CN107892895A - A kind of preparation method of modified silane polyethers glue - Google Patents
A kind of preparation method of modified silane polyethers glue Download PDFInfo
- Publication number
- CN107892895A CN107892895A CN201711446727.2A CN201711446727A CN107892895A CN 107892895 A CN107892895 A CN 107892895A CN 201711446727 A CN201711446727 A CN 201711446727A CN 107892895 A CN107892895 A CN 107892895A
- Authority
- CN
- China
- Prior art keywords
- preparation
- parts
- modified silane
- weight
- glue
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a kind of preparation method of modified silane polyethers glue.The preparation method comprises the following steps:1) by weight, 10~20 parts of plasticizer, 60~70 parts of powders, 1~2 part of silane coupler are placed in reactor and be stirred, vacuum drying;2) 0.1~0.5 part of antioxidant, 0.1~0.5 part of light stabilizer, 1~3 part of silane coupler, normal heating, cooling are added in the compound of step 1);3) 10~30 parts of modified silane polyether resin 30000T, 1~5 part of gas-phase silica are added in the compound of step 2), is stirred under vacuum;4) surplus silane coupler, 0.1~0.3 part of catalyst are added in the compound of step 3), is stirred under vacuum, pressurize obtains modified silane polyethers glue.The preparation method of the present invention, obtained modified silane polyethers glue have more excellent elongation and tensile strength, are particularly suitable for building the application in house ornamentation field and the making of transparent adhesive tape.
Description
Technical field
The invention belongs to fluid sealant technical field, is related to a kind of preparation method of modified silane polyethers glue.
Background technology
The full name of MS glue is modified silane polyethers glue, is new one to grow up after TR sealant, silicone adhesive, polyurethane adhesive
For building sealant.It is mainly used in the neck such as bonding, joint filling, seam, sealing and waterproof, reinforcement of architectural engineering and decorations
Domain;In recent years, as people constantly deepen to the understanding of MS glue advantage itself, in industrial circles such as refrigerator car, container, elevators
Application also constantly extending.
Traditional polyurethane sealant easily forms bubble due to containing free isocyanates, and when solidifying so that
It is restricted in many application fields.At present, domestic construction fluid sealant is instantly based on silicone adhesive, and by comparison, MS glue has
More, more prominent advantage:1. environmental-protecting performance is remarkable:Solvent-free addition, formaldehydeless toluene dimethylbenzene etc. pair in the production of MS glue
Human harmful substance's release, VOC content are minimum, environment-friendly and greens;2. widely bonding scope, more superpower bonding are strong
Degree, MS glue is applicable not only to most construction materials, more to the engineering plastics such as acrylic, ABS, lucite and concrete etc.
Porous materials have good cohesive force, have more, wider application than silicone adhesive, by experiment:The superpower structure glue of grand nation
Every square decimeter of 300KG/ can be born, adhesion strength is very good;3. oiliness molecule thing pollution building material surface and seam will not be escaped,
Permanent to keep the attractive in appearance of building, silicone adhesive can separate out small molecule thing, and together with rainwater and dust, difficulty is formed in facade
With the stains of removal;4. pair most of paint and coating mutually compatibility, colloid surface can paint covering with paint, and silicone adhesive can be because of surface tension
Contraction cause covering with paint to be unable to maintain that;5. the harmony of overall performance is also best.To sum up, conventional silicone sealant due to
Tearing strength is low, and covering with paint property is poor, easily pollutes building materials, is restricted its application.
Silane modified polyether seal glue (abbreviation MS fluid sealants) be it is a kind of using silyl-terminated polyether (using polyethers as main chain, two
End siloxane blocking) based on polymer prepare high-performance environment-friendly fluid sealant, it has had polyurethane sealant and silicone concurrently
The advantages of fluid sealant, the deficiency of respective performance is overcome, there is excellent mechanical strength, covering with paint property, resistance to soiling, and do not have in product
There are isocyanates and organic solvent, be the main direction of development of domestic and international novel elastic fluid sealant.
The content of the invention
In view of the shortcomings of the prior art, it is an object of the invention to provide a kind of preparation method of modified silane polyethers glue,
The adhesion strength of obtained modified silane polyethers glue is high, and elongation and tensile strength are good.
To use following technical scheme up to this purpose, the present invention:
The preparation method of the modified silane polyethers glue of the present invention, the preparation method comprise the following steps:
1) by weight, 10~20 parts of plasticizer, 60~70 parts of powder, 1~2 part of silane coupler are placed in
It is stirred in reactor, vacuum drying;
2) by weight, in the compound that step 1) obtains add 0.1~0.5 part antioxidant, 0.1~0.5 part
Light stabilizer, 1~3 part of silane coupler, normal heating, cooling processing;
3) 10~30 parts of modified silane polyether resin by weight, is added in the compound that step 2) obtains
30000T, 1~5 part of gas-phase silica, stir under vacuum condition;
4) by weight, added in the compound that step 3) obtains surplus silane coupler, 0.1~0.3 part
Catalyst, the modified silane polyethers glue is obtained after stirring, pressurize under vacuum condition.
