CN107858858A - For the buffer fillings agent in corrugated layer in high-strength corrugated board - Google Patents
For the buffer fillings agent in corrugated layer in high-strength corrugated board Download PDFInfo
- Publication number
- CN107858858A CN107858858A CN201711073183.XA CN201711073183A CN107858858A CN 107858858 A CN107858858 A CN 107858858A CN 201711073183 A CN201711073183 A CN 201711073183A CN 107858858 A CN107858858 A CN 107858858A
- Authority
- CN
- China
- Prior art keywords
- parts
- corrugated
- powder
- corrugated board
- corrugated paper
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
For the buffer fillings agent in corrugated layer in high-strength corrugated board, it is related to cardboard manufacture processing technique field, is prepared from the following components；80~100 parts of ABS plastic particle, 1~1.5 part of lapis lazuli powder, 1~2 part of halogen-free flameproof synergist, 1.5~3 parts of EP rubbers, 0.2~1 part of lubricant, 0.1~0.5 part of antioxidant, 1~2 part of initiator, 0.2~0.4 part of graphitic lubricant, 5~10 parts of polypropylene short fiber, 0.5~1 part of dimethicone, 5~8 parts of Vinylidene Chloride, 1.5~3 parts of sodium metasilicate, 1~2 part of Stiffening agent, 0.5~1 part of talcum powder, 0.5~1 part of surfactant, 3~5 parts of cryolite powder.The present invention plays good reinforcement effect to corrugated paper, there is provided buffer effect, moreover can also carry out dehumidifying to the space inside corrugated paper, the using effect of the corrugated paper after dehumidifying is more obvious.
Description
Technical field：
The present invention relates to cardboard to manufacture processing technique field, and in particular to in corrugated layer in high-strength corrugated board
Buffer fillings agent.
Background technology：
Corrugated board is the adherend of a multilayer, and it is at least made up of one layer of waveform core paper interlayer and a layer paperboard.
It has very high mechanical strength, can support collision in by handling process and fall and fall.The practical manifestation of corrugated case depends on three
Factor:The structure of the characteristic and carton of core paper and cardboard in itself.
Corrugated board is also known as corrugated cardboard.It is bonded, is had preferable by least one layer of corrugated paper and one layer of boxboard
Elasticity and extensibility.Mainly for the manufacture of carton, other sandwich and delicate articles packaging materials of carton.With local method straw pulp
With waste paper through mashing, the base board of similar manila board is made, then is machined and makes to roll into corrugated, then in its surface silicic acid
The adhesive such as sodium are bonded with boxboard.
The corrugation ripple of corrugated board is mutually juxtaposed in a row, mutually support, formation as the arched door connected one by one
Three-legged structure body, there is preferable mechanical strength, certain pressure, and springiness, cushioning effect can be also born from plane
It is good；The pad or container of variously-shaped size can be made as needed for it, easier than plastic. buffer material, quick；By temperature
Influence small, light-proofness is good, is never degenerated by illumination, is typically influenceed by humidity also smaller, but should not be grown in the larger environment of humidity
Phase uses, and this can influence its intensity.
The import corrugated case production of foreign trade supply is mainly quantified with paper from the import of the state such as the U.S., Japan, Finland, Canada
For 360g/m2 oxen card and 180g/m2 fluting mediums, also some be set to 337g/m2 oxen card and 160g/m2 fluting mediums.For
Improve domestic corrugated case production paper, there is part papermaking enterprise to also begin to manufacture experimently quantification of 360g/m2 and 420g/m2 leather boxes
Paperboard (kraft inner paper).Subsequently, as the construction of product and corrugated case production the paper manufacturing enterprise of a part of papermaking enterprise
Go into operation, carton production paper is of numerous names, and each rank, the boxboard of grammes per square metre and fluting medium are constantly launched, carton production
Enterprise increases cardboard choice.Corrugated case production paper material is required in corrugated board national standard (GB-6544-86)
Regulation is had to comply with, is respectively quantitatively 250g/m2,280g/m2,300g/m2,320g/m2,360g/m2 with boxboard, corrugation is former
Paper is 125g/m2,150g/m2,180g/m2, thus makes single, double corrugated board grammes per square metre left in 1000g/m2~1100g/m2
The right side, on the basis of ensuring to quantify, it ensure that the quality of carton.
The content of the invention：
The technical problems to be solved by the invention be to provide it is a kind of it is simple in construction, intensity is high, easy to process, material is new
Buffer fillings agent in grain husk, environmentally friendly high-strength corrugated board in corrugated layer.
