CN107892555A - A kind of manufacturing process of regeneration aggregate art brick - Google Patents
A kind of manufacturing process of regeneration aggregate art brick Download PDFInfo
- Publication number
- CN107892555A CN107892555A CN201710587921.6A CN201710587921A CN107892555A CN 107892555 A CN107892555 A CN 107892555A CN 201710587921 A CN201710587921 A CN 201710587921A CN 107892555 A CN107892555 A CN 107892555A
- Authority
- CN
- China
- Prior art keywords
- regeneration aggregate
- manufacturing process
- compound
- spoir
- kiln
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of manufacturing process of regeneration aggregate art brick, comprise the following steps：Regenerative micro powder is prepared, spoir particle is prepared, prepares vegetable material, mixing, rolling mix, ageing shaping, painting glaze, kiln system, kiln discharge；Stacking；Repairing, packaging, storage, the present invention has wearability good, it is light, resistant to elevated temperatures feature, the present invention effectively utilizes building waste, garden garbage and industrial waste, improve the recycling effect of waste, the addition of vegetable material can rest be more prone to, possesses excellent pest control and anticorrosion moisture protection, Maintenance free, service life is grown, and the optional scope of color is wide, it can be customized by customer requirement and the surface texturing effect of regeneration aggregate art brick is enriched, it is much better than stone material, can be matched in excellence or beauty timber, it is quality-high and inexpensive, stable performance, artistic brick product with cultural emotion succession function, it is not only environmentally friendly, and resource can be maximally utilized, beautification life living environment.
Description
Technical field
The present invention relates to building field, specially a kind of manufacturing process of regeneration aggregate art brick.
Background technology
Name or pattern are carved into wall-building brick and form art brick, is then built into wall, it is both handsome in appearance, there is reality again
Commemoration meaning, all it is widely used in school abroad, auditorium.But existing artistic brick product mostly using lithotome,
Timber is raw material, and is machined into carving characters or the mode of needle drawing case is made, and not only consumes substantial amounts of lithotome, timber, and
And stone material cost is high and optional color is less, wood preservation from decay anti-corrosion moisture protection is weaker, and maintenance cost is high.Building castoff refers to
Construction unit, unit in charge of construction is newly-built, renovating and enlarging and removes all kinds of buildings, structures, pipe network etc. and resident's decorations
Caused spoir, rejected material and other discarded objects during house.With the development of Process of Urbanization Construction, the building in engineering construction
Waste discharge amount increases year by year, and its regeneration work progress is slow, causes its utilization rate all relatively low always, rough at present
Landfill disposal occupy substantial amounts of land resource, not only wasting manpower and material resources carry out discharge place maintenance, also to vegetation,
Lower water has an impact, and causes the secondary pollution of environment.Therefore the utilization orientation of building castoff how is extended, improves construction waste
The utilization rate of thing, and then solve land resource and environmental problem caused by a large amount of discharges of building castoff, turn into political affairs
The technical problem solved is badly in need of in mansion and enviromental protection enterprise.
So how to design a kind of manufacturing process of regeneration aggregate art brick, turning into us will currently solve the problems, such as.
The content of the invention
It is an object of the invention to provide a kind of manufacturing process of regeneration aggregate art brick, building waste, garden are effectively utilized
Woods rubbish and industrial waste, improve the recycling effect of waste, the addition of vegetable material can rest be more prone to, possess excellent
Good pest control and anticorrosion moisture protection, Maintenance free, service life length, and also the optional scope of color is wide, can be customized by customer requirement
And the surface texturing effect of regeneration aggregate art brick is enriched, and is much better than stone material, the timber that can match in excellence or beauty, quality-high and inexpensive, stable performance,
Artistic brick product with cultural emotion succession function, it is not only environmentally friendly, and resource can be maximally utilized, beautification life is lived
Environment, the problem of can proposing to solve the problems mentioned in the above background technology.
