agent, 0.2-0.7 parts of wetting dispersing agent, 0.1-0.6 parts of defoamer.
Preferably, a kind of water-base epoxy texture coating, including AB components：The raw material of component A includes by weight：Epoxy
60-80 parts of resin, 12-16 parts of reactive diluent GGE, 2.5-3 parts of ether acetates, 40-60 parts of deionized water, talcum powder 80-
90 parts, 60-80 parts of barium sulfate, 0.2-0.5 parts of DISPERBYK-194N, 3-5 parts of Ludox, nm-class boron nitride aqueous dispersions 1-2
Part；
The raw material of B component includes by weight：10-18 parts of triethylene tetramine, 10-20 parts of absolute ethyl alcohol, diethylenetriamine 10-
18 parts, 0.2-0.5 parts of levelling agent, 0.2-0.7 parts of wetting dispersing agent, 0.1-0.6 parts of defoamer.
A in water-base epoxy texture coating:The weight ratio of B component is 3:1.
Levelling agent in B component is BYK-3455, defoamer BYK-023, wetting dispersing agent BYK-349.
The remarkable advantage of the present invention：
The addition of Nano silica sol can make film coated surface form complementary (as concavo-convex alternate) of geometries in the range of nanoscale
Interfacial structure, it is possible to increase the wearability of coating, chemical resistance, slow down photooxidation, extend and apply membrane lifetime.But Ludox is forming a film
During volume contraction it is larger, film is easy to crack, influences film using effect and service life.Nm-class boron nitride aqueous dispersions can be with
Ludox forms hydrogen bond, effectively suppresses volume contraction and cracking in its film forming procedure, Ludox and nm-class boron nitride moisture are dissipated
Liquid is used in conjunction with forming a film in film coated surface, significantly improves the weatherability, wearability, chemical resistance of coating, extends and applies membrane lifetime.
Embodiment
In order to make content of the present invention easily facilitate understanding, with reference to embodiment to of the present invention
Technical solution is described further, but the present invention is not limited only to this.
Embodiment 1
A kind of water-base epoxy texture coating, water-base epoxy texture coating include AB components：The raw material of component A wraps by weight
Include：Epoxy resin（E-44）70 parts, 14 parts of reactive diluent GGE, 2.8 parts of ether acetates, 50 parts of deionized water, talcum powder
85 parts, 70 parts of barium sulfate, 0.3 part of DISPERBYK-194N；
The raw material of B component includes by weight：15 parts of triethylene tetramine, 15 parts of absolute ethyl alcohol, 16 parts of diethylenetriamine, levelling
0.3 part of agent, 0.5 part of wetting dispersing agent, 0.4 part of defoamer.
A in water-base epoxy texture coating:The weight ratio of B component is 3:1.
Levelling agent in B component is BYK-3455, defoamer BYK-023, wetting dispersing agent BYK-349.
Embodiment 2
A kind of water-base epoxy texture coating, water-base epoxy texture coating include AB components：The raw material of component A wraps by weight
Include：Epoxy resin（E-44）60 parts, 12 parts of reactive diluent GGE, 2.5 parts of ether acetates, 40 parts of deionized water, talcum powder
80 parts, 60 parts of barium sulfate, 0.2 part of DISPERBYK-194N, 3 parts of Ludox, 1 part of nm-class boron nitride aqueous dispersions；
The raw material of B component includes by weight：10 parts of triethylene tetramine, 10 parts of absolute ethyl alcohol, 10 parts of diethylenetriamine, levelling
0.2 part of agent, 0.2 part of wetting dispersing agent, 0.1 part of defoamer.
A in water-base epoxy texture coating:The weight ratio of B component is 3:1.
Levelling agent in B component is BYK-3455, defoamer BYK-023, wetting dispersing agent BYK-349.
Embodiment 3
A kind of water-base epoxy texture coating, water-base epoxy texture coating include AB components：The raw material of component A wraps by weight
Include：Epoxy resin（E-44）80 parts, 16 parts of reactive diluent GGE, 3 parts of ether acetates, 60 parts of deionized water, talcum powder 90
Part, 80 parts of barium sulfate, 0.5 part of DISPERBYK-194N, 5 parts of Ludox, 2 parts of nm-class boron nitride aqueous dispersions；
The raw material of B component includes by weight：18 parts of triethylene tetramine, 20 parts of absolute ethyl alcohol, 18 parts of diethylenetriamine, levelling
0.5 part of agent, 0.7 part of wetting dispersing agent, 0.6 part of defoamer.
A in water-base epoxy texture coating:The weight ratio of B component is 3:1.
Levelling agent in B component is BYK-3455, defoamer BYK-023, wetting dispersing agent BYK-349.
Water-base epoxy texture coating obtained by embodiment 1-3 is tested for the property, the result is shown in table 1.
1 the performance test results of table
The foregoing is merely presently preferred embodiments of the present invention, all equivalent changes done according to scope of the present invention patent are with repairing
Decorations, should all belong to the covering scope of the present invention.
Claims (4)
- A kind of 1. water-base epoxy texture coating, it is characterised in that：Water-base epoxy texture coating includes AB components：The raw material of component A Include by weight：60-80 parts of epoxy resin, 12-16 parts of reactive diluent GGE, 2.5-3 parts of ether acetates, deionization 40-60 parts of water, 80-90 parts of talcum powder, 60-80 parts of barium sulfate, 0.2-0.5 parts of DISPERBYK-194N；The raw material of B component includes by weight：10-18 parts of triethylene tetramine, 10-20 parts of absolute ethyl alcohol, diethylenetriamine 10- 18 parts, 0.2-0.5 parts of levelling agent, 0.2-0.7 parts of wetting dispersing agent, 0.1-0.6 parts of defoamer.
- A kind of 2. water-base epoxy texture coating according to claim 1, it is characterised in that：Water-base epoxy texture coating includes AB components：The raw material of component A includes by weight：60-80 parts of epoxy resin, 12-16 parts of reactive diluent GGE, alcohol ether vinegar 2.5-3 parts of acid esters, 40-60 parts of deionized water, 80-90 parts of talcum powder, 60-80 parts of barium sulfate, DISPERBYK-194N 0.2- 0.5 part, 3-5 parts of Ludox, 1-2 parts of nm-class boron nitride aqueous dispersions；The raw material of B component includes by weight：10-18 parts of triethylene tetramine, 10-20 parts of absolute ethyl alcohol, diethylenetriamine 10- 18 parts, 0.2-0.5 parts of levelling agent, 0.2-0.7 parts of wetting dispersing agent, 0.1-0.6 parts of defoamer.
- 3. water-base epoxy texture coating according to claim 1 or 2, it is characterised in that：A in water-base epoxy texture coating:B The weight ratio of component is 3:1.
- 4. water-base epoxy texture coating according to claim 1 or 2, it is characterised in that：Levelling agent in B component is BYK- 3455th, defoamer BYK-023, wetting dispersing agent BYK-349.