The technical problems to be solved by the invention are realized using following technical scheme：
A kind of high-strength corrugated board, combined by boxboard, demarcation strip and corrugated paper, the boxboard is provided with
Lower two pieces, demarcation strip is provided among boxboard, the both sides of the demarcation strip are provided with corrugated paper, and the corrugated paper is continuous
Semicircle arcuation structure, hemispherical hollow cushion chamber is formed between corrugated paper and demarcation strip, corrugated paper and boxboard it
Between be filled with glue, the corrugated paper is internally provided with filler；
Further technology, the thickness of the boxboard are the half for separating plate thickness；
Further technology, the thickness of the corrugated paper are identical with boxboard thickness；
Further technology, the thickness of the corrugated paper are the half for separating plate thickness；
Further technology, the filler in the corrugated paper is water-based filler, is combined after drying with corrugated paper；
Further technology, the length of the corrugated paper are the 9/10 of boxboard paper length；
Further technology, the corrugated paper are uniformly arranged on the centre position of demarcation strip both sides, and the corrugated paper of both sides closes
It is symmetrical in demarcation strip；
A kind of high-strength corrugated board, by the cooperation of demarcation strip and corrugated paper, symmetrical corrugated paper is set to carry
High support strength, and the support force of corrugated paper is enhanced using semicircular arc structure, more preferable branch is played to boxboard
Support acts on, and the effect of demarcation strip can also play a part of reinforcement to fix corrugated paper, and stress point is provided for corrugated paper, also
Firm effect can be played, and being filled in the glue between corrugated paper and boxboard can increase between boxboard and corrugated paper
Firmness, improve the overall intensity of corrugated board；
The glue filled between corrugated paper and boxboard can play stickup effect corrugated paper can also be played it is fixed and
The effect of enhancing, wherein glue are prepared from the following components：30~50 parts of surfactant, 5~10 parts of antiager, defoaming
0.1~0.3 part of agent, 10~15 parts of toughener, 3~8 parts of accelerator, 20~25 parts of fire retardant, 1~3 part of borax, starch 10~12
Part, 50~80 parts of water.
Preferably, the glue, the raw material of following parts by weight is included：30~40 parts of surfactant, antiager 8~10
Part, 0.2~0.3 part of defoamer, 10~13 parts of toughener, 3~5 parts of accelerator, 22~25 parts of fire retardant, 1~2 part of borax, form sediment
10~11 parts of powder, 50~60 parts of water.
Preferably, the glue, the raw material of following parts by weight is included：40~50 parts of surfactant, antiager 5~8
Part, 0.1~0.2 part of defoamer, 13~15 parts of toughener, 5~8 parts of accelerator, 20~22 parts of fire retardant, 2~3 parts of borax, form sediment
11~12 parts of powder, 60~80 parts of water.
Preferably, the surfactant be lecithin, fatty glyceride, the one of which of sulfated castor oil.
Preferably, the antiager is zinc oxide, dilauryl thiodipropionate, the one of which of tertiary amine.
Preferably, the defoamer is dimethicone, higher alcohols, the one of which of polyether-modified silicon.
Preferably, the toughener is styrene-butadiene, haloflex, the one of which of neoprene.
Preferably, the accelerator is triethanolamine, ferric trichloride, the one of which of tetramethyl thiourea.
Preferably, the fire retardant is aluminium hydroxide, antimony oxide, the one of which of magnesium hydroxide.
During making, surfactant and antiager are loaded into reactor, be warming up to 230 DEG C be completely dissolved after, start stirring
It is warming up to 280 DEG C, is incubated 30 minutes, then add defoamer, toughener, be incubated 30 minutes, is then blended into accelerator, fire-retardant
Agent, borax, starch and water, insulated and stirred 20-30 minutes, glue is both obtained after taking the dish out of the pot.
Compared with common glue, this glue cost is low, and each raw material is environment-protecting and non-poisonous, has no irritating odor, and it is convenient that glue preserves,
It is not easy to solidify, is not easy using the corrugated board after glue by tear fracture, waterproof ability is outstanding, adds fire retardant, nonflammable, peace
It is complete reliable.
