CN107935635A - A kind of preparation method of pottery lamp part - Google Patents
A kind of preparation method of pottery lamp part Download PDFInfo
- Publication number
- CN107935635A CN107935635A CN201711202934.3A CN201711202934A CN107935635A CN 107935635 A CN107935635 A CN 107935635A CN 201711202934 A CN201711202934 A CN 201711202934A CN 107935635 A CN107935635 A CN 107935635A
- Authority
- CN
- China
- Prior art keywords
- pottery
- lamp part
- heat
- glazed body
- insulated
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of preparation method of pottery lamp part, including the preparation of pottery lamp part element tire, pottery lamp part element tire coating pottery glaze, pottery glazed body top layer coat the kiln-firing of heat-insulated colloid and heat-insulated pottery glazed body；The base substrate of pottery lamp part is made in the method for throwing shaping or injection forming, fires to obtain plain tire；Pretreated element tire is positioned on glazing platform, by pottery glaze slurry coated on pretreated plain tire top layer, is coated and is air-dried, obtain pottery glazed body；Heat-insulated colloid is coated on pottery glazed body top layer, after the completion of coating, the pottery glazed body after coating is dried at 100 ~ 150 DEG C, obtains the pottery glazed body of primary coating；Using the process of primary coating as circulation, continue to coat heat-insulated colloid on the pottery glazed body top layer of primary coating, dry secondary coating pottery glazed body；Pottery glazed body coats 1 ~ 2 time altogether, obtains heat-insulated pottery glazed body；Kiln-firing, kiln temperature heating is temperature-gradient method.The present invention realizes the heat-insulated purpose of pottery lamp part.
Description
Technical field
The present invention relates to a kind of preparation method of pottery lamp part.
Background technology
Pottery is one kind of porcelain, belongs to the category of porcelain.Pottery is by adding copper, phosphorus member in glaze
The colouring agents such as element, form via high-temperature firing, its glaze paint is colorful and is rich in change.Pottery is again " it is of the same colour to enter kiln, kiln discharge
Ten thousand is color " and it is civilized.Pottery has long history, and the Tang Dynasty pottery is the colouring agent using iron as pottery glaze, is fired at high temperature
Go out the colored glaze of black matrix locus coeruleus, the opacity of this locus coeruleus colored glaze is higher, in moon white or sky blue, has certain flowing
Property；The Song Dynasty is developed to, introducing cupric oxide again in pottery is the colouring agent of pottery glaze, and burns out band in green grass or young crops under reducing atmosphere
Dry, the purplish red furnace transmutation glaze to set each other off, meanwhile, glaze paint have also appeared earthworm and walk mud line and various silk hairy flow liners；To an ancient unit of weight in golden source period
Porcelain then based on reddish black, sky blue, separately has using reddish black sky blue as background color, and pottery of the glaze paint with purplish-red macula occurs, and belongs to
The technique of transmutation.
The production of pottery usually requires manufacturing procedure, moulding process, pattern making procedure, shaping work from sorting to product is burnt till
Sequence, biscuiting process, glazing process, glaze firing eight procedure such as process and pick process, manufacturing procedure include sorting and to selected originals
Expect the pretreatment carried out；Moulding process is that the mould of definite shape is made according to design idea；Molding is the mould type of having made
Turn over and model is made；Shaping is the species and different needs from product；It is molded by injection forming, throwing, shaping etc. of moulding adobe blocks
Method moulds the base substrate of pottery；Base substrate after shaping is fired in the case of unglazed, to increase the intensity of base substrate and water suction
Property；Glazing is by the plain tire after biscuiting, carries out glazing using the methods of rinsing glaze, leaching glaze, gloss firing, brushing glazing and point glaze, makes element
One layer of glaze slip with suitable thickness of tire surface attachment；Glaze firing be by the glazed body after glazing enter klining into；Finally according to pottery matter
Amount standard carries out pick and classification.Pottery lamp part is on the basis of pottery technique, and pendent lamp or desk lamp are used as using pottery product
Lamp holder or lampshade, lamp support lamp, pottery lamp part needs to be assembled into pendent lamp or desk lamp, thus pottery lamp part usually set it is single or
The multiple mounting holes of person（Installing port）, the electronic component of pendent lamp or desk lamp is then arranged at mounting hole（Installing port）, with pottery lamp part
Lamps and lanterns are assembled into jointly；On the other hand, amount of heat can be produced when lamp persistently uses, easily causes pottery lamp part mounting hole（Peace
Fill mouth）Locate the damage of electronic component.
