CN107910110A - A kind of charging unit cable - Google Patents

A kind of charging unit cable Download PDF

Info

Publication number
CN107910110A
CN107910110A CN201711118867.7A CN201711118867A CN107910110A CN 107910110 A CN107910110 A CN 107910110A CN 201711118867 A CN201711118867 A CN 201711118867A CN 107910110 A CN107910110 A CN 107910110A
Authority
CN
China
Prior art keywords
parts
layer
bars
conductor
average grain
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201711118867.7A
Other languages
Chinese (zh)
Inventor
不公告发明人
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201711118867.7A priority Critical patent/CN107910110A/en
Publication of CN107910110A publication Critical patent/CN107910110A/en
Pending legal-status Critical Current

Abstract

A kind of charging unit cable of the present invention, including three power wire cores, a bars control conductor；Wrap up three power wire cores and the braiding layer of a bars control conductor；The resin filling layer being filled between the braiding layer and three power wire cores, a bars control conductor；The oversheath being extruded in outside the braiding layer；The power wire core is by conductor, the insulating layer composition being extruded in outside the conductor；The signal control line core including three bars by transmitting control line；Wrap up the lapping layer of three bars transmission control line；The resin shielded layer being filled between the lapping layer and three bars transmission control line.The charging device of electric automobile cable of the present invention, using special structure design and environment-friendly materials, has a low smoke, zero halogen low toxicity characteristic, and light transmittance during cable fire is high, no HCL etchant gases release (gas pH value is 6.78)；This cable has good soft bending property and excellent shielding properties.

