CN107902913A - The production method of concave convered glass - Google Patents
The production method of concave convered glass Download PDFInfo
- Publication number
- CN107902913A CN107902913A CN201711084788.9A CN201711084788A CN107902913A CN 107902913 A CN107902913 A CN 107902913A CN 201711084788 A CN201711084788 A CN 201711084788A CN 107902913 A CN107902913 A CN 107902913A
- Authority
- CN
- China
- Prior art keywords
- glass
- glass baseplate
- code information
- parts
- production method
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of production method of concave convered glass, including:Glass baseplate is cleaned and dried with the cleaning machine equipped with ionized water and drying equipment;By the glass baseplate be put into the potassium nitrate solution 1~24 it is small when and keep the temperature conditionss of the first temperature range to carry out tempering processing;The glass baseplate is taken out from the potassium nitrate solution, is cooled to behind second temperature section and the glass baseplate is cleaned using pure water;The first 2 D code information is generated on the glass baseplate, first 2 D code information includes at least the thickness for needing to polish on the glass baseplate;First 2 D code information is read, the glass baseplate is polished according to first 2 D code information;The glass baseplate is put into inside recessed illiteracy liquid and carries out recessed illiteracy processing;Predetermined pattern is printed using the glass substrate surface is screen printed onto.The production method of above-mentioned concave convered glass, work efficiency is high and the concave convered glass effect produced is good.
Description
Technical field
The present invention relates to glass technology field, more particularly to the production method of concave convered glass.
Background technology
Glass be fused together by silica and other chemical substances formed (main production raw material is:Soda ash, stone
Lime stone, quartz).Contiguous network structure is formed in melting, cooling procedure medium viscosity, which gradually increases and hardens, causes what it was crystallized
Silicates nonmetallic materials.
The chemical composition of simple glass is Na2SiO3, CaSiO3, SiO2 or Na2OCaO6SiO2 etc., main component
It is silicate double salt, is a kind of non-crystalline solids of random structure.It is widely used in building, for every wind printing opacity, belonging to
Mixture.Separately have the oxide for being mixed into some metals or salt and show the coloured glass of color, and by physics or
Tempered glass etc. made from the method for person's chemistry.Sometimes some transparent plastics (such as polymethyl methacrylate) are also referred to as had
Machine glass.
There are following technical problem for conventional art:
Due to the artistry of concave convered glass, current concave convered glass is widely used.But existing recessed illiteracy glass
The production method work efficiency of glass is low, and obtained concave convered glass effect is bad.
The content of the invention
Based on this, it is necessary to for above-mentioned technical problem, there is provided a kind of production method of concave convered glass, work efficiency it is high and
The concave convered glass effect produced is good.
A kind of production method of concave convered glass, including:
Glass baseplate is cleaned and dried with the cleaning machine equipped with ionized water and drying equipment;
By the glass baseplate be put into the potassium nitrate solution 1~24 it is small when and keep the temperature strip of the first temperature range
Part carries out tempering processing;
The glass baseplate is taken out from the potassium nitrate solution, is cooled to behind second temperature section and to the glass
Base material is cleaned using pure water;
The first 2 D code information is generated on the glass baseplate, first 2 D code information includes at least the glass
The thickness polished is needed on base material;
First 2 D code information is read, the glass baseplate is polished according to first 2 D code information;
The glass baseplate is put into inside recessed illiteracy liquid and carries out recessed illiteracy processing;
Print predetermined pattern using the glass substrate surface is screen printed onto, air-dried after printed pattern 2 to 3 it is small when,
Dry again 1 to 2 it is small when;
Glass is sent into glass cleaning dryer, cleaning and drying, finished product;
Wherein, first temperature range is 445 degrees Celsius~450 degrees Celsius, and the second temperature section is Celsius for 20
~30 degrees Celsius of degree.
In other one embodiment, step " generate the first 2 D code information on the glass baseplate, described
One 2 D code information includes at least the thickness for needing to polish on the glass baseplate " in, generate first 2 D code information
Method is generated using laser code apparatus.
In other one embodiment, " first 2 D code information is read, according to first Quick Response Code in step
Information polishes the glass baseplate " in, polishing agent used be by percentage by weight the 2% aminotriacetic acid disodium, 2%
Alkyl acrylate, 2.2% pentadecanol polyoxyethylene ether, 1.2% surfactant, 0.4% defoamer, 5% ethanol, 1.6%
Laurate diethanol amine, enuatrol 1%, coconutalkyl alkylolamides phosphate ester salt 0.1% and excess water are prepared into.
In other one embodiment, " first 2 D code information is read, according to first Quick Response Code in step
Information polishes the glass baseplate " in, polishing agent used is cerium oxide.
In other one embodiment, the recessed illiteracy liquid includes 50 parts of hydrogen fluoride ammonia, barium sulfate 5 according to parts by weight
Part, 4 parts of hydrochloric acid, 6 parts of hydrofluoric acid and 20 parts of water.
