CN106833479A - Vehicle environment protection type single-component silylated polyether fluid sealant and preparation method thereof - Google Patents
Vehicle environment protection type single-component silylated polyether fluid sealant and preparation method thereof Download PDFInfo
- Publication number
- CN106833479A CN106833479A CN201710006784.2A CN201710006784A CN106833479A CN 106833479 A CN106833479 A CN 106833479A CN 201710006784 A CN201710006784 A CN 201710006784A CN 106833479 A CN106833479 A CN 106833479A
- Authority
- CN
- China
- Prior art keywords
- parts
- silane
- component
- fluid sealant
- environment protection
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of vehicle environment protection type single-component silylated polyether fluid sealant and preparation method thereof, belong to sealant or field of adhesive technology.The fluid sealant is prepared from by following component, and each component is in parts by weight:100 parts of silane modified polyether resin, 5 40 parts of plasticizer, 50 150 parts of filler, 0.1 15 parts of reinforcing agent, 0.1 15 parts of colouring agent, 0.5 10 parts of deicer, 0.1 8 parts of adhesive force crosslinking agent, 0.1 3 parts of heat stabilizer, 0.1 3 parts of ultraviolet absorber, 0.1 3 parts of hindered amine light stabilizer, 0.1 3 parts of antioxidant, 0.2 10 parts of silane coupler, 0.2 8.0 parts of catalyst.The fluid sealant has extremely low TVOC contents, meets European Union's TVOC standards, i.e. TOVC≤50 μ gC/g, can be widely applied to the fields such as automobile, track traffic, Aero-Space, ship warship, building decoration.
Description
Technical field
The present invention belongs to fluid sealant technical field, more particularly to vehicle with environment protection type single-component silylated polyether fluid sealant and
Its preparation method.
Background technology
Wide variety of fluid sealant mainly has polysulfide sealant, silicone sealant and polyurethane sealant in the market,
Polysulfide sealant, silicone sealant and polyurethane sealant still possess very big market at home.Wherein, polysulfide class glue is because of it
Low-temperature setting speed is slow, easy ageing hardening, weatherability are bad, intense irritation stink, thus it is commercially increasingly decayed;
Although polyurethanes fluid sealant intensity, tear, puncture, corrosion-resistant property are very well, because its isocyanide acid end group is to bin stability
Condition requirement it is harsh, while the CO discharged after solidification2Gas easily makes glue-line form bubble, it is slower be fully cured speed and
The easily tacky defect in surface after solidification, adding when it is bonded with nonporous substrate surface must the cumbersome construction technology of primary coat and ageing-resistant
Performance is short of so that its application is restricted;Silicone glue with rapid curing, bubble-free, and firm with nonporous substrate can glue
Knot, glue-line also has a good ageing-resistant performance, but because it can not be compatible well with other sealants and primary coat is poor, it is low by force
Degree tear resistance, oil resistance, puncture resistance are poor, and glue-line also easily separates out grease, easily pollution vehicle jewelry, influence vehicle
Space is attractive in appearance.Polysulfide sealant, silicone sealant and polyurethane sealant, its environmental-protecting performance substantially exceed European Union TVOC standards limit
System(TVOC standards, i.e. TOVC≤50 μ gC/g).
Silylation polyether seal glue(Abbreviation MS)It is a kind of cross-linked polymer based on silane-terminated polyether, tradition is most of
MS fluid sealants are mainly used in building trade, and the content requirement to glue TVOC is relatively low.With the raising of quality of life level, private savings
Vehicle and utility car are more and more essential in the life of people as the second space in life.Due to MS fluid sealants
Superior performance, is little by little applied in the decorations in vehicle, aviation, compartment.
The application of MS glue has a major impact to the environment of vehicle space.Generally, indoor TVOC concentration is in 0.2mg/m3Arrive
2mg/m3Between, when indoor concentration is in 0.16mg/m3~0.3mg/m3When, it is substantially harmless to health, but in vehicle decorative
This index is tended to exceed, particularly in the case of ornament materials improper use.Traditional MS fluid sealants glue is due to matching somebody with somebody
Than incorrect, its environmental-protecting performance does not reach the limitation of European Union TVOC standards(TVOC standards, i.e. TOVC≤50 μ
gC/g ), it is impossible to meet high-grade vehicle use demand.Existing market is badly in need of a kind of low silylation polyethers of environmentally friendly, TVOC contents
Fluid sealant.
