CN107936510A - A kind of antibacterial synthetic resin and preparation method thereof - Google Patents
A kind of antibacterial synthetic resin and preparation method thereof Download PDFInfo
- Publication number
- CN107936510A CN107936510A CN201711402784.0A CN201711402784A CN107936510A CN 107936510 A CN107936510 A CN 107936510A CN 201711402784 A CN201711402784 A CN 201711402784A CN 107936510 A CN107936510 A CN 107936510A
- Authority
- CN
- China
- Prior art keywords
- parts
- antibacterial
- synthetic resin
- auxiliary agent
- uniformly mixed
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of antibacterial synthetic resin, belongs to resin making technique field, the antibacterial synthetic resin, including following raw material:Polylactic acid, organic epoxy resin, polyphenylene sulfide, makrolon, poly butyric ester, hydrogenation p-phenylenediamine, Lauxite, acrylic resin, poly butyric ester, lauryl acrylate, calcium molybdate, trimethyl phosphate, pla-pcl, fluorine micro mist, nano imvite, zinc borate, chlorinated paraffin, dispersing agent C NF, single-walled carbon nanotube, chitosan, zinc oxide, silane coupling agent KH 560, antibacterial modified auxiliary agent, the antibacterial synthetic resin be through preparation base-material, prepare modified materials, and by the materials such as base-material, modified materials mix and etc. made of.The synthetic resin that the present invention is prepared has excellent anti-microbial property.
Description
Technical field
The present invention relates to the technical field of synthetic resin preparation process, more particularly to a kind of antibacterial synthetic resin and its preparation
Method.
Background technology
Synthetic resin is a kind of artificial synthesized a kind of high molecular polymer, for manufacturing synthetic fibers, coating, gluing
The basic material of agent, insulating materials etc., widely used resin concrete is also using synthetic resin as cementitious material.Since synthesis is set
Fat is compared with other competitive materials has obvious performance and cost advantage, its application also penetrates into national economy various aspects.
China applies for a patent a kind of document " synthetic resin and its preparation method and application (application publication number:
CN102174217A) " disclose a kind of compound resin composition, by weight percentage, it by 35% component A and 65%
Component B is formed;The component A is formed by the monomer polymerization of following parts by weight:20 parts of polyethylene, 20 parts of polypropylene, 15 parts of polyester,
8 parts of nylon, 10 parts of phthalic anhydrides and 4 parts of pentaerythrites;The component B is prepared by the raw material of following parts by weight:
57 parts of 20 parts of pine tar, 8 parts of naphthenic oil, 10 parts of coumarone indene resin, 5 parts of 420 resin and rubber powder, resin group of the present invention
Compound can efficiently use the discarded object of high molecular material, turn waste into wealth, and reduce environmental pollution, but its fire resistance can not expire
The demand of foot in actual use.
The content of the invention
To solve technical problem present in background technology, the present invention proposes a kind of antibacterial synthetic resin and its preparation side
Method, to solve in a kind of Chinese patent application document " synthetic resin and its preparation method and application (application publication number:
CN102174217A the problem of synthetic resin anti-microbial property is insufficient disclosed in) ".
A kind of antibacterial synthetic resin proposed by the present invention, including following raw material:Polylactic acid, organic epoxy resin, polyphenyl
Thioether, makrolon, poly butyric ester, hydrogenation p-phenylenediamine, Lauxite, acrylic resin, poly butyric ester, propylene
Sour lauryl, calcium molybdate, trimethyl phosphate, pla-pcl, fluorine micro mist, nano imvite, zinc borate, chlorinated paraffin, dispersant
CNF, single-walled carbon nanotube, chitosan, zinc oxide, silane coupling agent KH-560, antibacterial modified auxiliary agent;
The chitosan, zinc oxide, the weight ratio of silane coupling agent KH-560 and antibacterial modified auxiliary agent are (6-10):(8-
12):(4-6):(10-20).
Further, the weight ratio of the chitosan, zinc oxide, silane coupling agent KH-560 and antibacterial modified auxiliary agent is 8:
10:5:15.