Heating can be closed after temperature of charge reaches 80 DEG C in step 1), and observes temperature and does not exceed 80 DEG C to prevent later stage drop
The warm time is too long, and mixing speed can be suitably reduced after material stirring is uniform, is easy to post drop.Wherein, the vacuum for-
0.1~0MPa, for example, vacuum be -0.1MPa, -0.08MPa, -0.06MPa, -0.05MPa, -0.04MPa, -0.03MPa, -
0.02MPa、-0.01MPa;The temperature of drying be 60~80 DEG C, such as drying temperature for 60 DEG C, 61 DEG C, 62 DEG C, 63 DEG C, 64
℃、65℃、66℃、67℃、68℃、69℃、70℃、71℃、72℃、73℃、74℃、75℃、76℃、77℃、78℃、79
℃、80℃;The time of drying is 15~20min, for example, the time of drying be 15min, 16min, 17min, 18min, 19min,
20min, the main purpose of this step is material dispersion, degassing dehydration.
In step 2), the temperature of the heating is 65~70 DEG C, for example, the temperature of heating is 65 DEG C, 66 DEG C, 67 DEG C, 68
℃、69℃、70℃;The cooling processing is to be cooled to 50 DEG C after compound is maintained into 50~70min under the conditions of 65~70 DEG C.
While cooling, chemistry is removed water, and the moisture in compound is further reduced, whole process normal pressure.
, can after addition matrix resin modified silane polyether resin 30000T and thixotropic agent gas-phase silica in step 3)
To reduce the temperature of system, faster mixing speed is advantageous to gas silicon and disperseed, but easily elevates the temperature, and visual gas silicon disperses feelings
Condition suitably reduces stir speed (S.S.) and shortens the time, and the whipping temp of this step is at 40 DEG C or so.Modified silane polyether resin
30000T is more sensitive to liquid to steam ratio due to being blocked using both ends trimethyl, so should not be in the big step 1) of temperature high-moisture
Add, be adapted to add in this step.
In step 4), time for being stirred under the vacuum condition is 20~40min, for example, the time of stirring be 20min,
25min、30min、35min、40min;The vacuum of vacuum pressurize is -0.05~0MPa, for example, vacuum be -0.05MPa, -
0.04MPa、-0.03MPa、-0.02MPa、-0.01MPa.The temperature control of this step is below 40 DEG C, in order to avoid become after ingress of air
Matter.
The preparation method of the modified silane polyethers glue of the present invention, by controlling the order of addition of each raw material, drying and processing, stirring
The control of temperature, mixing time and vacuum is mixed, the factor for influenceing modified silane polyethers glue Storage period and stability is dropped to most
Low, the activity for the modified silane polyethers glue being thus prepared is high, and manufactured glue surface drying unsticking is rapid, need to only add minimal amount of
Catalyst.
Preferably, modified silane polyethers glue of the invention, by weight, including following preparing raw material:
Wherein, modified silane polyethers glue of the invention, by weight, including following preparing raw material:
Modified silane polyether resin 30000T10~30 part, for example, modified silane polyether resin parts by weight for 10 parts, 11
Part, 12 parts, 13 parts, 14 parts, 15 parts, 16 parts, 17 parts, 18 parts, 19 parts, 20 parts, 21 parts, 22 parts, 23 parts, 24 parts, 25 parts, 26
Part, 27 parts, 28 parts, 29 parts, 30 parts.
1~5 part of gas-phase silica, such as the parts by weight of gas-phase silica are 1 part, 2 parts, 3 parts, 4 parts, 5 parts.
1~5 part of silane coupler, such as the parts by weight of silane coupler are 1 part, 2 parts, 3 parts, 4 parts, 5 parts.
60~70 parts of powder, for example, powder parts by weight for 60 parts, 61 parts, 62 parts, 63 parts, 64 parts, 65 parts, 66 parts, 67
Part, 68 parts, 69 parts, 70 parts.
0.1~0.5 part of light stabilizer, for example, light stabilizer parts by weight for 0.1 part, 0.2 part, 0.3 part, 0.4 part, 0.5
Part.
10~20 parts of plasticizer, for example, plasticizer parts by weight for 10 parts, 11 parts, 12 parts, 13 parts, 14 parts, 15 parts, 16
Part, 17 parts, 18 parts, 19 parts, 20 parts.
0.1~0.3 part of catalyst, such as the parts by weight of catalyst are 0.1 part, 0.2 part, 0.3 part.