Moreover, the filler inside corrugated paper can play good reinforcement effect to corrugated paper, there is provided buffering
Effect, can also moreover dehumidifying be carried out to the space inside corrugated paper, the using effect of the corrugated paper after dehumidifying is more obvious；
For the buffer fillings agent in corrugated layer in high-strength corrugated board, it is prepared from the following components；ABS plastic
80~100 parts of grain, 1~1.5 part of lapis lazuli powder, 1~2 part of halogen-free flameproof synergist, 1.5~3 parts of EP rubbers, lubricant 0.2
~1 part, 0.1~0.5 part of antioxidant, 1~2 part of initiator, 0.2~0.4 part of graphitic lubricant, 5~10 parts of polypropylene short fiber, two
0.5~1 part of methyl-silicone oil, 5~8 parts of Vinylidene Chloride, 1.5~3 parts of sodium metasilicate, 1~2 part of Stiffening agent, 0.5~1 part of talcum powder, table
0.5~1 part of face activating agent, 3~5 parts of cryolite powder；
It is described be used for the buffer fillings agent component in high-strength corrugated board in corrugated layer preferred scheme be：ABS plastic
80~90 parts of particle, 1~1.5 part of lapis lazuli powder, 1~2 part of halogen-free flameproof synergist, 1.5~2 parts of EP rubbers, lubricant 0.2
~1 part, 0.1~0.5 part of antioxidant, 1~2 part of initiator, 0.2~0.4 part of graphitic lubricant, 5~8 parts of polypropylene short fiber, two
0.5~1 part of methyl-silicone oil, 5~8 parts of Vinylidene Chloride, 1.5~3 parts of sodium metasilicate, 1~2 part of Stiffening agent, 0.5~1 part of talcum powder, table
0.5~1 part of face activating agent, 3~4 parts of cryolite powder；
It is described be used for the buffer fillings agent in high-strength corrugated board in corrugated layer optimum proportion scheme be：ABS plastic
90 parts of particle, 1.5 parts of lapis lazuli powder, 1.5 parts of halogen-free flameproof synergist, 2 parts of EP rubbers, 0.5 part of lubricant, antioxidant 0.3
Part, 1.5 parts of initiator, 0.3 part of graphitic lubricant, 8 parts of polypropylene short fiber, 0.5 part of dimethicone, 5 parts of Vinylidene Chloride, silicic acid
3 parts of sodium, 2 parts of Stiffening agent, 1 part of talcum powder, 0.5 part of surfactant, 5 parts of cryolite powder.
Above-mentioned ABS plastic particle passes through modification before use, mixes ABS plastic particle with glycerine during processing, sweet
Oily usage amount is the 1/5 of ABS plastic granular mass；
The lapis lazuli powder passes through microwave treatment before use, using 400MHz frequency processing 18-25S；
The cryolite powder passes through microwave treatment before use, using 400MHz frequency processing 18-25S；
The dimethicone passes through heating treatment, dimethicone is warming up into 100-115 DEG C in flask, Ran Houheng
Temperature preserves 5 minutes, after to be cooled to normal temperature stand-by；
In order to improve the intensity of high-strength corrugated board of the present invention, the paper pulp of boxboard is made by following methods system
It is standby to form：
1), pretreatment of raw material
Maize straw is cut into the stalk section that length is 0.5~1.5cm；Fresh straw section is obtained, being then placed in water temperature is
Immersion treatment 10~50 minutes, stalk after must handling in the aqueous slkali that 60~90 DEG C of hot water or mass concentration is 5~30%
Section；
2), physics slurrying：
Fresh straw section obtained by step 1) is subjected to mechanical jordaning and thread rolling；Until the length of the stalk fibre muscle of gained
For 1~3mm；
3), carry out further thread rolling in the stalk fibre muscle obtained by step 2) plus after water and grind, until stalk fibre
The length of muscle is 0.3~0.5mm, obtains fiber pulp；The dosage of the water is 10%~15% of the stalk section dry weight in step 1)；
4), decolourize or colour：
Added in above-mentioned fiber pulp lime solution or KOH solution or NaOH solution that mass concentration is 0.1~2% or
H2O2Solution decolourizes, and bleaching time is 10~20 minutes；Drainage drains 30~60min minutes again, fiber pulp after must handling；Lime
Solution or KOH solution or NaOH solution or H2O2The volume ratio of solution and fiber pulp be 2~10%, so as to realize decolourize, bleaching with
Sofening treatment；
It is described to be colored as：
Dyestuff is added into the fiber pulp obtained by step 3), the dosage of dyestuff is 2% of the stalk section dry weight in step 1)
~10%, fiber pulp after must handling, so that stalk fibre muscle has particular color；
5), mechanical pulp mixes with chemical pulp
Fiber pulp mixes with cane syrup or secondary stock according to 1: 0.1~10 dry weight ratio after processing obtained by step 4),
So far the paper pulp for making boxboard prepares completion；
The corrugated board being process by above method preparation all has in intensity and fire retardancy to be significantly improved, and
And using effect of the moist increase under big humidity environment can also be resisted, corrugated board is prepared using the above method, and to corrugation
Cardboard carries out grouping experiment, and every group of selection sample number 5 is opened, and chooses three groups altogether, respectively the compression strength to corrugated board, water-fast energy
Power, moisture absorption ability, content of formaldehyde and burning-point are tested, and experimental result is counted into such as following table：
Understand that the beneficial effect of corrugated board prepared by the present invention is by upper table analysis：It is simple in construction, intensity is high, processing
Convenient, material is novel, environmental protection standard is high, has in compression strength, water-resistant capacity, moisture absorption ability etc. and is obviously improved, and increases
The waterproof and fire resistance property of corrugated board, be advantageous to extend the service life of corrugated board.