To achieve the above object, the present invention provides following technical scheme：
A kind of manufacturing process of regeneration aggregate art brick, comprises the following steps：
A, regeneration aggregate is prepared：Building waste is reclaimed, clean, obtain in building waste by concrete block, crushed stone and/
Or the reclaimed materials and spoir of brick and tile fragment composition；Reclaimed materials is dried, crush, sieved, obtains building below particle diameter 1.5mm
Building refuse recycled fine aggregate；Spoir is included into step b processing；
B, spoir particle is prepared：Obtained spoir is dried, crushed, sieves the spoir obtained below particle diameter 3mm
Grain is stand-by；
C, vegetable material is prepared：Garden garbage, trees, straw, rice chaff, wood is any one or two kinds of in cutting and above conduct
Vegetable material, the fiber dust being broken into below particle diameter 0.5mm, or directly using the useless slurry in paper mill, the coffee of coffee plant
Coffee slag, sugar refinery sugar residue in it is any one or two kinds of and above be used as vegetable material；
D, compound is prepared：The parts by weight of preparation process a regeneration aggregate are 5-10 parts, preparation process b spoir particle
Parts by weight be 90-95 parts, the parts by weight of preparation process c vegetable material are 1-5 parts；By ready regeneration aggregate and spoir
Grain is carried out after being well mixed, and is added ready vegetable material and is stirred mixing, and compound is obtained after well mixed；
E, rolling mix：Step d compound is carried out by abundant rolloff using edge runner；Then forced stirrer pair is used
The compound that rolling is crossed carries out action of forced stirring, while carries out moisturizing to compound, by the moisture control of compound in 8-10%；
F, ageing shaping：Compound after step e rolloffs are stirred is transported in ageing warehouse and is aged, and is aged warehouse
Temperature control at 15-45 DEG C, humid control is 70%, still aging more than 72h；The compound of ageing is sent into mandatory squeeze
Pressing machine, pass through adobe of the mould molding of different artistic shapes for different artistic shapes or building block base；
G, glaze is applied：According to the needs of finished product using spraying or other painting glaze equipment, adobe after shaping or building block base
The facade of non-adhering side carries out painting glaze；
H, kiln system：The adobe after glaze or building block base are applied under 30-50 DEG C of environment of temperature, is dried so that adobe or building block base
Moisture content in 4-6%, enter back into warm-up phase, preheating temperature is at 650 DEG C, time 2-4h；Fire into kiln, with cleaning natural gas
Roasting, 800-1200 DEG C of sintering temperature, roasting time 4-10h；The aeration-cooling 2-4h of cooling, 200- is dropped to kiln temperature in kiln
300℃；Kiln discharge；Regeneration aggregate art brick is made.
When carrying out moisturizing, it is necessary to use humidity sensor to measure water content in the step e, and pass to external control
Device processed, after now external controller processing, the signal of moisture content can be passed to display screen, and then be understood by display screen aqueous
Rate, can be accurately by moisture control in 8-10%.
After kiln step, also include stacking, repairing, packaging and storage step.
The palletization step is needed to use stacking machine, including frame, and having for being run on the long rails of frame top two is driven
The reciprocating moving trolley of dynamic device, the reversing frame with drive device on reciprocating moving trolley, installed in reversing frame
On the elevating lever with drive device, the gravity clamper of elevating lever bottom connection and be arranged on the position of region of interest
Sensor, the reversing frame, which includes centre, has rotary disk made of the steel metal plate of same diameter endoporus and concentric overlapping
And the revolution axle journal of affixed steel plate-like, the rotary disk and revolution axle journal be fixed on respectively on reciprocating moving trolley by
The reversing frame supporting arrangement that several rolling members are formed is supported；The reversing frame supporting arrangement is made up of two parts, first, peace
Some rolling members horizontal with the axis on reversing frame supporting arrangement connecting elements in lower section in the middle part of the car rack,
The rotary disk that rolling member axis is adjustable to ensure its upper limb to be in same level and be used on bearing and turning frame；Another is installation
The rolling of some vertical with the axis on reversing frame supporting arrangement connecting elements and rounded distributions of plane in the middle part of the car rack
Moving part, the revolution axle journal that rolling member axis is adjustable to ensure its inner rim to be in same periphery and be used on bearing and turning frame.