The content of the invention
It is close with environment protection type single-component silylated polyether it is an object of the invention to provide the low vehicle of a kind of environmental protection, TVOC contents
Sealing;The second object of the present invention is the production method for providing the vehicle environment-friendly type silane polyether seal glue.
To achieve the above objectives, the present invention uses and scheme is produced by below:
Vehicle environment protection type single-component silylated polyether fluid sealant, is prepared from by following component, each component in parts by weight,
100 parts of silane modified polyether resin
Plasticizer 5-40 parts
Filler 50-150 parts
Reinforcing agent 0.1-15 parts
Colouring agent 0.1-15 parts
Deicer 0.5-10 parts
0.1-8 parts of adhesive force crosslinking agent
Heat stabilizer 0.1-3 parts
Ultraviolet absorber 0.1-3 parts
Hindered amine light stabilizer 0.1-3 parts
Antioxidant 0.1-3 parts
Silane coupler 0.2-10 parts
Catalyst 0.2-8.0 parts.
It is preferably as follows component:
100 parts of silane modified polyether resin
Plasticizer 15-30 parts
Filler 70-120 parts
Reinforcing agent 0.4-10 parts
Colouring agent 1-10 parts
Deicer 1-5 parts
1-6 parts of adhesive force crosslinking agent
Heat stabilizer 1-2 parts
Ultraviolet absorber 1-2 parts
Hindered amine light stabilizer 1-2 parts
Antioxidant 1-2 parts
Silane coupler 1-5 parts
Catalyst 1-5 parts.
The above-mentioned silane modified polyether resin of the present invention is the polyethers and/or end triethoxy first for holding trimethoxysilyl
The polyethers of silylation, it is characterized in that end group at least contains 2 polyethers of hydrolyzable siloxanes base, such as KANEKA Products
S2O3H, S3O3H, SAT400, SAT010 etc..
The above-mentioned plasticizer of the present invention selects diisooctyl phthalate, polyalcohol esters of gallic acid, phosphoric acid ester or terminal methyl two
The PPOX ether of methoxysilyl, terminal methyl diethoxy silicyl PPOX ether or terminal methyl trimethoxy
The PPOX ether of base silicyl it is therein one or two(Molecular weight is not more than 2500, the polyoxy of hydrolyzable silane base
Change propylene ether capped).
Described filler is nano activated calcium carbonate, talcum powder, precipitated calcium carbonate, powdered whiting, surface-modified
One or more in flyash or wollastonite in powder.
The reinforcing agent selects one or more in superfine white carbon black, superfine carbon black, ultra-fine calcium powder, gas silicon, heavy silicon.
The colouring agent is nano grade titanium white powder, nanoscale carbon black, iron oxide red etc. or its arbitrary proportion mixture.
The deicer is the siloxane crosslinker or oxazole alkanes crosslinking agent of facile hydrolysis.As the U.S. steps the high-new group of figure
A-171 type silane deicer, the VTMO type silane deicers of German Evonik Degussa Corp..
The adhesive force crosslinking agent is modified amino or alkylsiloxane active oligomerization silane ether, such as N- (β-ammonia second
Base)-γ-aminopropyltrimethoxysilane, phenyltrimethoxysila,e(OFS-6124), γ-glycidyl ether oxygen propyl front three
TMOS, gamma-amino trimethoxy silane, gamma-methyl allyl acyloxypropyl trimethoxysilane
The silane coupler selects phenyltrimethoxysila,e(OFS-6124)And its derivative, N- (aminoethyls of β mono-)-γ-ammonia
One kind or its complex in propyl trimethoxy silicane, γ mercaptopropyitrimethoxy silane.
The ultraviolet absorber is salicylic acid esters, benzophenone class, benzotriazole, the substitution fine class of propylene or triazines.
Such as cyanogen spy's Products:UV9, UV24, UV3638, UV2337, UV5365, UV5411, UVI084, UV1164 etc.;Ciba
Products:TinuvinP、Tinuvin1120、Tinuvin326、Tinuvin327、Tinuvin329、Tinuvin99-2、
Tinuvin928 etc..
