CN107932701A - A kind of artificial quartz in lump releasing agent and preparation method thereof - Google Patents
A kind of artificial quartz in lump releasing agent and preparation method thereof Download PDFInfo
- Publication number
- CN107932701A CN107932701A CN201711105427.8A CN201711105427A CN107932701A CN 107932701 A CN107932701 A CN 107932701A CN 201711105427 A CN201711105427 A CN 201711105427A CN 107932701 A CN107932701 A CN 107932701A
- Authority
- CN
- China
- Prior art keywords
- agent
- artificial quartz
- water
- defoamer
- releasing agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of artificial quartz in lump releasing agent and preparation method thereof.The artificial quartz in lump releasing agent includes following component by weight percentage：Interleaving agent 1% 30%；Binding agent 1% 30%；Defoamer 0.5%；Surfactant 1% 3%；Coalescents 0.5% 1%；Water is surplus；It the described method comprises the following steps：Sequentially add water, defoamer, surfactant and the coalescents of formula ratio in a kettle first, stir evenly；Sequentially add the interleaving agent and binding agent of formula ratio while stirring in a kettle afterwards, be warming up to 70 90 DEG C, the addition time is 2h, keeps the temperature 3 6h, is got product after being cooled to room temperature.Artificial quartz in lump releasing agent provided by the present invention, it is the aqua product of environmental protection, and nonflammable explosive, which enters recirculated water and just clear up after a few days；It is easy that it is demoulded, and relatively demoulds wax, silicone oil mold release agent, off-type force smaller during the demoulding；Plate surface after it is demoulded is highly polished, can improve product qualification rate whereby.
Description
Technical field
The present invention relates to releasing agent, more particularly to a kind of artificial quartz in lump releasing agent and preparation method thereof.
Background technology
Releasing agent is a kind of functional materials between mould and finished product, it is used in two and is easy to adhesion each other
One interface coating of body surface, can make body surface be easy to depart from, it is smooth and clean.In the technique of generation artificial quartz in lump
, it is necessary to which plate and template are kept apart in flow, easy to smoothly demould.If use sexual isolation of brown paper, brown paper
Water quality may be caused to turn yellow after into recirculated water the pollution such as peculiar smell；And brown paper may enter inside plate, cause matter
Measure defect.If using demoulding wax, high temperature resistant wax, but its higher price are needed, and the high temperature resistant wax enters nothing after recirculated water
Method is separated and collected.If using silicone oil mold release agent, since silicone oil mold release agent is oiliness, combustibles, then it, which is preserved, uses
It is required that it is stringenter, so as to be difficult to promote and apply.
The content of the invention
In view of this, it is an object of the invention to provide a kind of artificial quartz in lump releasing agent and preparation method thereof.
In order to reach above-mentioned purpose, the present invention provides a kind of artificial quartz in lump releasing agent, wrap by weight percentage
Include following component：
Interleaving agent 1%-30%；
Binding agent 1%-30%；
Defoamer 0.5%；
Surfactant 1%-3%；
Coalescents 0.5%-1%；
Water surplus.
Further, wherein the artificial quartz in lump releasing agent, by weight percentage including following component：
Interleaving agent 4%；
Binding agent 5%；
Defoamer 0.5%；
Surfactant 1.5%；
Coalescents 0.5%；
Water 88.5%.
Further, wherein the artificial quartz in lump releasing agent, by weight percentage including following component：
Interleaving agent 8%；
Binding agent 10%；
Defoamer 0.5%；
Surfactant 1%；
Coalescents 0.5%；
Water 80%.
Further, wherein the artificial quartz in lump releasing agent, by weight percentage including following component：
Interleaving agent 20%；
Binding agent 15%；
Defoamer 0.5%；
Surfactant 1.5%；
Coalescents 1%；
Water 62%.
Further, wherein the artificial quartz in lump releasing agent, by weight percentage including following component：
Interleaving agent 30%；
Binding agent 20%；
Defoamer 0.5%；
Surfactant 2%；
Coalescents 1%；
Water 46.5%.
Further, wherein the interleaving agent is aqueous fluorine-carbon paint（Surface tension is reduced, improves isolation performance）；It is described viscous
Knot agent is polyvinyl alcohol, and the polyvinyl alcohol is the dry powder of 60 mesh.
Further, wherein the binding agent is polyvinyl alcohol, the polyvinyl alcohol is the dry powder of 60 mesh.
Further, wherein the defoamer is aqueous defoamer.
Further, wherein the defoamer is silicone oil emulsion.
Further, wherein the surfactant is lauryl sodium sulfate.