Description

A kind of charging unit cable
Technical field
The present invention relates to a kind of cable, more particularly to a kind of charging unit cable.
Background technology
New-energy electric vehicle compared with orthodox car, have operate steadily, noiseless, pollution-free, low-carbon emission, Gao An Congruent characteristic, and application prospect is had a vast market, it has been included in《National Program for Medium-to Long-term Scientific and Technological Development》With 《National " 12th Five-Year Plan " scientific and technological development planning》, with a wide range of popularization of electric automobile and commercial application, electronic vapour Car charging pile cabling requirements amount also doubles therewith.Since charging pile is larger with cable load current value（The largest of about reach 400A）, electricity Conductor easily generates heat in cable energization operation, and frequently pulls movement in use, for a long time exposed to outdoor environment, easily by vapour The destruction corrosion of the factors such as car rolls, solar radiation, air oxidation, wet water environment and soda acid compound, therefore, need to be to charging Stake proposes the requirement of higher with performance indicators such as the resistance to oxidation of cable, weatherability, wearability and resistance to mechanical external force.
Chinese patent discloses a kind of charging pile cable (CN201320068080), which is followed successively by from inside to outside：It is more The mutually twisted insulated wire cores of root, twining package tape, braiding layer, oversheath, the insulated wire cores are followed successively by silver-plated copper and lead from inside to outside Body and insulating layer, between the insulated wire cores, and are provided with filler, filler between the insulated wire cores and twining package tape Selected from non-absorbent material, braiding layer is braided steel wire, and the outside diameter of cable is 8~30mm.
Chinese patent discloses a kind of direct-current charging post private cable (CN201420171093), including cable core, outside cable core It is surrounded with OPP twining package tapes, non-woven fabrics twining package tape and sheath week successively from inside to outside, cable core includes connection and confirms cable, communication Cable, cathode power supply line, anode power cord and ground wire, connection confirm that cable includes outside and is surrounded with the two of OPP twining package tapes Root connection confirms line and an aramid yarn, and the communications cable includes being disposed with OPP twining package tapes, tinned copper wire from inside to outside The core of braiding layer, insulating layer, core include two order wires and an aramid yarn, and cathode power supply line, anode power cord, connect The conductor that ground wire is provided with insulating layer by outside forms, and conductor is twisted by stranded copper wire, and the gap portion in cable core is equal It is provided with filler.
The content of the invention
The purpose of the present invention is overcome the technological deficiency of existing cable, there is provided one kind have high intensity, high tenacity, it is wear-resisting, Oil resistant, it is ageing-resistant, low smoke, zero halogen is less toxic the characteristics of；Dissipated with excellent bending property and shielding properties, and prominent heat conduction The charging device of electric automobile cable of hot property.
The charging device of electric automobile cable of the present invention, including three power wire cores, a bars control conductor；Parcel institute State three power wire cores and the braiding layer of a bars control conductor；Be filled in the braiding layer and three power wire cores, Resin filling layer between one bars control conductor；The oversheath being extruded in outside the braiding layer；The power wire core is by leading Body, the insulating layer composition being extruded in outside the conductor；The signal control line core including three bars by transmitting control line；Parcel Three bars transmit the lapping layer of control line；The resin being filled between the lapping layer and three bars transmission control line Shielded layer.
As an optimization, the charging device of electric automobile cable, including three power wire cores, a bars control conductor；Bag Wrap up in three power wire cores and the PET mesh grid tube layer of a bars control conductor；Be filled in the PET mesh grids tube layer and Resin filling layer between three power wire cores, a bars control conductor；It is extruded in outside the PET mesh grids tube layer Thermoplastic polyurethane elastomer oversheath；The power wire core is extruded in the multiply soft copper by multiply soft copper silk stranded conductor Thermoplastic polyester elastomer insulating layer composition outside silk stranded conductor；The signal control line core is controlled by being transmitted including three bars Line processed；Wrap up the Teflon adhesive tape lapping layer of three bars transmission control line；It is filled in the Teflon adhesive tape lapping layer and institute State the resin shielded layer between three bars transmission control line.
As an optimization, the charging device of electric automobile cable, three bars transmit control line by tinning steel-in-copper conductor, The insulating sheath composition being extruded in outside the tinning steel-in-copper conductor.
As an optimization, the charging device of electric automobile cable, the resin shielded layer and resin filling layer, by following heavy The component of amount number is made：65~70 parts of acrylic resin, 35~40 parts of waterborne polyurethane resin, isomeric alcohol polyethenoxy ether 1 ~1.2 parts, 2~2.5 parts of average grain diameter 40nm nano strontium titanates, 3~4 parts of average grain diameter 30nm nanometer zinc ferrites, diethylene glycol 3~4 parts of monobutyl ether, 4~5 parts of average grain diameter 20um hydroxyapatites, 2~3 parts of sec-Butyl Acetate, titanium acetylacetone 1.2~1.5 Part, 8~20 parts of average grain diameter 8um silica 1s, 10~12 parts of average grain diameter 4um calcined kaolins powder, average grain diameter 2um are sub- 4~5 parts of titanium oxide, 1~1.5 part of propylgallate, 2~2.5 parts of erythorbic acid sodium.
The charging device of electric automobile cable, compound resin used in resin shielded layer and resin filling layer, by following Method is made：
(1) by 1 part of isomeric alcohol polyethenoxy ether, it is added in 20 parts of pure water, then adds average grain diameter 40nm nano-titaniums Sour 2 parts of strontium, 3 parts of average grain diameter 30nm nanometer zinc ferrites；Stirred 5 minutes with magnetic stirrer, ultrasonic wave shakes under the conditions of 85 DEG C Swing 120 minutes；Then when drying 6 is small in 90 DEG C of baking ovens；
