CN107916566A - A kind of preparation method of covering of the fan Mould-proof shell fabric - Google Patents
A kind of preparation method of covering of the fan Mould-proof shell fabric Download PDFInfo
- Publication number
- CN107916566A CN107916566A CN201711045388.7A CN201711045388A CN107916566A CN 107916566 A CN107916566 A CN 107916566A CN 201711045388 A CN201711045388 A CN 201711045388A CN 107916566 A CN107916566 A CN 107916566A
- Authority
- CN
- China
- Prior art keywords
- parts
- fabric
- covering
- preparation
- fan
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of preparation method of covering of the fan Mould-proof shell fabric of the present invention, includes the following steps:S1:Anti-mildew agent is configured, natural fiber or terylene, the pure spinning of acrylic, or yarn weaved fabric are put into anti-mildew agent and soaked, after soaking 24 48h, the fabric in medicament is stirred and continues to soak 24 48h;S2:Dried under natural environment;S3:Post-processing is carried out to fabric, including dyes, print and embroiders;S4:The web surface completed to post-processing is coated mould proof antibacterial paint;S5:Drying;Drying temperature is 30 ° 40 °; fabric is immersed in anti-mildew agent so that anti-mildew agent is immersed in fabric, while is coated mould proof antibacterial paint in the web surface that post-processing is completed; micron order protective layer is formed, the covering of the fan fabric of antimildew and antibacterial function admirable is prepared.
Description
Technical field
The present invention relates to fan making technical field, specifically, is related to a kind of preparation method of covering of the fan Mould-proof shell fabric.
Background technology
Fan is air inducing articles for use, the thing of summertime indispensability.Chinese Han nationality's fan culture has deep cultural deposits, is han nationality
One integration section of culture, it is with bamboo culture, buddhism culture close relation.Always there is the title of " Zhi Shan kingdoms " in China.
The species of fan includes feather fan, cattail leaf fan, pheasant fan, circular fan, folding fan, thin,tough silk mandarin fan, golden paint fan, black paper fan, sandalwood fan etc..It is included in
The system fan skill of List of National Intangible Cultural Heritage has Law Firm Suzhou Jiangsu sandalwood fan, Zhejiang Hangzhou Wang Xing notes fan, Chongqing honor
Prosperous folding fan, Zigong, Sichuan Gong fan, Xinhui of Guangdong Province's palm-leaf fun, Huzhou feather fan.In modern market, processor is by fan making by paper
Face has changed fabric into so that the collection of fan is easier to preserve, and the service life also strengthens, and moulding is also increasingly abundanter, but fabric
The problem of moisture absorption is mouldy and damaged can be faced.
The content of the invention
The present invention proposes a kind of preparation method of covering of the fan Mould-proof shell fabric, exists to solve fan fabric in the prior art
The mouldy and damaged deficiency of the moisture absorption.
The technical proposal of the invention is realized in this way:
A kind of preparation method of covering of the fan Mould-proof shell fabric, includes the following steps:
S1:Anti-mildew agent is configured, natural fiber or terylene, the pure spinning of acrylic, or yarn weaved fabric are put into anti-mildew agent
Middle immersion, after soaking 24-48h, stirs the fabric in medicament and continues to soak 24-48h;
S2:Dried under natural environment;
S3:Post-processing is carried out to fabric, including dyes, print and embroiders;
S4:The web surface completed to post-processing is coated mould proof antibacterial paint;
S5:Drying;Drying temperature is 30 ° -40 °.
Further, the anti-mildew agent includes the component of following parts by weight:4-10 parts of zinc acetate, sodium thiosulfate 5-8
Part, 5-9 parts of acetic acid, 5-14 parts of polymeric aluminum chloride, 4-18 parts of Substance, 5-18 parts of lignin and excess water.
Further, the anti-mildew agent includes the component of following parts by weight:6 parts of zinc acetate, 7 parts of sodium thiosulfate, vinegar
6 parts of acid, 8 parts of polymeric aluminum chloride, 13 parts of Substance, 10 parts of lignin and excess water
Further, the Substance includes the distillation extract of the fruit of a cubeb litsea tree, mustard, Chinese cassia tree, cassia bark and garlic.
Further, the mould proof antibacterial paint includes the component of following parts by weight:3~8 parts of polyacrylamide, acrylic acid
10~14 parts of ethyl ester, 8~11 parts of silica, 20-25 parts of oyster shell whiting, 3~8 parts of chitosan quaternary ammonium salt, 13~18 parts of montmorillonite
And excess water.
Further, the mould proof antibacterial paint includes the component of following parts by weight:8 parts of polyacrylamide, acrylic acid second
12 parts of ester, 9 parts of silica, 22 parts of oyster shell whiting, 3 parts of chitosan quaternary ammonium salt, 13 parts of montmorillonite and excess water.