Further, in units of parts by weight, including following raw material:40-60 parts of polylactic acid, organic epoxy resin 15-
35 parts, 5-15 parts of polyphenylene sulfide, 8-16 parts of makrolon, 4-8 parts of poly butyric ester, hydrogenation 3-9 parts of p-phenylenediamine, ureaformaldehyde tree
2-6 parts of fat, 1-5 parts of acrylic resin, 3-6 parts of poly butyric ester, 2-8 parts of lauryl acrylate, 1-5 parts of calcium molybdate, phosphoric acid
4-8 parts of trimethyl, 3-9 parts of pla-pcl, 2-6 parts of fluorine micro mist, 1-4 parts of nano imvite, 3-5 parts of zinc borate, chlorinated paraffin 4-8
Part, 3-9 parts of dispersing agent C NF, 2-5 parts of single-walled carbon nanotube, 6-10 parts of chitosan, 8-12 parts of zinc oxide, silane coupling agent KH-
560 4-6 parts, it is auxiliary agent 10-20 parts antibacterial modified.
Further, the raw material of the antibacterial modified auxiliary agent includes by weight:5-15 parts of natural zeolite, mass fraction are
The nitre that 3-6 parts of lanthanum chloride solution that 4-8 parts of sodium chloride solution, the mass fraction of 5-15% is 4-8%, mass fraction are 3-5%
Sour 2-5 parts of solution of silver, 1-5 parts of ethyl orthosilicate, 3-6 parts of vinyltriethoxysilane, 4-8 parts of ammonium hydroxide, acetate butyrate fiber
It is 3-9 parts plain.
Further, the antibacterial modified auxiliary agent is prepared by following technique:It is 5- by natural zeolite and mass fraction
15% sodium chloride solution is uniformly mixed, and stirs 1-3h, and filtering means dehydration, drying, then roasts 0.5-1.5h in 450-550 DEG C,
It is subsequently placed in the lanthanum chloride solution that mass fraction is 4-8%, stirs 1-3h, filtering means dehydration, drying, is subsequently placed in 180-220
DEG C roasting 0.5-1.5h, be subsequently placed in mass fraction be 3-5% silver nitrate solution in, stir 2-4h, obtain material after drying
a;Material a, ethyl orthosilicate, vinyltriethoxysilane and ammonium hydroxide are uniformly mixed, stir 5-7h, vacuum filter, with nothing
Water-ethanol washs 2-4 times, and after then adding acetylbutyrylcellulose mixing, stirring 20-40min obtains antibacterial modified auxiliary agent.
The present invention also provides a kind of preparation method of antibacterial synthetic resin, include the following steps:
Polylactic acid, organic epoxy resin, polyphenylene sulfide and makrolon, be uniformly mixed by S1 by weight, is warming up to
80-90 DEG C, 20-40min is kept the temperature, is subsequently added into calcium molybdate, trimethyl phosphate, pla-pcl, fluorine micro mist, nano imvite, boron
Sour zinc, chlorinated paraffin and single-walled carbon nanotube are uniformly mixed, and are continuously heating to 110-120 DEG C, 1-2h are kept the temperature, then in 1500-
2500r/min rotating speeds stir 30-50min, are cooled to room temperature to obtain base-material;
Chitosan, zinc oxide, silane coupling agent KH-560 and antibacterial modified auxiliary agent, be uniformly mixed by S2, is warming up to 80-90
DEG C, 10-20min is kept the temperature, then 10-20min is stirred in 650-850r/min rotating speeds, is cooled to room temperature to obtain modified materials;
Base-material, is warming up to 80-90 DEG C by S3, is kept the temperature 30-50min, is subsequently added into and changes blanking, poly butyric ester, hydrogenation
P-phenylenediamine, Lauxite, acrylic resin, poly butyric ester, lauryl acrylate and dispersing agent C NF are uniformly mixed, in
1050-1350r/min rotating speeds stir 20-40min, are cooled to room temperature to obtain antibacterial synthetic resin.
The invention has the advantages that:(1) by the data of embodiment 1-3 and comparative example 6 as it can be seen that using embodiment 1-
The anti-microbial property of 3 antibacterial synthetic resin significantly improves;At the same time by the data of embodiment 1-3 as it can be seen that embodiment 1 is optimal implementation
Example.