The repairing step is manual operation, and repairing is processed to obtained regeneration aggregate art brick profile.
The glaze to be dropped to applying glaze in the step g is collected, and the glaze after collection is used to repair in step to be repaired.
It need to be packed during the packaging with automatic packaging machine.
The temperature of the storage is normal temperature, and the humidity be put in storage is less than 14%.
Compared with prior art, the beneficial effects of the invention are as follows：The present invention effectively utilizes building waste, garden garbage and work
Industry waste material, improves the recycling effect of waste, the addition of vegetable material can rest be more prone to, possess excellent insect prevention and prevent
Rotten moisture protection, Maintenance free, service life length, and also the optional scope of color is wide, and can be by customer requirement customization and Regenerated Bone
The surface texturing effect of material art brick is enriched, and is much better than stone material, the timber that can match in excellence or beauty, quality-high and inexpensive, stable performance, has cultural feelings
Propagated sensation holds the artistic brick product of function, not only environmentally friendly, and can maximally utilize resource, beautification life living environment.
Brief description of the drawings
Fig. 1 is the preparation flow figure of the present invention.
Embodiment
Below in conjunction with the accompanying drawing in the embodiment of the present invention, the technical scheme in the embodiment of the present invention is carried out clear, complete
Site preparation describes, it is clear that described embodiment is only part of the embodiment of the present invention, rather than whole embodiments.It is based on
Embodiment in the present invention, those of ordinary skill in the art are obtained every other under the premise of creative work is not made
Embodiment, belong to the scope of protection of the invention.
Referring to Fig. 1, the present invention provides a kind of manufacturing process of regeneration aggregate art brick, comprise the following steps：
A, regeneration aggregate is prepared：Building waste is reclaimed, clean, obtain in building waste by concrete block, crushed stone and/
Or the reclaimed materials and spoir of brick and tile fragment composition；Reclaimed materials is dried, crush, sieved, obtains building below particle diameter 1.5mm
Building refuse recycled fine aggregate；Spoir is included into step b processing；
B, spoir particle is prepared：Obtained spoir is dried, crushed, sieves the spoir obtained below particle diameter 3mm
Grain is stand-by；
C, vegetable material is prepared：Garden garbage, trees, straw, rice chaff, wood is any one or two kinds of in cutting and above conduct
Vegetable material, the fiber dust being broken into below particle diameter 0.5mm, or directly using the useless slurry in paper mill, the coffee of coffee plant
Coffee slag, sugar refinery sugar residue in it is any one or two kinds of and above be used as vegetable material；
D, compound is prepared：The parts by weight of preparation process a regeneration aggregate are 5-10 parts, preparation process b spoir particle
Parts by weight be 90-95 parts, the parts by weight of preparation process c vegetable material are 1-5 parts；By ready regeneration aggregate and spoir
Grain is carried out after being well mixed, and is added ready vegetable material and is stirred mixing, and compound is obtained after well mixed；
E, rolling mix：Step d compound is carried out by abundant rolloff using edge runner；Then forced stirrer pair is used
The compound that rolling is crossed carries out action of forced stirring, while carries out moisturizing to compound, by the moisture control of compound in 8-10%；
F, ageing shaping：Compound after step e rolloffs are stirred is transported in ageing warehouse and is aged, and is aged warehouse
Temperature control at 15-45 DEG C, humid control is 70%, still aging more than 72h；The compound of ageing is sent into mandatory squeeze
Pressing machine, pass through adobe of the mould molding of different artistic shapes for different artistic shapes or building block base；
G, glaze is applied：According to the needs of finished product using spraying or other painting glaze equipment, adobe after shaping or building block base
The facade of non-adhering side carries out painting glaze；
H, kiln system：The adobe after glaze or building block base are applied under 30-50 DEG C of environment of temperature, is dried so that adobe or building block base
Moisture content in 4-6%, enter back into warm-up phase, preheating temperature is at 650 DEG C, time 2-4h；Fire into kiln, with cleaning natural gas
Roasting, 800-1200 DEG C of sintering temperature, roasting time 4-10h；The aeration-cooling 2-4h of cooling, 200- is dropped to kiln temperature in kiln
300℃；Kiln discharge；Regeneration aggregate art brick is made.