(2) by 1.2 parts of titanium acetylacetone, 8 parts of average grain diameter 8um silica 1s, 10 parts of average grain diameter 4um calcined kaolins powder, 4 parts of average grain diameter 2um Asias titanium oxide, adds high-speed kneading machine Hybrid Heating to 90~100 DEG C, is uniformly mixed；
(3) by 3 parts of diethylene glycol monobutyl ether, 2 parts of sec-Butyl Acetate, the mixing of 4 parts of average grain diameter 20um hydroxyapatites, 50~ 60 DEG C, stir evenly;
(4) by 65 parts of acrylic resin, 35 parts of waterborne polyurethane resin, add in vertical mould wash mixer and stir evenly, then The mixture added in step (2) stirs 3 minutes under the conditions of 80~85 DEG C, then adds the mixture in step (3) 90 Stir 3 minutes under the conditions of~95 DEG C, the mixture then added in step (1) stirs 3 minutes under the conditions of 70~75 DEG C, finally Under the conditions of 45~55 DEG C, sequentially add 1 part of propylgallate, 2 parts of erythorbic acid sodium, stirring 3 minutes compound resin.
The charging device of electric automobile cable of the present invention is low with Halogen using special structure design and environment-friendly materials Cigarette low toxicity characteristic, light transmittance during cable fire is high, no HCL etchant gases release (gas pH value is 6.78)；This cable has Good soft bending property and excellent shielding properties, control and transmit to the signal of voltage, electric current etc. in charging process, With good anti-electromagnetic interference, the characteristics of stable signal transmission；Anti- askew folding more than 20000 times, it is wear-resisting more than 50000 times, resistance to Mill more than 50000 times.Particularly this cable has prominent heat conduction and heat radiation performance, is adapted to radiate during large current charge.The present invention Using the oversheath with the excellent comprehensive performance such as high intensity, high tenacity, wear-resisting, oil resistant；Small product size of the present invention is small, weight Gently, ageing-resistant, physical mechanical property is excellent, easy for installation, safe to use, reliable.
Brief description of the drawings
Fig. 1 is the structure diagram of charging device of electric automobile cable of the present invention.
Embodiment
The invention will be further described for example given below plan, but is not to be construed as to the scope of the present invention Limitation, those skilled in the art's some the nonessential modifications and adaptations of content to the present invention according to the present invention, still fall within this The protection domain of invention.
Embodiment 1：As shown in Figure 1, charging device of electric automobile cable, including three power wire cores 1, bars control Core 2；Wrap up the PET mesh grids tube layer 3 of three power wire cores, the 1 and one bars control conductor 2；It is filled in the PET Resin filling layer 4 between mesh grid tube layer 3 and three power wire cores 1, a bars control conductor 2；It is extruded in described Thermoplastic polyurethane elastomer Germany BASF 1185A thermoplastic polyurethane elastomer rubber outside PET mesh grids tube layer 3 （TPU）5；Power wire core 1 is by multiply soft copper silk stranded conductor 11, the U.S. being extruded in outside the multiply soft copper silk stranded conductor 11 Du Pont's TPEE-6356 thermoplastic polyester elastomers（TPEE）Insulating layer 12 forms；Signal control line core 2 including three bars by passing Defeated control line 21；Wrap up the Teflon adhesive tape lapping layer 22 of three bars transmission control line 21；It is filled in the Teflon adhesive tape Resin shielded layer 23 between lapping layer 22 and three bars transmission control line 21.Three bars transmit control line 21 by Tinning steel-in-copper conductor 211, the Dupont TPEE-6356 thermoplastic polyesters being extruded in outside the tinning steel-in-copper conductor 211 Elastomer（TPEE）Insulating sheath 212 forms.
Charging device of electric automobile cable, resin shielded layer and resin filling layer, are made by the following method：
(1) by isomeric alcohol polyethenoxy ether（EH-9）1 kilogram, it is added in 20 kilograms of pure water, then adds average grain diameter 2 kilograms of 40nm nano strontium titanates, 3 kilograms of average grain diameter 30nm nanometer zinc ferrites；Stirred 5 minutes with magnetic stirrer, at 85 DEG C Under the conditions of ultrasonic oscillation 120 minutes；Then when drying 6 is small in 90 DEG C of baking ovens；
(2) by Nanjing Pin Ning coupling agents Co., Ltd（AA-75）1.2 kilograms of titanium acetylacetone, average grain diameter 8um silica 1s 8 Kilogram, 10 kilograms of average grain diameter 4um calcined kaolins powder, 4 kilograms of average grain diameter 2um Asias titanium oxide, add high-speed kneading machine mix Conjunction is heated to 90~100 DEG C, is uniformly mixed；
(3) 3 kilograms of diethylene glycol monobutyl ether, 2 kilograms of sec-Butyl Acetate, 4 kilograms of average grain diameter 20um hydroxyapatites are mixed, At 50~60 DEG C, stir evenly；
(4) 65 kilograms of Pests in Tianjin Binhai New Area An Delong developments in science and technology Co., Ltd DM-2221 acrylic resins, Jining inscription are reached 35 kilograms of new material Co., Ltd HK7080 waterborne polyurethane resins, add in vertical mould wash mixer and stir evenly, Ran Houjia Enter the mixture in step (2) and stir 3 minutes under the conditions of 80~85 DEG C, then add mixture in step (3) 90~ Stirred under the conditions of 95 DEG C 3 minutes, the mixture then added in step (1) stirs 3 minutes under the conditions of 70~75 DEG C, finally exists Under the conditions of 45~55 DEG C, sequentially add 1 kilogram of propylgallate, 2 kilograms of erythorbic acid sodium, stirring 3 minutes compound tree Fat.
Resin material of the present invention, using unique formula, acts synergistically between each component and protrudes；With good thermal conductivity The fire resistance that can and protrude；With excellent heat-proof aging oil resistance and unexpected capability of electromagnetic shielding, reach Using other components and the unapproachable performance of auxiliary combination.The composite resin material, thermal conductivity factor 0.467W/mK；Anti-flammability (m), charing height is 0.48, oxygen index (OI) 40%.Using SJ20524 Materials ' Shielding Effectiveness test method test shielding properties >= 56dB (30MHz~1.5GHz)；Tensile strength 21.79MPa, elongation at break 386%, tearing strength 29.61KN/m.Hot-air 185 DEG C × 168 h of senile experiment, tensile strength change rate：10.7%th, elongation at break change rate -11.6%.