(2) by embodiment 1 and the data of comparative example 1-5 as it can be seen that chitosan, zinc oxide, silane coupling agent KH-560 and anti-
Bacterium modified additive adds play synergistic effect in antibacterial synthetic resin is prepared at the same time, significantly improves antibacterial synthetic resin
Anti-microbial property, this is probably:Chitosan, zinc oxide, silane coupling agent KH-560 and antibacterial modified auxiliary agent are transported as modified system
In the preparation for using synthetic resin, it make use of the graft modification of silane coupling agent KH-560 to act on, realize chitosan, zinc oxide
Realize and be grafted with the hydroxyl on antibacterial modified auxiliary agent surface and the base-material of synthetic resin, impart the excellent antibiotic property of synthetic resin
Can, while the antibacterial humidification of antibacterial modified auxiliary agent is make use of, wherein antibacterial modified auxiliary agent is by by natural zeolite and chlorination
Sodium solution is uniformly mixed, and stirring, filtering means dehydration, drying, then roasts, and it is molten to be subsequently placed in the lanthanum chloride that mass fraction is 4-8%
In liquid, stirring, filtering means dehydration, drying, then roasts, is subsequently placed in silver nitrate solution, stirs, material a is obtained after drying;Will
Material a, ethyl orthosilicate, vinyltriethoxysilane and ammonium hydroxide are uniformly mixed, and stirring, vacuum filter, is washed with absolute ethyl alcohol
Wash, after then adding acetylbutyrylcellulose mixing, stirring obtains antibacterial modified auxiliary agent, and zeolite surface has substantial amounts of ball thing to deposit
, and composite zeolite surface apertures are reduced compared with modified zeolite, this is probably since the AgNO3 adsorbed on zeolite granular surface does not have
Elution completely, the Ag2O being decomposed to form in drying course reunite on its surface, cause zeolite portion aperture to be blocked, therefore silver
Being removed in type antibacterial zeolite particles has the cation exchange position and hole that a certain number of silver are present in antibacterial sorbing material in the form of an ion
Outside road, there is part Ag2O to be present in the surface of material, so as to ensure that silver and Escherichia coli there are enough contacts area.It is modified
In recombination process, most of sodium ion and silver ion are entered inside zeolite by ion exchange, and composite zeolite denitrogenation is to lean on zeolite
With NH4+ ion exchange occurs for the cations such as the sodium ion in structure, and dephosphorization is the electrostatic suction by the hydrous zirconia gel of zeolite surface
Attached, antibacterial is because the loading of the antibacterial Ag ions of bactericidal property, applies in the preparation of synthetic resin of the present invention, in silane idol
Under the action of joining agent KH-560, realize and carry out grafting with the major ingredient of synthetic resin and combined, effectively increase the anti-of synthetic resin
Bacterium performance.
Embodiment
The present invention is described in detail with reference to specific embodiment, it should be appreciated that embodiment is served only for illustrating this hair
It is bright, rather than for limiting the invention, any modification made on the basis of the present invention, equivalent substitution etc. are in this hair
In bright protection domain.
In embodiment, the antibacterial synthetic resin, in units of parts by weight, including following raw material:Polylactic acid 40-60
Part, epoxy resin 15-35 parts organic, 5-15 parts of polyphenylene sulfide, 8-16 parts of makrolon, 4-8 parts of poly butyric ester, hydrogenation
3-9 parts of p-phenylenediamine, 2-6 parts of Lauxite, 1-5 parts of acrylic resin, 3-6 parts of poly butyric ester, lauryl acrylate 2-8
Part, 1-5 parts of calcium molybdate, 4-8 parts of trimethyl phosphate, 3-9 parts of pla-pcl, 2-6 parts of fluorine micro mist, 1-4 parts of nano imvite, boric acid
3-5 parts of zinc, 4-8 parts of chlorinated paraffin, 3-9 parts of dispersing agent C NF, 2-5 parts of single-walled carbon nanotube, 6-10 parts of chitosan, zinc oxide 8-
12 parts, it is 4-6 parts of silane coupling agent KH-560, auxiliary agent 10-20 parts antibacterial modified.
The antibacterial modified auxiliary agent is prepared by following technique:By weight by 5-15 parts of natural zeolites and 4-8 parts of matter
The sodium chloride solution that amount fraction is 5-15% is uniformly mixed, and stirs 1-3h, filtering means dehydration, drying, then in 450-550 DEG C of roasting
0.5-1.5h, is subsequently placed in the lanthanum chloride solution that 3-6 parts of mass fractions are 4-8%, stirs 1-3h, filtering means dehydration, is dried, so
180-220 DEG C of roasting 0.5-1.5h is placed on, is subsequently placed in the silver nitrate solution that 2-5 parts of mass fractions are 3-5%, stirs 2-
4h, obtains material a after drying;By a, 1-5 parts of ethyl orthosilicates of material, 3-6 parts of vinyltriethoxysilane and 4-8 parts of ammonium hydroxide
It is uniformly mixed, stirs 5-7h, vacuum filter, is washed 2-4 times with absolute ethyl alcohol, is then added 3-9 parts of acetylbutyrylcelluloses and is mixed
After conjunction, stirring 20-40min obtains antibacterial modified auxiliary agent.