The heat stabilizer is piperidine derivative, such as cyanogen spy Products:UV3346、UV-292、UV3529、UV3853、
UV290S, UV3581, UV38535 etc.;Ciba Specialty Chemicals' product:Tinuvin770、Tinuvin770DF、Tinuvin292、
Tinuvin5050, Tinuvin5151, Tinunvin-68, Tinuvin5060 etc..
The Tinuvin770 type products of the hindered amine light stabilizer such as Ciba.
Described catalyst is the organic acid salts such as metallic tin, lead, iron, titanate ester, aliphatic acid tin compound and alkane
The composite catalyst of base aminated compounds.Such as dibutyl tin laurate, dibutyltin diacetate, double (second phthalein acetone is cruel) two fourths
Composite catalyst of Ji Xi, phthalic acid dibutyl tin or stannous octoate and dodecyl amine etc..
The antioxidant is polynary Hinered phenols age resistor.1010 type age resistor products of such as Ciba.
The vehicle is as follows with the preparation method of environment protection type single-component silylated polyether fluid sealant:Successively will be anti-by formula design
Ultraviolet absorber, antioxidant, light stabilizer, heat stabilizer, filler and reinforcing agent, pigment are put into hybrid reactor,
60-160 DEG C, dry inert gas protection under, dehydration pretreatment mixing;Add silane modified polyether resin, plasticizer item by item again,
Vacuumize 110-120 DEG C of heating stirring reaction;Then less than 40-30 DEG C is cooled to, deicer, adhesive force is added and is promoted crosslinking
Agent, coupling agent, catalyst, under vacuum, stirring reaction is obtained vehicle environment protection type single-component silylated polyether fluid sealant.
Innovative point of the present invention or principle:From formulation optimization, optimization processing technology is improved the present invention, particularly catalyst
Selection, obtain superpower MS fluid sealants and odorlessness, TVOC be extremely low, meet the requirement of environmental protection.
The present invention has the beneficial effect that:
(1)Using MS fluid sealants obtained in the present invention, film surface is smooth, spot-resistant performance and contaminated resistance are excellent, and MS is close
The TVOC contents of sealing are extremely low, and in below 50 μ gC/g, content meets European standard.With odorlessness, health environment-friendly, scrubbing resistance,
Adhesive property is excellent, good hand touch, the decoration excellent feature of performance.(2)Manufacturing technique method of the present invention is easy, swift to operate, practicality
By force, industrialized production is conducive to.
Specific embodiment
Embodiment of the present invention is described in detail below in conjunction with embodiment, but those skilled in the art will
Understand, the following example is merely to illustrate the present invention, and is not construed as limiting the scope of the present invention.It is unreceipted specific in embodiment
Condition person, the condition advised according to normal condition or manufacturer is carried out.Agents useful for same or the unreceipted production firm person of instrument, are
The conventional products that can be obtained by commercially available purchase.
Embodiment 1
By following formulas vehicle environment protection type single-component silylated polyether fluid sealant is prepared with technique:
Nm-class active calcium carbonate 500g, powdered whiting 100g, precipitated calcium carbonate 500g, fumed silica are weighed respectively
50g, titanium dioxide 50g, 1010 type age resistor 10g, N-220 white carbon 4g, Tinuvin326 type ultraviolet absorber 10g,
Tinuvin770 types light stabilizer, heat stabilizer 10g are put into double planetary mixer together, are heated to 120 DEG C, dry inert gas
Under protection, dehydration pretreatment mixing is slowly stirred (25-50rPm) 120 minutes;Add S303H type silane modified polyether resins
1000g, DIDP plasticizer(Diisooctyl phthalate)150g, vacuumizes and is heated to 110 DEG C, high-speed stirred
(1000rPm) 150 minutes, is cooled to 40 DEG C, adds A-171 type silane dehydrating agent 30g, is slowly stirred (250rPm) 25 minutes,
Silane coupler phenyltrimethoxysila,e 20g is added, (250rpm) is slowly stirred 25 minutes, OFS-6124 is added(Phenyl three
Methoxy silane)Type silane attaches power crosslinking agent 10g, is slowly stirred (25Orpm) 25 minutes, adds dibutyl tin laurate
With dodecyl amine composite catalyst 10g, (25Orpm) is slowly stirred 25 minutes, discharge.Properties of product testing result is shown in Table 1:
The close jelly technical parameter of the silane modified polyether of 1 embodiment of table 1
Embodiment 2
By following formulas vehicle environment protection type single-component silylated polyether fluid sealant is prepared with technique:
Nm-class active calcium carbonate 300g, powdered whiting 100g, precipitated calcium carbonate 300g, iron oxide red 100g, 1010 types are weighed respectively
Age resistor 10g, N-220 white carbon 100g, Tinuvin326 type ultraviolet absorber 20g, Tinuvin770 type light stabilizer 20g,
Tinunvin-68 heat stabilizers 20g is put into double planetary mixer together, is heated to 80 DEG C, is slowly stirred 120 points of (25-50rPm)
Clock, adds S203H type silane modified polyether resin 200g, S303H type silane modified polyether resin 800g, DIDP plasticizer
300g, vacuumizes and is heated to 120 DEG C, and high-speed stirred (1000rPm) 150 minutes is cooled to 30 DEG C, adds A-171 type silane
Deicer 30g, is slowly stirred (250rPm) 25 minutes, adds silane coupler phenyltrimethoxysila,e 20g, is slowly stirred
(250rpm) 25 minutes, adds gamma-amino trimethoxy silane adhesive force crosslinking agent 60g, is slowly stirred (25Orpm) 25 minutes,
Stannous octoate and dodecyl amine composite catalyst 20g are added, (25Orpm) is slowly stirred 25 minutes, discharged.The fluid sealant of embodiment 2
Properties of product testing result is shown in Table 2:
The close jelly technical parameter of the silane modified polyether of 2 embodiment of table 2
Embodiment 3
By following formulas vehicle environment protection type single-component silylated polyether fluid sealant is prepared with technique:
Weigh respectively nm-class active calcium carbonate 1200g, titanium dioxide 50g, 1010 type age resistor 10g, N-220 white carbon 4g,
Tinuvin326 type ultraviolet absorber 10g, Tinuvin770 types light stabilizer, heat stabilizer 10g are put into double-planet stirring together
Machine, is heated to 110 DEG C, is slowly stirred (25-50rPm) 120 minutes;Addition S203H type silane modified polyether resins 200g,
S303H type silane modified polyether resins 800g, DIDP plasticizer 170g vacuumize and are heated to 110 DEG C, high-speed stirred
(1000rPm) 150 minutes, is cooled to 40 DEG C, adds VTMO type silane deicer 25g, is slowly stirred (250rPm) 25 minutes,
Silane coupler phenyltrimethoxysila,e 25g is added, (250rpm) is slowly stirred 25 minutes, addition N- (β-aminoethyl)-γ-
Aminopropyl trimethoxysilane adhesive force crosslinking agent 50g, is slowly stirred (25Orpm) 25 minutes, add dibutyltin diacetate with
Dodecyl amine composite catalyst 15g, is slowly stirred (25Orpm) 25 minutes, discharging.The fluid sealant properties of product of embodiment 3 detection knot
Fruit is shown in Table 3:
The close jelly technical parameter of the silane modified polyether of 3 embodiment of table 3
Comparative example
The performance indications of the conventional automobile-used traditional MS fluid sealants glue of existing market:
Claims (4)
1. vehicle environment protection type single-component silylated polyether fluid sealant, it is characterised in that be prepared from by following component, each component with
Weight portion meter:
100 parts of silane modified polyether resin
Plasticizer 5-40 parts
Filler 50-150 parts
Reinforcing agent 0.1-15 parts
Colouring agent 0.1-15 parts
Deicer 0.5-10 parts
0.1-8 parts of adhesive force crosslinking agent
Heat stabilizer 0.1-3 parts
Ultraviolet absorber 0.1-3 parts
Hindered amine light stabilizer 0.1-3 parts
Antioxidant 0.1-3 parts
Silane coupler 0.2-10 parts
Catalyst 0.2-8.0 parts;
The silane modified polyether resin is to hold the polyethers of trimethoxysilyl and/or gathering for end triethoxysilyl