Further, wherein the coalescents are propandiol butyl ether.
Further, wherein the water is tap water.
In addition, the present invention provides a kind of preparation method of above-mentioned artificial quartz in lump releasing agent, comprise the following steps：
1）Sequentially add water, defoamer, surfactant and the coalescents of formula ratio in a kettle first, stir evenly；
2）Sequentially add the interleaving agent and binding agent of formula ratio while stirring in a kettle afterwards, be warming up to 70-90 DEG C, add
Time is 2h（Completion 2h is added from beginning to join）, 3-6h is kept the temperature, is got product after being cooled to room temperature.
Invention further provides the application method of above-mentioned artificial quartz in lump releasing agent, by the artificial quartz in lump releasing agent
Brush is sprayed on mould, it is kept uniform, moistened surface.
The artificial quartz in lump releasing agent brush is sprayed on mould, it is kept uniform, moistened surface
The invention has the advantages that：
1st, artificial quartz in lump releasing agent provided by the present invention, its for environmental protection aqua product, it is nonflammable explosive, the releasing agent into
Enter recirculated water just to clear up after a few days；
2nd, artificial quartz in lump releasing agent provided by the present invention, it is easy that it is demoulded, and relatively demoulds wax, silicone oil mold release agent, during the demoulding from
Type power smaller；
3rd, artificial quartz in lump releasing agent provided by the present invention, the plate surface after it is demoulded is highly polished, can improve production whereby
Product qualification rate.
Embodiment
The present invention is explained with reference to embodiment, and case study on implementation is merely to illustrate the present invention.Unless stated otherwise, it is of the invention
In used technological means be method known in those skilled in the art.In addition, embodiment be interpreted as it is illustrative,
The scope being not intended to limit the present invention, the spirit and scope of the invention are limited only by the claims that follow.
Embodiment 1：
A kind of artificial quartz in lump releasing agent, by weight percentage including following component：Aqueous fluorine-carbon paint（It is commercially available, liquid）4%；
Polyvinyl alcohol（It is commercially available, dry powder）5%；Silicone oil emulsion（Liquid）0.5%；Surfactant（It can be lauryl sodium sulfate, powder
Shape, it is soluble easily in water）1.5%；Coalescents（It can be propandiol butyl ether, liquid）0.5%；Water（It can be tap water）
88.5%。
The preparation method of above-mentioned artificial quartz in lump releasing agent, comprises the following steps：
1）Sequentially add in a kettle first 88.5% water, 0.5% defoamer, 1.5% surfactant and 0.5% into
Film auxiliary agent, stirs evenly；
2）Sequentially add 4% aqueous fluorine-carbon paint and 5% polyvinyl alcohol in a kettle afterwards, be warming up to 70-90 DEG C, during addition
Between be 2h, keep the temperature 3-6h, got product after being cooled to room temperature.
Embodiment 2：
A kind of artificial quartz in lump releasing agent, by weight percentage including following component：Aqueous fluorine-carbon paint（It is commercially available, liquid）8%；
Polyvinyl alcohol（It is commercially available, dry powder）10%；Defoamer（It can be silicone oil emulsion, liquid）0.5%；Surfactant（It can be
Lauryl sodium sulfate, powdery are soluble easily in water）1%；Coalescents（It can be propandiol butyl ether, liquid）0.5%；Water（It can
Think tap water）80%.
The preparation method of above-mentioned artificial quartz in lump releasing agent, comprises the following steps：
1）Water, 0.5% defoamer, 1% surfactant and 0.5% film forming for sequentially adding 80% in a kettle first help
Agent, stirs evenly；
2）Sequentially add 8% aqueous fluorine-carbon paint and 10% polyvinyl alcohol while stirring in a kettle afterwards, be warming up to 70-90
DEG C, the addition time is 2h, keeps the temperature 3-6h, is got product after being cooled to room temperature.
Embodiment 3：
A kind of artificial quartz in lump releasing agent, by weight percentage including following component：Aqueous fluorine-carbon paint（It is commercially available, liquid）20%；
Polyvinyl alcohol（It is commercially available, dry powder）15%；Silicone oil emulsion（Liquid）0.5%；Surfactant（It can be lauryl sodium sulfate,
Powdery, it is soluble easily in water）1.5%；Coalescents（It can be propandiol butyl ether, liquid）1%；Water（It can be tap water）62%.