The preparation method of the antibacterial synthetic resin, comprises the following steps:
Polylactic acid, organic epoxy resin, polyphenylene sulfide and makrolon, be uniformly mixed by S1 by weight, is warming up to
80-90 DEG C, 20-40min is kept the temperature, is subsequently added into calcium molybdate, trimethyl phosphate, pla-pcl, fluorine micro mist, nano imvite, boron
Sour zinc, chlorinated paraffin and single-walled carbon nanotube are uniformly mixed, and are continuously heating to 110-120 DEG C, 1-2h are kept the temperature, then in 1500-
2500r/min rotating speeds stir 30-50min, are cooled to room temperature to obtain base-material;
Chitosan, zinc oxide, silane coupling agent KH-560 and antibacterial modified auxiliary agent, be uniformly mixed by S2, is warming up to 80-90
DEG C, 10-20min is kept the temperature, then 10-20min is stirred in 650-850r/min rotating speeds, is cooled to room temperature to obtain modified materials;
Base-material, is warming up to 80-90 DEG C by S3, is kept the temperature 30-50min, is subsequently added into and changes blanking, poly butyric ester, hydrogenation
P-phenylenediamine, Lauxite, acrylic resin, poly butyric ester, lauryl acrylate and dispersing agent C NF are uniformly mixed, in
1050-1350r/min rotating speeds stir 20-40min, are cooled to room temperature to obtain antibacterial synthetic resin.
Below by more specific embodiment, the present invention will be described.
Embodiment 1
A kind of antibacterial synthetic resin, in units of parts by weight, including following raw material:50 parts of polylactic acid, Organic fluoride asphalt mixtures modified by epoxy resin
25 parts of fat, 10 parts of polyphenylene sulfide, 12 parts of makrolon, 6 parts of poly butyric ester, hydrogenation 6 parts of p-phenylenediamine, 4 parts of Lauxite,
3 parts of acrylic resin, 4.5 parts of poly butyric ester, 4 parts of lauryl acrylate, 3 parts of calcium molybdate, 6 parts of trimethyl phosphate, it is poly-
6.5 parts of lactone, 4 parts of fluorine micro mist, 3 parts of nano imvite, 4 parts of zinc borate, 6 parts of chlorinated paraffin, 6 parts of dispersing agent C NF, single wall carbon
3.5 parts of nanotube, 8 parts of chitosan, 10 parts of zinc oxide, 5 parts of silane coupling agent KH-560,15 parts of antibacterial modified auxiliary agent.
The antibacterial modified auxiliary agent is prepared by following technique:By weight by 10 parts of natural zeolites and 6 parts of quality point
Number is uniformly mixed for 10% sodium chloride solution, stirs 2h, filtering means dehydration, drying, then roasts 1h in 500 DEG C, be subsequently placed in
4.5 parts of mass fractions are in 6% lanthanum chloride solution, stir 2h, filtering means dehydration, drying, is subsequently placed in 200 DEG C of roasting 1h, so
It is placed in the silver nitrate solution that 3.5 parts of mass fractions are 4%, stirs 3h, material a is obtained after drying;By material a, 3 parts of positive silicon
Acetoacetic ester, 4.5 parts of vinyltriethoxysilane and 6 parts of ammonium hydroxide are uniformly mixed, and stir 6h, vacuum filter, is washed with absolute ethyl alcohol
Wash 3 times, after then adding 6 parts of acetylbutyrylcellulose mixing, stirring 30min obtains antibacterial modified auxiliary agent.