Brief description of the drawings：
Fig. 1 is a kind of structural representation of high-strength corrugated board；
Fig. 2 is corrugated paper and partition plate structure schematic diagram in a kind of high-strength corrugated board；
Fig. 3 is corrugated paper structure schematic diagram in a kind of high-strength corrugated board；
Wherein：1- boxboards；2- demarcation strips；3- corrugated papers；4- glue；5- cushion chambers.
Embodiment：
In order that the technical means, the inventive features, the objects and the advantages of the present invention are easy to understand, tie below
Conjunction is specifically illustrating, and the present invention is expanded on further.
, it is necessary to explanation in description of the invention, the orientation of instruction such as term " vertical ", " on ", " under ", " level " or
Person's position relationship is based on orientation shown in the drawings or position relationship, is for only for ease of and describes this practicality and simplify to describe,
Rather than instruction either implies that signified device or element must have specific orientation, with specific azimuth configuration and behaviour
Make, therefore be not considered as limiting the invention.
In description of the invention, it is also necessary to explanation, unless otherwise clear and definite regulation and limitation, term " setting ", " peace
Dress ", " connected ", " connection " should be interpreted broadly, for example, it may be fixedly connected or be detachably connected, or integratedly
Connection, can be mechanical connection or electrical connection, can be directly connected to or be connected by intermediary, can
To be the connection of two element internals.For the ordinary skill in the art, can understand as the case may be above-mentioned
The concrete meaning of term in the present invention.
Embodiment 1：
As shown in Figure 1-Figure 3：A kind of high-strength corrugated board, combined by boxboard 1, demarcation strip 2 and corrugated paper 3,
Boxboard 1 is provided with two pieces up and down, and demarcation strip 2 is provided among boxboard 1, and the both sides of demarcation strip 2 are provided with corrugated paper 3,
Corrugated paper 3 is continuous semicircle arcuation structure, and hemispherical hollow cushion chamber 5 is formed between corrugated paper 3 and demarcation strip 2,
Glue 4 is filled between corrugated paper 3 and boxboard 1, corrugated paper 3 is internally provided with filler；
The thickness of boxboard 1 is the half of the thickness of demarcation strip 2；
The thickness of corrugated paper 3 is identical with the thickness of boxboard 1；
The thickness of corrugated paper 3 is the half of the thickness of demarcation strip 2；
Filler in corrugated paper 3 is water-based filler, is combined after drying with corrugated paper 3；
The length of corrugated paper 3 is the 9/10 of the length of boxboard 1；
Corrugated paper 3 is uniformly arranged on the centre position of the both sides of demarcation strip 2, and the corrugated paper 3 of both sides is mutually right on demarcation strip 2
Claim.
Embodiment 2：
As shown in Figure 1-Figure 3：A kind of high-strength corrugated board, by the cooperation of demarcation strip 2 and corrugated paper 3, it is mutually right to make
The corrugated paper 3 of title can improve support strength, and the support force of corrugated paper 3 is enhanced using semicircular arc structure, right
Boxboard 1 plays more preferable supporting role, and the effect of demarcation strip 2 can also play a part of reinforcement to fix corrugated paper 3,
Stress point is provided for corrugated paper 3, moreover it is possible to play firm effect, and the energy of glue 4 being filled between corrugated paper 3 and boxboard 1
Enough increase the firmness between boxboard 1 and corrugated paper 3, improve the overall intensity of corrugated board.