In other one embodiment, in step, " using being screen printed onto, the glass substrate surface printing is predetermined
Pattern, air-dry after printed pattern 2 to 3 it is small when, then dry 1 to 2 it is small when " in, the ink that silk-screen printing uses is corrosion-resistanting ink.
In other one embodiment, the corrosion-resistanting ink includes 10 parts of anti-biotic material, spices 15 according to parts by weight
Part, 13 parts of acrylic emulsion, 13 parts of glycerine, 12 parts of colorant, 1.1 parts of water-based thickener, 1.2 parts of aqueous defoamer, water-based levelling
20 parts of 0.5 part of agent and water.
In other one embodiment, step " generate the first 2 D code information on the glass baseplate, described
One 2 D code information includes at least the thickness for needing to polish on the glass baseplate " in, to the thickness of glass baseplate polishing
For 1% to the 1.5% of the thickness of the glass baseplate.
In other one embodiment, " glass baseplate is put into inside recessed illiteracy liquid in step and carries out recessed illiteracy processing "
In, the glass baseplate is 3 degree to 6 degree with the recessed angle for covering liquid liquid level.
The production method of above-mentioned concave convered glass, work efficiency is high and the concave convered glass effect produced is good.
Brief description of the drawings
Fig. 1 is a kind of flow chart of the production method of concave convered glass provided by the embodiments of the present application.
Embodiment
In order to make the purpose , technical scheme and advantage of the present invention be clearer, with reference to the accompanying drawings and embodiments, it is right
The present invention is further elaborated.It should be appreciated that the specific embodiments described herein are merely illustrative of the present invention, and
It is not used in the restriction present invention.
It is a kind of flow chart of the production method of concave convered glass provided by the embodiments of the present application refering to Fig. 1.
A kind of production method of concave convered glass, including:
S110, by glass baseplate cleaned and dried with the cleaning machine equipped with ionized water and drying equipment.
S120, the glass baseplate is put into the potassium nitrate solution 1~24 it is small when and keep the first temperature range
Temperature conditionss carry out tempering processing.
S130, take out the glass baseplate from the potassium nitrate solution, is cooled to behind second temperature section and to institute
Glass baseplate is stated to clean using pure water.
S140, generate the first 2 D code information on the glass baseplate, and first 2 D code information includes at least institute
State the thickness for needing to polish on glass baseplate.
S150, read first 2 D code information, and the glass baseplate is polished according to first 2 D code information.
The glass baseplate, is put into the recessed illiteracy processing of recessed illiteracy liquid the inside progress by S160.
S170, print predetermined pattern using being screen printed onto the glass substrate surface, and 2 to 3 are air-dried after printed pattern
Hour, then dry 1 to 2 it is small when.
Glass, is sent into glass cleaning dryer, cleaning and drying, finished product by S180.
Wherein, first temperature range is 445 degrees Celsius~450 degrees Celsius, and the second temperature section is Celsius for 20
~30 degrees Celsius of degree.
In other one embodiment, step " generate the first 2 D code information on the glass baseplate, described
One 2 D code information includes at least the thickness for needing to polish on the glass baseplate " in, generate first 2 D code information
Method is generated using laser code apparatus.
In other one embodiment, " first 2 D code information is read, according to first Quick Response Code in step
Information polishes the glass baseplate " in, polishing agent used be by percentage by weight the 2% aminotriacetic acid disodium, 2%
Alkyl acrylate, 2.2% pentadecanol polyoxyethylene ether, 1.2% surfactant, 0.4% defoamer, 5% ethanol, 1.6%
Laurate diethanol amine, enuatrol 1%, coconutalkyl alkylolamides phosphate ester salt 0.1% and excess water are prepared into.
In other one embodiment, " first 2 D code information is read, according to first Quick Response Code in step
Information polishes the glass baseplate " in, polishing agent used is cerium oxide.
In other one embodiment, the recessed illiteracy liquid includes 50 parts of hydrogen fluoride ammonia, barium sulfate 5 according to parts by weight
Part, 4 parts of hydrochloric acid, 6 parts of hydrofluoric acid and 20 parts of water.
In other one embodiment, in step, " using being screen printed onto, the glass substrate surface printing is predetermined
Pattern, air-dry after printed pattern 2 to 3 it is small when, then dry 1 to 2 it is small when " in, the ink that silk-screen printing uses is corrosion-resistanting ink.
In other one embodiment, the corrosion-resistanting ink includes 10 parts of anti-biotic material, spices 15 according to parts by weight
Part, 13 parts of acrylic emulsion, 13 parts of glycerine, 12 parts of colorant, 1.1 parts of water-based thickener, 1.2 parts of aqueous defoamer, water-based levelling
20 parts of 0.5 part of agent and water.