The beneficial aspects of the present invention are:Fabric is immersed in anti-mildew agent so that anti-mildew agent is immersed in fabric,
The web surface completed at the same time in post-processing is coated mould proof antibacterial paint, forms micron order protective layer, is prepared mould proof
The covering of the fan fabric of excellent antibacterial performance.
Embodiment
The technical solution in the embodiment of the present invention is clearly and completely described below, it is clear that described embodiment
Only part of the embodiment of the present invention, instead of all the embodiments.Based on the embodiments of the present invention, the common skill in this area
Art personnel all other embodiments obtained without creative efforts, belong to the model that the present invention protects
Enclose.
Embodiment:
A kind of preparation method of covering of the fan Mould-proof shell fabric, includes the following steps:
S1:Anti-mildew agent is configured, natural fiber or terylene, the pure spinning of acrylic, or yarn weaved fabric are put into anti-mildew agent
Middle immersion, after soaking 24-48h, stirs the fabric in medicament and continues to soak 24-48h;
Wherein:The anti-mildew agent includes the component of following parts by weight:6 parts of zinc acetate, 7 parts of sodium thiosulfate, acetic acid 6
Part, 8 parts of polymeric aluminum chloride, 13 parts of Substance, 10 parts of lignin and excess water, it is grey that the Substance includes mountain
Son, mustard, Chinese cassia tree, cassia bark and the distillation of garlic extract.
S2:Dried under natural environment;
S3:Post-processing is carried out to fabric, including dyes, print and embroiders;
S4:The web surface completed to post-processing is coated mould proof antibacterial paint;
Wherein, the mould proof antibacterial paint includes the component of following parts by weight:8 parts of polyacrylamide, ethyl acrylate 12
Part, 9 parts of silica, 22 parts of oyster shell whiting, 3 parts of chitosan quaternary ammonium salt, 13 parts of montmorillonite and excess water.
S5:Drying;Drying temperature is 30 ° -40 °.
Fabric is immersed in anti-mildew agent so that anti-mildew agent is immersed in fabric, while in the face that post-processing is completed
Material surface is coated mould proof antibacterial paint, forms micron order protective layer, and the covering of the fan face of antimildew and antibacterial function admirable is prepared
Material.
The foregoing is merely illustrative of the preferred embodiments of the present invention, is not intended to limit the invention, all essences in the present invention
With within principle, any modification, equivalent replacement, improvement and so on, should all be included in the protection scope of the present invention god.
Claims (6)
- A kind of 1. preparation method of covering of the fan Mould-proof shell fabric, it is characterised in that:Include the following steps:S1:Anti-mildew agent is configured, natural fiber or terylene, the pure spinning of acrylic, or yarn weaved fabric are put into anti-mildew agent and soaked Bubble, after soaking 24-48h, stirs the fabric in medicament and continues to soak 24-48h;S2:Dried under natural environment;S3:Post-processing is carried out to fabric, including dyes, print and embroiders;S4:The web surface completed to post-processing is coated mould proof antibacterial paint;S5:Drying;Drying temperature is 30 ° -40 °.
- A kind of 2. preparation method of covering of the fan Mould-proof shell fabric according to claim 1, it is characterised in that:The anti-mildew agent Include the component of following parts by weight:4-10 parts of zinc acetate, 5-8 parts of sodium thiosulfate, 5-9 parts of acetic acid, 5-14 parts of polymeric aluminum chloride, 4-18 parts of Substance, 5-18 parts of lignin and excess water.
- A kind of 3. preparation method of covering of the fan Mould-proof shell fabric according to claim 2, it is characterised in that:The anti-mildew agent Include the component of following parts by weight:6 parts of zinc acetate, 7 parts of sodium thiosulfate, 6 parts of acetic acid, 8 parts of polymeric aluminum chloride, bacteriostatic activity thing 13 parts of matter, 10 parts of lignin and excess water.
- A kind of 4. preparation method of covering of the fan Mould-proof shell fabric according to claim 2, it is characterised in that:The bacteriostatic activity Material includes the distillation extract of the fruit of a cubeb litsea tree, mustard, Chinese cassia tree, cassia bark and garlic.
- A kind of 5. preparation method of covering of the fan Mould-proof shell fabric according to claim 1, it is characterised in that:The antimildew and antibacterial Coating includes the component of following parts by weight:3~8 parts of polyacrylamide, 10~14 parts of ethyl acrylate, 8~11 parts of silica, 20-25 parts of oyster shell whiting, 3~8 parts of chitosan quaternary ammonium salt, 13~18 parts of montmorillonite and excess water.
- A kind of 6. preparation method of covering of the fan Mould-proof shell fabric according to claim 5, it is characterised in that:The antimildew and antibacterial Coating includes the component of following parts by weight:8 parts of polyacrylamide, 12 parts of ethyl acrylate, 9 parts of silica, 22 parts of oyster shell whiting, 3 parts of chitosan quaternary ammonium salt, 13 parts of montmorillonite and excess water.