Embodiment 3：
Filler inside corrugated paper can play good reinforcement effect to corrugated paper, there is provided buffer effect, not only
Can also so dehumidifying be carried out to the space inside corrugated paper, the using effect of the corrugated paper after dehumidifying is more obvious；
For the buffer fillings agent in corrugated layer in high-strength corrugated board, it is prepared from the following components；ABS plastic
80 parts of grain, 1 part of lapis lazuli powder, 1 part of halogen-free flameproof synergist, 1.5 parts of EP rubbers, 0.2 part of lubricant, 0.1 part of antioxidant, draw
Send out 1 part of agent, 0.2 part of graphitic lubricant, 5 parts of polypropylene short fiber, 0.5 part of dimethicone, 5 parts of Vinylidene Chloride, sodium metasilicate 1.5
Part, 1 part of Stiffening agent, 0.5 part of talcum powder, 0.5 part of surfactant, 3 parts of cryolite powder；
Above-mentioned ABS plastic particle passes through modification before use, mixes ABS plastic particle with glycerine during processing, sweet
Oily usage amount is the 1/5 of ABS plastic granular mass；
The lapis lazuli powder passes through microwave treatment before use, using 400MHz frequency processing 18S；
The cryolite powder passes through microwave treatment before use, using 400MHz frequency processing 18S；
The dimethicone passes through heating treatment, and dimethicone is warming up into 100 DEG C in flask, and then constant temperature is protected
Deposit 5 minutes, after to be cooled to normal temperature stand-by；
Embodiment 4：
Filler inside corrugated paper can play good reinforcement effect to corrugated paper, there is provided buffer effect, not only
Can also so dehumidifying be carried out to the space inside corrugated paper, the using effect of the corrugated paper after dehumidifying is more obvious；
For the buffer fillings agent in corrugated layer in high-strength corrugated board, it is prepared from the following components；ABS plastic
Grain 90 parts, 1.5 parts of lapis lazuli powder, 1.5 parts of halogen-free flameproof synergist, 2 parts of EP rubbers, 0.5 part of lubricant, 0.3 part of antioxidant,
1.5 parts of initiator, 0.3 part of graphitic lubricant, 8 parts of polypropylene short fiber, 0.5 part of dimethicone, 5 parts of Vinylidene Chloride, sodium metasilicate 3
Part, 2 parts of Stiffening agent, 1 part of talcum powder, 0.5 part of surfactant, 5 parts of cryolite powder.
Above-mentioned ABS plastic particle passes through modification before use, mixes ABS plastic particle with glycerine during processing, sweet
Oily usage amount is the 1/5 of ABS plastic granular mass；
The lapis lazuli powder passes through microwave treatment before use, using 400MHz frequency processing 20S；
The cryolite powder passes through microwave treatment before use, using 400MHz frequency processing 20S；
The dimethicone passes through heating treatment, and dimethicone is warming up into 110 DEG C in flask, and then constant temperature is protected
Deposit 5 minutes, after to be cooled to normal temperature stand-by；
Embodiment 5：
Filler inside corrugated paper can play good reinforcement effect to corrugated paper, there is provided buffer effect, not only
Can also so dehumidifying be carried out to the space inside corrugated paper, the using effect of the corrugated paper after dehumidifying is more obvious；
For the buffer fillings agent in corrugated layer in high-strength corrugated board, it is prepared from the following components；ABS plastic
00 part of grain, 1.5 parts of lapis lazuli powder, 2 parts of halogen-free flameproof synergist, 3 parts of EP rubbers, 1 part of lubricant, 0.5 part of antioxidant, initiation
2 parts of agent, 0.4 part of graphitic lubricant, 10 parts of polypropylene short fiber, 1 part of dimethicone, 8 parts of Vinylidene Chloride, 3 parts of sodium metasilicate, increasing are firm
2 parts of agent, 1 part of talcum powder, 1 part of surfactant, 5 parts of cryolite powder.