The preparation method of above-mentioned artificial quartz in lump releasing agent, comprises the following steps：
1）Water, 0.5% defoamer, 1.5% surfactant and 1% film forming for sequentially adding 62% in a kettle first help
Agent, stirs evenly；
2）Sequentially add 20% aqueous fluorine-carbon paint and 15% polyvinyl alcohol while stirring in a kettle afterwards, be warming up to 70-
90 DEG C, the addition time is 2h, keeps the temperature 3-6h, is got product after being cooled to room temperature.
Embodiment 4：
A kind of artificial quartz in lump releasing agent, by weight percentage including following component：Aqueous fluorine-carbon paint（It is commercially available, liquid）30%；
Polyvinyl alcohol（It is commercially available, dry powder）20%；Silicone oil emulsion（Liquid）0.5%；Surfactant（It can be lauryl sodium sulfate,
Powdery, it is soluble easily in water）2%；Coalescents（It can be propandiol butyl ether, liquid）1%；Water（It can be tap water）46.5%.
The preparation method of above-mentioned artificial quartz in lump releasing agent, comprises the following steps：
1）Water, 0.5% defoamer, 2% surfactant and 1% film forming for sequentially adding 46.5% in a kettle first help
Agent, stirs evenly；
2）Sequentially add 30% aqueous fluorine-carbon paint and 20% polyvinyl alcohol while stirring in a kettle afterwards, be warming up to 70-
90 DEG C, the addition time is 2h, keeps the temperature 3-6h, is got product after being cooled to room temperature.
Performance test
In order to test the performance of artificial quartz in lump releasing agent of the present invention, test specimen is prepared according to relevant standard, to embodiment
Releasing agent described in 1-4 is tested for the property.Test data is as shown in table 1.
Table 1
Can smoothly it be taken off when in use as it can be seen from table 1 the artificial quartz in lump releasing agent described in 1-4 of the embodiment of the present invention has
Mould, do not dissolve and without layering the advantages of.
Although above the present invention is described in detail with a general description of the specific embodiments,
On the basis of the present invention, it can be made some modifications or improvements, this will be apparent to those skilled in the art.Cause
This, these modifications or improvements, belong to the scope of protection of present invention without departing from theon the basis of the spirit of the present invention.
Claims (10)
1. a kind of artificial quartz in lump releasing agent, it is characterised in that by weight percentage including following component：
Interleaving agent 1%-30%；
Binding agent 1%-30%；
Defoamer 0.5%；
Surfactant 1%-3%；
Coalescents 0.5%-1%；
Water surplus.
2. artificial quartz in lump releasing agent as claimed in claim 1, it is characterised in that include such as the following group by weight percentage
Point：
Interleaving agent 4%；
Binding agent 5%；
Defoamer 0.5%；
Surfactant 1.5%；
Coalescents 0.5%；
Water 88.5%.
3. artificial quartz in lump releasing agent as claimed in claim 1, it is characterised in that include such as the following group by weight percentage
Point：
Interleaving agent 8%；
Binding agent 10%；
Defoamer 0.5%；
Surfactant 1%；
Coalescents 0.5%；
Water 80%.
4. artificial quartz in lump releasing agent as claimed in claim 1, it is characterised in that include such as the following group by weight percentage
Point：
Interleaving agent 20%；
Binding agent 15%；
Defoamer 0.5%；
Surfactant 1.5%；
Coalescents 1%；
Water 62%.
5. artificial quartz in lump releasing agent as claimed in claim 1, it is characterised in that include such as the following group by weight percentage
Point：
Interleaving agent 30%；
Binding agent 20%；
Defoamer 0.5%；
Surfactant 2%；
Coalescents 1%；
Water 46.5%.
6. such as claim 1-5 any one of them artificial quartz in lump releasing agents, it is characterised in that the interleaving agent is water-based fluorine
Carbon paint；The binding agent is polyvinyl alcohol, and the polyvinyl alcohol is the dry powder of 60 mesh.
7. artificial quartz in lump releasing agent as claimed in claim 6, it is characterised in that the defoamer is aqueous defoamer.
8. artificial quartz in lump releasing agent as claimed in claim 7, it is characterised in that the defoamer is silicone oil emulsion.
9. artificial quartz in lump releasing agent as claimed in claim 8, it is characterised in that the surfactant is dodecyl sulphur
Sour sodium；The coalescents are propandiol butyl ether；The water is tap water.
10. the preparation method of the artificial quartz in lump releasing agent described in a kind of claim 9, it is characterised in that comprise the following steps：
1）Sequentially add water, defoamer, surfactant and the coalescents of formula ratio in a kettle first, stir evenly；
2）Sequentially add the interleaving agent and binding agent of formula ratio while stirring in a kettle afterwards, be warming up to 70-90 DEG C, add
Time is 2h, keeps the temperature 3-6h, is got product after being cooled to room temperature.