The preparation method of the antibacterial synthetic resin, comprises the following steps:
Polylactic acid, organic epoxy resin, polyphenylene sulfide and makrolon, be uniformly mixed by S1 by weight, is warming up to
85 DEG C, 30min is kept the temperature, is subsequently added into calcium molybdate, trimethyl phosphate, pla-pcl, fluorine micro mist, nano imvite, zinc borate, chlorine
Fossil waxes and single-walled carbon nanotube are uniformly mixed, and are continuously heating to 115 DEG C, keep the temperature 1.5h, are then stirred in 2000r/min rotating speeds
40min, is cooled to room temperature to obtain base-material;
Chitosan, zinc oxide, silane coupling agent KH-560 and antibacterial modified auxiliary agent, be uniformly mixed by S2, is warming up to 85 DEG C,
15min is kept the temperature, then 15min is stirred in 750r/min rotating speeds, is cooled to room temperature to obtain modified materials;
Base-material, is warming up to 85 DEG C by S3, is kept the temperature 40min, is subsequently added into and changes blanking, poly butyric ester, hydrogenation to benzene two
Amine, Lauxite, acrylic resin, poly butyric ester, lauryl acrylate and dispersing agent C NF are uniformly mixed, in 1200r/
Min rotating speeds stir 30min, are cooled to room temperature to obtain antibacterial synthetic resin.
Embodiment 2
A kind of antibacterial synthetic resin, in units of parts by weight, including following raw material:40 parts of polylactic acid, Organic fluoride asphalt mixtures modified by epoxy resin
35 parts of fat, 5 parts of polyphenylene sulfide, 16 parts of makrolon, 4 parts of poly butyric ester, hydrogenation 9 parts of p-phenylenediamine, 2 parts of Lauxite,
It is 5 parts of acrylic resin, 3 parts of poly butyric ester, 8 parts of lauryl acrylate, 1 part of calcium molybdate, 8 parts of trimethyl phosphate, poly- interior
3 parts of ester, 6 parts of fluorine micro mist, 1 part of nano imvite, 5 parts of zinc borate, 4 parts of chlorinated paraffin, 9 parts of dispersing agent C NF, single
2 parts of pipe, 10 parts of chitosan, 8 parts of zinc oxide, 6 parts of silane coupling agent KH-560,10 parts of antibacterial modified auxiliary agent.
The antibacterial modified auxiliary agent is prepared by following technique:By weight by 5 parts of natural zeolites and 8 parts of mass fractions
It is uniformly mixed for 5% sodium chloride solution, stirs 3h, filtering means dehydration, drying, then roasts 1.5h in 450 DEG C, be subsequently placed in 3
Part mass fraction is in 8% lanthanum chloride solution, stirs 1h, filtering means dehydration, drying, is subsequently placed in 220 DEG C of roasting 0.5h, then
It is placed in the silver nitrate solution that 5 parts of mass fractions are 3%, stirs 4h, material a is obtained after drying;By material a, 1 part of positive silicic acid second
Ester, 6 parts of vinyltriethoxysilane and 4 parts of ammonium hydroxide are uniformly mixed, and stir 7h, and vacuum filter, is washed 2 times with absolute ethyl alcohol,
Then after adding 9 parts of acetylbutyrylcellulose mixing, stirring 20min obtains antibacterial modified auxiliary agent.
The preparation method of the antibacterial synthetic resin, comprises the following steps:
Polylactic acid, organic epoxy resin, polyphenylene sulfide and makrolon, be uniformly mixed by S1 by weight, is warming up to
80 DEG C, 40min is kept the temperature, is subsequently added into calcium molybdate, trimethyl phosphate, pla-pcl, fluorine micro mist, nano imvite, zinc borate, chlorine
Fossil waxes and single-walled carbon nanotube are uniformly mixed, and are continuously heating to 110 DEG C, keep the temperature 2h, are then stirred in 1500r/min rotating speeds
50min, is cooled to room temperature to obtain base-material;
Chitosan, zinc oxide, silane coupling agent KH-560 and antibacterial modified auxiliary agent, be uniformly mixed by S2, is warming up to 80 DEG C,
20min is kept the temperature, then 20min is stirred in 650r/min rotating speeds, is cooled to room temperature to obtain modified materials;
Base-material, is warming up to 80 DEG C by S3, is kept the temperature 50min, is subsequently added into and changes blanking, poly butyric ester, hydrogenation to benzene two
Amine, Lauxite, acrylic resin, poly butyric ester, lauryl acrylate and dispersing agent C NF are uniformly mixed, in 1050r/
Min rotating speeds stir 40min, are cooled to room temperature to obtain antibacterial synthetic resin.