Embodiment 2：Charging device of electric automobile cable, structure is such as embodiment 1, and difference is, resin shielded layer And resin filling layer, it is made by the following method：
(1) by isomeric alcohol polyethenoxy ether（EH-9）1.2 kilograms, it is added in 20 kilograms of pure water, then adds average grain 2.5 kilograms of footpath 40nm nano strontium titanates, 4 kilograms of average grain diameter 30nm nanometer zinc ferrites；Stirred 5 minutes with magnetic stirrer, Ultrasonic oscillation 120 minutes under the conditions of 85 DEG C；Then when drying 6 is small in 90 DEG C of baking ovens；
(2) by Nanjing Pin Ning coupling agents Co., Ltd（AA-75）1.5 kilograms of titanium acetylacetone, average grain diameter 8um silica 20 Kilogram, 12 kilograms of average grain diameter 4um calcined kaolins powder, 5 kilograms of average grain diameter 2um Asias titanium oxide, add high-speed kneading machine mix Conjunction is heated to 90~100 DEG C, is uniformly mixed；
(3) 4 kilograms of diethylene glycol monobutyl ether, 3 kilograms of sec-Butyl Acetate, 5 kilograms of average grain diameter 20um hydroxyapatites are mixed, At 50~60 DEG C, stir evenly；
(4) 70 kilograms of Pests in Tianjin Binhai New Area An Delong developments in science and technology Co., Ltd DM-2221 acrylic resins, Jining inscription are reached 40 kilograms of new material Co., Ltd HK7080 waterborne polyurethane resins, add in vertical mould wash mixer and stir evenly, Ran Houjia Enter the mixture in step (2) and stir 3 minutes under the conditions of 80~85 DEG C, then add mixture in step (3) 90~ Stirred under the conditions of 95 DEG C 3 minutes, the mixture then added in step (1) stirs 3 minutes under the conditions of 70~75 DEG C, finally exists Under the conditions of 45~55 DEG C, sequentially add 1.5 kilograms of propylgallate, 2.5 kilograms of erythorbic acid sodium, stirring 3 minutes it is multiple Resin.Resin material of the present invention, using unique formula, acts synergistically between each component and protrudes；With good thermal conductivity The fire resistance that can and protrude；With excellent heat-proof aging oil resistance and unexpected capability of electromagnetic shielding, reach Using other components and the unapproachable performance of auxiliary combination.The composite resin material, thermal conductivity factor 0.461W/mK；Anti-flammability (m), charing height is 0.48, oxygen index (OI) 40%.Using SJ20524 Materials ' Shielding Effectiveness test method test shielding properties >= 57dB (30MHz~1.5GHz)；Tensile strength 21.55MPa, elongation at break 385%, tearing strength 29.33KN/m.Hot-air 185 DEG C × 168 h of senile experiment, tensile strength change rate：10.9%th, elongation at break change rate -11.8%.
Comparative example 1：Charging device of electric automobile cable, structure is such as embodiment 1, and difference is, resin shielded layer And resin filling layer, it is made by the following method：
(1) by isomeric alcohol polyethenoxy ether（EH-9）1 kilogram, it is added in 20 kilograms of pure water, then adds average grain diameter 2 kilograms of 40nm nano strontium titanates；Stirred 5 minutes with magnetic stirrer, ultrasonic oscillation 120 minutes under the conditions of 85 DEG C；Then When drying 6 is small in 90 DEG C of baking ovens；
(2) by Nanjing Pin Ning coupling agents Co., Ltd（AA-75）1.2 kilograms of titanium acetylacetone, average grain diameter 8um silica 1s 8 Kilogram, 10 kilograms of average grain diameter 4um calcined kaolins powder, 4 kilograms of average grain diameter 2um Asias titanium oxide, add high-speed kneading machine mix Conjunction is heated to 90~100 DEG C, is uniformly mixed；
(3) 65 kilograms of Pests in Tianjin Binhai New Area An Delong developments in science and technology Co., Ltd DM-2221 acrylic resins, Jining inscription are reached 35 kilograms of new material Co., Ltd HK7080 waterborne polyurethane resins, add in vertical mould wash mixer and stir evenly, Ran Houjia Enter the mixture in step (2) and stir 3 minutes under the conditions of 80~85 DEG C, then add mixture in step (1) 70~ Stirred 3 minutes under the conditions of 75 DEG C, finally under the conditions of 45~55 DEG C, sequentially add 1 kilogram of propylgallate, erythorbic acid sodium 2 kilograms, stirring 3 minutes compound resin.The composite resin material, thermal conductivity factor 0.412W/mK；Anti-flammability (m), charing are high Spend for 0.38, oxygen index (OI) 39%.Shielding properties >=50dB (30MHz are tested using the test method of SJ20524 Materials ' Shielding Effectiveness ~1.5GHz)；Tensile strength 18.79MPa, elongation at break 369%, tearing strength 26.61KN/m.Hot air aging experiment 185 DEG C × 168 h, tensile strength change rate：10.7%th, elongation at break change rate -12.2%.
Comparative example 2：Charging device of electric automobile cable, structure is such as embodiment 1, and difference is, resin shielded layer And resin filling layer, it is made by the following method：
(1) by isomeric alcohol polyethenoxy ether（EH-9）1.2 kilograms, it is added in 20 kilograms of pure water, then adds average grain 4 kilograms of footpath 30nm nanometer zinc ferrites；Stirred 5 minutes with magnetic stirrer, ultrasonic oscillation 120 minutes under the conditions of 85 DEG C；So When drying 6 is small in 90 DEG C of baking ovens afterwards；
(2) by Nanjing Pin Ning coupling agents Co., Ltd（AA-75）1.5 kilograms of titanium acetylacetone, average grain diameter 8um silica 30 Kilogram, 5 kilograms of average grain diameter 2um Asias titanium oxide, add high-speed kneading machine Hybrid Heating to 90~100 DEG C, be uniformly mixed；
(3) by 5 kilograms of 4 kilograms of diethylene glycol monobutyl ether, average grain diameter 20um hydroxyapatites mixing, at 50~60 DEG C, stirring Uniformly；
(4) 70 kilograms of Pests in Tianjin Binhai New Area An Delong developments in science and technology Co., Ltd DM-2221 acrylic resins, Jining inscription are reached 40 kilograms of new material Co., Ltd HK7080 waterborne polyurethane resins, add in vertical mould wash mixer and stir evenly, Ran Houjia Enter the mixture in step (2) and stir 3 minutes under the conditions of 80~85 DEG C, then add mixture in step (3) 90~ Stirred under the conditions of 95 DEG C 3 minutes, the mixture then added in step (1) stirs 3 minutes under the conditions of 70~75 DEG C, finally exists Under the conditions of 45~55 DEG C, add 1.5 kilograms of propylgallate, stirring 3 minutes compound resin.The composite resin material, Thermal conductivity factor 0.391W/mK；Anti-flammability (m), charing height are 0.42, oxygen index (OI) 39%.Using SJ20524 Materials ' Shielding Effectiveness Test method test shielding properties >=55dB (30MHz~1.5GHz)；Tensile strength 18.95MPa, elongation at break 378%, Tearing strength 25.33KN/m.185 DEG C × 168 h, tensile strength change rate are tested in hot air aging：12.2%th, elongation at break Change rate -14.5%.

