CN107936326A - A kind of butadiene-styrene rubber of high-tensile - Google Patents
A kind of butadiene-styrene rubber of high-tensile Download PDFInfo
- Publication number
- CN107936326A CN107936326A CN201711382731.7A CN201711382731A CN107936326A CN 107936326 A CN107936326 A CN 107936326A CN 201711382731 A CN201711382731 A CN 201711382731A CN 107936326 A CN107936326 A CN 107936326A
- Authority
- CN
- China
- Prior art keywords
- parts
- butadiene
- styrene rubber
- tensile
- coupling agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of butadiene-styrene rubber of high-tensile, each component and shared parts by weight are:35 50 parts of butadiene-styrene rubber, 4 10 parts of methyl vinyl silicone rubber, 5 10 parts of nano-calcium carbonate, 15 20 parts of coupling agent, 5 11 parts of zinc oxide, 38 parts of stearic acid, 25 parts of microcrystalline wax, 7 15 parts of plasticizer, 26 parts of carbon black, 10 14 parts of pitch.Gained butadiene-styrene rubber of the invention, can make it obtain high tensile strength, significant effect.
Description
Technical field
The present invention relates to a kind of rubber, is specifically a kind of butadiene-styrene rubber of high-tensile.
Background technology
Butadiene-styrene rubber is that a kind of performance is similar with natural rubber, but its tensile strength is relatively low, has at some to tensile strength
It is required that occasion can not use.
The content of the invention
The present invention provides a kind of butadiene-styrene rubber of high-tensile, can make it that butadiene-styrene rubber is strong with excellent tension
Degree.
To achieve the above object, the present invention provides following formula:
A kind of butadiene-styrene rubber of high-tensile, each component and shared parts by weight are:35-50 parts of butadiene-styrene rubber, methyl
4-10 parts of vinylsiloxane rubber, 5-10 parts of nano-calcium carbonate, 15-20 parts of coupling agent, 5-11 parts of zinc oxide, 3-8 parts of stearic acid are micro-
2-5 parts of spar wax, 7-15 parts of plasticizer, 2-6 parts of carbon black, 10-14 parts of pitch.
Preferably, the nano-calcium carbonate is 50-100 nanometers of particle diameter.
Preferably, the coupling agent is the compound of nitro coupling agent and alcohols.
Gained butadiene-styrene rubber of the invention, can make it obtain high tensile strength, significant effect.
Embodiment
A kind of butadiene-styrene rubber of high-tensile, each component and shared parts by weight are:35-50 parts of butadiene-styrene rubber, methyl
4-10 parts of vinylsiloxane rubber, 5-10 parts of nano-calcium carbonate, 15-20 parts of coupling agent, 5-11 parts of zinc oxide, 3-8 parts of stearic acid are micro-
2-5 parts of spar wax, 7-15 parts of plasticizer, 2-6 parts of carbon black, 10-14 parts of pitch.The nano-calcium carbonate is received for particle diameter 50-100
Rice, the coupling agent are the compound of nitro coupling agent and alcohols.
In order to make the purpose , technical scheme and advantage of the present invention be clearer, with reference to embodiments, to the present invention
It is further elaborated, it will be appreciated that the specific embodiments described herein are merely illustrative of the present invention, is not used to
Limit the present invention.
Embodiment 1:
A kind of butadiene-styrene rubber of high-tensile, each component and shared parts by weight are:35 parts of butadiene-styrene rubber, ethylene methacrylic
4 parts of base silicon rubber, 5 parts of nano-calcium carbonate, 15 parts of coupling agent, 5 parts of zinc oxide, 3 parts of stearic acid, 2 parts of microcrystalline wax, plasticizer 7
Part, 2 parts of carbon black, 10 parts of pitch.
Embodiment 2:
A kind of butadiene-styrene rubber of high-tensile, each component and shared parts by weight are:41 parts of butadiene-styrene rubber, ethylene methacrylic
6 parts of base silicon rubber, 8 parts of nano-calcium carbonate, 18 parts of coupling agent, 8 parts of zinc oxide, 5 parts of stearic acid, 4 parts of microcrystalline wax, plasticizer 10
Part, 4 parts of carbon black, 12 parts of pitch.
Embodiment 3:
A kind of butadiene-styrene rubber of high-tensile, each component and shared parts by weight are:50 parts of butadiene-styrene rubber, ethylene methacrylic
10 parts of base silicon rubber, 10 parts of nano-calcium carbonate, 20 parts of coupling agent, 11 parts of zinc oxide, 8 parts of stearic acid, 5 parts of microcrystalline wax, plasticising
15 parts of agent, 6 parts of carbon black, 14 parts of pitch.
Claims (3)
1. a kind of butadiene-styrene rubber of high-tensile, it is characterised in that each component and shared parts by weight are:Butadiene-styrene rubber 35-
50 parts, 4-10 parts of methyl vinyl silicone rubber, 5-10 parts of nano-calcium carbonate, 15-20 parts of coupling agent, 5-11 parts of zinc oxide, tristearin
It is 3-8 parts sour, 2-5 parts of microcrystalline wax, 7-15 parts of plasticizer, 2-6 parts of carbon black, 10-14 parts of pitch.
2. the butadiene-styrene rubber of high-tensile according to claim 1, it is characterised in that the nano-calcium carbonate is particle diameter
50-100 nanometers.
3. the butadiene-styrene rubber of high-tensile according to claim 1 or 2, it is characterised in that the coupling agent is nitro
The compound of coupling agent and alcohols.