Embodiment 3
A kind of antibacterial synthetic resin, in units of parts by weight, including following raw material:60 parts of polylactic acid, Organic fluoride asphalt mixtures modified by epoxy resin
15 parts of fat, 15 parts of polyphenylene sulfide, 8 parts of makrolon, 8 parts of poly butyric ester, hydrogenation 3 parts of p-phenylenediamine, 6 parts of Lauxite,
It is 1 part of acrylic resin, 6 parts of poly butyric ester, 2 parts of lauryl acrylate, 5 parts of calcium molybdate, 4 parts of trimethyl phosphate, poly- interior
9 parts of ester, 2 parts of fluorine micro mist, 4 parts of nano imvite, 3 parts of zinc borate, 8 parts of chlorinated paraffin, 3 parts of dispersing agent C NF, single
5 parts of pipe, 6 parts of chitosan, 12 parts of zinc oxide, 4 parts of silane coupling agent KH-560,20 parts of antibacterial modified auxiliary agent.
The antibacterial modified auxiliary agent is prepared by following technique:By weight by 15 parts of natural zeolites and 4 parts of quality point
Number is uniformly mixed for 15% sodium chloride solution, stirs 1h, filtering means dehydration, drying, then roasts 0.5h in 550 DEG C, then put
In the lanthanum chloride solution that 6 parts of mass fractions are 4%, 3h is stirred, filtering means dehydration, drying, is subsequently placed in 180 DEG C of roasting 1.5h,
It is subsequently placed in the silver nitrate solution that 2 parts of mass fractions are 5%, stirs 2h, material a is obtained after drying;By material a, 5 parts of positive silicon
Acetoacetic ester, 3 parts of vinyltriethoxysilane and 8 parts of ammonium hydroxide are uniformly mixed, and stir 5h, vacuum filter, 4 are washed with absolute ethyl alcohol
Secondary, after then adding 3 parts of acetylbutyrylcellulose mixing, stirring 40min obtains antibacterial modified auxiliary agent.
The preparation method of the antibacterial synthetic resin, comprises the following steps:
Polylactic acid, organic epoxy resin, polyphenylene sulfide and makrolon, be uniformly mixed by S1 by weight, is warming up to
90 DEG C, 20min is kept the temperature, is subsequently added into calcium molybdate, trimethyl phosphate, pla-pcl, fluorine micro mist, nano imvite, zinc borate, chlorine
Fossil waxes and single-walled carbon nanotube are uniformly mixed, and are continuously heating to 120 DEG C, keep the temperature 1h, are then stirred in 2500r/min rotating speeds
30min, is cooled to room temperature to obtain base-material;
Chitosan, zinc oxide, silane coupling agent KH-560 and antibacterial modified auxiliary agent, be uniformly mixed by S2, is warming up to 90 DEG C,
10min is kept the temperature, then 10min is stirred in 850r/min rotating speeds, is cooled to room temperature to obtain modified materials;
Base-material, is warming up to 90 DEG C by S3, is kept the temperature 30min, is subsequently added into and changes blanking, poly butyric ester, hydrogenation to benzene two
Amine, Lauxite, acrylic resin, poly butyric ester, lauryl acrylate and dispersing agent C NF are uniformly mixed, in 1350r/
Min rotating speeds stir 20min, are cooled to room temperature to obtain antibacterial synthetic resin.
Comparative example 1
It is essentially identical with the preparation process of embodiment 1, have only the difference is that lacking in the raw material of preparation antibacterial synthetic resin
Chitosan, zinc oxide, silane coupling agent KH-560 and antibacterial modified auxiliary agent.
Comparative example 2
It is essentially identical with the preparation process of embodiment 1, have only the difference is that lacking in the raw material of preparation antibacterial synthetic resin
Chitosan.
Comparative example 3
It is essentially identical with the preparation process of embodiment 1, have only the difference is that lacking in the raw material of preparation antibacterial synthetic resin
Zinc oxide.
Comparative example 4
It is essentially identical with the preparation process of embodiment 1, have only the difference is that lacking in the raw material of preparation antibacterial synthetic resin
Silane coupling agent KH-560.
Comparative example 5
It is essentially identical with the preparation process of embodiment 1, have only the difference is that lacking in the raw material of preparation antibacterial synthetic resin
Antibacterial modified auxiliary agent.
Comparative example 6
Using a kind of Chinese patent application document " synthetic resin and its preparation method and application (application publication number:
CN102174217A) " technique of embodiment prepares antibacterial synthetic resin material.