In other one embodiment, step " generate the first 2 D code information on the glass baseplate, described
One 2 D code information includes at least the thickness for needing to polish on the glass baseplate " in, to the thickness of glass baseplate polishing
For 1% to the 1.5% of the thickness of the glass baseplate.
In other one embodiment, " glass baseplate is put into inside recessed illiteracy liquid in step and carries out recessed illiteracy processing "
In, the glass baseplate is 3 degree to 6 degree with the recessed angle for covering liquid liquid level.
Each technical characteristic of embodiment described above can be combined arbitrarily, to make description succinct, not to above-mentioned reality
Apply all possible combination of each technical characteristic in example to be all described, as long as however, the combination of these technical characteristics is not deposited
In contradiction, the scope that this specification is recorded all is considered to be.
Embodiment described above only expresses the several embodiments of the present invention, its description is more specific and detailed, but simultaneously
Cannot therefore it be construed as limiting the scope of the patent.It should be pointed out that come for those of ordinary skill in the art
Say, without departing from the inventive concept of the premise, various modifications and improvements can be made, these belong to the protection of the present invention
Scope.Therefore, the protection domain of patent of the present invention should be determined by the appended claims.
Claims (9)
- A kind of 1. production method of concave convered glass, it is characterised in that including:Glass baseplate is cleaned and dried with the cleaning machine equipped with ionized water and drying equipment;By the glass baseplate be put into the potassium nitrate solution 1~24 it is small when and keep the temperature conditionss of the first temperature range into The processing of row tempering;The glass baseplate is taken out from the potassium nitrate solution, is cooled to behind second temperature section and to the glass baseplate Cleaned using pure water;The first 2 D code information is generated on the glass baseplate, first 2 D code information includes at least the glass baseplate The upper thickness for needing to polish;First 2 D code information is read, the glass baseplate is polished according to first 2 D code information;The glass baseplate is put into inside recessed illiteracy liquid and carries out recessed illiteracy processing;Print predetermined pattern using the glass substrate surface is screen printed onto, air-dried after printed pattern 2 to 3 it is small when, then dry It is dry 1 to 2 it is small when;Glass is sent into glass cleaning dryer, cleaning and drying, finished product;Wherein, first temperature range be 445 degrees Celsius~450 degrees Celsius, the second temperature section for 20 degrees Celsius~ 30 degrees Celsius.
- 2. the production method of concave convered glass according to claim 1, it is characterised in that in step " in the glass baseplate The first 2 D code information of upper generation, first 2 D code information include at least the thickness for needing to polish on the glass baseplate " In, the method for generating first 2 D code information is generated using laser code apparatus.
- 3. the production method of concave convered glass according to claim 1, it is characterised in that " read the described 1st in step Code information is tieed up, the glass baseplate is polished according to first 2 D code information " in, polishing agent used is by percentage by weight The 2% aminotriacetic acid disodium, 2% alkyl acrylate, 2.2% pentadecanol polyoxyethylene ether, 1.2% surface-active Agent, 0.4% defoamer, 5% ethanol, 1.6% laurate diethanol amine, enuatrol 1%, coconutalkyl alkylolamides phosphate ester salt 0.1% and excess water be prepared into.
- 4. the production method of concave convered glass according to claim 1, it is characterised in that " read the described 1st in step Code information is tieed up, the glass baseplate is polished according to first 2 D code information " in, polishing agent used is cerium oxide.
- 5. the production method of concave convered glass according to claim 1, it is characterised in that the recessed illiteracy liquid is according to parts by weight Including 20 parts of 50 parts of hydrogen fluoride ammonia, 5 parts of barium sulfate, 4 parts of hydrochloric acid, 6 parts of hydrofluoric acid and water.
- 6. the production method of concave convered glass according to claim 1, it is characterised in that " use and be screen printed onto in step The glass substrate surface prints predetermined pattern, air-dried after printed pattern 2 to 3 it is small when, then dry 1 to 2 it is small when " in, silk screen The ink that printing uses is corrosion-resistanting ink.
- 7. the production method of concave convered glass according to claim 6, it is characterised in that the corrosion-resistanting ink is according to parts by weight Counting includes 10 parts of anti-biotic material, 15 parts of spices, 13 parts of acrylic emulsion, 13 parts of glycerine, 12 parts of colorant, 1.1 parts of water-based thickener, 20 parts of 1.2 parts of aqueous defoamer, 0.5 part of aqueous levelling agent and water.
- 8. the production method of concave convered glass according to claim 1, it is characterised in that in step " in the glass baseplate The first 2 D code information of upper generation, first 2 D code information include at least the thickness for needing to polish on the glass baseplate " In, the thickness to glass baseplate polishing is 1% to the 1.5% of the thickness of the glass baseplate.
- 9. the production method of concave convered glass according to claim 1, it is characterised in that in step " by the glass baseplate It is put into inside recessed illiteracy liquid and carries out recessed illiteracy processing " in, the glass baseplate is 3 degree to 6 degree with the recessed angle for covering liquid liquid level.