0.1~0.5 part of antioxidant, such as the parts by weight of antioxidant are 0.1 part, 0.2 part, 0.3 part, 0.4 part, 0.5 part.
The silane coupler is vinyltrimethoxy silane and N- (β-aminoethyl)-γ-aminopropyl trimethoxy silicon
Alkane.
The mass ratio of vinyltrimethoxy silane and N- (β-the aminoethyl)-γ-aminopropyltrimethoxysilane is
(1~4):(1~4), such as the matter of vinyltrimethoxy silane and N- (β-aminoethyl)-γ-aminopropyltrimethoxysilane
Amount is than being 1:1、1:2、1:3、1:4、2:1、2:3、3:1、3:2、4:1、4:3.
The powder is the mixture of nanometer calcium, active coarse whiting and titanium dioxide.
The mass ratio of the nanometer calcium, active coarse whiting and titanium dioxide is (1~2):(2~4):(0.1~0.2).
The light stabilizer is light stabilizer 765.
The plasticizer is phthalic ester plasticizer;
Preferably, the phthalic ester plasticizer is phthalic acid diethyl last of the ten Heavenly stems ester and/or phthalic acid two
Second last of the ten Heavenly stems nonyl ester.
The catalyst is organotin catalysts, it is preferable that the organotin catalysts are dibutyl tin laurate.
The antioxidant is antioxidant 1010 and/or antioxidant 1076.
Preferably, modified silane polyethers glue of the invention, by weight, including following preparing raw material:
Compared with prior art, beneficial effects of the present invention are:
(1) preparation method of modified silane polyethers glue of the invention, by controlling the order of addition of each raw material, at drying
The control of reason, whipping temp, mixing time and vacuum, the factor drop of modified silane polyethers glue Storage period and stability will be influenceed
To minimum, the activity for the modified silane polyethers glue being thus prepared is high, and manufactured glue surface drying unsticking is rapid, need to only add few
The catalyst of amount.
(2) modified silane polyethers glue made from the preparation method of modified silane polyethers glue of the invention, has and preferably stretches
Long rate and tensile strength, more than 350%, tensile strength is particularly suitable for building house ornamentation field in more than 4.6MPa elongation
Using, for example, in the building gap filler of low modulus, nail-free glue, kitchen and bath's glue etc..
(3) modified silane polyethers glue made from the preparation method of modified silane polyethers glue of the invention, clear, is adapted to
Make transparent adhesive tape.
Embodiment
Technical scheme is further illustrated below by embodiment.
Unless specific instructions, various raw materials of the invention are commercially available buys, or is prepared according to the conventional method of this area
Obtain.
The preparation method of the modified silane polyethers glue of the present invention, the preparation method comprise the following steps:
1) by weight, 10~20 parts of plasticizer, 60~70 parts of powder, 1~2 part of silane coupler are placed in
It is stirred in reactor, vacuum drying;
2) by weight, in the compound that step 1) obtains add 0.1~0.5 part antioxidant, 0.1~0.5 part
Light stabilizer, 1~3 part of silane coupler, normal heating, cooling processing;
3) 10~30 parts of modified silane polyether resin by weight, is added in the compound that step 2) obtains
30000T, 1~5 part of gas-phase silica, stir under vacuum condition;
4) by weight, added in the compound that step 3) obtains surplus silane coupler, 0.1~0.3 part
Catalyst, the modified silane polyethers glue is obtained after stirring, pressurize under vacuum condition.
The modified silane polyethers glue of following examples is prepared using above-mentioned preparation method.
Embodiment 1
The modified silane polyethers glue of the present embodiment, by weight, including following preparing raw material:
Embodiment 2
The modified silane polyethers glue of the present embodiment, by weight, including following preparing raw material:
Embodiment 3
The modified silane polyethers glue of the present embodiment, by weight, including following preparing raw material:
Embodiment 4
The modified silane polyethers glue of the present embodiment, by weight, including following preparing raw material:
Embodiment 5
The modified silane polyethers glue of the present embodiment, by weight, including following preparing raw material:
Comparative example 1
The modified silane polyethers glue of this comparative example, by weight, including following preparing raw material:
Comparative example 2
The modified silane polyethers glue of this comparative example, by weight, including following preparing raw material:
Comparative example 3
The modified silane polyethers glue of this comparative example, by weight, including following material:
Comparative example 4
The modified silane polyethers glue of this comparative example, by weight, including following material:
The performance of modified silane polyethers glue made from embodiment 1-5 and comparative example 1-4 is tested, experimental result such as table
Shown in 1.