The antibacterial synthetic resin for measuring embodiment 1-3 and comparative example 1-6 carries out indices detection, obtained testing result
Such as following table:
(1) by the data of embodiment 1-3 and comparative example 6 as it can be seen that anti-microbial property using embodiment 1-3 antibacterial synthetic resin
Significantly improve;At the same time by the data of embodiment 1-3 as it can be seen that embodiment 1 is optimum embodiment.
(2) by embodiment 1 and the data of comparative example 1-5 as it can be seen that chitosan, zinc oxide, silane coupling agent KH-560 and anti-
Bacterium modified additive adds play synergistic effect in antibacterial synthetic resin is prepared at the same time, significantly improves antibacterial synthetic resin
Anti-microbial property, this is probably:Chitosan, zinc oxide, silane coupling agent KH-560 and antibacterial modified auxiliary agent are transported as modified system
In the preparation for using synthetic resin, it make use of the graft modification of silane coupling agent KH-560 to act on, realize chitosan, zinc oxide
Realize and be grafted with the hydroxyl on antibacterial modified auxiliary agent surface and the base-material of synthetic resin, impart the excellent antibiotic property of synthetic resin
Can, while the antibacterial humidification of antibacterial modified auxiliary agent is make use of, wherein antibacterial modified auxiliary agent is by by natural zeolite and chlorination
Sodium solution is uniformly mixed, and stirring, filtering means dehydration, drying, then roasts, and it is molten to be subsequently placed in the lanthanum chloride that mass fraction is 4-8%
In liquid, stirring, filtering means dehydration, drying, then roasts, is subsequently placed in silver nitrate solution, stirs, material a is obtained after drying;Will
Material a, ethyl orthosilicate, vinyltriethoxysilane and ammonium hydroxide are uniformly mixed, and stirring, vacuum filter, is washed with absolute ethyl alcohol
Wash, after then adding acetylbutyrylcellulose mixing, stirring obtains antibacterial modified auxiliary agent, and zeolite surface has substantial amounts of ball thing to deposit
, and composite zeolite surface apertures are reduced compared with modified zeolite, this is probably due to adsorbing the AgNO on zeolite granular surface3No
Elution completely, the Ag being decomposed to form in drying course2O reunites on its surface, causes zeolite portion aperture to be blocked, therefore silver
Being removed in type antibacterial zeolite particles has the cation exchange position and hole that a certain number of silver are present in antibacterial sorbing material in the form of an ion
Outside road, there is part Ag2O is present in the surface of material, so as to ensure that silver and Escherichia coli have enough contacts area.It is modified
In recombination process, most of sodium ion and silver ion are entered inside zeolite by ion exchange, and composite zeolite denitrogenation is to lean on zeolite
The cations such as the sodium ion in structure and NH4+Generation ion exchange, dephosphorization are the electrostatic suctions by the hydrous zirconia gel of zeolite surface
Attached, antibacterial is because the loading of the antibacterial Ag ions of bactericidal property, applies in the preparation of synthetic resin of the present invention, in silane idol
Under the action of joining agent KH-560, realize and carry out grafting with the major ingredient of synthetic resin and combined, effectively increase the anti-of synthetic resin
Bacterium performance.
The foregoing is only a preferred embodiment of the present invention, but protection scope of the present invention be not limited thereto,
Any one skilled in the art the invention discloses technical scope in, technique according to the invention scheme and its
Inventive concept is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.
Claims (6)
1. a kind of antibacterial synthetic resin, it is characterised in that including following raw material:Polylactic acid, organic epoxy resin, polyphenylene sulfide
Ether, makrolon, poly butyric ester, hydrogenation p-phenylenediamine, Lauxite, acrylic resin, poly butyric ester, acrylic acid
Lauryl, calcium molybdate, trimethyl phosphate, pla-pcl, fluorine micro mist, nano imvite, zinc borate, chlorinated paraffin, dispersant
CNF, single-walled carbon nanotube, chitosan, zinc oxide, silane coupling agent KH-560, antibacterial modified auxiliary agent;
The chitosan, zinc oxide, the weight ratio of silane coupling agent KH-560 and antibacterial modified auxiliary agent are (6-10):(8-12):
(4-6):(10-20).
2. antibacterial synthetic resin according to claim 1, it is characterised in that the chitosan, zinc oxide, silane coupling agent
The weight ratio of KH-560 and antibacterial modified auxiliary agent is 8:10:5:15.
