CN107881782A - Spinning sizing agent - Google Patents

Spinning sizing agent Download PDF

Info

Publication number
CN107881782A
CN107881782A CN201711227527.8A CN201711227527A CN107881782A CN 107881782 A CN107881782 A CN 107881782A CN 201711227527 A CN201711227527 A CN 201711227527A CN 107881782 A CN107881782 A CN 107881782A
Authority
CN
China
Prior art keywords
parts
sizing agent
spinning sizing
polyvinyl alcohol
sio
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201711227527.8A
Other languages
Chinese (zh)
Inventor
蒋宏
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Suzhou Runhong Trade Co Ltd
Original Assignee
Suzhou Runhong Trade Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Suzhou Runhong Trade Co Ltd filed Critical Suzhou Runhong Trade Co Ltd
Priority to CN201711227527.8A priority Critical patent/CN107881782A/en
Publication of CN107881782A publication Critical patent/CN107881782A/en
Pending legal-status Critical Current

Abstract

The present invention relates to a kind of spinning sizing agent, by following weight than each component form：8 parts of polyvinyl alcohol, 12 parts of glass polyacrylate, 35 parts of SiO 2 modified starch, 60 parts of water, 3 parts of defoamers.Spinning sizing agent provided by the invention, using polyvinyl alcohol, polyvinyl alcohol and SiO 2 modified starch composition, normal-temperature dissolution, it is not required to heat, so as to reach the purpose of energy-conservation.

Description

Spinning sizing agent
Technical field
The present invention relates to a kind of spinning sizing agent, belongs to textile material technical field.
Background technology
Warp sizing is one of woven committed step.Slurry used in the prior art is varied, still, upper In sizing process, heating is a required procedure.And heating needs to consume mass energy.
The content of the invention
The invention solves technical problem to be：The shortcomings that overcoming above-mentioned technology, there is provided a kind of to be capable of preventing for normal temperature starching Slurry.
In order to solve the above-mentioned technical problem, technical scheme proposed by the present invention is：A kind of spinning sizing agent, by following weight ratio Each component composition：8 parts of polyvinyl alcohol, 12 parts of glass polyacrylate, 35 parts of SiO 2 modified starch, 60 parts of water, 3 parts of defoamings Agent.
Spinning sizing agent provided by the invention, using polyvinyl alcohol, polyvinyl alcohol and SiO 2 modified starch composition, normal temperature Dissolving, is not required to heat, so as to reach the purpose of energy-conservation.
Embodiment
The spinning sizing agent of the present embodiment, by following weight than each component form：8 parts of polyvinyl alcohol, 12 parts of glass polypropylene Acid esters, 35 parts of SiO 2 modified starch, 60 parts of water, 3 parts of defoamers.
The present invention is not limited to the concrete technical scheme described in above-described embodiment, and in addition to the implementation, the present invention may be used also To there is other embodiment.For those skilled in the art, within the spirit and principles of the invention, that is made appoints The technical scheme of the formation such as what modification, equivalent substitution, improvement, should be included in the scope of the protection.

Claims (1)

  1. A kind of 1. spinning sizing agent, it is characterised in that by following weight than each component form：8 parts of polyvinyl alcohol, 12 parts of glass poly- third Olefin(e) acid ester, 35 parts of SiO 2 modified starch, 3 parts of defoamers, 60 parts of water.
CN201711227527.8A 2017-11-29 2017-11-29 Spinning sizing agent Pending CN107881782A (en)