CN107892853A - A kind of anti-skid wearable vehicle steering - Google Patents
A kind of anti-skid wearable vehicle steering Download PDFInfo
- Publication number
- CN107892853A CN107892853A CN201711359370.4A CN201711359370A CN107892853A CN 107892853 A CN107892853 A CN 107892853A CN 201711359370 A CN201711359370 A CN 201711359370A CN 107892853 A CN107892853 A CN 107892853A
- Authority
- CN
- China
- Prior art keywords
- parts
- skid wearable
- powder
- vehicle steering
- modified
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of anti-skid wearable vehicle steering, including steering wheel main body, one layer of anti-skid wearable layer is sprayed on the steering wheel main body, it includes following components according to the mass fraction：It is acrylic resin modified：50 60 parts, phenol-formaldehyde resin modified：30 40 parts, superfine alumina silicate：59 parts, anti-skid wearable powder：15 20 parts, n-butyl acetate:36 parts, dibutyl tin dilaurate：13 parts, butyl rubber：9 17 parts, glass fibre：8 12 parts, azodicarbonamide be modified castor oil：23 parts, surface modified calcium carbonate：6 12 parts, filler：10 15 parts, peroxidized t-butyl perbenzoate：47 parts, vinyltrimethoxy silane：68 parts, aluminium hydroxide：23 parts, the western dicarboxylic anhydride of suitable fourth：14 parts, pigment：5 11 parts, curing agent：35 parts, stabilizer：12 parts, coupling agent:36 parts, solvent：58 parts, the present invention has good wear-resisting antiskid performance.
Description
Technical field
The present invention relates to a kind of anti-skid wearable vehicle steering.
Background technology
For the steering wheel in the transfer of the vehicles such as vehicle, usually it is made up of support, spoke and hub core, and
Catching plate slippage easily occurs because of driver's hand perspiration for present steering wheel, so as to which accident occurs.
The content of the invention
The technical problems to be solved by the invention are the shortcomings that presence for above prior art, there is provided a kind of anti-skidding resistance to
Grind vehicle steering.
The present invention solve above technical problem technical scheme be：A kind of anti-skid wearable vehicle steering, including steering wheel
Main body, one layer of anti-skid wearable layer is sprayed on the steering wheel main body, it includes following components according to the mass fraction：Modified propylene
Acid resin：50-60 parts, phenol-formaldehyde resin modified：30-40 parts, superfine alumina silicate：5-9 parts, anti-skid wearable powder：15-20 parts, second
Sour N-butyl:3-6 parts, dibutyl tin dilaurate：1-3 parts, butyl rubber：9-17 parts, glass fibre：8-12 parts, azo diformazan
Acid amides is modified castor oil：2-3 parts, surface modified calcium carbonate：6-12 parts, filler：10-15 parts, peroxidized t-butyl perbenzoate：
4-7 parts, vinyltrimethoxy silane：6-8 parts, aluminium hydroxide：2-3 parts, the western dicarboxylic anhydride of suitable fourth：1-4 parts, pigment：5-11 parts,
Curing agent：3-5 parts, stabilizer：1-2 parts, coupling agent:3-6 parts, solvent：5-8 parts.
The technical scheme that further limits of the present invention is：
Foregoing filler count in parts by weight including：Compound rare-earth 1-2 parts, barium sulfate：4-8 parts, kaolin：It is 10-13 parts, organic
Bentonite:15-18 parts, silicon powder：20-25 parts, carbon fiber powder：8-11 parts.
Foregoing anti-skid wearable powder is the mixture of diamond dust, hollow ceramic micro mist and gluey graphite powder.
Foregoing curing agent is vinyl triamine DETA aminoethyl piperazines AE.
Foregoing pigment is one or more in titanium dioxide, pearl essence, nano zine oxide.
Foregoing stabilizer is magnesium stearate or zinc stearate.
Foregoing solvent is propane diols and ethyl acetate in mass ratio 4:1 mixture.
Foregoing includes following components according to the mass fraction：Include following components according to the mass fraction：Modified acroleic acid tree
Fat：55 parts, phenol-formaldehyde resin modified：34 parts, superfine alumina silicate：5 parts, anti-skid wearable powder：15 parts, n-butyl acetate:3 parts, two
The fourth tin of laurate two：1 part, butyl rubber：12 parts, glass fibre：10 parts, azodicarbonamide be modified castor oil：2 parts, table
Face modified calcium carbonate：8 parts, filler：12 parts, peroxidized t-butyl perbenzoate：5 parts, vinyltrimethoxy silane：6 parts, hydrogen-oxygen
Change aluminium：2 parts, the western dicarboxylic anhydride of suitable fourth：2 parts, pigment：8 parts, curing agent：4 parts, stabilizer：1 part, coupling agent:5 parts, solvent：6 parts.