When carrying out moisturizing, it is necessary to use humidity sensor to measure water content in the step e, and pass to external control
Device processed, after now external controller processing, the signal of moisture content can be passed to display screen, and then be understood by display screen aqueous
Rate, can be accurately by moisture control in 8-10%.
After kiln step, also include stacking, repairing, packaging and storage step.
The palletization step is needed to use stacking machine, including frame, and having for being run on the long rails of frame top two is driven
The reciprocating moving trolley of dynamic device, the reversing frame with drive device on reciprocating moving trolley, installed in reversing frame
On the elevating lever with drive device, the gravity clamper of elevating lever bottom connection and be arranged on the position of region of interest
Sensor, the reversing frame, which includes centre, has rotary disk made of the steel metal plate of same diameter endoporus and concentric overlapping
And the revolution axle journal of affixed steel plate-like, the rotary disk and revolution axle journal be fixed on respectively on reciprocating moving trolley by
The reversing frame supporting arrangement that several rolling members are formed is supported；The reversing frame supporting arrangement is made up of two parts, first, peace
Some rolling members horizontal with the axis on reversing frame supporting arrangement connecting elements in lower section in the middle part of the car rack,
The rotary disk that rolling member axis is adjustable to ensure its upper limb to be in same level and be used on bearing and turning frame；Another is installation
The rolling of some vertical with the axis on reversing frame supporting arrangement connecting elements and rounded distributions of plane in the middle part of the car rack
Moving part, the revolution axle journal that rolling member axis is adjustable to ensure its inner rim to be in same periphery and be used on bearing and turning frame.
The repairing step is manual operation, and repairing is processed to obtained regeneration aggregate art brick profile.
The glaze to be dropped to applying glaze in the step g is collected, and the glaze after collection is used to repair in step to be repaired.
It need to be packed during the packaging with automatic packaging machine.
The temperature of the storage is normal temperature, and the humidity be put in storage is less than 14%.
Based on above-mentioned, it is an advantage of the current invention that the present invention effectively utilizes building waste, garden garbage and industrial waste,
Improve the recycling effect of waste, the addition of vegetable material can rest be more prone to, it is moistureproof to possess excellent pest control and anticorrosion
Ability, Maintenance free, service life length, and also the optional scope of color is wide, can be customized by customer requirement and regeneration aggregate is artistic
The surface texturing effect of brick is enriched, and is much better than stone material, the timber that can match in excellence or beauty, quality-high and inexpensive, stable performance, has the succession of cultural emotion
The artistic brick product of function, it is not only environmentally friendly, and resource can be maximally utilized, beautification life living environment.
Although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
A variety of changes, modification can be carried out to these embodiments, replace without departing from the principles and spirit of the present invention by understanding
And modification, the scope of the present invention is defined by the appended.