Claims (1)

  1. A kind of 1. charging device of electric automobile cable, it is characterised in that：Including three power wire cores, a bars control conductor； Wrap up three power wire cores and the PET mesh grid tube layer of a bars control conductor；It is filled in the PET mesh grids tube layer Resin filling layer between three power wire cores, a bars control conductor；It is extruded in outside the PET mesh grids tube layer Thermoplastic polyurethane elastomer oversheath；
    The power wire core is by multiply soft copper silk stranded conductor, the thermoplastic poly being extruded in outside the multiply soft copper silk stranded conductor Ester elastomer insulating layer forms；
    The signal control line core including three bars by transmitting control line；Wrap up the Teflon glue of three bars transmission control line Band lapping layer；The resin shielded layer being filled between the Teflon adhesive tape lapping layer and three bars transmission control line；
    The resin shielded layer and resin filling layer, are made by the component of following parts by weight：It is 70 parts of acrylic resin, water-based 40 parts of polyurethane resin, 1.2 parts of isomeric alcohol polyethenoxy ether, 2.5 parts of average grain diameter 40nm nano strontium titanates, average grain diameter 30nm 4 parts of nanometer zinc ferrite, 4 parts of diethylene glycol monobutyl ether, 5 parts of average grain diameter 20um hydroxyapatites, 3 parts of sec-Butyl Acetate, acetyl 1.5 parts of acetone titanium, 20 parts of average grain diameter 8um silica, 12 parts of average grain diameter 4um calcined kaolins powder, average grain diameter 2um are sub- 5 parts of titanium oxide, 1.5 parts of propylgallate, 2 part 2.5 of erythorbic acid sodium.
CN201711118867.7A 2016-07-10 2016-07-10 A kind of charging unit cable Pending CN107910110A (en)