Foregoing includes following components according to the mass fraction：It is acrylic resin modified：57 parts, phenol-formaldehyde resin modified：36 parts,
Superfine alumina silicate：8 parts, anti-skid wearable powder：19 parts, n-butyl acetate:4 parts, dibutyl tin dilaurate：2 parts, butyl rubber：
15 parts, glass fibre：11 parts, azodicarbonamide be modified castor oil：3 parts, surface modified calcium carbonate：11 parts, filler：14
Part, peroxidized t-butyl perbenzoate：6 parts, vinyltrimethoxy silane：7 parts, aluminium hydroxide：3 parts, the western dicarboxylic anhydride of suitable fourth：3
Part, pigment：10 parts, curing agent：5 parts, stabilizer：2 parts, coupling agent:5 parts, solvent：7 parts.
The beneficial effects of the invention are as follows：The present invention has good anti-skidding, anti-wear performance, adds butyl rubber, improves it
Anti-wear performance, anti-skid wearable powder is added, improves its wear-resisting and skid resistance, avoided that catching plate slippage occurs because of hand perspiration, cause to pacify
Full accident；Superfine alumina silicate is added, there is scrub resistance, weatherability, surface drying time can be shortened in addition, while improve coating
Dispersive property and workability, the suspension of filler can be improved, avoid the precipitated and separated phenomenon of coating.
Embodiment
Embodiment 1
The present embodiment provides a kind of anti-skid wearable vehicle steering, including steering wheel main body, and one layer is sprayed on steering wheel main body
Anti-skid wearable layer, it includes following components according to the mass fraction：It is acrylic resin modified：55 parts, phenol-formaldehyde resin modified：34 parts,
Superfine alumina silicate：5 parts, anti-skid wearable powder：15 parts, n-butyl acetate:3 parts, dibutyl tin dilaurate：1 part, butyl rubber：
12 parts, glass fibre：10 parts, azodicarbonamide be modified castor oil：2 parts, surface modified calcium carbonate：8 parts, filler：12 parts,
Peroxidized t-butyl perbenzoate：5 parts, vinyltrimethoxy silane：6 parts, aluminium hydroxide：2 parts, the western dicarboxylic anhydride of suitable fourth：2 parts,
Pigment：8 parts, curing agent：4 parts, stabilizer：1 part, coupling agent:5 parts, solvent：6 parts；
Wherein, foregoing filler count in parts by weight including：1 part of compound rare-earth, barium sulfate：5 parts, kaolin：10 parts, organic bentonite
Profit soil:15 parts, silicon powder：22 parts, carbon fiber powder：9 parts；Anti-skid wearable powder is diamond dust, hollow ceramic micro mist and gluey stone
The mixture of ink powder；Curing agent is vinyl triamine DETA aminoethyl piperazines AE；Pigment is titanium dioxide, pearl essence, nano oxygen
Change the mixture of zinc；Stabilizer is magnesium stearate；Solvent is propane diols and ethyl acetate in mass ratio 4:1 mixture.
Embodiment 2
The present embodiment provides kind of an anti-skid wearable vehicle steering, including steering wheel main body, and one layer is sprayed on steering wheel main body and is prevented
Sliding wearing layer, it includes following components according to the mass fraction：It is acrylic resin modified：57 parts, phenol-formaldehyde resin modified：36 parts, it is super
Thin alumina silicate：8 parts, anti-skid wearable powder：19 parts, n-butyl acetate:4 parts, dibutyl tin dilaurate：2 parts, butyl rubber：15
Part, glass fibre：11 parts, azodicarbonamide be modified castor oil：3 parts, surface modified calcium carbonate：11 parts, filler：14 parts,
Peroxidized t-butyl perbenzoate：6 parts, vinyltrimethoxy silane：7 parts, aluminium hydroxide：3 parts, the western dicarboxylic anhydride of suitable fourth：3 parts,
Pigment：10 parts, curing agent：5 parts, stabilizer：2 parts, coupling agent:5 parts, solvent：7 parts；
Wherein, foregoing filler count in parts by weight including：Compound rare-earth：1.5 parts, barium sulfate:6 parts, kaolin：12 parts, have
Machine bentonite:16 parts, silicon powder：23 parts, carbon fiber powder：10 parts；Anti-skid wearable powder is diamond dust, hollow ceramic micro mist and glue
The mixture of shape graphite powder；Curing agent is vinyl triamine DETA aminoethyl piperazines AE；Pigment is titanium dioxide, pearl essence, received
The mixture of rice zinc oxide；Stabilizer is magnesium stearate；Solvent is propane diols and ethyl acetate in mass ratio 4:1 mixture.
In addition to the implementation, the present invention can also have other embodiment.It is all to use equivalent substitution or equivalent transformation shape
Into technical scheme, all fall within the protection domains of application claims.
Claims (9)
1. a kind of anti-skid wearable vehicle steering, including steering wheel main body, it is characterised in that：Sprayed on the steering wheel main body
One layer of anti-skid wearable layer, it includes following components according to the mass fraction：It is acrylic resin modified：50-60 parts, modified phenolic resin
Fat：30-40 parts, superfine alumina silicate：5-9 parts, anti-skid wearable powder：15-20 parts, n-butyl acetate:3-6 parts, tin dilaurate two
Fourth tin：1-3 parts, butyl rubber：9-17 parts, glass fibre：8-12 parts, azodicarbonamide are modified castor oil：2-3 parts, table
Face modified calcium carbonate：6-12 parts, filler：10-15 parts, peroxidized t-butyl perbenzoate：4-7 parts, vinyltrimethoxy silane：
6-8 parts, aluminium hydroxide：2-3 parts, the western dicarboxylic anhydride of suitable fourth：1-4 parts, pigment：5-11 parts, curing agent：3-5 parts, stabilizer：1-2
Part, coupling agent:3-6 parts, solvent：5-8 parts.
2. high-strength impact-resistant fascia according to claim 1, it is characterised in that：The filler is in parts by weight
Meter includes：Compound rare-earth 1-2 parts, barium sulfate：4-8 parts, kaolin：10-13 parts, organobentonite:15-18 parts, silicon powder：
20-25 parts, carbon fiber powder：8-11 parts.
3. anti-skid wearable vehicle steering according to claim 1, it is characterised in that：Described anti-skid wearable powder is gold
The mixture of emery, hollow ceramic micro mist and gluey graphite powder.
4. anti-skid wearable vehicle steering according to claim 1, it is characterised in that：The curing agent is vinyl triamine
DETA aminoethyl piperazines AE.
5. anti-skid wearable vehicle steering according to claim 1, it is characterised in that：The pigment is titanium dioxide, pearly-lustre
It is one or more in powder, nano zine oxide.
6. anti-skid wearable vehicle steering according to claim 1, it is characterised in that：The stabilizer be magnesium stearate or
Zinc stearate.
7. anti-skid wearable vehicle steering according to claim 1, it is characterised in that：The solvent is propane diols and acetic acid
Ethyl ester in mass ratio 4:1 mixture.
8. anti-skid wearable vehicle steering according to claim 1, it is characterised in that：Include according to the mass fraction with the following group
Point：Include following components according to the mass fraction：It is acrylic resin modified：55 parts, phenol-formaldehyde resin modified：34 parts, superfine alumina silicate：
5 parts, anti-skid wearable powder：15 parts, n-butyl acetate:3 parts, dibutyl tin dilaurate：1 part, butyl rubber：12 parts, glass fibers
Dimension：10 parts, azodicarbonamide be modified castor oil：2 parts, surface modified calcium carbonate：8 parts, filler：12 parts, benzoyl peroxide first
Tert-butyl acrylate：5 parts, vinyltrimethoxy silane：6 parts, aluminium hydroxide：2 parts, the western dicarboxylic anhydride of suitable fourth：2 parts, pigment：8 parts, it is solid
Agent：4 parts, stabilizer：1 part, coupling agent:5 parts, solvent：6 parts.
9. anti-skid wearable vehicle steering according to claim 1, it is characterised in that：Include according to the mass fraction with the following group
Point：It is acrylic resin modified：57 parts, phenol-formaldehyde resin modified：36 parts, superfine alumina silicate：8 parts, anti-skid wearable powder：19 parts, second
Sour N-butyl:4 parts, dibutyl tin dilaurate：2 parts, butyl rubber：15 parts, glass fibre：11 parts, azodicarbonamide is changes
Property castor oil：3 parts, surface modified calcium carbonate：11 parts, filler：14 parts, peroxidized t-butyl perbenzoate：6 parts, vinyl front three
TMOS：7 parts, aluminium hydroxide：3 parts, the western dicarboxylic anhydride of suitable fourth：3 parts, pigment：10 parts, curing agent：5 parts, stabilizer：2 parts, idol
Join agent:5 parts, solvent：7 parts.