Claims (8)
- A kind of 1. manufacturing process of regeneration aggregate art brick, it is characterised in that：Comprise the following steps：A, regeneration aggregate is prepared：Building waste is reclaimed, cleans, obtains in building waste by concrete block, crushed stone and/or brick The reclaimed materials and spoir of watt fragment composition；Reclaimed materials is dried, crush, sieved, obtains the building rubbish below particle diameter 1.5mm Rubbish recycled fine aggregate；Spoir is included into step b processing；B, spoir particle is prepared：Obtained spoir is dried, crushed, the spoir particle obtained below particle diameter 3mm is sieved and treats With；C, vegetable material is prepared：Garden garbage, trees, straw, rice chaff, wood are any one or two kinds of in cutting and are used as plant above Material, the fiber dust being broken into below particle diameter 0.5mm, or directly use the useless slurry in paper mill, coffee plant coffee grounds, Any one or two kinds of and above is used as vegetable material in the sugar residue in sugar refinery；D, compound is prepared：The parts by weight of preparation process a regeneration aggregate are 5-10 parts, the weight of preparation process b spoir particle Amount part is 90-95 parts, and the parts by weight of preparation process c vegetable material are 1-5 parts；Ready regeneration aggregate and spoir particle are entered After row is well mixed, adds ready vegetable material and be stirred mixing, compound is obtained after well mixed；E, rolling mix：Step d compound is carried out by abundant rolloff using edge runner；Then using forced stirrer to rolling The compound crossed carries out action of forced stirring, while carries out moisturizing to compound, by the moisture control of compound in 8-10%；F, ageing shaping：Compound after step e rolloffs are stirred is transported in ageing warehouse and is aged, and is aged the temperature in warehouse Degree control is at 15-45 DEG C, and humid control is 70%, still aging more than 72h；The compound of ageing is sent into mandatory be squeezed into Type machine, pass through adobe of the mould molding of different artistic shapes for different artistic shapes or building block base；G, glaze is applied：According to the needs of finished product using spraying or other painting glaze equipment, adobe after shaping or building block base it is non-stick The facade of junction carries out painting glaze；H, kiln system：The adobe after glaze or building block base are applied under 30-50 DEG C of environment of temperature, is dried so that adobe or building block base contain Water rate enters back into warm-up phase in 4-6%, and preheating temperature is at 650 DEG C, time 2-4h；Fire into kiln, roasted with cleaning natural gas Burn, 800-1200 DEG C of sintering temperature, roasting time 4-10h；The aeration-cooling 2-4h of cooling, 200- is dropped to kiln temperature in kiln 300℃；Kiln discharge；Regeneration aggregate art brick is made.
- A kind of 2. manufacturing process of regeneration aggregate art brick according to claim 1, it is characterised in that：In the step e When carrying out moisturizing, it is necessary to use humidity sensor to measure water content, and external controller is passed to, now external controller After processing, the signal of moisture content can be passed to display screen, and then moisture content is understood by display screen, can accurately will be aqueous Rate is controlled in 8-10%.
- A kind of 3. manufacturing process of regeneration aggregate art brick according to claim 1, it is characterised in that：After kiln step, Also include stacking, repairing, packaging and storage step.
- A kind of 4. manufacturing process of regeneration aggregate art brick according to claim 3, it is characterised in that：The palletization step Need to use stacking machine, including frame, the reciprocating moving trolley with drive device run on the long rails of frame top two, The reversing frame with drive device on reciprocating moving trolley, the lifting with drive device on reversing frame Bar, the gravity clamper of elevating lever bottom connection and the position sensor for being arranged on region of interest, the reversing frame include Centre has time of rotary disk made of the steel metal plate of same diameter endoporus and concentric overlapping and affixed steel plate-like Rotating shaft neck, the rotary disk and revolution axle journal are fixed on being returned by what several rolling members were formed on reciprocating moving trolley respectively Pivoted frame supporting arrangement is supported；The reversing frame supporting arrangement is made up of two parts, and one is mounted in the middle part of the car rack Some rolling members horizontal with the axis on reversing frame supporting arrangement connecting elements in lower section, rolling member axis is adjustable to ensure The rotary disk that its upper limb is in same level and is used on bearing and turning frame；It is another to be mounted in upper plane in the middle part of car rack The rolling member of some vertical with axis on reversing frame supporting arrangement connecting elements and rounded distributions, rolling member axis is adjustable with Ensure the revolution axle journal that its inner rim is in same periphery and is used on bearing and turning frame.
- A kind of 5. manufacturing process of regeneration aggregate art brick according to claim 3, it is characterised in that：The repairing step For manual operation, repairing is processed to obtained regeneration aggregate art brick profile.
- A kind of 6. manufacturing process of regeneration aggregate art brick according to claim 3, it is characterised in that：To the step g The glaze that middle painting glaze drops is collected, and the glaze after collection is used to repair in step to be repaired.
- A kind of 7. manufacturing process of regeneration aggregate art brick according to claim 3, it is characterised in that：Needed during the packaging Packed with automatic packaging machine.
- A kind of 8. manufacturing process of regeneration aggregate art brick according to claim 3, it is characterised in that：The temperature of the storage Spend for normal temperature, and the humidity be put in storage is less than 14%.