3. antibacterial synthetic resin according to claim 1 or 2, it is characterised in that in units of parts by weight, including following original
Material:40-60 parts of polylactic acid, epoxy resin 15-35 parts organic, 5-15 parts of polyphenylene sulfide, 8-16 parts of makrolon, poly- hydroxyl fourth
4-8 parts of acid esters, hydrogenation 3-9 parts of p-phenylenediamine, 2-6 parts of Lauxite, 1-5 parts of acrylic resin, 3-6 parts of poly butyric ester,
2-8 parts of lauryl acrylate, 1-5 parts of calcium molybdate, 4-8 parts of trimethyl phosphate, 3-9 parts of pla-pcl, 2-6 parts of fluorine micro mist, nanometer
1-4 parts of montmorillonite, 3-5 parts of zinc borate, 4-8 parts of chlorinated paraffin, 3-9 parts of dispersing agent C NF, 2-5 parts of single-walled carbon nanotube, shell gather
It is 6-10 parts sugared, 8-12 parts of zinc oxide, 4-6 parts of silane coupling agent KH-560, auxiliary agent 10-20 parts antibacterial modified.
4. according to claim 1-3 any one of them antibacterial synthetic resin, it is characterised in that the original of the antibacterial modified auxiliary agent
Material includes by weight:4-8 parts of sodium chloride solution that 5-15 parts of natural zeolite, mass fraction are 5-15%, mass fraction 4-
8% 3-6 parts of lanthanum chloride solution, 1-5 parts of 2-5 parts of silver nitrate solution, ethyl orthosilicate, the vinyl that mass fraction is 3-5%
3-6 parts of triethoxysilane, 4-8 parts of ammonium hydroxide, 3-9 parts of acetylbutyrylcellulose.
5. according to claim 1-4 any one of them antibacterial synthetic resin, it is characterised in that the antibacterial modified auxiliary agent is by such as
It is prepared by lower technique:Natural zeolite and mass fraction are uniformly mixed for the sodium chloride solution of 5-15%, stir 1-3h, filtering
Dehydration, drying, then roasts 0.5-1.5h in 450-550 DEG C, is subsequently placed in the lanthanum chloride solution that mass fraction is 4-8%,
1-3h is stirred, filtering means dehydration, drying, is subsequently placed in 180-220 DEG C of roasting 0.5-1.5h, it is 3-5% to be subsequently placed in mass fraction
Silver nitrate solution in, stir 2-4h, material a is obtained after drying;By material a, ethyl orthosilicate, vinyltriethoxysilane
It is uniformly mixed with ammonium hydroxide, stirs 5-7h, vacuum filter, is washed 2-4 times with absolute ethyl alcohol, is then added acetylbutyrylcellulose and is mixed
After conjunction, stirring 20-40min obtains antibacterial modified auxiliary agent.
6. a kind of preparation method according to claim 1-5 any one of them antibacterial synthetic resin, it is characterised in that including such as
Lower step:
Polylactic acid, organic epoxy resin, polyphenylene sulfide and makrolon, be uniformly mixed by S1 by weight, is warming up to 80-90
DEG C, keep the temperature 20-40min, be subsequently added into calcium molybdate, trimethyl phosphate, pla-pcl, fluorine micro mist, nano imvite, zinc borate,
Chlorinated paraffin and single-walled carbon nanotube are uniformly mixed, and are continuously heating to 110-120 DEG C, 1-2h are kept the temperature, then in 1500-2500r/
Min rotating speeds stir 30-50min, are cooled to room temperature to obtain base-material;
Chitosan, zinc oxide, silane coupling agent KH-560 and antibacterial modified auxiliary agent, be uniformly mixed by S2, is warming up to 80-90 DEG C,
10-20min is kept the temperature, then 10-20min is stirred in 650-850r/min rotating speeds, is cooled to room temperature to obtain modified materials;
Base-material, is warming up to 80-90 DEG C by S3, is kept the temperature 30-50min, is subsequently added into and changes blanking, poly butyric ester, hydrogenation to benzene
Diamines, Lauxite, acrylic resin, poly butyric ester, lauryl acrylate and dispersing agent C NF are uniformly mixed, in 1050-
1350r/min rotating speeds stir 20-40min, are cooled to room temperature to obtain antibacterial synthetic resin.