Above-mentioned ABS plastic particle passes through modification before use, mixes ABS plastic particle with glycerine during processing, sweet
Oily usage amount is the 1/5 of ABS plastic granular mass；
The lapis lazuli powder passes through microwave treatment before use, using 400MHz frequency processing 25S；
The cryolite powder passes through microwave treatment before use, using 400MHz frequency processing 25S；
The dimethicone passes through heating treatment, and dimethicone is warming up into 115 DEG C in flask, and then constant temperature is protected
Deposit 5 minutes, after to be cooled to normal temperature stand-by；
Filler is prepared respectively using embodiment 3-5 method, then carries out corrugated paper in conjunction with embodiment 1-2 mechanism
The processing of plate, the corrugated board then processed respectively to the filler prepared using embodiment 3-5 carry out performance detection, inspection
It is as follows to survey result：
The present invention is can be seen that by upper table experimental contrast analysis to prepare in high-strength corrugated board in corrugated layer
Buffer fillings agent can play good reinforcement effect to corrugated paper, there is provided buffer effect, moreover can also be in corrugated paper
The space in portion carries out dehumidifying, and the using effect of the corrugated paper after dehumidifying is more obvious.
The general principle and principal character and advantages of the present invention of the present invention has been shown and described above.The technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the simply explanation described in above-described embodiment and specification is originally
The principle of invention, without departing from the spirit and scope of the present invention, various changes and modifications of the present invention are possible, these changes
Change and improvement all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appended claims and its
Equivalent thereof.
Claims (7)
1. for the buffer fillings agent in corrugated layer in high-strength corrugated board, it is characterised in that：By the component of following mass parts
It is prepared；80~100 parts of ABS plastic particle, 1~1.5 part of lapis lazuli powder, 1~2 part of halogen-free flameproof synergist, EP rubbers
1.5~3 parts, 0.2~1 part of lubricant, 0.1~0.5 part of antioxidant, 1~2 part of initiator, 0.2~0.4 part of graphitic lubricant, third
5~10 parts of synthetic fibre chopped fiber, 0.5~1 part of dimethicone, 5~8 parts of Vinylidene Chloride, 1.5~3 parts of sodium metasilicate, Stiffening agent 1~2
Part, 0.5~1 part of talcum powder, 0.5~1 part of surfactant, 3~5 parts of cryolite powder.
2. the buffer fillings agent according to claim 1 being used in high-strength corrugated board in corrugated layer, it is characterised in that：
Each component mass fraction is：80~90 parts of ABS plastic particle, 1~1.5 part of lapis lazuli powder, 1~2 part of halogen-free flameproof synergist, second
Third 1.5~2 parts of rubber, 0.2~1 part of lubricant, 0.1~0.5 part of antioxidant, 1~2 part of initiator, graphitic lubricant 0.2~
0.4 part, 5~8 parts of polypropylene short fiber, 0.5~1 part of dimethicone, 5~8 parts of Vinylidene Chloride, 1.5~3 parts of sodium metasilicate, increase it is firm
1~2 part of agent, 0.5~1 part of talcum powder, 0.5~1 part of surfactant, 3~4 parts of cryolite powder.
3. the buffer fillings agent according to claim 1 being used in high-strength corrugated board in corrugated layer, it is characterised in that：
Each component mass fraction is：90 parts of ABS plastic particle, 1.5 parts of lapis lazuli powder, 1.5 parts of halogen-free flameproof synergist, EP rubbers 2
Part, 0.5 part of lubricant, 0.3 part of antioxidant, 1.5 parts of initiator, 0.3 part of graphitic lubricant, 8 parts of polypropylene short fiber, dimethyl-silicon
0.5 part of oil, 5 parts of Vinylidene Chloride, 3 parts of sodium metasilicate, 2 parts of Stiffening agent, 1 part of talcum powder, 0.5 part of surfactant, cryolite powder 5
Part.
4. the buffer fillings agent according to claim 1 being used in high-strength corrugated board in corrugated layer, it is characterised in that：
The ABS plastic particle passes through modification before use, mixes ABS plastic particle with glycerine during processing, glycerine usage amount
For the 1/5 of ABS plastic granular mass.
5. the buffer fillings agent according to claim 1 being used in high-strength corrugated board in corrugated layer, it is characterised in that：
The lapis lazuli powder passes through microwave treatment before use, using 400MHz frequency processing 18-25S.
6. the buffer fillings agent according to claim 1 being used in high-strength corrugated board in corrugated layer, it is characterised in that：
The cryolite powder passes through microwave treatment before use, using 400MHz frequency processing 18-25S.
7. the buffer fillings agent according to claim 1 being used in high-strength corrugated board in corrugated layer, it is characterised in that：
The dimethicone passes through heating treatment, and dimethicone is warming up into 100-115 DEG C in flask, and then constant temperature preserves 5
Minute, after to be cooled to normal temperature stand-by.