Ether;
The plasticizer is diisooctyl phthalate, polyalcohol esters of gallic acid, phosphoric acid ester or terminal methyl dimethoxy first silicon
The PPOX ether of alkyl, terminal methyl diethoxy silicyl PPOX ether or terminal methyl trimethoxysilyl
PPOX ether it is therein one or two;
Described filler is nano activated calcium carbonate, talcum powder, precipitated calcium carbonate, powdered whiting, surface-modified fine coal
Ash or wollastonite in powder in one or more;
The reinforcing agent is one or more in superfine white carbon black, superfine carbon black, ultra-fine calcium powder, gas silicon, heavy silicon;
The colouring agent is nano grade titanium white powder, nanoscale carbon black, iron oxide red or its mixture;
The deicer is the siloxane crosslinker or oxazole alkanes crosslinking agent of facile hydrolysis;
The adhesive force crosslinking agent is modified amino or alkylsiloxane active oligomerization silane ether;
The silane coupler is phenyltrimethoxysila,e and its derivative, N- (aminoethyls of β mono-)-γ-aminopropyl trimethoxy
One kind or its complex in base silane, γ mercaptopropyitrimethoxy silane;
The ultraviolet absorber is salicylic acid esters, benzophenone class, benzotriazole, the substitution fine class of propylene or triazines;
The heat stabilizer is piperidine derivative;
The hindered amine light stabilizer is Tinuvin770 type products;
Described catalyst is metallic tin, lead, iron organic acid salt, titanate ester or aliphatic acid tin compound and alkyl amine
The composite catalyst of compound;
The antioxidant is polynary Hinered phenols age resistor.
2. vehicle as claimed in claim 1 environment protection type single-component silylated polyether fluid sealant, it is characterised in that by following component
It is prepared from, each component is in parts by weight:
100 parts of silane modified polyether resin
Plasticizer 15-30 parts
Filler 70-120 parts
Reinforcing agent 0.4-10 parts
Colouring agent 1-10 parts
Deicer 1-5 parts
1-6 parts of adhesive force crosslinking agent
Heat stabilizer 1-2 parts
Ultraviolet absorber 1-2 parts
Hindered amine light stabilizer 1-2 parts
Antioxidant 1-2 parts
Silane coupler 1-5 parts
Catalyst 1-5 parts.
3. vehicle as claimed in claim 1 or 2 environment protection type single-component silylated polyether fluid sealant, it is characterised in that
The silane modified polyether resin selects S2O3H, S3O3H, SAT400 or SAT010;
The deicer selects A-171 type silane deicers or VTMO type silane deicers;
The ultraviolet absorber select UV9, UV24, UV3638, UV2337, UV5365, UV5411, UVI084, UV1164 or
TinuvinP, Tinuvin1120, Tinuvin326, Tinuvin327, Tinuvin329, Tinuvin99-2 or
Tinuvin928;
The heat stabilizer select UV3346, UV-292, UV3529, UV3853, UV290S, UV3581, UV38535 or
Tinuvin770, Tinuvin770DF, Tinuvin292, Tinuvin5050, Tinuvin5151, Tinunvin-68 or
Tinuvin5060;
The hindered amine light stabilizer selects Tinuvin770 type products;
The antioxidant is 1010 type age resistor products;
The catalyst selects dibutyl tin laurate, dibutyltin diacetate, double (second phthalein acetone is cruel) dibutyl tins, adjacent benzene two
The composite catalyst of formic acid dibutyl tin or stannous octoate and dodecyl amine.
4. the method for preparing vehicle environment protection type single-component silylated polyether fluid sealant as claimed in claim 1 or 2, its feature exists
In realizing by the following method:By formula successively by ultraviolet absorber, antioxidant, light stabilizer, heat stabilizer, filler
Put into hybrid reactor with reinforcing agent, pigment, under 60-160 DEG C, dry inert gas protection, dehydration pretreatment mixing;
Add silane modified polyether resin, plasticizer item by item again, vacuumize 110-120 DEG C of heating stirring reaction;Then it is cooled to 40-30
Below DEG C, deicer, adhesive force crosslinking agent, coupling agent, catalyst are added, under vacuum, stirring reaction is obtained vehicle
With environment protection type single-component silylated polyether fluid sealant.