The content of the invention
In order to solve deficiency of the prior art, the present invention relates to a kind of preparation method of pottery lamp part, pottery lamp is realized
The heat-insulated purpose of part, avoids in the case where lamp is opened for a long time, inside the pottery lamp part caused by temperature is excessive or near
Electronic component damage.
A kind of preparation method of pottery lamp part, it is characterised in that：Preparation including pottery lamp part element tire, pottery lamp part element tire
Coat pottery glaze, pottery glazed body top layer coats the kiln-firing of heat-insulated colloid and heat-insulated pottery glazed body.
Further, the preparation of the pottery lamp part element tire is molded with throwing or the method for injection forming makes pottery lamp part
Base substrate, base substrate dehydration hardening after to base substrate carry out rotary cut repair to obtain pottery lamp part essence base；Obtained pottery lamp part essence base is entered
Kiln biscuiting, firing temperature are 900 ~ 950 DEG C, obtain pottery lamp part element tire.
Further, the pottery lamp part element tire coats concretely comprising the following steps for pottery glaze：
Step 1: with hairbrush by the lime-ash on the pottery element tire surface and inner cavity Jing Guo biscuiting, then the element after lime-ash is cleared up
Tire surface spraying water, erases the floating ash on plain tire top layer with sponge or cotton afterwards, obtains the plain tire of pretreatment；
Step 2: pottery glaze raw material is crushed, after ball milling, drying and screening, obtains pottery glaze powder, into pottery glaze powder
Water is added, stirs and ultrasonic, obtains pottery glaze slurry；
Step 3: pretreated plain tire is positioned on glazing platform, by pottery glaze slurry coated on pretreated plain tire
Top layer, after the completion of coating, the plain tire after coating is air-dried, obtains the plain tire of a glazing；Using the process of a glazing as circulation, after
Continue a glazing plain tire top layer coat pottery glaze slurry, dry secondary glazing plain tire；Plain tire glazing 1 ~ 3 altogether
It is secondary, obtain pottery glazed body.
Further, the pottery glazed body top layer coats concretely comprising the following steps for heat-insulated colloid：Heat-insulated colloid is coated on an ancient unit of weight
Enamel base top layer, after the completion of coating, the pottery glazed body after coating is dried at 100 ~ 150 DEG C, obtains the pottery glaze of primary coating
Base；Using the process of primary coating as circulation, continue to coat heat-insulated colloid on the pottery glazed body top layer of primary coating, dry secondary
The pottery glazed body of coating；Pottery glazed body coats 1 ~ 2 time altogether, obtains heat-insulated pottery glazed body.
Further, the kiln-firing process of the heat-insulated pottery glazed body, kiln temperature heating is temperature-gradient method, and kiln temperature is warming up to
2h is kept the temperature at 100 ~ 150 DEG C, continues to heat up, to 2 ~ 5h is kept the temperature at 400 ~ 450 DEG C, 3 ~ 5h is kept the temperature when being warming up to 850 ~ 900 DEG C, rises
Temperature keeps the temperature 1 ~ 3h to 2 ~ 3h is kept the temperature at 950 DEG C when being warming up to 1250 ~ 1430 DEG C.
Further, the heat-insulated colloid includes colloid coating and tiny balloon.
Further, the tiny balloon is to be by the tiny balloon of pretreatment, the process of pretreatment：Configuration
The sodium hydroxide solution of 0.5moL/L, and cenosphere is immersed and is cleaned by ultrasonic 30 ~ 60min in sodium hydroxide solution, clean
Cheng Hou, takes out pretreated cenosphere and dries.
Further, the preparation method of the heat-insulated colloid is：The configuration soluble in water of nine water ferric nitrates and barium nitrate is molten
Liquid, is each configured to the nine water iron nitrate solutions of 0.44moL/L and the barium nitrate solution of 0.04moL/L, and two kinds of solution are mixed
Afterwards, stir and add citric acid, and it is 7 ~ 8 to adjust PH with ammonium hydroxide, is then concentrated by evaporation at 65 ~ 85 DEG C, obtains colloid coating；In advance
Cenosphere after processing adds in colloid coating in batches, stir 8 ~ 12h, continue to be concentrated by evaporation at 85 ~ 100 DEG C, obtain every
Hot glue body.
Further, the pottery glaze raw material includes potassium feldspar, calcite, Agate, talcum, the first colouring agent, grass
Wood ash, stannic oxide, calcium phosphate and zinc oxide.
Further, the colouring agent is the one or more in cupric oxide, di-iron trioxide or cobalt oxide.
Beneficial effects of the present invention are：
1st, the preparation method of a kind of pottery lamp part of the invention, is coated by the preparation of pottery lamp part element tire, pottery lamp part element tire
Pottery glaze, pottery glazed body top layer coat the process of the kiln-firing of heat-insulated colloid and heat-insulated pottery glazed body, realize pottery lamp part
The heat-insulated purpose in top layer, avoids the damage of electronic component；
2nd, the present invention prepares heat-insulated colloid using sol-gel process, and the cenosphere in adiabatic gum body is uniformly dispersed, and colloidal quality
Ground is easy to be coated on pottery glazed body top layer；
3rd, the kiln temperature heating during heat-insulated pottery glazed body kiln-firing of the invention is temperature-gradient method, ensures pottery glazed body top layer
Citrate and gel thermal decomposition process in heat-insulated colloid are smoothed out.
Embodiment
In order to which those skilled in the art better understood when technical solution provided by the present invention, with reference to specific
Embodiment income illustrates.
This case will can be illustrated and is fully understood by following embodiment so that the personage for being familiar with this skill can be according to this
Complete, the embodiment of right this case not can be limited its embodiment by following.
A kind of preparation method of pottery lamp part includes the preparation of pottery lamp part element tire, pottery lamp part element tire coating pottery glaze
Material, pottery glazed body top layer coat the kiln-firing of heat-insulated colloid and heat-insulated pottery glazed body, realize the heat-insulated mesh in pottery lamp part top layer
, avoid the damage of electronic component at pottery lamp part mounting hole or installing port.
The preparation of pottery lamp part element tire is molded with throwing or the method for injection forming makes the base substrate of pottery lamp part, and base substrate takes off
Rotary cut is carried out to base substrate after water hardening and repairs to obtain pottery lamp part essence base；Obtained pottery lamp part essence base is entered into kiln biscuiting, fires temperature
Spend for 900 ~ 950 DEG C, obtain pottery lamp part element tire.
Pottery lamp part element tire coating pottery glaze concretely comprises the following steps：
Step 1: with hairbrush by the lime-ash on the pottery element tire surface and inner cavity Jing Guo biscuiting, then the element after lime-ash is cleared up
Tire surface spraying water, erases the floating ash on plain tire top layer with sponge or cotton afterwards, obtains the plain tire of pretreatment；
Step 2: pottery glaze raw material is crushed, after ball milling, drying and screening, obtains pottery glaze powder, into pottery glaze powder
Water is added, stirs and ultrasonic, obtains pottery glaze slurry；
Step 3: pretreated plain tire is positioned on glazing platform, by pottery glaze slurry coated on pretreated plain tire
Top layer, after the completion of coating, the plain tire after coating is air-dried, obtains the plain tire of a glazing；Using the process of a glazing as circulation, after
Continue a glazing plain tire top layer coat pottery glaze slurry, dry secondary glazing plain tire；Plain tire glazing 1 ~ 3 altogether
It is secondary, obtain pottery glazed body.
Pottery glazed body top layer coats concretely comprising the following steps for heat-insulated colloid：Prepare heat-insulated colloid first, by nine water ferric nitrates and
Barium nitrate configuration solution soluble in water, is each configured to the nine water iron nitrate solutions of 0.44moL/L and the barium nitrate of 0.04moL/L
Solution, after two kinds of solution are mixed, stirs and adds citric acid, and it is 7 ~ 8 to adjust PH with ammonium hydroxide, is then steamed at 65 ~ 85 DEG C
Hair concentration, obtains colloid coating；Pretreated cenosphere adds in colloid coating in batches, 8 ~ 12h is stirred, at 85 ~ 100 DEG C
Under continue to be concentrated by evaporation, obtain heat-insulated colloid；Heat-insulated colloid is coated on pottery glazed body top layer afterwards, after the completion of coating, will be coated
Pottery glazed body afterwards is dried at 100 ~ 150 DEG C, obtains the pottery glazed body of primary coating；Using the process of primary coating as circulation, after
Continue and coat heat-insulated colloid on the pottery glazed body top layer of primary coating, dry secondary coating pottery glazed body；Pottery glazed body is altogether
Coating 1 ~ 2 time, obtains heat-insulated pottery glazed body；Heat-insulated colloid is prepared using sol-gel process, the cenosphere in adiabatic gum body disperses
Uniformly, and colloid quality is easy to be coated on pottery glazed body top layer.
During the kiln-firing of heat-insulated pottery glazed body, kiln temperature heating is temperature-gradient method, and kiln temperature is warming up to 100 ~ 150 DEG C
Shi Baowen 2h, continue to heat up, and to 2 ~ 5h is kept the temperature at 400 ~ 450 DEG C, keep the temperature 3 ~ 5h when being warming up to 850 ~ 900 DEG C, are warming up to 950 DEG C
2 ~ 3h of Shi Baowen, 1 ~ 3h is kept the temperature when being warming up to 1250 ~ 1430 DEG C；Kiln temperature during heat-insulated pottery glazed body kiln-firing, which heats up, is
Temperature-gradient method, ensures that the citrate in pottery glazed body top layer heat-insulated colloid and gel thermal decomposition process are smoothed out.
The foregoing description of the disclosed embodiments, enables professional and technical personnel in the field to realize or use the present invention.
A variety of modifications to these embodiments will be apparent for those skilled in the art, as defined herein
General Principle can be realized in other embodiments without departing from the spirit or scope of the present invention.Therefore, it is of the invention
The embodiments shown herein is not intended to be limited to, and is to fit to and the principles and novel features disclosed herein phase one
The most wide scope caused.
Claims (10)
- A kind of 1. preparation method of pottery lamp part, it is characterised in that：Preparation including pottery lamp part element tire, pottery lamp part element tire apply Cover pottery glaze, pottery glazed body top layer coats the kiln-firing of heat-insulated colloid and heat-insulated pottery glazed body.
- A kind of 2. preparation method of pottery lamp part according to claim 1, it is characterised in that：The pottery lamp part element tire The base substrate that pottery lamp part is made in the method for throwing shaping or injection forming is prepared, rotary cut is carried out to base substrate after base substrate dehydration hardening Repair to obtain pottery lamp part essence base；Obtained pottery lamp part essence base is entered into kiln biscuiting, firing temperature is 900 ~ 950 DEG C, obtains pottery lamp Part element tire.
- A kind of 3. preparation method of pottery lamp part according to claim 1, it is characterised in that：The pottery lamp part element tire applies Cover concretely comprising the following steps for pottery glaze：Step 1: with hairbrush by the lime-ash on the pottery element tire surface and inner cavity Jing Guo biscuiting, then the element after lime-ash is cleared up Tire surface spraying water, erases the floating ash on plain tire top layer with sponge or cotton afterwards, obtains the plain tire of pretreatment；Step 2: pottery glaze raw material is crushed, after ball milling, drying and screening, obtains pottery glaze powder, into pottery glaze powder Water is added, stirs and ultrasonic, obtains pottery glaze slurry；Step 3: pretreated plain tire is positioned on glazing platform, by pottery glaze slurry coated on pretreated plain tire Top layer, after the completion of coating, the plain tire after coating is air-dried, obtains the plain tire of a glazing；Using the process of a glazing as circulation, after Continue a glazing plain tire top layer coat pottery glaze slurry, dry secondary glazing plain tire；Plain tire glazing 1 ~ 3 altogether It is secondary, obtain pottery glazed body.
- A kind of 4. preparation method of pottery lamp part according to claim 1, it is characterised in that：The pottery glazed body top layer applies Cover concretely comprising the following steps for heat-insulated colloid：Heat-insulated colloid is coated on pottery glazed body top layer, after the completion of coating, by the pottery after coating Glazed body is dried at 100 ~ 150 DEG C, obtains the pottery glazed body of primary coating；Using the process of primary coating as circulation, continue once The pottery glazed body top layer of coating coats heat-insulated colloid, dry secondary coating pottery glazed body；Pottery glazed body coats 1 ~ 2 altogether It is secondary, obtain heat-insulated pottery glazed body.
- A kind of 5. preparation method of pottery lamp part according to claim 1, it is characterised in that：The heat-insulated pottery glazed body Kiln-firing process, kiln temperature heating is temperature-gradient method, and kiln temperature keeps the temperature 2h when being warming up to 100 ~ 150 DEG C, continues to heat up, to 400 ~ 2 ~ 5h is kept the temperature at 450 DEG C, 3 ~ 5h is kept the temperature when being warming up to 850 ~ 900 DEG C, 2 ~ 3h is kept the temperature when being warming up to 950 DEG C, it is warming up to 1250 ~ 1 ~ 3h is kept the temperature at 1430 DEG C.
- A kind of 6. preparation method of pottery lamp part according to claim 1 or 4, it is characterised in that：The heat-insulated colloid bag Include colloid coating and tiny balloon.
- A kind of 7. preparation method of pottery lamp part according to claim 6, it is characterised in that：The tiny balloon is process The tiny balloon of pretreatment, the process of pretreatment are：The sodium hydroxide solution of 0.5moL/L is configured, and cenosphere is immersed into hydrogen It is cleaned by ultrasonic 30 ~ 60min in sodium hydroxide solution, after the completion of cleaning, takes out pretreated cenosphere and dry.
- A kind of 8. preparation method of pottery lamp part according to claim 6, it is characterised in that：The preparation of the heat-insulated colloid Method is：By nine water ferric nitrates and barium nitrate configuration solution soluble in water, the nine water ferric nitrates for being each configured to 0.44moL/L are molten The barium nitrate solution of liquid and 0.04moL/L, after two kinds of solution are mixed, stirs and adds citric acid, and it is 7 to adjust PH with ammonium hydroxide ~ 8, then it is concentrated by evaporation at 65 ~ 85 DEG C, obtains colloid coating；Pretreated cenosphere adds in colloid coating in batches, 8 ~ 12h is stirred, continues to be concentrated by evaporation at 85 ~ 100 DEG C, obtains heat-insulated colloid.
- A kind of 9. preparation method of pottery lamp part according to claim 1 or 3, it is characterised in that：The pottery glaze is former Material includes potassium feldspar, calcite, Agate, talcum, the first colouring agent, plant ash, stannic oxide, calcium phosphate and zinc oxide.
- A kind of 10. preparation method of pottery lamp part according to claim 9, it is characterised in that：The colouring agent is oxidation One or more in copper, di-iron trioxide or cobalt oxide.