Table 1
Example | Adhesion strength (MPa) | Elongation (%) | Tensile strength (MPa) |
Embodiment 1 | 1.3 | 410 | 4.8 |
Embodiment 2 | 1.2 | 360 | 5.7 |
Embodiment 3 | 1.5 | 350 | 5.4 |
Embodiment 4 | 1.6 | 421 | 6.1 |
Embodiment 5 | 1.2 | 378 | 4.6 |
Comparative example 1 | 0.8 | 350 | 4.2 |
Comparative example 2 | 0.7 | 332 | 3.7 |
Comparative example 3 | 0.9 | 310 | 3.7 |
Comparative example 4 | 0.6 | 298 | 3.8 |
Relative to comparative example, modified silane polyethers glue of the invention, adhesion strength is high, in more than 1.2MPa, elongation and
Tensile strength is good, and for elongation more than 350%, tensile strength is particularly suitable for building the application in house ornamentation field in more than 4.6MPa,
The building gap filler of low modulus, nail-free glue, kitchen and bath's glue etc. in such as.In addition, the modified silane polyethers glue of the present invention, clarification is saturating
It is bright, it is adapted to make transparent adhesive tape.
The present invention illustrates the detailed process equipment of the present invention and technological process by above-described embodiment, but the present invention is not
Above-mentioned detailed process equipment and technological process are confined to, that is, does not mean that the present invention has to rely on above-mentioned detailed process equipment and work
Skill flow could be implemented.Person of ordinary skill in the field is it will be clearly understood that any improvement in the present invention, to product of the present invention
The equivalence replacement of each raw material and the addition of auxiliary element, the selection of concrete mode etc., all fall within protection scope of the present invention and public affairs
Within the scope of opening.
Claims (10)
1. a kind of preparation method of modified silane polyethers glue, it is characterised in that the preparation method comprises the following steps:
1) 10~20 parts of plasticizer, 60~70 parts of powder, 1~2 part of silane coupler by weight, are placed in reaction
It is stirred in kettle, vacuum drying;
2) by weight, the antioxidant of 0.1~0.5 part of addition, 0.1~0.5 part of light in the compound that step 1) obtains
Stabilizer, 1~3 part of silane coupler, normal heating, cooling processing;
3) by weight, the modified silane polyether resin 30000T of 10~30 parts of addition, 1 in the compound that step 2) obtains
~5 parts of gas-phase silica, stir under vacuum condition;
4) by weight, the silane coupler of addition surplus, 0.1~0.3 part of catalysis in the compound that step 3) obtains
Agent, the modified silane polyethers glue is obtained after stirring, pressurize under vacuum condition.
2. preparation method according to claim 1, it is characterised in that in step 1), the vacuum is -0.1~0MPa;
Preferably, the temperature of the drying is 60~80 DEG C;
Preferably, the time of the drying is 15~20min.
3. preparation method according to claim 1 or 2, it is characterised in that in step 2), the temperature of the heating for 65~
70℃;
Preferably, the cooling processing is to be cooled to 50 DEG C after compound is maintained into 50~70min under the conditions of 65~70 DEG C.
4. according to the preparation method described in one of claim 1-3, it is characterised in that in step 4), stirred under the vacuum condition
The time mixed is 20~40min;
Preferably, the vacuum of the vacuum pressurize is -0.05~0MPa.
5. according to the preparation method described in one of claim 1-4, it is characterised in that the modified silane polyethers glue is by weight
Meter, including following preparing raw material:
6. according to the preparation method described in one of claim 1-5, it is characterised in that the silane coupler is vinyl front three
TMOS and N- (β-aminoethyl)-γ-aminopropyltrimethoxysilane;
Preferably, the mass ratio of vinyltrimethoxy silane and N- (β-the aminoethyl)-γ-aminopropyltrimethoxysilane
For (1~4):(1~4).
7. according to the preparation method described in one of claim 1-6, it is characterised in that the powder is nanometer calcium, active coarse whiting
With the mixture of titanium dioxide;
Preferably, the mass ratio of the nanometer calcium, active coarse whiting and titanium dioxide is (1~2):(2~4):(0.1~0.2).
8. according to the preparation method described in one of claim 1-7, it is characterised in that the light stabilizer is light stabilizer 765;
Preferably, the plasticizer is phthalic ester plasticizer;
Preferably, the phthalic ester plasticizer is phthalic acid diethyl last of the ten Heavenly stems ester and/or the phthalic acid diethyl last of the ten Heavenly stems
Nonyl ester.
9. according to the preparation method described in one of claim 1-8, it is characterised in that the catalyst is organotin catalysts;
Preferably, the organotin catalysts are dibutyl tin laurate;
Preferably, the antioxidant is antioxidant 1010 and/or antioxidant 1076.
10. according to the preparation method described in one of claim 1-9, it is characterised in that the modified silane polyethers glue is by weight
Part meter, including following preparing raw material: