CN107867100A - Position flower pattern transfer membrane and its manufacture craft - Google Patents
Position flower pattern transfer membrane and its manufacture craft Download PDFInfo
- Publication number
- CN107867100A CN107867100A CN201711218229.2A CN201711218229A CN107867100A CN 107867100 A CN107867100 A CN 107867100A CN 201711218229 A CN201711218229 A CN 201711218229A CN 107867100 A CN107867100 A CN 107867100A
- Authority
- CN
- China
- Prior art keywords
- flower pattern
- layer
- transfer membrane
- pattern transfer
- coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Present invention positioning flower pattern transfer membrane and its manufacture craft are related to transfer membrane field, the positioning flower pattern transfer membrane includes substrate layer, release layer, flower pattern layer and rubberised layer, the release layer is coated on substrate layer, coated on release layer, the rubberised layer is coated on the back side of substrate layer the flower pattern layer.Transfer membrane is set to have positioning flower pattern by the present invention, it is good that property is tried out in thermoprint so that the outward appearance for the product being transferred is more rich various, attractive in appearance.
Description
Technical field
The present invention relates to transfer membrane field, more particularly to positioning flower pattern transfer membrane and its manufacture craft.
Background technology
Positioning flower pattern transfer membrane is applied PUR and formed by the coating multiple coating on wide-range film base material, the then back of the body, then
Flower pattern will be positioned comprehensively by the method for heating, pressurizeing or part is transferred to various synthetic leathers, natural leather, textile and paper
Etc. surface, be widely used on the products such as footwear material, case and bag, clothing leather and paper.
But existing positioning its finished product stability of flower pattern transfer membrane and glossiness are poor, and its thermoprint applicability and water-fastness
Property is all bad.
Therefore, need a kind of new positioning flower pattern transfer membrane improve its stability, glossiness, thermoprint applicability and water-fastness
Property.
The content of the invention
To achieve the above object, the present invention adopts the following technical scheme that：Position flower pattern transfer membrane, it is characterised in that：It is described
Positioning flower pattern transfer membrane includes substrate layer, release layer, flower pattern layer and rubberised layer, and the release layer is coated on substrate layer, described
For flower pattern layer coated on release layer, the rubberised layer is coated on the substrate layer back side.
Further, the substrate layer backside coating has PUR.
Further, the substrate layer is the plastic-based film made of PET, OPP, PP at least one material.
Further, the coatings that the release layer is matched by mould release, alcohol and water form, and the coating thickness is
1~5um.
Further, the weight proportion of mould release, alcohol and water is 1：5：5.
Further, the flower pattern layer is formed by the coatings of ink and solvent burden ratio, the coating thickness be 10~
15um。
Further, ink and the solvent allotment ratio is allocated according to color.
Further, the rubberised layer is formed by the coatings of gum and solvent burden ratio, the coating thickness be 10~
30um。
Further, the weight proportion of the gum and solvent is 2:1.
Further, the manufacture craft of flower pattern transfer membrane is positioned, is comprised the following steps；
S1：Each coating to be coated is diluted, PP films are pacified as cloth base material, allotment is applied from 10-30um PP films
On coating machine, coating machine is opened, sets baking temperature and coating speed；
S2：Release layer is coated with, and sets baking temperature as 110 °~140 °, coating speed 120m/min；Using 220 net rolls
Coating；
S3：Flower pattern layer is coated with, and sets baking temperature as 70 °~80 °, coating speed 90m/min, is applied using flower pattern net roll
Cloth, 20~80g/m of wet coating amount2；
S4：Rubberised layer, baking temperature is set as 40 °~80 °, coating speed 100m/min.
Beneficial effects of the present invention are：
1. making transfer membrane have positioning flower pattern by the present invention, it is good that property is tried out in thermoprint so that the outward appearance for the product being transferred is more
It is rich and varied, attractive in appearance；
2. the present invention uses oiliness mould release by the mould release of release layer, water resistance, heat resistance are good；
3. the present invention by rubberised layer, rubberised layer use gum and solvent, finished product is not easy to fade, reach stability it is good with
Glossiness is good.
4. flower pattern transfer membrane thermoprint applicability of the present invention is good, various leathers can be adhered well to, on textile surface, no
It is easy to fall off；
Brief description of the drawings
The invention will be further described for accompanying drawing, but the embodiment in accompanying drawing does not form any limitation of the invention.
Fig. 1 is the structural representation that one embodiment of the invention provides；
1- substrate layer 2- release layer 3- flower pattern layer 4- rubberised layers
Embodiment
The invention will be further described below in conjunction with the accompanying drawings, wherein using Fig. 1 direction as standard.
Fig. 1-as shown in, one embodiment of the invention provide positioning flower pattern transfer membrane, including substrate layer 1, release layer 2,
Flower pattern layer 3 and rubberised layer 4, release layer 2 is coated on substrate layer 1, and coated on release layer 2, rubberised layer 4 is coated on flower pattern layer 3
The back side of substrate layer 1；
The plastic-based film made of the materials such as PET, OPP, PP of substrate layer 1, in the backside coating PUR of substrate layer 1.
Release layer 2 is by mould release, alcohol and water according to 1:5:What the coatings of 5 allotment ratio proportioning formed, coating
The thickness of coating is 1~5um, when air humidity is larger, to prevent from turning white, can add alcohol more, when alcohol-free, also be can use
Water replaces, and mould release is preferably aqueous polyurethane coating, and decorative pattern is exactly transferred to various each by the main effect of decorative pattern transfer membrane
On the product of sample, the main function of release layer is just so that during the transfer of decorative pattern transfer membrane and intactly can departed from substrate layer, therefore
The mould release of selection is extremely important, and aqueous polyurethane has good coating machinery performance, a film forming, and release effect is good after film forming,
Layer upper surface is bright and clean, smooth, and transparency is high, can transmission metal gloss very well；With good water resistance, solvent resistance and resistance to old
Change performance, resistance to cleaning after film forming, it is not easy to come off, stability is good.
Flower pattern layer 3 is formed by the coatings of ink and solvent allotment ratio, and the allotment ratio of ink and solvent is according to face
Se Laiding.The effect of flower pattern layer 3 is display flower pattern；
Rubberised layer 4 is by gum and solvent according to 2:What 1 allotment ratio formed to allocate coatings, coating thickness 10
~30um.Rubberised layer 4 uses heat molten type polyurethane resin, and the effect of rubberised layer 4 is to turn the transfer printing coating on flower pattern transfer membrane
Shifting is adhered to by boiling hot object, is considerably increased the adhesive force after blocking film transfer using hot melt type polyurethane resin, is not easy to take off
Fall.
The manufacture craft of positioning flower pattern transfer membrane comprises the following steps：
S1：Each coating to be coated is diluted, PP films are pacified as cloth base material, allotment is applied from 10-30um PP films
On coating machine, coating machine is opened, sets baking temperature and coating speed；
S2：Release layer be coated with, by six section oven cooking cycles, six section oven cooking cycle temperature be respectively set as 110 °, 130 °,
140 °, 140 °, 130 ° and 110 °, coating speed 120m/min；It is coated with using 220 net rolls；
S3：Flower pattern layer be coated with, by six section oven cooking cycles, six section oven cooking cycle temperature be respectively set as 70 °, 80 °, 80 °,
80 °, 80 ° and 80 °, coating speed 90m/min, it is coated with using flower pattern net roll, 20~80g/m of wet coating amount2；
S4：Rubberised layer, by six section oven cooking cycles, six section oven cooking cycle temperature set respectively 70 °, 80 °, 40 °, 40 °,
40 ° and 40 °, coating speed 100m/min.
Each technical characteristic of embodiment described above can be combined arbitrarily, to make description succinct, not to above-mentioned reality
Apply all possible combination of each technical characteristic in example to be all described, as long as however, the combination of these technical characteristics is not deposited
In contradiction, the scope that this specification is recorded all is considered to be.
Embodiment described above only expresses the several embodiments of the present invention, and its description is more specific and detailed, but simultaneously
Can not therefore it be construed as limiting the scope of the patent.It should be pointed out that come for one of ordinary skill in the art
Say, without departing from the inventive concept of the premise, various modifications and improvements can be made, these belong to the protection of the present invention
Scope.Therefore, the protection domain of patent of the present invention should be determined by the appended claims.
Claims (10)
1. position flower pattern transfer membrane, it is characterised in that：The positioning flower pattern transfer membrane include substrate layer, release layer, flower pattern layer and
Rubberised layer, the release layer is coated on substrate layer, and for the flower pattern layer coated on release layer, the rubberised layer is coated on base material
The back side of layer.
2. positioning flower pattern transfer membrane according to claim 1, it is characterised in that：The substrate layer backside coating has hot melt
Glue.
3. positioning flower pattern transfer membrane according to claim 1, it is characterised in that：The substrate layer be by PET, OPP, PP extremely
Plastic-based film made of a kind of few material.
4. positioning flower pattern transfer membrane according to claim 1, it is characterised in that：The release layer by mould release, alcohol and
The coatings of water proportioning form, and the coating thickness is 1~5um.
5. positioning flower pattern transfer membrane according to claim 4, it is characterised in that：The weight of the mould release, alcohol and water
Match as 1：5：5.
6. positioning flower pattern transfer membrane according to claim 1, it is characterised in that：The flower pattern layer is by ink and solvent burden ratio
Coatings form, the coating thickness is 10~15um.
7. positioning flower pattern transfer membrane according to claim 6, it is characterised in that：Ink and the solvent allotment ratio according to
Color is allocated.
8. positioning flower pattern transfer membrane according to claim 1, it is characterised in that：The rubberised layer is by gum and solvent burden ratio
Coatings form, the coating thickness is 10~30um.
9. positioning flower pattern transfer membrane according to claim 8, it is characterised in that：The weight proportion of the gum and solvent is
2:1。
10. position the manufacture craft of flower pattern transfer membrane, it is characterised in that：Comprise the following steps；
S1：Each coating to be coated is diluted, PP films are arranged on as cloth base material, allotment is applied from 10-30um PP films
On coating machine, coating machine is opened, sets baking temperature and coating speed；
S2：Release layer is coated with, and sets baking temperature as 110 °~140 °, coating speed 120m/min；Applied using 220 net rolls
Cloth；
S3：Flower pattern layer is coated with, and sets baking temperature as 70 °~80 °, coating speed 90m/min, is coated with using flower pattern net roll,
20~80g/m of wet coating amount2；
S4：Rubberised layer, baking temperature is set as 40 °~80 °, coating speed 100m/min.